CN1226530A - 一种锂渣混凝土 - Google Patents

一种锂渣混凝土 Download PDF

Info

Publication number
CN1226530A
CN1226530A CN99114694A CN99114694A CN1226530A CN 1226530 A CN1226530 A CN 1226530A CN 99114694 A CN99114694 A CN 99114694A CN 99114694 A CN99114694 A CN 99114694A CN 1226530 A CN1226530 A CN 1226530A
Authority
CN
China
Prior art keywords
concrete
lithium
lithium slag
mix
incorporation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN99114694A
Other languages
English (en)
Inventor
胡平
张文权
刘成基
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN99114694A priority Critical patent/CN1226530A/zh
Publication of CN1226530A publication Critical patent/CN1226530A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种锂渣混凝土,该混凝土是在浇筑时,将锂渣作为掺合料掺入其中,其锂渣既可以单独掺入,又可以与粉煤灰联合掺入。该锂渣混凝土不仅使锂渣变废为宝,而且提高了砼的强度,明显改善了砼的抗冲磨、耐久性能等技术指标。同时还节约了水泥,降低了工程造价,有较好的经济效益和社会效益。

Description

一种锂渣混凝土
本发明涉及一种建筑上所用的混凝土。
锂渣是利用锂辉石经1200℃煅烧生产碳酸锂时产生的废渣。每生产1吨碳酸锂将排出8～10吨锂渣。于是，大量的锂渣堆积如山，不但占地而且对环境造成严重的污染。然而锂渣中又含有较多的无定形二氧化硅、三氧化二铝，具有较高的火山灰活性。其价格又十分低廉。因此锂渣具有很好的使用价值和开发价值。
本发明的目的在于提供一种利用锂渣作为掺合料来配制砼。从而达到提高砼的强度，生产高性能砼；并同时达到节约水泥，降低工程造价的目的。
本发明的目的是这样来实现的：根据工程设计的技术指标的要求，锂渣既可以单独掺入，又可以与粉煤灰联合掺入。单独掺入时，锂渣的掺入量占砼胶凝材料总量的15～40％。与粉煤灰联掺时，锂渣的掺入量占砼胶凝材料总量的10～20％，粉煤灰的掺入量为15～25％。
本发明所用的锂渣应达到如下技术指标：细度为0.045mm方孔筛筛余量≤20％；烧失量不超过10％；需水比不超过110％；SO3含量不超过6％。
本发明在砼中掺入锂渣以后，由于锂渣含有较多的具有较高活性的无定形SiO2、Al2O3等，易与水泥水化产生的Ca(OH)2反应产生稳定的硅酸钙水化物凝胶和水化铝酸钙。由于消耗Ca(OH)2使水泥的水化反应更加充分，同时也使Ca(OH)2的晶体粒细化，有利于混凝土界面的粘结。其二锂渣含有SO4 2-、AeO2-和Ca2+等离子，要与水泥熟料中C3A化合生成水化硫铝酸钙。这些地水化硫铝酸钙会充填于水泥石的毛细孔与气孔中，并能与纤维状的C-S-H凝胶微晶交织成网络状，使水泥的结构更加致密。同时水化硫铝酸钙具有微膨胀性，它能有效地补偿混凝土温度应力应变，防止收缩变形裂缝产生。克服一般混凝土，特别是大体积混凝土的各种缺陷。其三混凝土中掺入锂渣后，其抗冲磨强度高达0.6916～1.6293h/kg/m2，可在水工建筑物及公路路面混凝土等广泛应用。
下面结合实施例对本发明作进一步叙述：
实施例1在浇筑坝体砼时，将符合技术指标的锂渣按砼胶凝料材总量的20％掺入，同时掺入20％的江油粉煤灰。
实施例2在浇筑厂房砼时，将符合技术指标的锂渣按砼总胶凝材料总量的15％掺入，同时掺入25％的江油粉煤灰。
实施例3在浇注抗冲磨砼时，将符合技术指标的锂渣按砼胶凝材料总量的15％单独掺入，也可以在掺入10％的锂渣以后，再掺入10％的江油粉煤灰。
综上所述，锂渣掺入混凝土以后，对混凝土的强度、应力应变、干缩变形、抗渗抗冻等各种性能均有明显改善，其锂渣凝可在工业与民用建筑、交通、水泥制品行业中广泛推广。

Claims (2)

1、一种锂渣混凝土，其特征是在浇筑混凝土时在拌合过程中掺入锂渣，其锂渣既可以单独掺入，又可以与粉煤灰联掺；单独掺入时，锂渣的掺入量占砼胶凝材料总重量的15～40％；联掺时，锂渣的掺入量占砼胶凝材料总重量的15～20％，粉煤灰的掺入量为15～25％。
2、根据权利要求1所述的锂渣混凝土，其特征是所掺入的锂渣其细度为0.045mm方孔筛筛余量≤20％；烧失量不超10％；需水比不超过110％；SO3含量不超过6％。
CN99114694A 1999-03-05 1999-03-05 一种锂渣混凝土 Pending CN1226530A (zh)