CN118139748A - 铅笔或化妆料的轴体 - Google Patents
铅笔或化妆料的轴体 Download PDFInfo
- Publication number
- CN118139748A CN118139748A CN202280068114.2A CN202280068114A CN118139748A CN 118139748 A CN118139748 A CN 118139748A CN 202280068114 A CN202280068114 A CN 202280068114A CN 118139748 A CN118139748 A CN 118139748A
- Authority
- CN
- China
- Prior art keywords
- pencil
- shaft
- cosmetic
- shaft body
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
提供：具有与现有的木轴同样的易切削性、对环境的负荷少的铅笔芯(包含色铅笔芯)的轴体、或、眼线、眉笔、眼影等棒状化妆料等化妆料的轴体等。本公开的铅笔或化妆料的轴体的特征在于，其为由轴体材料组合物覆盖铅笔芯或棒状化妆料而成的铅笔或化妆料的轴体，前述轴体材料组合物至少含有自然来源的体质材料和自然来源的粘合材料。
Description
技术领域
本说明书涉及：具有与现有的木轴同样的易切削性、耐落下性、耐水性、对环境的负荷少、能容易制造的铅笔芯或化妆料的轴体。
背景技术
以往，作为铅笔、棒状化妆料等的轴体，出于柔软、容易用刀、铅笔刀进行切削等理由，使用有给使用者提供良好的感触的天然木材、特别是美国产的红杉(redcedar)等天然木材。
然而，近年来，由于森林采伐等乱伐而逐渐减少，出于这种情况，环境破坏的问题备受关注，红杉等其获得也变得困难等，进行了替代材料的开发。
以往，作为铅笔、棒状化妆料等的轴体的替代材料的技术，例如已知有：
1)一种铅笔，其特征在于，在包含热塑性树脂、润滑剂以及石墨或者颜料的芯材的棒状外周面，沿轴向交替且连续地一体形成凸条和凹条，在该芯材的外侧，如与该芯材的凹凸面密合那样，形成包含热塑性树脂、纤维素纤维质和发泡剂的轴材，且该轴材中的纤维素纤维质的一部分以侵入状混入至芯材的棒状外周面的凹凸部(例如参照专利文献1)；
2)为了提供即使用铅笔刀切削也完全没有障碍、而且该轴的加工性优异因此能廉价地制造的铅笔，提供一种铅笔，其在轴中插通有芯，所述轴如下得到：在树脂中混合实施了磨碎处理而成的纤维素系微粉粒，将混合物通过挤出或注射成型而成型，进一步该成型体形成为铅笔的轴状而得到(例如参照专利文献2)；
3)为了提供作为代替木轴的合成轴，具有优异的刚度、切削性、耐油脂渗透性等物理特性和良好的使用感、而且废弃后容易分解、能以低热量进行燃烧、焚烧时不产生有害物质的生物降解性铅笔型化妆品用合成轴和其制造方法，提供一种中空筒状的生物降解性铅笔型化妆品用合成轴，其是将包含淀粉酯、和增强用填料的生物降解性热塑性材料作为基材并成型而得到的，所述淀粉酯是由短链酰基和长链酰基取代同一淀粉分子的反应性羟基的氢而成的(例如参照专利文献3)；
4)一种铅笔，其特征在于，其是用由热发泡性树脂形成的发泡树脂涂层覆盖木制的轴的表面而成的(例如参照专利文献4)；等。
然而，上述专利文献1～4中，现状是对环境的负荷尚较大，如果想要制造对环境的负荷少者，则存在易切削性、耐落下性、耐水性等降低等课题。
现有技术文献
专利文献
专利文献1：日本特开昭60-204399号公报(权利要求书、实施例等)
专利文献2：日本特开平6-255296号公报(权利要求书、实施例等)
专利文献3：日本特开2001-192502号公报(权利要求书、实施例等)
专利文献4：日本特开2014-19042号公报(权利要求书、实施例等)
发明内容
发明要解决的问题
本公开是针对上述现有的课题等想要消除而作出的，其目的在于，提供：具有与现有的木轴同样的易切削性、耐落下性、耐水性、对环境的负荷少、能容易制造的铅笔芯或棒状化妆料的轴体等。
用于解决问题的方案
本公开人等针对上述现有的课题进行了深入研究，结果发现：其为由轴体材料组合物覆盖铅笔芯或棒状化妆料而成的铅笔或化妆料的轴体，前述轴体材料组合物至少含有特定的体质材料和粘合材料，从而得到上述目标铅笔或化妆料的轴体，至此完成了本公开。
即，本公开的铅笔或化妆料的轴体的特征在于，其为由轴体材料组合物覆盖铅笔芯或棒状化妆料而成的铅笔或化妆料的轴体，前述轴体材料组合物至少含有自然来源的体质材料和自然来源的粘合材料。
优选前述轴体材料组合物的天然来源指数(不含水)为75％以上。
优选前述轴体材料组合物中，自然来源的粘合材料为羧甲基纤维素或其盐，或还含有使粘合材料进行酯交联的具有羧酸基的交联剂。
本公开的铅笔的特征在于，至少具备：铅笔芯、和将该铅笔芯覆盖成型而成的轴体，前述轴体为上述构成的轴体，另外，本公开的棒状化妆品的特征在于，至少具备：棒状化妆料、和将该棒状化妆料覆盖成型而成的轴体，前述轴体为上述构成的轴体。
发明的效果
根据本公开，可以提供：具有与现有的木轴同样的易切削性、耐落下性、对环境的负荷少、能容易制造的铅笔芯或化妆料的轴体、以及具备该轴体的铅笔、棒状化妆品等。
本公开的目的和效果特别是通过使用权利要求中被指出的构成要素和组合来认识且得到。上述一般的说明和后述的详细的说明这两者是示例性的和说明性的，不限制权利要求书中记载的本公开。
具体实施方式
以下，对本公开的实施方式详细进行说明。但本公开的技术的范围不限定于下述中详述的实施方式，应注意权利要求书中记载的发明和其均等物所涉及的方面。另外，本公开可以基于本说明书中公开的内容和该领域中的技术常识(包括常规技术选择、显而易见性)而实施。
本公开的铅笔或化妆料的轴体的特征在于，其为由轴体材料组合物覆盖铅笔芯或棒状化妆料而成的铅笔或化妆料的轴体，前述轴体材料组合物至少含有自然来源的体质材料和自然来源的粘合材料。
作为本公开中使用的自然来源的体质材料，可以举出由自然来源的木材等得到的木屑、木粉、粉末纤维素、或自然来源的无机粉体等。
作为可以使用的木屑，既可以使用阔叶树材来源者也可以使用针叶树材来源者，没有特别限定。本公开中使用的木屑的具体树种，可以举出杉、松、落叶松、赤松、库页冷杉、柏、山毛榉、七叶树、栎、水楢、枹栎、椴树、桦树、春榆、柳安木、异叶铁杉等。特别适合使用杉、柏边材、山毛榉、七叶树、水楢等。另外，也可以有效利用制造这些木材时产生的废弃物。进而，这些木屑可以使用至少1种(可以为1种，也可以组合2种以上，以下同样)。
对于木屑的大小，从分散性、成型性的方面等出发，期望平均粒径为10目以上，进一步从粉碎所耗费的能量成本的方面等出发，期望使用200目以下的范围内者。
作为可以使用的木粉，例如可以使用由上述木屑中示例的各树种得到的木粉、由上述木屑、废木材得到的木粉、砂粉等中的至少1种。另外，为了进一步改善分散性、成型性，作为木粉的平均粒径的上限，例如优选2000μm以下，作为下限，例如优选100μm以上，也可以为经微纤维化的纤维状者。需要说明的是，本公开中的平均粒径可以设为依据激光衍射·散射法而测得的值。
作为可以使用的粉末纤维素，优选将自然来源的植物的纤维素纤维进行微粉碎而得到的纤维素粉末，优选其平均粒径为100μm以下、优选10～50μm的范围者。作为粉末纤维素，例如可以使用通过如下方法而制造的具有恒定粒径分布的结晶性纤维素粉末：将精选纸浆进行酸水解后得到未分解残渣，将得到的未分解残渣进行纯化/干燥并粉碎/筛分，或者也可以使用商品名“KC Flock”(NIPPON PAPER INDUSTRIES CO.,LTD.制)、商品名“Ceolus”(旭化成化学株式会社制)、商品名“Avicel”(FMC公司制)等市售品。
作为可以使用的自然来源的无机粉体，可以使用滑石、碳酸钙、碳酸钙镁石(Huntite)、高岭土、绢云母、膨润土、氧化钛等中的至少1种。
作为这些无机粉体的平均粒径的上限，例如优选50μm以下，作为下限，例如优选1μm。
这些自然来源的体质材料的含量相对于轴体材料组合物总量，期望优选设为60～90质量％、进一步优选设为70～80质量％。通过使该自然来源的体质材料的含量为60质量％以上，从而成为能使用的切削性，通过设为90质量％以下，从而可以形成能使用的强度。
另外，这些自然来源的体质材料中、无机粉体所占的比例通过为60质量％以下，从而改善轴体的耐落下性，制成铅笔或化妆料的情况下，可以防止铅笔芯或棒状化妆料的内部破损。
作为本公开中使用的自然来源的粘合材料，可以使用纤维素纤维(包含纳米纤维)、甲基纤维素或其盐、羧甲基纤维素或其盐、羟甲基丙基纤维素或其盐、乙酸纤维素或其盐、藻酸钠等中的至少1种。作为上述各纤维素的盐，可以举出钠、铵、钙等。
这些粘合材料优选为水溶性，进一步从赋予耐水性的方面出发，优选为羧甲基纤维素铵。
这些自然来源的粘合材料的含量相对于轴体材料组合物总量，期望优选设为10～40质量％、进一步优选设为20～30质量％。
通过使该自然来源的粘合材料的含量为10质量％以上，从而成为能使用的强度，通过设为40质量％以下，从而可以形成能使用的切削性。
本公开中的轴体材料组合物中，除上述自然来源的体质材料、自然来源的粘合材料之外，从进一步发挥本公开的效果的方面、赋予耐水性的方面出发，可以还含有使前述粘合材料进行交联的交联剂等。
作为使前述粘合材料进行交联的交联剂，优选使粘合材料进行酯交联的具有羧酸基的交联剂，具体而言，可以举出琥珀酸、苹果酸、马来酸、酒石酸、柠檬酸、聚丙烯酸等。
对于这些交联剂的含量，相对于轴体材料组合物总量，从体现耐水性的方面、抑制吸湿所导致的强度降低的方面、抑制材料的变色的方面出发，期望优选设为0.1～5质量％、进一步优选设为0.5～2质量％。
进而，本公开的轴体材料组合物中，除上述自然来源的体质材料、自然来源的粘合材料、交联剂之外，根据需要还可以适宜含有用于使轴体着色的着色剂(染料、无机颜料、有机颜料)、氧化铁、氧化锌、炭黑、天然色素等。
对于这些轴体材料组合物，从进一步发挥本公开的效果的方面、对环境的负荷的方面出发，优选天然来源指数(不含水)为75％以上。
该“天然来源指数(不含水)”是指ISO 16128所涉及的指数表示，该天然来源指数(不含水)通过设为75％以上、进一步优选设为85％以上，从而进而变得得到对环境的负荷极其少的、铅笔芯或化妆料的轴体。
使该轴体材料组合物的天然来源指数(不含水)为75％以上时，可以适宜选择前述自然来源的体质材料、自然来源的粘合材料而实现。
本公开的铅笔或化妆料的轴体如下得到：用例如亨舍尔混合机、行星搅拌机、捏合机等混炼机等，将由上述自然来源的体质材料、天然来源的粘合材料等构成的配混组合物进行干式混合后，以水分率成为40～80％的方式，加入水(纯化水、蒸馏水等)进行混炼，得到浆料，边进一步将该浆料进行加热、脱气等边进行混炼，得到使水分率为30～60％左右的粘土状的混合物，用挤出成型机等，用规定直径的模具，在覆盖的铅笔芯、化妆料的外周覆盖上述材料并将该混合物干燥，由此可以得到铅笔、化妆料。或者，通过如下方法从而也可以得到铅笔、化妆料：用挤出成型机等，用规定直径的模具、或T模头等，将混炼物成型为圆棒或板状并干燥，从而得到成型体，制作得到的成型体，将它们加工并插入铅笔芯、化妆料。需要说明的是，根据挤出成型等时的压制压力、含水率、天然来源的体质材料和粘合材料等的组合，可以广泛控制轴体的物性，因此，得到适合于能满足要求的轴体的质感、强度、成型性等的铅笔或化妆料的轴体。
本公开中，由上述轴体材料组合物覆盖的铅笔芯的组成、形态等没有特别限定，可以举出煅烧铅笔芯(包含煅烧色铅笔芯)、非煅烧铅笔芯(包含非煅烧色铅笔芯)等。作为煅烧铅笔芯，例如可以举出使硅油、液体石蜡、轴油、角鲨烷、α-烯烃低聚物等油状物、蜡类浸渗在芯体中而得到的煅烧铅笔芯等，所述芯体如下得到：将石墨等着色成分、氯乙烯树脂、偏二氯乙烯树脂、乙酸乙烯酯树脂、氯化聚乙烯、聚乙烯醇、丙烯酰胺树脂、氯化链烷烃树脂、酚醛树脂、呋喃树脂、脲树脂、丁基橡胶等有机粘合材料、苯二甲酸酯等增塑剂、甲乙酮、水等溶剂、硬脂酸盐等稳定剂、硬脂酸等润滑剂、炭黑等填充材料等材料混合并分散、混炼，挤出成型为细线状，对得到的物质实施热处理直至煅烧温度，从而得到。
另外，由上述轴体材料组合物覆盖的棒状化妆料的组成、形态等也没有特别限定，可以举出：将眼线、眉笔、唇线、遮瑕铅笔、眼影铅笔等用途中使用的各配混组成、例如作为粘合材料的油脂、蜡、脂肪酸、烃等蜡类、粘土类与着色剂和体质材料混炼，成型为棒状而得到的化妆料等，它们可以为煅烧型的棒状化妆料、非煅烧型的棒状化妆料等，均可。
如此构成的本公开的铅笔芯或化妆料的轴体具有与现有的木轴同样的易切削性、耐落下性、耐水性，对环境的负荷少，可以无改良地使用现有的铅笔、化妆料的成型时使用的成型机等，因此，得到能容易制造的铅笔芯或化妆料的轴体。
本公开的铅笔的特征在于，至少将上述铅笔芯覆盖成型而成的轴体为上述构成的轴体，另外，本公开的棒状化妆品的特征在于，至少将上述棒状化妆料覆盖成型而成的轴体为上述构成的轴体。
本公开中，可以将铅笔芯、棒状化妆料成型为任意形状、例如截面形状为圆形(包含椭圆)、三角形、六边形等多边形形状、管形状等，因此，利用覆盖成型、切削加工等各种加工方法，可以形成各形状等的铅笔、棒状化妆品。
实施例
以下，根据实施例、比较例对本公开进行说明，但本公开不限定于这些实施例。
实施例1～8和比较例1的铅笔芯使用的是，根据下述制法得到的铅笔芯。
将石墨60质量％、粘土40质量％在混合亨舍尔混合机中进行干式混合后，以水分率成为40％的方式加入纯化水并进行混炼。边将得到的浆料进行加热、脱气边进行混炼，得到使水分率为30％左右的粘土状的混合物。用油压柱塞式挤出成型机，用直径2.5mm的模具，将其成型，将该成型体在60℃环境下干燥后，在800～1400℃下煅烧12～24小时，得到直径2.0mm的芯体。使α-烯烃低聚物浸渗于得到的芯体中，得到直径2.0mm、硬度HB的铅笔芯。
(实施例1)
碳酸钙镁石粉末(平均粒径2μm)90质量％
纤维素粉末(平均粒径45μm)10质量％
该轴体材料组合物的天然来源指数(不含水)为100.0％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为40％的方式加入纯化水并进行混炼。
边将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为30％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。
将该成型体在60℃环境下干燥，得到铅笔。
(实施例2)
杉系木材木屑(16目)70质量％
羧甲基纤维素钠30质量％
该轴体材料组合物的天然来源指数(不含水)为92.5％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入纯化水并进行混炼。边将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。将该成型体在60℃环境下干燥，得到铅笔。
(实施例3)
滑石(平均粒径8μm)40质量％
杉系木材木屑(16目)40质量％
羧甲基纤维素钠20质量％
该轴体材料组合物的天然来源指数(不含水)为95.0％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入纯化水并进行混炼。边将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。将该成型体在60℃环境下干燥，得到铅笔。
(实施例4)
滑石(平均粒径8μm)30质量％
纤维素粉末(平均粒径45μm)60质量％
羧甲基纤维素钠10质量％
该轴体材料组合物的天然来源指数(不含水)为97.5％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入纯化水并进行混炼。边将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。将该成型体在60℃环境下干燥，得到铅笔。
(实施例5)
滑石(平均粒径8μm)30质量％
纤维素粉末(平均粒径45μm)60质量％
羧甲基纤维素铵10质量％
该轴体材料组合物的天然来源指数(不含水)为97.5％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入纯化水并进行混炼。边将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。将该成型体在60℃环境下干燥，在180℃下加热使粘合材料非水溶化，得到铅笔。
(实施例6)
滑石(平均粒径8μm)30质量％
纤维素粉末(平均粒径45μm)60质量％
羧甲基纤维素钠10质量％
该轴体材料组合物的天然来源指数(不含水)为97.5％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入5％琥珀酸水溶液并进行混炼。边将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。该该成型体在60℃环境下进行干燥后，在180℃下加热使粘合材料交联，得到铅笔。
(实施例7)
滑石(平均粒径8μm)30质量％
纤维素粉末(平均粒径45μm)60质量％
甲基纤维素10质量％
该轴体材料组合物的天然来源指数(不含水)为97.5％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入纯化水并进行混炼。边将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。将该成型体在60℃环境下干燥，得到铅笔。
(实施例8)
滑石(平均粒径8μm)30质量％
纤维素粉末(平均粒径45μm)60质量％
甲基纤维素10质量％
该轴体材料组合物的天然来源指数(不含水)97.5％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入5％琥珀酸水溶液并进行混炼。将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，在直径2.0mm、硬度HB的铅笔芯外周覆盖材料。该该成型体在60℃环境下进行干燥后，在180℃下加热使粘合材料交联，得到铅笔。
(实施例9)
〈固体化妆料的制备〉
使上述配混材料溶解，在其中加入铁黑10份和氧化铁红19份(总量100份)，搅拌、分散后，在混合机中混炼，利用冷却至室温的挤出成型机得到2.0mm的褐色的固体化妆料。
滑石(平均粒径8μm)30质量％
纤维素粉末(平均粒径45μm)60质量％
甲基纤维素10质量％
上述的轴体材料组合物的天然来源指数(不含水)97.5％。
将上述配混组合物在亨舍尔混合机中进行干式混合后，以水分率成为50％的方式加入纯化水并进行混炼。将该得到的浆料进行加热、脱气边进行混炼，得到使水分率为40％左右的粘土状的混合物。将其用油压柱塞式挤出成型机，用直径9.0mm的模具，覆盖上述直径2.0mm的固体化妆料。将该成型体在60℃环境下干燥，得到棒状化妆品。
(比较例1)
铅笔(对实施了重量比2％的石蜡浸渗处理的翠柏板材进行切削加工，覆盖上述直径2.0mm、硬度HB的铅笔芯的铅笔)
(比较例2)
为使用了公知的再生天然原料的铅笔，使用热塑性树脂作为粘合材料，因此，使用非自然来源的原料。由下述组成构成，天然来源指数为70.0％。
聚丙烯(PP)20质量％
木粉70质量％
马来酸酐经接枝而得到的聚丙烯1质量％
酰胺蜡3质量％
硬脂酸1质量％
氮化硼5质量％
对于上述中得到的实施例1～9和比较例1～2的铅笔，根据天然来源指数、下述评价方法，对易切削性进行评价。
将这些结果示于下述表1。
(天然来源指数)
实施例1～9和比较例1～2的轴体的天然来源指数(不含水)如下求出：根据除芯之外的轴材中配混的原料的重量比，ISO 16128中定义的、用自然原料和自然来源的原料中的自然来源的部分的不含水的重量，用百分率算出组成比，从而求出。该值越高，动物、植物来源的材料比率越高，石油来源的材料的用量越少，因此，可以表示对环境的负荷越小。
(易切削性的评价方法)
对于实施例1～9和比较例1～2的铅笔，利用铅笔刀，将前端调整为直径2mm后，使用连接于旋转力矩测定装置的固定治具上设置的铅笔刀，用手旋转与铅笔刀为相反侧，进行切削直至芯变尖。测定此期间的旋转力矩的峰值，以下述评价基准设为易切削性(切削性)的评价。该值如果低于0.1N则能容易地切削，如果超过0.2N·m则可以说硬而难以切削。
评价基准：
○：容易切削(低于0.1N·m)
△：切削(0.1N·m以上且低于0.2N·m)
×：不易切削(0.2N·m以上)
[表1]
| 非自然来源的原料 | 天然来源指数 | 易切削性 | |
| 实施例1 | 无 | 100.0％ | ○ |
| 实施例2 | 无 | 92.5％ | △ |
| 实施例3 | 无 | 95.0％ | △ |
| 实施例4 | 无 | 97.5％ | ○ |
| 实施例5 | 无 | 97.5％ | ○ |
| 实施例6 | 无 | 97.5％ | ○ |
| 实施例7 | 无 | 97.5％ | ○ |
| 实施例8 | 无 | 97.5％ | ○ |
| 实施例9 | 无 | 97.5％ | ○ |
| 比较例1 | 无 | 97.9％ | ○ |
| 比较例2 | 有 | 70.0％ | △ |
如果考察上述表1的评价结果，则可以确认：为本公开的范围内的实施例1～9具有与现有的比较例1、2同样的易切削性，且对环境的负荷少、能容易制造。另外，实施例2～9中，维持高的天然来源指数，且使体质材料中的无机粉体比率为60％以下，从而进行10次自75cm的高度向混凝土地板的自由落下并进行评价时，铅笔或化妆料主体、和铅笔芯或棒状化妆料中未见破损，确认了具有充分的耐落下性。进而，实施例5、6、8中的使用羧甲基纤维素铵作为自然来源的粘合材料，从而实现非水溶化、或利用具有酯交联的羧酸基的交联剂进行交联而成者中，评价了耐水性(使制造好的铅笔浸渍于纯化水中24小时后的耐水性)，结果确认到未崩解，确认了可以发挥充分的耐水性。
产业上的可利用性
得到适合于铅笔芯(包含色铅笔芯)、眼线、眉笔、眼影等棒状化妆料等的铅笔或化妆料的轴体等。
Claims (6)
1.一种铅笔或化妆料的轴体，其特征在于，其为由轴体材料组合物覆盖铅笔芯或棒状化妆料而成的铅笔或化妆料的轴体，所述轴体材料组合物至少含有自然来源的体质材料和自然来源的粘合材料。
2.根据权利要求1所述的铅笔或化妆料的轴体，其特征在于，所述轴体材料组合物的天然来源指数(不含水)为75％以上。
3.根据权利要求1或2所述的铅笔或化妆料的轴体，其特征在于，所述自然来源的粘合材料为羧甲基纤维素或其盐。
4.根据权利要求1或2所述的铅笔或化妆料的轴体，其特征在于，所述轴体材料组合物中，还含有使粘合材料进行酯交联的具有羧酸基的交联剂。
5.一种铅笔，其特征在于，至少具备：铅笔芯、和将该铅笔芯覆盖成型而成的轴体，所述轴体为权利要求1或2所述的轴体。
6.一种棒状化妆品，其至少具备：棒状化妆料、和将该棒状化妆料覆盖成型而成的轴体，所述轴体为权利要求1或2所述的轴体。