CN117107244A - 一种金属板材防腐方法 - Google Patents
一种金属板材防腐方法 Download PDFInfo
- Publication number
- CN117107244A CN117107244A CN202311071283.4A CN202311071283A CN117107244A CN 117107244 A CN117107244 A CN 117107244A CN 202311071283 A CN202311071283 A CN 202311071283A CN 117107244 A CN117107244 A CN 117107244A
- Authority
- CN
- China
- Prior art keywords
- metal plate
- zinc pyrithione
- corrosion
- mass ratio
- monensin sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于金属板材防腐技术领域，具体涉及一种金属板材防腐方法。一种金属板材防腐组合物，所述金属板材防腐组合物的有效成分由莫能菌素钠与吡啶硫硐锌按1‑20：20‑1的质量比复配而成。本发明莫能菌素钠与吡啶硫酮锌按一定质量比进行复配时，对抑制黑曲霉、桔青霉、产黄青霉和绿色木霉等多种霉菌的生长具有增效作用，可提高对霉菌的防控效果，进而可为金属板材的防腐提供支持。
Description
技术领域
本发明属于金属板材防腐技术领域，具体涉及一种金属板材防腐方法。
背景技术
金属板材铝合金材料具有强度高、密度小、力学性能好和易加工等优点，广泛应用于各种工程材料以及飞机和舰船等高端设备。铝合金在自然条件下会在其表面形成一层三氧化二铝膜，具有良好的附着力和自愈合性，对铝合金材料具有良好的保护作用。在沿海高温、高湿、高盐海洋环境中，金属板材铝合金制品常会出现小孔腐蚀、缝隙腐蚀、电偶腐蚀以及微生物腐蚀。其中，微生物腐蚀是一个复杂的电化学过程，微生物腐蚀的发生、发展与微生物的滋生、在金属板材表面附着以及微生物新陈代谢产物等直接相关，通过生物氧化显著地加速金属的腐蚀。霉菌是主要的腐蚀性微生物，对金属板材腐蚀性较强的代表性霉菌主要包括：黑曲霉、华根霉、鲁氏毛霉、总状毛霉、黄曲霉、产黄青霉和桔青霉等。
通过在金属板材制品上喷涂防腐剂或防腐涂料进而在金属板材制品上构筑抗菌涂层，可有效防控霉菌对金属板材制品的腐蚀。现有技术报道了环境友好型和高效杀菌剂吡啶硫酮锌可以显著抑制霉菌在金属板材表面的附着和吸附以及生物膜的形成，可以显著降低金属板材的腐蚀速度。但长期使用单一成分杀菌剂容易使霉菌产生抗药性，导致杀菌剂的抗菌效果降低。将不同杀菌活性成分进行复配，其中具有增效作用的复配组合可以提高防控效果，有效解决抗药性这一问题，但并非将任意不同杀菌活性成分进行复配都可以取得增效作用。
发明人通过室内试验发现将莫能菌素钠与吡啶硫酮锌按一定质量比进行复配时，对抑制黑曲霉、桔青霉、产黄青霉和绿色木霉等多种霉菌的生长具有增效作用，可提高对霉菌的防控效果，进而可为金属板材的防腐提供支持。目前还未见到莫能菌素钠与吡啶硫酮锌复配的相关报道。
公开于该背景技术部分的信息仅仅旨在增加对本发明的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
发明内容
本发明的目的在于提供一种金属板材防腐方法，以解决背景技术中单独使用吡啶硫酮锌进行防腐时存在的问题。
为实现上述目的，本发明提供了如下技术方案：
一种金属板材防腐组合物，所述金属板材防腐组合物的有效成分由莫能菌素钠与吡啶硫硐锌按1-20：20-1的质量比复配而成。
效果更好的，所述莫能菌素钠与吡啶硫酮锌的质量比为8：1。
效果更好的，所述莫能菌素钠与吡啶硫酮锌的质量比为1：16。
本发明还提供了一种金属板材抗菌涂层或防腐涂料，包括所述的金属板材防腐组合物。
本发明还提供了一种金属板材防腐方法，在金属板材制品上喷涂所述的金属板材抗菌涂层或防腐涂料。
与现有技术相比，本发明具有如下有益效果：
本发明莫能菌素钠与吡啶硫酮锌按一定质量比进行复配时，对抑制黑曲霉、桔青霉、产黄青霉和绿色木霉等多种霉菌的生长具有增效作用，可提高对霉菌的防控效果，进而可为金属板材的防腐提供支持。
具体实施方式
下面对本发明专利的技术方案进行清楚、完整的描述，显然，所描述的实施例是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域所属的技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例
1.供试霉菌
表1供试霉菌
2.试验药剂
95％莫能菌素钠原药(CAS：22373-78-0，上海源叶生物科技有限公司)、99％吡啶硫酮锌原药(武汉欣欣佳丽生物科技有限公司)
试验药剂用二甲基亚砜溶解后用质量分数0.1％的吐温-80水溶液稀释成单剂母液；设置多组配比，各单剂和每组配比再用0.1％吐温-80水溶液按照等比方法稀释成5个质量浓度梯度，备用。
3.试验方法
菌丝生长速率法(慕立义1994)。将1mL试验药剂与9mL冷却至45℃左右的PDA培养基混匀，倒入无菌培养皿中，待培养基凝固后形成带药平板。用打孔器在培养4d的菌株边缘打取直径5mm的霉菌菌饼，接种到带药平板中央，同时设以0.1％吐温-80水溶液的处理为对照，每个质量浓度药液及对照设置5个平板。放入培养箱中，26±1℃下继续培养。待对照菌落直径长至培养皿直径的2/3时，用十字交叉法测量霉菌菌落生长直径，计算抑制率。
4.数据分析
用DPS软件对试验药剂浓度对数值和菌丝生长抑制率几率值进行回归分析，计算各处理药剂的EC50，根据孙云沛法计算共毒系数(CTC值)，并根据计算的共毒系数(CTC值)评价药剂的增效作用。结果见表1-4。
表1莫能菌素钠与吡啶硫酮锌复配对黑曲霉的毒力
由表1可知，莫能菌素钠与吡啶硫酮锌复配，在1-20：20-1质量比范围内，对抑制黑曲霉的生长具有增效作用。说明，本发明的防腐组合物可提高对黑曲霉的防控效果，进而可为金属板材的防腐提供支持。
表2莫能菌素钠与吡啶硫酮锌复配对桔青霉的毒力
由表2可知，莫能菌素钠与吡啶硫酮锌复配，在1-20：20-1质量比范围内，对抑制桔青霉的生长具有增效作用。说明，本发明的防腐组合物可提高对桔青霉的防控效果，进而可为金属板材的防腐提供支持。
表3莫能菌素钠与吡啶硫酮锌复配对产黄青霉的毒力
由表3可知，莫能菌素钠与吡啶硫酮锌复配，在1-20：20-1质量比范围内，对抑制产黄青霉的生长具有增效作用。说明，本发明的防腐组合物可提高对产黄青霉的防控效果，进而可为金属板材的防腐提供支持。
表4莫能菌素钠与吡啶硫酮锌复配对绿色木霉的毒力
由表4可知，莫能菌素钠与吡啶硫酮锌复配，在1-20：20-1质量比范围内，对抑制绿色木霉的生长具有增效作用。说明，本发明的防腐组合物可提高对绿色木霉的防控效果，进而可为金属板材的防腐提供支持。
综上所述，莫能菌素钠与吡啶硫酮锌按一定质量比进行复配时，对抑制黑曲霉、桔青霉、产黄青霉和绿色木霉等多种霉菌的生长具有增效作用，可提高对霉菌的防控效果，进而可为金属板材的防腐提供支持。
前述对本发明的具体示例性实施方案的描述是为了说明和例证的目的。这些描述并非想将本发明限定为所公开的精确形式，并且很显然，根据上述教导，可以进行很多改变和变化。对示例性实施例进行选择和描述的目的在于解释本发明的特定原理及其实际应用，从而使得本领域的技术人员能够实现并利用本发明的各种不同的示例性实施方案以及各种不同的选择和改变。本发明的范围意在由权利要求书及其等同形式所限定。
Claims (5)
1.一种金属板材防腐组合物，其特征在于，所述金属板材防腐组合物的有效成分由莫能菌素钠与吡啶硫硐锌按1-20：20-1的质量比复配而成。
2.根据权利要求1所述的金属板材防腐组合物，其特征在于，所述莫能菌素钠与吡啶硫酮锌的质量比为8：1。
3.根据权利要求1所述的金属板材防腐组合物，其特征在于，所述莫能菌素钠与吡啶硫酮锌的质量比为1：16。
4.一种金属板材抗菌涂层或防腐涂料，其特征在于，包括权利要求1-3任一项所述的金属板材防腐组合物。
5.一种金属板材防腐方法，其特征在于，在金属板材制品上喷涂权利要求4所述的金属板材抗菌涂层或防腐涂料。