CN1200411A - 冷成形钢 - Google Patents
冷成形钢 Download PDFInfo
- Publication number
- CN1200411A CN1200411A CN98106194A CN98106194A CN1200411A CN 1200411 A CN1200411 A CN 1200411A CN 98106194 A CN98106194 A CN 98106194A CN 98106194 A CN98106194 A CN 98106194A CN 1200411 A CN1200411 A CN 1200411A
- Authority
- CN
- China
- Prior art keywords
- steel
- ppm
- weight
- cold
- cold forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
提出了一种适合用于冷成形及经合金熔化及精炼而得到的钢,其特征在于此合金成分(重量%)如下:C0.80—1.50%,Mn< 1%,Si< 1%,P≤0.030%,S≤0.005%,Cr6.25—9%,Ni< 0.50%,Mo1.0—3%,Al< 0.15%,V0.20—0.40%,Nb0.60—1.5%,N< 150ppm,O< 50ppm,Ti或Zr500—1500ppm,余为Fe及生产此金属时特有的杂质。
Description
本发明涉及一种冷成形用的，并提供优良耐磨性的钢。
这种钢是通过将钢熔化和精炼而得到的，其特征在于该合金的成分(重量％)如下：
优选范围 宽的范围
C 1-1.20％ 0.80-1.50％
Mn 0.30-0.50％ ＜1％
Si 0.80-1％ ＜1％
P ≤0.020％ ≤0.030％
S ≤0.005％ ≤0.005％
Cr 8-8.50％ 6.25-9％
Ni ＜0.30％ ＜0.50％
Mo 2-2.30％ 1.80-3％
Al ＜200ppm ＜0.15％
V 0.20-0.40％ 0.20-0.40％
Nb 0.60-0.90％ 0.60-1.5％
N ＜130ppm ＜150ppm
O ＜30ppm ＜50ppmTi或Zr 500-1000ppm 500-1500ppm其余为Fe及生产此金属时特有的杂质。
此钢是经电熔化，接着在加热的钢包中精炼，真空脱气及重熔过程而加工成的。
在此钢中，C和Nb形成铌的碳化物，而Ti或Zr便于获得自形的铌的碳化物。形成铌的碳化物的化学计算关系是约1％的Nb对0.12％的C。过量的C被钢中的Cr、Mo和V含量平衡。
本发明的钢的硬度大于60Hrc。它显示出以下性能的组合：耐磨性、机加工性和以前从来得到过的韧性。
通过按Charpy测试法测定韧性。在1050℃下处理7×10×55mm参考试样、止于油中，接着是2小时、560℃的退火。就超过或等于60Hrc的硬度而言，它显示出等于或大于40焦耳的断裂功。
本发明的冷成形钢改善了耐磨性，它包括以下三种形式：
—明显改善的磨耗。
—由于该钢优良的韧性而明显改善的去皮损耗，
—也明显改善的粘附损耗。
本发明不只限于所述的和所述的实施方案，而覆盖所有可能的变化。
Claims (2)
1、一种用于冷成形及经合金熔化及精炼而得到的钢，其特征在于此合金的成分(重量％)如下：
C 0.80-1.50％
Mn ＜1％
Si ＜1％
P ≤0.030％
S ≤0.005％
Cr 6.25-9％
Ni ＜0.50％
Mo 1.80-3％
Al ＜0.15％
V 0.20-0.40％
Nb 0.60-1.5％
N ＜150ppm
O ＜50ppmTi或Zr 500-1500ppm余为Fe及生产此金属时特有的杂质。
2、权利要求1的钢，其特征在于该合金成分(重量％)如下：
C 1-1.20％
Mn 0.30-0.50％
Si 0.80-1％
P ≤0.020％
S ≤0.005％
Cr 8-8.50％
Ni ＜0.30％
Mo 2-2.30％
Al ＜200ppm
V 0.20-0.40％
Nb 0.60-0.90％
N ＜130ppm
O ＜30ppmTi或Zr 500-1000ppm余为Fe和生产此金属时特有的杂质。