CN104532165A - 一种改良型冷轧辊 - Google Patents
一种改良型冷轧辊 Download PDFInfo
- Publication number
- CN104532165A CN104532165A CN201410791591.9A CN201410791591A CN104532165A CN 104532165 A CN104532165 A CN 104532165A CN 201410791591 A CN201410791591 A CN 201410791591A CN 104532165 A CN104532165 A CN 104532165A
- Authority
- CN
- China
- Prior art keywords
- roll
- cooling
- temperature
- heating
- cold roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (5)