CN1180080A - 永久性丙纶抗静电母粒 - Google Patents

永久性丙纶抗静电母粒 Download PDF

Info

Publication number
CN1180080A
CN1180080A CN 97105683 CN97105683A CN1180080A CN 1180080 A CN1180080 A CN 1180080A CN 97105683 CN97105683 CN 97105683 CN 97105683 A CN97105683 A CN 97105683A CN 1180080 A CN1180080 A CN 1180080A
Authority
CN
China
Prior art keywords
polypropylene
master granule
antistatic master
perpetural
polypropylene fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 97105683
Other languages
English (en)
Inventor
徐法欣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGDONG PROV INST OF CHEMICAL FIBRE
Original Assignee
SHANGDONG PROV INST OF CHEMICAL FIBRE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGDONG PROV INST OF CHEMICAL FIBRE filed Critical SHANGDONG PROV INST OF CHEMICAL FIBRE
Priority to CN 97105683 priority Critical patent/CN1180080A/zh
Publication of CN1180080A publication Critical patent/CN1180080A/zh
Pending legal-status Critical Current

Abstract

本发明涉及聚丙烯均聚物的技术。这种永久性丙纶抗静电母粒,包括聚丙烯,羟乙基烷基胺,且其按重量百分比为聚丙烯60—90%,羟乙基烷基胺10—40%。该抗静电母粒添加后纺丝熔体的流变性变好,纺丝工艺易于掌握,抗静电效果好,纺丝温度低,节能。且在造粒时还可与抗老化剂、抗氧化剂、抗紫外线吸收剂等混合后造粒。

Description

永久性丙纶抗静电母粒
本发明属于聚丙烯均聚物的技术领域。
聚丙烯具有芯吸效应，导湿性强，质轻抗腐蚀，在工业和装饰领域获得了广泛应用。但由于聚丙烯结构规整，不含极性基因，吸湿性差。特别严重的是它的体积比电阻很高。达M×1016Ω·cm，因此轻轻摩擦就会产生严重的静电，使得纺织，织造产生一系列生产障碍，梳棉破网，缠辊，并条相互排斥等。严重影响了聚丙烯纤维在纺织行业和衣着领域的应用，而且织物带静电，极易被污染，污物紧粘，从而导致商品价值暴跌，而静电放电导致的灾害事故也是不容忽视的。日本国专利昭63-113053登载了以无规聚丙烯树脂、聚丙烯树脂以及防静电干扰剂制得防静电干扰粉末的技术，它虽能掺入聚丙烯中起到抗静电的作用，但它只能用于混炼造粒，模压成形等方面，而不能用于混入切片用常规方法纺丝，从而极大的限制了它的应用范围。只起一种抗静电剂的作用。而采用添加共混法制备永久抗静电性丙纶纤维，必须解决加入的抗静电剂对聚丙烯可纺性的影响，对纤维结构的影响，对织物物理化学性能的影响，还必须考虑纺丝工艺。
本发明的目的是提供一种可直接添加到聚丙烯中，按常规方法即可制得具有永久性抗静电性的丙纶纤维的抗静电母粒。
这种永久性丙纶抗静电母粒，包括聚丙烯，羟乙基烷基胺，且其按重量百分比为聚丙烯60-90％，羟乙基烷基胺10-40％。
该抗静电母粒的熔融指数很高，添加后纺丝熔体的流变性变好，纺丝工艺易于掌握，纺丝时温度较通常低5-10℃，降低了纺丝机的功耗，起到节能的作用。且在造粒时，可视需要与抗氧化剂，抗老化剂，抗紫外线吸收剂等添加剂混合后造粒。现有的抗静电剂熔点低，直接用于纺丝时添加，会造成不进料，无法纺丝。而将该种母粒直接添加到聚丙烯中，即可用普通螺杆纺丝机纺出纤维。
本发明的抗静电母粒的制造方法没有特别的限制，将抗静电剂羟乙基烷基胺和聚丙烯在高速混料机内混合均匀后，用普通双螺杆挤出造粒机即可加工出来。即用众所周知的手段进行。
下面结合实施例对本发明作详细叙述。
其实施例如表1所示：
表1
Figure A9710568300041
在高速混料机中按表1中的重量百分比加入羟乙基烷基胺羟乙基烷基胺为特征值是30-40％的粉末状羟乙基烷基胺，和聚丙烯粉料，聚丙烯为熔融指数为MZ＝10-30的粉状聚丙烯，混合均匀后，经双螺杆挤出造粒机加工成直径φ＝2-5mm，长L＝2-5mm的粒状物。且本发明抗静电剂在丙纶纤维中的添加量低，在丙纶纤维中含量低于2％，从比较例可以看出，其抗静电效果显著，使用方便。
表2
Figure A9710568300051
在同一纺丝设备，同一熔体压力下，纺制相同规格的抗静电丙纶纤维，添加抗静电母粒后纺丝时节能效果如表三所示：
表3
在制造抗静电母粒时，随着抗静电剂含量的增大，双螺杆挤出机的温度略为下降。因此节能，但当抗静电剂含量高于40％时，挤出会不成条，难以生产。

Claims (3)

1、一种永久性丙纶抗静电母粒，包括聚丙烯，其特征是还包括羟乙基烷基胺，且其按重量百分比为聚丙烯60-90％，羟乙基烷基胺10-40％。
2、根据权利要求1所述的永久性丙纶抗静电母粒，其特征是聚丙烯为熔融指数为MZ＝10-30的粉状聚丙烯。
3、根据权利要求1所述的永久性丙给抗静电母粒，其特征是羟乙基烷基胺为特征值是30-40％的粉末状羟乙基烷基胺。
CN 97105683 1997-01-30 1997-01-30 永久性丙纶抗静电母粒 Pending CN1180080A (zh)