CN117924555A - 一种催化剂组分、催化剂体系及其应用和烯烃聚合方法 - Google Patents
一种催化剂组分、催化剂体系及其应用和烯烃聚合方法 Download PDFInfo
- Publication number
- CN117924555A CN117924555A CN202211313727.6A CN202211313727A CN117924555A CN 117924555 A CN117924555 A CN 117924555A CN 202211313727 A CN202211313727 A CN 202211313727A CN 117924555 A CN117924555 A CN 117924555A
- Authority
- CN
- China
- Prior art keywords
- compound
- catalyst component
- formula
- alkyl group
- branched
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种催化剂组分、催化剂体系及其应用和烯烃聚合方法,涉及烯烃聚合技术领域。该催化剂组分包含卤化镁加合物、钛化合物和任选的至少一种给电子体化合物的反应产物,该卤化镁加合物的通式为:MgX1Y‑mR1OH‑n(LB1)‑k(LB2)‑p(LB3)‑q(LB4),其中,LB1为式(II)所示的烃氧基苯甲酸酯系化合物,LB2为式(III)所示的羟基苯甲酸酯系化合物,LB3为R6OH,LB4为钛酸酯化合物。由该催化剂组分形成的催化剂体系在用于烯烃聚合时,在高氢浓度条件下显示出更强的定向能力,制备的聚合物树脂等规指数更高,同时所得聚合物的颗粒形态好,球形度更高。
Description
技术领域
本发明涉及烯烃聚合技术领域,具体而言,涉及一种催化剂组分、催化剂体系及其应用和烯烃聚合方法。
背景技术
将钛化合物及给电子体化合物负载于活性卤化镁上以制备Ziegler-Natta催化剂是现有技术所公知的。其中,所述的活性卤化镁经常采用卤化镁与醇的加合物,将其作为载体与卤化钛和给电子体化合物反应后得到球形催化剂,所述球形催化剂在用于烯烃(特别是丙烯)聚合时,具有较高的聚合活性和立体定向能力,所得聚合物也具有较好的颗粒形态和较高的表观密度。
已公开的卤化镁·醇加合物大多是氯化镁的醇合物,通常包括氯化镁和醇二元组分。其中,有些已公开的氯化镁与醇的加合物还含有少量的水。为了改善以卤化镁加合物为载体的烯烃聚合催化剂的聚合性能,研究人员开始尝试将除醇和水外的其它给电子体化合物引入到卤化镁与醇的加合物制备过程中。
CN1169840C和CN1286863C公开了一种“氯化镁-醇-邻苯二甲酸酯”球形氯化镁加合物,但是,以该加合物与四氯化钛反应形成的催化剂在用于丙烯聚合时聚合活性低且氢调敏感性差。CN103073661B合成的含有脂肪环醚的多组分醇镁加合物载体,在保持催化剂的聚合活性、定向能力等聚合性能不受损的情况下,有效改善了催化剂的形态稳定性;CN102796131B和CN105622423B既解决了多组分载体易发黏的问题,同时在催化剂的定向能力、氢调敏感性和聚合活性等方面也得到了有效的改善和提高。但是随着加氢量的提升,现有专利技术催化剂的定向能力通常有较为明显的降低,这对于高流动高刚聚丙烯树脂的生产来说,是需要进一步改进提升的。
发明内容
为解决现有技术中随着加氢量的提升,烯烃聚合催化剂的定向能力通常有较为明显降低的技术问题,本发明的目的之一在于提供一种催化剂组分,该催化剂组分用于烯烃聚合时,在高氢浓度条件下显示出更强的立体定向能力,制备的聚合物树脂的等规指数更高,同时聚合物的颗粒形态好,球形度更高。
本发明的目的之二在于提供一种催化剂体系。
本发明的目的之三在于提供一种与目的之一和目的之二相对应的催化剂组分和催化剂体系在烯烃聚合领域中的应用。
本发明的目的之四在于提供一种与上述目的相对应的烯烃聚合方法。
为实现上述目的之一,本发明采取的技术方案如下:
一种催化剂组分,该催化剂组分包含卤化镁加合物、钛化合物和任选的至少一种给电子体化合物的反应产物;
所述卤化镁加合物如式(I)所示,
MgX1Y-mR1OH-n(LB1)-k(LB2)-p(LB3)-q(LB4) 式(I)
式(I)中,X1为氯或溴;Y为氯、溴、C1-C14的直链烷基、C3-C14的支链烷基、C6-C14的芳基、C1-C14的直链烷氧基、C3-C14的支链烷氧基和C6-C14的芳氧基中的任意一种;
LB1为式(II)所示的烃氧基苯甲酸酯系化合物,
LB2为式(III)所示的羟基苯甲酸酯系化合物,
LB3为式(IV)所示的醇,
R6OH 式(IV)
LB4为式(V)所示的钛酸酯化合物,
(R1′O)a(R2′O)b(R3′O)cTiZd 式(V)
R1为C1-C12的直链烷基、C3-C12的支链烷基、C3-C10的环烷基和C7-C10的芳烷基中的任意一种;
R2、R3、R4和R5各自为氢、卤素、硝基、C1-C20的直链烷基、C3-C20的支链烷基、C3-C20的环烷基、C6-C20的芳基和C7-C20的芳烷基中的任意一种;R2、R3、R4和R5中的两个或两个以上任选地相互键合,以形成环;
R6与R1不相同,为C1-C20的直链烷基、C3-C20的支链烷基、C3-C20的环烷基、C6-C20的芳基和C7-C20的芳烷基中的任意一种;
R1′、R2′和R3′相同或不同,选自C1-C10的直链烷基或C3-C10的支链烷基;Z与Y相同或不同,为氯、溴、C1-C14的直链烷基、C3-C14的支链烷基、C6-C14的芳基、C1-C14的直链烷氧基、C3-C14的支链烷氧基和C6-C14的芳氧基中的任意一种;a、b、c和d独立为0-4的整数,且a+b+c+d=4;
m、n、k、p和q以摩尔计,分别满足以下条件:
m=1-5,
0.001≤n+k≤0.3,
0.2≤k/n≤20,
p≤k,且0.0005≤p<0.05,
q=0.001-0.1。
在本发明的一些优选实施例中,Y为氯、溴、C1-C5的直链烷基、C3-C5的支链烷基、C6-C10的芳基、C1-C5的直链烷氧基、C3-C5的支链烷氧基和C6-C10的芳氧基中的任意一种。
在本发明的一些优选实施例中,所述MgXY为一种含镁化合物或两种以上含镁化合物的混合物。
在本发明的一些优选实施例中,所述MgXY为二氯化镁、二溴化镁、氯化苯氧基镁、氯化异丙氧基镁和氯化正丁氧基镁中的一种或多种。
在本发明的一些实施例中,所述MgXY为二氯化镁。这里需要说明的是,从原料易得性的角度出发,MgXY优选为二氯化镁。
在本发明的一些优选实施例中,式(I)的R1OH中,R1为C1-C6的直链烷基、C3-C6的支链烷基。
在本发明的一些优选实施例中,式(I)的R1OH中,R1为甲基、乙基、正丙基、异丙基、正丁基、异丁基和正己基中的任意一种。
本发明中,所述R1OH的具体实例可以包括但不限于:甲醇、乙醇、正丙醇、异丙醇、正丁醇、异丁醇、正戊醇、异戊醇、正己醇、正辛醇、2-乙基己醇、乙二醇、1,3-丙二醇和苯基甲醇。
根据本发明,式(II)中,R1的定义与式(I)的R1OH中R1的定义相同,在此不再赘述。
在本发明的一些优选实施例中,R2、R3、R4和R5各自为氢、C1-C8的直链烷基、C3-C8的支链烷基、C3-C6的环烷基、C6-C10的芳基和C7-C10的芳烷基中的任意一种。
在本发明的一些优选实施例中,R2、R3、R4和R5各自为氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、异戊基、环戊基、正已基、正庚基和甲苯基中的任意一种。
在本发明的一些优选实施例中,R6与R1不相同,R6为C1-C6的直链烷基、C3-C6的支链烷基、C3-C6的环烷基、C6-C10的芳基和C7-C10的芳烷基中的任意一种。
在本发明的一些优选实施例中,R6与R1不相同,R6为甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、正已基、苄基和苯乙基中的任意一种。
在本发明的一些优选实施例中,所述LB1为4-烷氧基苯甲酸酯系化合物和/或2-烷氧基苯甲酸酯系化合物。
在本发明的一些优选实施例中,所述LB1为2-烷氧基苯甲酸酯系化合物。
这里需要说明的是,本发明中,作为LB1的烃氧基苯甲酸酯系化合物的具体实例可以包括但不限于:2-甲氧基苯甲酸甲酯、2-甲氧基苯甲酸乙酯、2-甲氧基苯甲酸正丙酯、2-甲氧基苯甲酸异丙酯、2-甲氧基苯甲酸正丁酯、2-甲氧基苯甲酸异丁酯、2-甲氧基苯甲酸正戊酯、2-甲氧基苯甲酸正己酯、2-甲氧基苯甲酸苄酯、2-甲氧基苯甲酸苯乙酯、2-甲氧基-3-甲基苯甲酸甲酯、2-甲氧基-4-甲基苯甲酸甲酯、2-甲氧基-5-甲基苯甲酸甲酯、2-甲氧基-3-乙基苯甲酸甲酯、2-甲氧基-4-乙基苯甲酸甲酯、2-甲氧基-5-乙基苯甲酸甲酯、2-甲氧基-3-甲基苯甲酸乙酯、2-甲氧基-4-甲基苯甲酸乙酯、2-甲氧基-5-甲基苯甲酸乙酯、2-甲氧基-3-乙基苯甲酸乙酯、2-甲氧基-4-乙基苯甲酸乙酯、2-甲氧基-5-乙基苯甲酸乙酯、2-甲氧基-3-甲基苯甲酸正丙酯、2-甲氧基-4-甲基苯甲酸正丙酯、2-甲氧基-5-甲基苯甲酸正丙酯、2-甲氧基-3-乙基苯甲酸正丙酯、2-甲氧基-4-乙基苯甲酸正丙酯、2-甲氧基-5-乙基苯甲酸正丙酯、2-甲氧基-3-甲基苯甲酸异丙酯、2-甲氧基-4-甲基苯甲酸异丙酯、2-甲氧基-5-甲基苯甲酸异丙酯、2-甲氧基-3-乙基苯甲酸异丙酯、2-甲氧基-4-乙基苯甲酸异丙酯、2-甲氧基-5-乙基苯甲酸异丙酯、2-甲氧基-3-甲基苯甲酸异丁酯、2-甲氧基-4-甲基苯甲酸异丁酯、2-甲氧基-5-甲基苯甲酸异丁酯、2-甲氧基-3-乙基苯甲酸异丁酯、2-甲氧基-4-乙基苯甲酸异丁酯、2-甲氧基-5-乙基苯甲酸异丁酯、2-甲氧基-3-正丙基苯甲酸乙酯、2-甲氧基-4-正丙基苯甲酸乙酯、2-甲氧基-5-正丙基苯甲酸乙酯、2-甲氧基-4-异丙基苯甲酸乙酯、2-甲氧基-4-异丁基苯甲酸乙酯、2-甲氧基-4-叔丁基苯甲酸乙酯、2-甲氧基-4-戊基苯甲酸乙酯、2-甲氧基-4-异戊基苯甲酸乙酯、2-甲氧基-4-环戊基苯甲酸乙酯、2-乙氧基苯甲酸甲酯、2-乙氧基苯甲酸乙酯、2-乙氧基苯甲酸正丙酯、2-乙氧基苯甲酸异丙酯、2-乙氧基苯甲酸正丁酯、2-乙氧基苯甲酸异丁酯、2-乙氧基苯甲酸正戊酯、2-乙氧基苯甲酸正己酯、2-乙氧基苯甲酸苄酯、2-乙氧基苯甲酸苯乙酯、2-正丁氧基苯甲酸甲酯、2-正丁氧基苯甲酸乙酯、2-正丁氧基苯甲酸正丙酯、2-正丁氧苯甲酸异丙酯、2-正丁氧基苯甲酸正丁酯、2-正丁氧基苯甲酸异丁酯、2-正丁氧基苯甲酸正戊酯、2-正丁氧基苯甲酸正己酯、2-正丁氧基苯甲酸苄酯和2-正丁氧基苯甲酸苯乙酯。
根据本发明,式(III)中,R1、R2、R3、R4和R5的定义与前文所述相同,在此不再赘述。
在本发明的一些优选实施例中,所述LB2为4-羟基苯甲酸酯系化合物和/或2-羟基苯甲酸酯系化合物。
在本发明的一些优选实施例中,所述LB2为2-羟基苯甲酸酯系化合物。
这里需要说明的是,本发明中,作为LB2的羟基苯甲酸酯系化合物的具体实例可以包括但不限于:2-羟基苯甲酸甲酯、2-羟基苯甲酸乙酯、2-羟基苯甲酸正丙酯、2-羟基苯甲酸异丙酯、2-羟基苯甲酸正丁酯、2-羟基苯甲酸异丁酯、2-羟基苯甲酸正戊酯、2-羟基苯甲酸正己酯、2-羟基苯甲酸苄酯、2-羟基苯甲酸苯乙酯、2-羟基-3-甲基苯甲酸甲酯、2-羟基-4-甲基苯甲酸甲酯、2-羟基-5-甲基苯甲酸甲酯、2-羟基-3-乙基苯甲酸甲酯、2-羟基-4-乙基苯甲酸甲酯、2-羟基-5-乙基苯甲酸甲酯、2-羟基-3-甲基苯甲酸乙酯、2-羟基-4-甲基苯甲酸乙酯、2-羟基-5-甲基苯甲酸乙酯、2-羟基-3-乙基苯甲酸乙酯、2-羟基-4-乙基苯甲酸乙酯、2-羟基-5-乙基苯甲酸乙酯、2-羟基-3-甲基苯甲酸正丙酯、2-羟基-4-甲基苯甲酸正丙酯、2-羟基-5-甲基苯甲酸正丙酯、2-羟基-3-乙基苯甲酸正丙酯、2-羟基-4-乙基苯甲酸正丙酯、2-羟基-5-乙基苯甲酸正丙酯、2-羟基-3-甲基苯甲酸异丙酯、2-羟基-4-甲基苯甲酸异丙酯、2-羟基-5-甲基苯甲酸异丙酯、2-羟基-3-乙基苯甲酸异丙酯、2-羟基-4-乙基苯甲酸异丙酯、2-羟基-5-乙基苯甲酸异丙酯、2-羟基-3-甲基苯甲酸异丁酯、2-羟基-4-甲基苯甲酸异丁酯、2-羟基-5-甲基苯甲酸异丁酯、2-羟基-3-乙基苯甲酸异丁酯、2-羟基-4-乙基苯甲酸异丁酯、2-羟基-5-乙基苯甲酸异丁酯、2-羟基-3-正丙基苯甲酸乙酯、2-羟基-4-正丙基苯甲酸乙酯、2-羟基-5-正丙基苯甲酸乙酯、2-羟基-4-异丙基苯甲酸乙酯、2-羟基-4-异丁基苯甲酸乙酯、2-羟基-4-叔丁基苯甲酸乙酯、2-羟基-4-正戊基苯甲酸乙酯、2-羟基-4-异戊基苯甲酸乙酯和2-羟基-4-环戊基苯甲酸乙酯。
根据本发明,式(IV)中,R6的定义与式(II)中R6的定义相同,在此不再赘述。
本发明中,所述LB3的具体实例可以包括但不限于:甲醇、乙醇、正丙醇、异丙醇、正丁醇、异丁醇、叔丁醇、正戊醇、异戊醇、正己醇、2-乙基己醇、苯酚和苯基乙醇。
在本发明的一些优选实施例中,所述式(V)中,R1′、R2′和R3′相同或不同,为C1-C6的直链烷基或C3-C6的支链烷基。
在本发明的一些优选实施例中,所述式(V)中,Z为氯、溴、C1-C6的直链烷氧基或C3-C6的支链烷氧基;a、b、c和d独立为0-4的整数,且a+b+c+d=4。
在本发明的一些优选实施例中,LB4为钛酸四烷基酯中的一种或多种。
本发明中,所述LB4的具体实例可以包括但不限于:钛酸四甲酯、钛酸四乙酯、钛酸四丙酯、钛酸四异丙酯、钛酸四丁酯和钛酸四异丁酯。
在本发明的一些优选实施例中,m、n、k、p和q以摩尔计,分别满足以下条件:
m=2-3.5,
0.005≤n+k≤0.15,
0.5≤k/n≤10,
p≤k,且0.001≤p≤0.04,
q=0.002-0.05。
在本发明的一些优选实施例中,m、n、k、p和q以摩尔计,分别满足以下条件:
m为2.4-3.5,
0.01≤n+k≤0.1,
1≤k/n≤6,
p≤k,且0.004≤p≤0.04,
q=0.003-0.03。
根据本发明的卤化镁加合物还可以含有水,所述水来自于合成原料和反应介质所带的微量水和/或在加合物制备中以分开组分添加的水。
在本发明的一些优选实施例中,所述式(I)中,X1和Y均为氯;R1为甲基、乙基、正丙基、异丙基、正丁基、异丁基和正己基中的任意一种;
LB1为式(VI)所示的2-烷氧基苯甲酸酯,
式(VI)中,R1为甲基、乙基、正丙基、异丙基、正丁基、异丁基和正己基中的任意一种;
R2、R3、R4和R5各自独立为氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、异戊基、环戊基、正已基、正庚基和甲苯基中的任意一种;
R6为甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、正已基、苄基和苯乙基中的任意一种;
LB2为式(VII)所示的2-羟基苯甲酸酯,
式(VII)中,R1为甲基、乙基、正丙基、异丙基、正丁基、异丁基和正已基中的任意一种;
R2、R3、R4和R5各自为氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、异戊基、环戊基、正已基、正庚基和甲苯基中的任意一种;
LB3为通式R6OH所示化合物,R6为甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、正已基、苄基和苯乙基中的任意一种;
LB4为式(V)所示的钛酸酯化合物,选自钛酸四甲酯、钛酸四乙酯、钛酸四丙酯、钛酸四异丙酯、钛酸四丁酯、钛酸四异丁酯中的一种或多种;
m、n、k、p和q以摩尔计,分别满足以下条件:
m=2.4-3.5,
0.01≤n+k≤0.1,
1≤k/n≤6,
p≤k,且0.004≤p≤0.04,
q=0.003-0.03。
本发明的卤化镁加合物通过以下方式制备:
本发明提供一种卤化镁加合物的制备方法,包括如下步骤:
(1)将通式为MgX1Y的化合物与通式为R1OH的化合物以及烃氧基苯甲酰系化合物和水混合,并将得到的混合物加热,以得到液态的含镁化合物;
(2)在惰性液体介质存在下,将上述液态的含镁化合物乳化,并将乳化产物急冷成形,得到球形的固体颗粒;
(3)将上述球形的固体颗粒和钛酸酯化合物在惰性分散介质中进行接触反应,生成所述卤化镁加合物;
其中,X1、Y和R1的定义各自与式(I)中的定义相同,钛酸酯化合物的定义与式(I)中LB4的定义相同,
所述烃氧基苯甲酰系化合物如式(VIII)所示,
式(VIII)中,X2为卤素原子中的任意一种,优选为氯;R2、R3、R4、R5和R6的定义各自与式(II)和式(III)中的定义相同。
本发明中,所述水可以来自原料中,比如MgX1Y中含水,在上述制备方法中,可以根据实际情况调整水的使用量以及使用含水或不含水的MgX1Y。这里需要说明的是,以重量百分比计,所述MgX1Y不含水是指MgX1Y中的水含量为低于0.2%,本领域内通常称为无水MgX1Y,所述水含量采用卡尔费休方法测定。可以通过控制MgX1Y的干燥条件和/或将MgX1Y与对水有反应活性的物质接触,从而调整MgX1Y中的水含量。所述对水有反应活性的物质可以为HCl气流。
这里还需要说明的一点是,当上述卤化镁加合物制备方法中采用无水MgX1Y时,须以分开组分的方式加入水以进行反应。
在上述制备方式中,除MgX1Y外的其余原料在使用前进行无水化处理,以将所用原料中的水分控制在不影响试验结果的范围内。一般地,R1OH的水含量为低于100ppm(以重量计),烃氧基苯甲酰系化合物的水含量为低于10ppm(以重量计),惰性液体介质的水含量为低于50ppm(以重量计),钛酸酯化合物的水含量为低于10ppm(以重量计)。控制或降低固体物料或液体物料中水含量的方法在本领域中是众所周知的,例如:可以将液体物料进行蒸馏和/或与吸水剂(如分子筛)接触,可以向加热的固体物料或液体物料中持续通入高纯惰性气流,如高纯氮气流。
在本发明的一些优选实施例中,相对于1摩尔以镁计的MgX1Y,R1OH的使用量为1-5.5摩尔,烃氧基苯甲酰系化合物的使用量为0.001-0.32摩尔,水的使用量为0.011-0.081摩尔,钛酸酯化合物的使用量为0.005-3摩尔。
在本发明的一些优选实施例中,相对于1摩尔以镁计的MgX1Y,R1OH的使用量为2-3.7摩尔,烃氧基苯甲酰系化合物的使用量为0.005-0.14摩尔,水的使用量为0.016-0.053摩尔,钛酸酯化合物的使用量为0.02-1摩尔。
在本发明的一些优选实施例中,相对于1摩尔以镁计的MgX1Y,R1OH的使用量为2.4-3.7摩尔,烃氧基苯甲酰系化合物的使用量为0.01-0.072摩尔,水的使用量为0.021-0.043摩尔,钛酸酯化合物的使用量为0.05-0.6摩尔。
在上述制备方式中,所述钛酸酯化合物为式(V)所示的LB4,所述的MgX1Y、R1OH和LB4的定义与卤化镁加合物式(I)中的定义相同,在此不再赘述。
在本发明的一些优选实施例中,所述烃氧基苯甲酰系化合物为4-烃氧基苯甲酰系化合物和/或2-烃氧基苯甲酰系化合物。
在本发明的一些优选实施例中,所述烃氧基苯甲酰系化合物为2-烃氧基苯甲酰系化合物。
这里需要说明的是,本发明中,所述烃氧基苯甲酰系化合物的具体实例可以包括但不限于:2-甲氧基苯甲酰氯、2-甲氧基-3-甲基苯甲酰氯、2-甲氧基-4-甲基苯甲酰氯、2-甲氧基-5-甲基苯甲酰氯、2-甲氧基-3-乙基苯甲酰氯、2-甲氧基-4-乙基苯甲酰氯、2-甲氧基-5-乙基苯甲酰氯、2-甲氧基-3-正丙基苯甲酰氯、2-甲氧基-4-正丙基苯甲酰氯、2-甲氧基-5-正丙基苯甲酰氯、2-甲氧基-4-异丙基苯甲酰氯、2-甲氧基-4-异丁基苯甲酰氯、2-甲氧基-4-叔丁基苯甲酰氯、2-甲氧基-4-戊基苯甲酰氯、2-甲氧基-4-异戊基苯甲酰氯、2-甲氧基-4-环戊基苯甲酰氯、2-乙氧基苯甲酰氯和2-正丁氧基苯甲酰氯。
根据本发明的方法,将MgX1Y、R1OH、烃氧基苯甲酰系化合物和水混合,并将得到的混合物加热,以得到液态的含镁化合物,对于所述混合物加热的条件没有特别限定,只要加热的条件使得MgX1Y能够与R1OH、烃氧基苯甲酰系化合物和水发生反应,从而形成液态的含镁化合物即可。一般地,加热的条件可以包括:温度可以为80-140℃,时间可以为0.5-4小时。
在本发明的制备方法中,进一步包括在惰性液体介质存在下,将所述为液态的含镁化合物乳化,并将乳化产物急冷成形,得到球形的固体颗粒。
惰性液体介质可以为本领域常用的各种不与含镁化合物发生化学相互作用的液体介质,例如:硅油和/或烃系溶剂。具体地,惰性液体介质可以为煤油、石蜡油、凡士林油、白油、甲基硅油、乙基硅油、甲基乙基硅油、苯基硅油和甲基苯基硅油中的至少一种。
惰性液体介质的用量可以根据MgX1Y的具体用量来选择。一般地,相对于1摩尔以镁计的MgX1Y,惰性液体介质的用量为0.2-13L;优选地,相对于1摩尔以镁计的MgX1Y,惰性液体介质的用量为0.6-6.5L。
可以将液态的含镁化合物与惰性液体介质混合,并将得到的混合物乳化,从而实现将所述液态的含镁化合物乳化。
还可以将部分惰性液体介质作为制备液态的含镁化合物的反应介质,从而得到含有液态的含镁化合物的混合液,然后将该混合液与剩余部分惰性液体介质混合并乳化,进而实现将液态的含镁化合物乳化。
也可以将全部惰性液体介质作为制备所述液态的含镁化合物的反应介质,从而得到含有液态的含镁化合物的混合液,将该混合液乳化,进而实现将液态的含镁化合物乳化。
需要时,也可任选地向惰性液体介质中加入一些表面活性剂,如脂肪酸甘油酯、脂肪酸山梨坦、聚山梨酯、聚氧乙烯醚或聚氧乙烯-聚氧丙烯共聚物。表面活性剂的用量可以为本领域的常规用量,例如:相对于1摩尔以镁计的MgX1Y,表面活性剂的用量可以为0.001-1摩尔。
根据本发明的方法,可以采用本领域技术人员公知的各种方法将液态的含镁化合物乳化,例如:可以在惰性液体介质存在下,将液态的含镁化合物进行高速剪切,从而将液态的含镁化合物乳化。高速剪切的方法是本领域技术人员所公知的,例如:CN1151183C公开的高速搅拌法(即,将液态的含镁化合物在惰性液体介质中以2000-5000转/分钟的速度进行搅拌);CN1267508C公开的将液态的含镁化合物与惰性液体介质的混合物在旋转的超重力床中进行(旋转的速度可以为100-3000转/分钟)分散;CN1463990A公开的将液态的含镁化合物与硅油和白油的混合物在乳化机中以1500-8000转/分钟的速度输出;US6020279公开的通过喷雾法将含有液态的含镁化合物的混合物乳化。
根据本发明的方法,可以采用本领域技术人员公知的方法将乳化产物急冷成形,从而得到球形的固体颗粒。例如:可以通过将乳化产物转移到液体冷却介质中的方法将乳化产物急冷以成形。
液体冷却介质可以为本领域常用的各种不与含镁化合物发生化学相互作用的液体介质。例如,液体冷却介质可以为惰性烃系溶剂。液体冷却介质的具体实例可以包括但不限于:正戊烷、正己烷、正庚烷、汽油和石油醚。
本发明中,液体冷却介质在使用前进行无水化处理,以将所用液体冷却介质中的水分控制在不影响试验结果的范围内。一般地,将液体冷却介质的水含量控制为不高于5ppm(以重量计)。控制或降低液体冷却介质中水含量的方法在本领域中是众所周知的,例如:可以将液体物料进行蒸馏和/或与吸水剂(如分子筛)接触,可以向加热的液体物料中持续通入高纯惰性气流,如高纯氮气流。
液体冷却介质的温度以能够使所述乳化产物冷却并成形为准。一般地,液体冷却介质的温度可以为-50℃至0℃,优选为-40℃至-20℃。对于冷却介质的用量没有特别的限制,只要冷却介质的用量足以将乳化产物冷却并成形即可。具体地,冷却介质与乳化产物的体积比为(1-15):1,优选为(2-9):1。
根据本发明的方法,球形固体颗粒和钛酸酯化合物接触反应的条件没有特别的限制,优选情况下,将球形固体颗粒与钛酸酯化合物在-20-10℃的条件下先预接触5-60分钟,然后升温至20-80℃继续反应1-6小时;更优选地,将球形固体颗粒与钛酸酯化合物在-15-5℃的条件下先预接触5-30分钟,然后升温至30-70℃继续反应1-5小时。
根据本发明的方法,惰性分散介质可以为本领域常用的各种不与卤化镁加合物发生化学相互作用的液体介质。例如,惰性分散介质可以为惰性烃类溶剂。所述惰性分散介质的具体实例可以包括但不限于:正戊烷、正己烷、正庚烷、汽油和石油醚。
根据本发明的方法,为了获得卤化镁加合物,上述制备方法还可以包括将经急冷成形得到的球形固体颗粒和/或将经接触反应后得到的固体产物进行过滤、洗涤和干燥,所述洗涤与干燥可以采用本领域技术人员公知的方法进行。例如,所述洗涤使用惰性烃类溶剂,可以为正戊烷、正己烷、正庚烷、石油醚和汽油中的一种或多种;所述洗涤的次数为1-10次;所述干燥的温度为不高于35℃,优选为25-30℃;所述干燥的时间为0.5-3小时,优选1-2h。所述干燥可以在常压或降低压力的条件下进行。
本发明中,根据本发明的卤化镁加合物制备方法制备的卤化镁加合物为球形。
根据本发明的催化剂组分,由于使用了式(I)所示卤化镁加合物,在用于高氢浓度条件下的烯烃聚合反应时,显示出更强的定向能力,且聚合物的形态良好,球形度更高。
本发明对于所述催化剂组分中的钛化合物以及任选的给电子体化合物的种类以及用量没有特别限定,可以为本领域常用的各种钛化合物和给电子体化合物。
在本发明的一些优选实施例中,所述钛化合物可以为三卤化钛和通式Ti(OR7)4- eX3 e所示的钛化合物中的一种或多种,该通式中,R7可以为C1-C10的直链烷基和C3-C10的支链烷基中的任意一种,X3可以为卤素,e为0-4的整数。
在本发明的一些优选实施例中,所述钛化合物为四氯化钛、四溴化钛、四碘化钛、四丁氧基钛、四乙氧基钛、一氯三丁氧基钛、二氯二丁氧基钛、三氯一丁氧基钛、一氯三乙氧基钛、二氯二乙氧基钛、三氯一乙氧基钛和三氯化钛中的一种或多种。
在本发明的一些优选实施例中,所述钛化合物为四氯化钛。
根据本发明的催化剂组分可以采用本领域公知的方法来制备,例如:可以通过将所述卤化镁加合物颗粒直接与钛化合物接触,以进行反应。优选地,制备所述催化剂组分的方法包括:将所述卤化镁加合物悬浮于冷的钛化合物或钛化合物与惰性溶剂的混合液中(所述钛化合物或钛化合物与惰性溶剂的混合物的温度可以为-40℃至0℃,优选为-25℃至-15℃),然后将得到的混合物加热至40-130℃,优选加热至80-130℃,并在上述温度下维持0.5-2小时,然后进行固液分离并收集固体;接着,将得到的固体悬浮于钛化合物中,并将得到的混合物加热至60-130℃,优选加热至80-130℃,并在上述温度下维持0.5-2小时,然后进行固液分离并收集固体,该操作可以进行一次或多次,优选进行2-4次;最后,用惰性溶剂洗涤得到的固体,所述惰性溶剂优选为脂肪烃或芳烃,例如:正己烷、正庚烷、正辛烷、正癸烷和甲苯。
一般地,根据实际应用的需要,特别是对用于α-烯烃(如丙烯)聚合的催化剂组分而言,为了得到高等规度的α-烯烃聚合物(如丙烯聚合物),在所述催化剂组分的制备过程中还可以任选地加入至少一种给电子体化合物。为了与后述催化剂体系中的外给电子体化合物相区别,一般也将催化剂组分中的上述给电子体化合物称为内给电子体化合物。根据本发明,所述给电子体化合物的加入可以在卤化镁加合物颗粒与钛化合物反应前、反应中或反应后进行,优选在卤化镁加合物颗粒与钛化合物反应的同时进行。
根据本发明的催化剂组分,所述给电子体化合物可以为本领域常用的各种给电子体化合物。
在本发明的一些优选实施例中,所述给电子体化合物可以为酯、醚、酮、胺和硅烷中的一种或多种。
在本发明的一些优选实施例中,所述给电子体化合物为酯和二醚型化合物中的一种或多种。
本发明中,所述酯可以为一元脂肪族羧酸酯、多元脂肪族羧酸酯、一元芳香族羧酸酯、多元芳香族羧酸酯和二醇酯中的一种或多种。本发明中,所述酯优选为多元芳香族羧酸酯,最优选为二元芳香族羧酸烷基酯。
本发明中,术语“一元脂肪族羧酸酯”是指由一元脂肪族羧酸与一元醇通过酯化反应形成的化合物。术语“多元脂肪族羧酸酯”是指由多元脂肪族羧酸与一元醇通过酯化反应形成的化合物。术语“一元芳香族羧酸酯”是指由一元芳香族羧酸与一元醇通过酯化反应形成的化合物。术语“多元芳香族羧酸酯”是指多元芳香族羧酸与一元醇通过酯化反应形成的化合物。
本发明中,所述一元脂肪族羧酸酯、多元脂肪族羧酸酯、一元芳香族羧酸酯和多元芳香族羧酸酯的实例可以为苯甲酸酯、邻苯二甲酸酯、丙二酸酯、琥珀酸酯、戊二酸酯、新戊酸酯和碳酸酯;优选为苯甲酸烷基酯、邻苯二甲酸烷基酯、丙二酸烷基酯、琥珀酸烷基酯、戊二酸烷基酯、新戊酸烷基酯和碳酸烷基酯。
具体地,本发明中,所述一元脂肪族羧酸酯、多元脂肪族羧酸酯、一元芳香族羧酸酯和多元芳香族羧酸酯的实例可以为但不限于:苯甲酸乙酯、邻苯二甲酸二乙酯、邻苯二甲酸二异丁酯、邻苯二甲酸二正丁酯、邻苯二甲酸二异辛酯、邻苯二甲酸二正辛酯、丙二酸二乙酯、丙二酸二正丁酯、丙二酸二异丁酯、2,3-二异丙基琥珀酸二乙酯、2,3-二异丙基琥珀酸二异丁酯、2,3-二异丙基琥珀酸二正丁酯、2,3-二异丙基琥珀酸二甲酯、2,2-二甲基琥珀酸二异丁酯、2-乙基-2-甲基琥珀酸二异丁酯、2-乙基-2-甲基琥珀酸二乙酯、戊二酸二乙酯、戊二酸二正丁酯、戊二酸二异丁酯、碳酸二甲酯、碳酸二乙酯、碳酸二异丁酯、己二酸二乙酯、己二酸二正丁酯、癸二酸二乙酯、癸二酸二正丁酯、顺丁烯二酸二乙酯、顺丁烯二酸二正丁酯、萘二羧酸二乙酯、萘二羧酸二正丁酯、偏苯三酸三乙酯、偏苯三酸三正丁酯、联苯三酸三乙酯、联苯三酸三正丁酯、均苯四酸四乙酯和均苯四酸四正丁酯。
本发明中,术语“二醇酯”是指二元醇与一元羧酸或多元羧酸通过酯化反应形成的化合物。例如,所述二醇酯可以为式(IX)所示的化合物:
式IX中,RI、RII、RIII、RIV、RV和RVI各自为氢、C1-C10的脂肪烃基、C6-C10的芳基和C7-C10的芳烷基中的任意一种;或者RI、RII、RIII、RIV、RV和RVI中的两个或两个以上相互键合,以形成环;RVII和RVIII各自为C1-C10的直链烷基、C3-C10的支链烷基、C3-C20的环烷基、C6-C20的芳基和C7-C20的芳基脂肪烃基中的任意一种。
优选地,RI、RII、RIII、RIV、RV和RVI各自为氢、C1-C6的直链烷基、C3-C6的支链的烷基、C2-C6的直链烯基、C3-C6的支链的烯基、C3-C6的环烷基、C6-C10的芳基和C7-C10的芳烷基中的任意一种;或者,RI、RII、RIII、RIV、RV和RVI中的两个或两个以上相互键合,以形成环;RVII和RVIII各自为C1-C6的直链烷基、C3-C6的支链烷基、C3-C6的环烷基、C6-C10的芳基、C7-C10的芳烷基和C7-C10的芳烯基中的任意一种。
更优选地,RI、RII、RV和RVI中的至少一个为氢,且RI、RII、RV和RVI不同时为氢。
进一步优选地,RI和RII中至少有一个为氢,且在RI和RII中仅有一个为氢时,RI和RII中的另一个基团为甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、苯基和卤代苯基中的任意一种;RV和RVI中至少有一个为氢,且在RV和RVI中仅有一个为氢时,RV和RVI中的另一个基团为甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、苯基和卤代苯基中的任意一种;RIII和RIV各自为氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、烯丙基、正戊基、异戊基和正己基中的任意一种,或者RIII和RIV相互键合在一起形成芴基;RVII和RVIII各自为甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、新戊基、环戊基、环己基、苯基、卤代苯基、甲苯基、卤代甲基苯基、苄基、苯乙基和苯乙烯基中的任意一种。
本发明中,所述二醇酯的具体实例可以为但不限于:1,3-丙二醇二苯甲酸酯、2-甲基-1,3-丙二醇二苯甲酸酯、2-乙基-1,3-丙二醇二苯甲酸酯、2,2-二甲基-1,3-丙二醇二苯甲酸酯、(R)-1-苯基-1,3-丙二醇二苯甲酸酯、1,3-二苯基-1,3-丙二醇二苯甲酸酯、1,3-二苯基-1,3-丙二醇二正丙酸酯、1,3-二苯基-2-甲基-1,3-丙二醇二正丙酸酯、1,3-二苯基-2-甲基-1,3-丙二醇二乙酸酯、1,3-二苯基-2,2-二甲基-1,3-丙二醇二苯甲酸酯、1,3-二苯基-2,2-二甲基-1,3-丙二醇二正丙酸酯、1,3-二叔丁基-2-乙基-1,3-丙二醇二苯甲酸酯、1,3-二苯基-1,3-丙二醇二乙酸酯、1,3-二异丙基-1,3-丙二醇二(4-正丁基苯甲酸)酯、1-苯基-2-氨基-1,3-丙二醇二苯甲酸酯、1-苯基-2-甲基-1,3-丁二醇二苯甲酸酯、1-苯基-2-甲基-1,3-丁二醇二新戊酸酯、3-正丁基-2,4-戊二醇二苯甲酸酯、3,3-二甲基-2,4-戊二醇二苯甲酸酯、(2S,4S)-(+)-2,4-戊二醇二苯甲酸酯、(2R,4R)-(+)-2,4-戊二醇二苯甲酸酯、2,4-戊二醇二(对氯苯甲酸)酯、2,4-戊二醇二(间氯苯甲酸)酯、2,4-戊二醇二(对溴苯甲酸)酯、2,4-戊二醇二(邻溴苯甲酸)酯、2,4-戊二醇二(对甲基苯甲酸)酯、2,4-戊二醇二(对叔丁基苯甲酸)酯、2,4-戊二醇二(对正丁基苯甲酸)酯、2-甲基-1,3-戊二醇二(对氯苯甲酸)酯、2-甲基-1,3-戊二醇二(对甲基苯甲酸)酯、2-正丁基-1,3-戊二醇二(对甲基苯甲酸)酯、2-甲基-1,3-戊二醇二(对叔丁基苯甲酸)酯、2-甲基-1,3-戊二醇二新戊酸酯、2-甲基-3-肉桂酰氧基-1-正戊醇苯甲酸酯、2,2-二甲基-1,3-戊二醇二苯甲酸酯、2,2-二甲基-3-肉桂酰氧基-1-正戊醇苯甲酸酯、2-乙基-1,3-戊二醇二苯甲酸酯、2-正丁基-1,3-戊二醇二苯甲酸酯、2-烯丙基-1,3-戊二醇二苯甲酸酯、2-甲基-1,3-戊二醇二苯甲酸酯、2-乙基-1,3-戊二醇二苯甲酸酯、2-正丙基-1,3-戊二醇二苯甲酸酯、2-正丁基-1,3-戊二醇二苯甲酸酯、2,2-二正丙基-1,3-戊二醇二苯甲酸酯、1,3-戊二醇二(对氯苯甲酸)酯、1,3-戊二醇二(间氯苯甲酸)酯、1,3-戊二醇二(对溴苯甲酸)酯、1,3-戊二醇二(邻溴苯甲酸)酯、1,3-戊二醇二(对甲基苯甲酸)酯、1,3-戊二醇二(对叔丁基苯甲酸)酯、1,3-戊二醇二(对丁基苯甲酸)酯、3-肉桂酰氧基-1-正戊醇苯甲酸酯、1,3-戊二醇二肉桂酸酯、1,3-戊二醇二正丙酸酯、2-乙基-1,3-戊二醇二苯甲酸酯、2-正丁基-1,3-戊二醇二苯甲酸酯、2-烯丙基-1,3-戊二醇二苯甲酸酯、2,2,4-三甲基-1,3-戊二醇二异丙基甲酸酯、1-三氟甲基-3-甲基-2,4-戊二醇二苯甲酸酯、2,4-戊二醇二对氟代甲基苯甲酸酯、2,4-戊二醇二(2-呋喃甲酸)酯、2-甲基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3-甲基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、4-甲基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、5-甲基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、6-甲基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3-乙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、4-乙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、5-乙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、6-乙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3-正丙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、4-正丙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、5-正丙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、6-正丙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3-正丁基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、4-正丁基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、5-正丁基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、6-正丁基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,5-二甲基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,5-二乙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,5-二正丙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,5-二正丁基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,3-二甲基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,3-二乙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,3-二正丙基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3,3-二正丁基-6-(1-正庚烯)基-2,4-庚二醇二苯甲酸酯、3-乙基-3,5-庚二醇二苯甲酸酯、4-乙基-3,5-庚二醇二苯甲酸酯、5-乙基-3,5-庚二醇二苯甲酸酯、3-正丙基-3,5-庚二醇二苯甲酸酯、4-正丙基-3,5-庚二醇二苯甲酸酯、3-正丁基-3,5-庚二醇二苯甲酸酯、2,3-二甲基-3,5-庚二醇二苯甲酸酯、2,4-二甲基-3,5-庚二醇二苯甲酸酯、2,5-二甲基-3,5-庚二醇二苯甲酸酯、2,6-二甲基-3,5-庚二醇二苯甲酸酯、3,5-二甲基-3,5-庚二醇二苯甲酸酯、4,4-二甲基-3,5-庚二醇二苯甲酸酯、4,5-二甲基-3,5-庚二醇二苯甲酸酯、4,6-二甲基-3,5-庚二醇二苯甲酸酯、6,6-二甲基-3,5-庚二醇二苯甲酸酯、2-甲基-3-乙基-3,5-庚二醇二苯甲酸酯、2-甲基-4-乙基-3,5-庚二醇二苯甲酸酯、2-甲基-5-乙基-3,5-庚二醇二苯甲酸酯、3-甲基-3-乙基-3,5-庚二醇二苯甲酸酯、3-甲基-4-乙基-3,5-庚二醇二苯甲酸酯、3-甲基-5-乙基-3,5-庚二醇二苯甲酸酯、4-甲基-3-乙基-3,5-庚二醇二苯甲酸酯、4-甲基-4-乙基-3,5-庚二醇二苯甲酸酯、9,9-双(苯甲酰氧基甲基)芴、9,9-双((间甲氧基苯甲酰氧基)甲基)芴、9,9-双((间氯苯甲酰氧基)甲基)芴、9,9-双((对氯苯甲酰氧基)甲基)芴、9,9-双(肉桂酰氧基甲基)芴、9-(苯甲酰氧基甲基)-9-(丙酰氧基基甲基)芴、9,9-双(丙酰氧基甲基)芴、9,9-双(丙烯酰氧基甲基)芴和9,9-双(新戊酰氧基甲基)芴。
CN1213080C、CN1169845C、WO 03/068828和WO 03/068723公开了上述二醇酯化合物,其相关内容在此引入本发明作为参考。
根据本发明,所述二醚型化合物可以为本领域常用的各种能够作为烯烃聚合催化剂内给电子体化合物的二醚型化合物。例如,所述二醚型化合物可以为通式(X)所示的1,3-二醚型化合物:
式(X)中,RI、RII、RIII、RIV、RV和RVI各自为氢、卤素、C1-C20的直链烷基、C3-C20的支链烷基、C3-C20的环烷基、C6-C20的芳基和C7-C20的芳烷基中的任意一种,或者,RI、RII、RIII、RIV、RV和RVI中的两个或两个以上相互键合,以形成环;RVII和RVIII各自为C1-C20的直链烷基、C3-C20的支链烷基、C3-C20的环烷基、C6-C20的芳基和C7-C20的芳烷基中的任意一种。
优选地,RI、RII、RV和RVI为氢;RVII和RVIII各自为C1-C4的直链烷基和C3-C4的支链烷基中的任意一种,更优选为甲基;RIII为甲基、乙基、正丙基或者异丙基,RIV为乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、异戊基、2-乙基己基、环戊基、环己基、甲基环己基、苯基和苄基中的任意一种;或者,RIII为氢,RIV为乙基、正丁基、仲丁基、叔丁基、2-乙基己基、环己基乙基、二苯基甲基、对氯苯基、1-萘基和1-十氢萘基中的任意一种;或者,RIII和RIV相同,且为乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、新戊基、苯基、苄基、环己基和环戊基中的任意一种;或者,RIII和RIV相互键合,以形成环戊二烯基、芴基或茚基。
CN1015062B和CN1121368C公开了上述二醚型化合物,其公开的相关内容全部引入本发明作为参考。
根据本发明,所述卤化镁加合物的用量、钛化合物的用量以及给电子体化合物的用量可以根据预期的催化剂组分的组成进行适当的选择。
在本发明的一些优选实施例中,以卤化镁加合物中的镁计,所述钛化合物、给电子体化合物与所述卤化镁加合物的摩尔比为(5-100):(0-0.5):1。
在本发明的一些优选实施例中,以卤化镁加合物中的镁计,所述钛化合物、给电子体化合物与所述卤化镁加合物的摩尔比为(20-80):(0.05-0.35):1。这里需要说明的是,本发明中,钛化合物的量为包括在制备本发明催化剂组分过程中使用的钛化合物的总量。
为实现上述目的之二,本发明采取的技术方案如下:
一种催化剂体系,该催化剂体系包含下述组分或下述组分的反应产物:
1)上述的催化剂组分;
2)一种或者多种有机铝化合物;
3)任选地,至少一种外给电子体化合物。
所述有机铝化合物为烷基铝倍半氯化物和式(XI)所示化合物中的一种或多种,
AlR8R9R10 式(XI)
式(XI)中,R8、R9和R10各自独立为氯、C1-C8的直链烷基和C3-C8的支链烷基中的任意一种,且R8、R9和R10中的至少一个为C1-C8的直链烷基和C3-C8的支链烷基中的任意一种;
所述外给电子体化合物为羧酸、酸酐、酯、酮、醚、醇、有机磷化合物和有机硅化合物中的一种或多种;优选地,所述外给电子体为通式R11 xR12 ySi(OR13)z所示的有机硅化合物,该通式中,R11、R12和R13各自为C1-C18的烃基或含有杂原子的C1-C18的烃基;x和y各自为0-2的整数,z为1-3的整数,且x+y+z=4。
在本发明的一些优选实施例中,所述有机铝化合物为三烷基铝化合物、一氯二烷基铝化合物、二氯一烷基铝化合物和烷基铝倍半氯化物中的一种或多种。
在本发明的一些优选实施例中,所述有机铝化合物为三乙基铝、三异丁基铝、三正丁基铝、三正己基铝、三正辛基铝、一氯二乙基铝、一氯二异丁基铝、一氯二正丁基铝、一氯二正己基铝、二氯一乙基铝、二氯一异丁基铝、二氯一正丁基铝、二氯一正己基铝和三氯三乙基二铝中的一种或多种。
在本发明的一些优选实施例中,以铝计的所述有机铝化合物和以钛计的所述催化剂组分的摩尔比为(1-2000):1。
在本发明的一些优选实施例中,以铝计的所述有机铝化合物和以钛计的所述催化剂组分的摩尔比为(20-700):1。
在烯烃特别是α-烯烃(例如丙烯或1-丁烯)的有机立构聚合的情况下,根据本发明的催化剂体系还可以包含与用作内给电子体的化合物相同或者不同的给电子体化合物作为外给电子体化合物。本发明中,所述有机铝化合物与任选的外给电子体化合物可以单独或作为两种成分的混合物与催化剂组分接触反应。
根据本发明的催化剂体系,所述外给电子体化合物可以为本领域常用的各种外给电子体化合物,例如:所述外给电子体化合物可以为羧酸、酸酐、酯、酮、醚、醇、有机磷化合物和有机硅化合物中的一种或多种。优选地,所述外给电子体为通式R11 xR12 ySi(OR13)z所示的有机硅化合物,该通式中,R11、R12和R13各自为C1-C18的烃基或含有杂原子的C1-C18的烃基;x和y各自为0-2的整数,z为1-3的整数,且x+y+z=4。更优选地,通式R11 xR12 ySi(OR13)z中,R11和R12中的至少一个选自C3-C10的含或不含杂原子的支链烷基、C3-C10的含或不含杂原子的环烷基和C6-C10的芳基中的任意一种,R13为C1-C10的直链烷基和C3-C10的支链烷基中的任意一种,优选为甲基;x为1,y为1,z为2;或者,R12为C3-C10的支链烷基或C3-C10的环烷基,且R13为甲基,x为0,y为1,z为3。
本发明中,所述有机硅化合物的实例可以为但不限于:环己基甲基二甲氧基硅烷、二异丙基二甲氧基硅烷、正丁基环己基二甲氧基硅烷、二异丁基二甲氧基硅烷、二苯基二甲氧基硅烷、甲基叔丁基二甲氧基硅烷、二环戊基二甲氧基硅烷、2-乙基哌啶基-2-叔丁基二甲氧基硅烷、(1,1,1-三氟-2-丙基)-2-乙基哌啶基二甲氧基硅烷、(1,1,1-三氟-2-丙基)-甲基二甲氧基硅烷、环己基三甲氧基硅烷、叔丁基三甲氧基硅烷和叔己基三甲氧基硅烷。
一般地,相对于1摩尔以铝计的有机铝化合物,所述外给电子体化合物的用量可以为0.005-0.5摩尔;优选地,相对于1摩尔以铝计的有机铝化合物,所述外给电子体化合物的用量为0.01-0.4摩尔。
根据本发明的催化剂体系,在所述内给电子体为酯,特别是多元羧酸酯和二醇酯的情况下,优选以上述给电子体化合物中的一种或多种作为外给电子体;在所述内给电子体为醚,特别是式(X)所示的1,3-二醚型化合物时,可以不使用外给电子体,这是因为催化剂体系的立体定向能力对于用于各种用途的聚合物而言已经足够高。
为实现上述目的之三,本发明采取的技术方案如下:
一种上述的催化剂组分或上述的催化剂体系在烯烃聚合领域中的应用。
为实现上述目的之四,本发明采取的技术方案如下:
一种烯烃聚合方法,包括:使烯烃在上述的催化剂体系的存在下进行聚合反应。
一般地,根据本发明的烯烃聚合方法,所述烯烃可以为通式CH2=CHR14所示的烯烃,其中,R14可以为氢、C1-C12的直链烷基、C3-C12的支链烷基和C6-C12的芳基中的任意一种。根据本发明的烯烃聚合方法,必要时,所述烯烃还可以含有少量的二烯烃。根据本发明的烯烃聚合方法,所述烯烃优选为丙烯,或者丙烯和CH2=CHR14所示的烯烃,其中,R14为氢和C2-C6的直链烷基和C3-C6的支链烷基中的任意一种。
根据本发明的烯烃聚合方法,所述烯烃的聚合既可以是均聚,也可以是共聚。所述烯烃的聚合可以按照本领域的常规方法进行,例如,所述聚合可以为本体聚合、气相聚合、淤浆聚合或液相本体-气相组合聚合。根据本发明的烯烃聚合方法,所述烯烃聚合条件可以为本领域的常规条件,例如,聚合温度可以为0-150℃,优选为60-90℃;聚合压力可以为常压或加压。
相对于现有技术,本发明至少具有如下优点或有益效果:
根据本发明的以式(I)所示卤化镁加合物MgX1Y-mR1OH-n(LB1)-k(LB2)-p(LB3)-q(LB4)为载体合成的催化剂组分,由该催化剂组分形成的催化剂体系在用于烯烃聚合时,在高氢浓度条件下显示出更强的定向能力,制备的聚合物树脂等规指数更高,同时所得聚合物的颗粒形态好,球形度更高。这对于高流动聚烯烃树脂生产中提高树脂的刚性性能是十分有利的。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚,下面将对本发明的技术方案进行清楚、完整的示例性描述。
需要说明的是,在不冲突的情况下,本发明中的实施例及实施例中的特征可以相互组合。
以下结合实施例详细说明本发明,但不因此限制本发明的范围。
本发明中,涉及的测试方法如下:
1、聚合物熔融指数(MI):根据ASTM D1238-99中规定的方法测定。
2、聚合物等规指数(II):采用正庚烷抽提法测定(正庚烷沸腾抽提6小时),具体操作为:称取2g干燥的聚合物样品,置于索氏抽提器中用沸腾的正庚烷抽提6小时,然后,将剩余物干燥至恒重,所得剩余物的重量(g)与2的比值即为等规指数。
3、采用气相色谱法来测定卤化镁加合物中的醇和LB的含量,采用化学滴定法来测定卤化镁加合物中Mg的含量。
4、采用分光光度法测定卤化镁加合物中Ti的含量。
5、聚合物的球形度SPHT使用Camsizer仪器采集,。对于理想球体,SPHT值为1。若不为理想球体,则SPHT小于1。SPHT值约接近1,颗粒越接近球形。
以下实施例中的白油商购自广州市铭恩石油化工有限公司;氯化镁商购自抚顺市鑫宜钛厂;无水乙醇商购自北京化工厂,为分析纯;甲基硅油商购自道康宁(上海)有限公司,粘度为300厘泊/20℃;2-甲氧基苯甲酰氯商购自TOKYO KASEI KOGYO CO.LTD,试剂级;钛酸四乙酯和钛酸四丁酯商购自北京百灵威科技有限公司,试剂级。
实施例1
(1)卤化镁加合物的制备
在500mL的反应釜中,加入150mL白油、30g含有0.44wt%水分的氯化镁、50mL无水乙醇和1mL 2-甲氧基苯甲酰氯,在搅拌下升温至120℃;恒温反应2小时后,将混合物压入预热至120℃的300mL甲基硅油中,以1600转/分钟的速度搅拌30分钟,以进行乳化;然后,将乳化产物用氮气压入预先冷却至-30℃的2L已烷中,以固化成形;过滤除去液体,用300mL已烷洗涤固体5次,得球形固体颗粒。
在300mL的玻璃反应瓶中,氮气保护条件下,依次加入120mL己烷、1.2mL钛酸四乙酯,冷却至-10℃,加入上述制备的球形固体颗粒12.0g,并维持-10℃搅拌10分钟;之后,缓慢升温至60℃,并恒温反应2h;滤除液体,用60℃的已烷对得到的固体洗涤5次(己烷用量为90mL/次);之后在30℃下真空干燥1.5小时,从而得到卤化镁加合物。
(2)催化剂组分的制备
在300mL的玻璃反应瓶中,氮气保护条件下,依次加入18mL己烷、90mL四氯化钛,冷却至-20℃,加入8.0g上述(1)制备的卤化镁加合物,并在-20℃搅拌30分钟;然后,缓慢升温至110℃,并在升温过程中加入1.5mL邻苯二甲酸二异丁酯;在110℃恒温反应40分钟后,滤除液体;加入80mL四氯化钛,升温至120℃,在120℃维持30分钟后滤除液体;重复上述操作一次;最后用60℃的已烷对得到的固体洗涤5次(己烷用量为80mL/次),并真空干燥所得固体物,从而得到球形催化剂组分。
(3)烯烃均聚合反应1
在氮气保护下,向5L的不锈钢高压反应釜中依次加入5mL三乙基铝的己烷溶液(浓度为0.5mmol/mL)、1mL环己基甲基二甲氧基硅烷的己烷溶液(浓度为0.1mmol/mL)和9mg上述(2)制备的球形催化剂组分;关闭高压釜,加入1.5L(标准体积)氢气和2.3L液体丙烯;升温至70℃,反应1小时;然后,降温,卸压,出料,并进行干燥,从而得到聚丙烯。
(4)烯烃均聚合反应2
采用与(3)相同的方法进行丙烯聚合,不同的是,氢气的用量为6.0L氢气(标准体积)。
对比例1
本对比例与实施例1基本相同,区别在于:卤化镁加合物的制备中,不加入钛酸四乙酯进行接触反应。
对比例2
本对比例与实施例1基本相同,区别在于:卤化镁加合物的制备中,不加入2-甲氧基苯甲酰氯进行反应。
实施例2
本实施例与实施例1基本相同,区别在于:卤化镁加合物的制备中,钛酸四乙酯的加入量为5.0ml。
实施例3
本实施例与实施例1基本相同,区别在于:卤化镁加合物的制备中,钛酸四乙酯与球形固体颗粒接触反应的温度为40℃,反应时间为4h。
实施例4
本实施例与实施例1基本相同,区别在于:卤化镁加合物的制备中,将1.2ml钛酸四乙酯替换为2.0ml钛酸四丁酯。
实施例5
本实施例与实施例1基本相同,区别在于:卤化镁加合物的制备中,钛酸四乙酯与球形固体颗粒预接触的温度为0℃。
实施例6
本实施例与实施例1基本相同,区别在于:在500mL的反应釜中,加入150mL白油、30g含有1.2wt%水分的氯化镁、54mL无水乙醇和3mL 2-甲氧基苯甲酰氯,在搅拌下升温至130℃;恒温反应2小时后,将混合物压入预热至130℃的300mL甲基硅油中,以1600转/分钟的速度搅拌30分钟,以进行乳化。
实施例7
本实施例与实施例1基本相同,区别在于:在500mL的反应釜中,加入150mL白油、30g无水氯化镁、50m无水乙醇、1mL 2-甲氧基苯甲酰氯和0.15g水,在搅拌下升温至120℃。
对比例3
本对比例与实施例7基本相同,区别在于:卤化镁加合物的制备中,不加入钛酸四乙酯进行接触反应。
实施例1-7以及对比例1-3中,制得的卤化镁加合物的组成如表1所示,烯烃均聚合反应1和2的实验结果如表2所示。
表1卤化镁加合物的组成
注:LB1:2-甲氧基苯甲酸乙酯,LB2:2-羟基苯甲酸乙酯;LB3:甲醇;LB4:钛酸四乙酯;LB4 a:钛酸四丁酯。
表2烯烃均聚合反应实验结果
表2分别列出了由本发明实施例1-7以及对比例1-3所提供催化剂组分及其催化剂体系在用于不同氢气浓度条件下的丙烯均聚合结果。从表2中数据可以看出,与现有技术的催化剂组分和催化剂体系相比,本发明提供的催化剂组分及其催化剂体系用于丙烯聚合时,随着氢气浓度的增加,定向能力下降不明显,也就是说,在高氢浓度条件下显示出更加优异的定向能力,制备的聚合物树脂等规指数更高,且聚合物球形度更好,这对于高流动高刚性聚烯烃树脂的生产是有利的。
应当注意的是,以上所述的实施例仅用于解释本发明,并不构成对本发明的任何限制。通过参照典型实施例对本发明进行了描述,但应当理解为其中所用的词语为描述性和解释性词汇,而不是限定性词汇。可以按规定在本发明权利要求的范围内对本发明作出修改,以及在不背离本发明的范围和精神内对本发明进行修订。尽管其中描述的本发明涉及特定的方法、材料和实施例,但是并不意味着本发明限于其中公开的特定例,相反,本发明可扩展至其他所有具有相同功能的方法和应用。
Claims (16)
1.一种催化剂组分,该催化剂组分包含卤化镁加合物、钛化合物和任选的至少一种给电子体化合物的反应产物,其特征在于,所述卤化镁加合物如式(I)所示,
MgX1Y-mR1OH-n(LB1)-k(LB2)-p(LB3)-q(LB4) 式(I)
式(I)中,X1为氯或溴;
Y为氯、溴、C1-C14的直链烷基、C3-C14的支链烷基、C6-C14的芳基、C1-C14的直链烷氧基、C3-C14的支链烷氧基和C6-C14的芳氧基中的任意一种;
LB1为式(II)所示的烃氧基苯甲酸酯系化合物,
LB2为式(III)所示的羟基苯甲酸酯系化合物,
LB3为式(IV)所示的醇,
R6OH 式(IV)
LB4为式(V)所示的钛酸酯化合物,
(R1′O)a(R2′O)b(R3′O)cTiZd 式(V)
R1为C1-C12的直链烷基、C3-C12的支链烷基、C3-C10的环烷基和C7-C10的芳烷基中的任意一种;
R2、R3、R4和R5各自为氢、卤素、硝基、C1-C20的直链烷基、C3-C20的支链烷基、C3-C20的环烷基、C6-C20的芳基和C7-C20的芳烷基中的任意一种;R2、R3、R4和R5中的两个或两个任选地以上相互键合,以形成环;
R6与R1不相同,为C1-C20的直链烷基、C3-C20的支链烷基、C3-C20的环烷基、C6-C20的芳基和C7-C20的芳烷基中的任意一种;
R1′、R2′和R3′相同或不同,选自C1-C10的直链烷基或C3-C10的支链烷基;Z与Y相同或不同,为氯、溴、C1-C14的直链烷基、C3-C14的支链烷基、C6-C14的芳基、C1-C14的直链烷氧基、C3-C14的支链烷氧基和C6-C14的芳氧基中的任意一种;a、b、c和d独立为0-4的整数,且a+b+c+d=4;
m、n、k、p和q以摩尔计,分别满足以下条件:
m=1-5,
0.001≤n+k≤0.3,
0.2≤k/n≤20,
p≤k,且0.0005≤p<0.05,
q=0.001-0.1。
2.根据权利要求1所述的催化剂组分,其特征在于,其中,Y为氯、溴、C1-C5的直链烷基、C3-C5的支链烷基、C6-C10的芳基、C1-C5的直链烷氧基、C3-C5的支链烷氧基和C6-C10的芳氧基中的任意一种;
优选地,所述MgX1Y为二氯化镁、二溴化镁、氯化苯氧基镁、氯化异丙氧基镁和氯化正丁氧基镁中的一种或多种。
3.根据权利要求1或2所述的催化剂组分,其特征在于,其中,R1为C1-C6的直链烷基、C3-C6的支链烷基;
优选地,R1为甲基、乙基、正丙基、异丙基、正丁基、异丁基和正己基中的任意一种。
4.根据权利要求1-3中任一项所述的催化剂组分,其特征在于,其中,R2、R3、R4和R5各自为氢、C1-C8的直链烷基、C3-C8的支链烷基、C3-C6的环烷基、C6-C10的芳基和C7-C10的芳烷基中的任意一种;
优选地,R2、R3、R4和R5各自为氢、甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、异戊基、环戊基、正已基、正庚基和甲苯基中的任意一种。
5.根据权利要求1-4中任一项所述的催化剂组分,其特征在于,其中,R6与R1不相同,R6为C1-C6的直链烷基、C3-C6的支链烷基、C3-C6的环烷基、C6-C10的芳基和C7-C10的芳烷基中的任意一种;
优选地,R6与R1不相同,R6为甲基、乙基、正丙基、异丙基、正丁基、异丁基、叔丁基、正戊基、正已基、苄基和苯乙基中的任意一种。
6.根据权利要求1-5中任一项所述的卤化镁加合物,其特征在于,所述LB1为4-烷氧基苯甲酸酯系化合物和/或2-烷氧基苯甲酸酯系化合物,优选为2-烷氧基苯甲酸酯系化合物;
和/或,所述LB2为4-羟基苯甲酸酯系化合物和/或2-羟基苯甲酸酯系化合物,优选为2-羟基苯甲酸酯系化合物。
7.根据权利要求1-6中任一项所述的催化剂组分,其特征在于,其中,R1′、R2′和R3′相同或不同,为C1-C6的直链烷基或C3-C6的支链烷基;
和/或,Z为氯、溴、C1-C6的直链烷氧基或C3-C6的支链烷氧基;a、b、c和d独立为0-4的整数,且a+b+c+d=4。
8.根据权利要求1-7中任一项所述的催化剂组分,其特征在于,所述LB4为钛酸四烷基酯中的一种或多种;
优选地,LB4为钛酸四甲酯、钛酸四乙酯、钛酸四丙酯、钛酸四异丙酯、钛酸四丁酯和钛酸四异丁酯中的一种或多种。
9.根据权利要求1-8中任一项所述的催化剂组分,其特征在于,其中,m、n、k、p和q以摩尔计,分别满足以下条件:
m=2-3.5,
0.005≤n+k≤0.15,
0.5≤k/n≤10,
p≤k,且0.001≤p≤0.04,
q=0.002-0.05;
优选地,m、n、k、p和q以摩尔计,分别满足以下条件:
m为2.4-3.5,
0.01≤n+k≤0.1,
1≤k/n≤6,
p≤k,且0.004≤p≤0.04,
q=0.003-0.03。
10.根据权利要求1-9中任一项所述的催化剂组分,其特征在于,所述钛化合物为三卤化钛和通式Ti(OR7)4-eX3 e所示的钛化合物中的一种或多种,该通式中,R7为C1-C10的直链烷基和C3-C10的支链烷基中的任意一种,X3为卤素,e为0-4的整数。
11.根据权利要求1-10中任一项所述的催化剂组分,其特征在于,所述给电子体化合物为酯、醚、酮、胺和硅烷中的一种或多种;优选地,所述给电子体化合物为酯和二醚类化合物中的一种或多种。
12.根据权利要求1-11中任一项所述的催化剂组分,其特征在于,以卤化镁加合物中的镁计,钛化合物及给电子体化合物的用量与卤化镁加合物用量的摩尔比为(5-100):(0-0.5):1,优选为(20-80):(0.05-0.35):1。
13.一种催化剂体系,该催化剂体系包含下述组分或下述组分的反应产物:
1)权利要求1-12中任一项所述的催化剂组分;
2)一种或者多种有机铝化合物;
3)任选地,至少一种外给电子体化合物;
所述有机铝化合物为烷基铝倍半氯化物和式(XI)所示化合物中的一种或多种,
AlR8R9R10 式(XI)
式(XI)中,R8、R9和R10各自独立为氯、C1-C8的直链烷基和C3-C8的支链烷基中的任意一种,且R8、R9和R10中的至少一个为C1-C8的直链烷基和C3-C8的支链烷基中的任意一种;
所述外给电子体化合物为羧酸、酸酐、酯、酮、醚、醇、有机磷化合物和有机硅化合物中的一种或多种;优选地,所述外给电子体为通式R11 xR12 ySi(OR13)z所示的有机硅化合物,该通式中,R11、R12和R13各自为C1-C18的烃基或含有杂原子的C1-C18的烃基;x和y各自为0-2的整数,z为1-3的整数,且x+y+z=4。
14.根据权利要求13所述的催化剂体系,其特征在于,以铝计的所述有机铝化合物和以钛计的所述催化剂组分的摩尔比为(1-2000):1,优选为(20-700):1;
和/或,所述外给电子体化合物与以铝计的有机铝化合物的摩尔比为(0.005-0.5):1,优选为(0.01-0.4):1。
15.一种权利要求1-12中任一项所述的催化剂组分或权利要求13或14所述的催化剂体系在烯烃聚合领域中的应用。
16.一种烯烃聚合方法,包括:使烯烃在权利要求13或14所述的催化剂体系的存在下进行聚合反应。