CN117511276A - 一种绿色环保建筑内墙防腐涂料 - Google Patents
一种绿色环保建筑内墙防腐涂料 Download PDFInfo
- Publication number
- CN117511276A CN117511276A CN202311758029.1A CN202311758029A CN117511276A CN 117511276 A CN117511276 A CN 117511276A CN 202311758029 A CN202311758029 A CN 202311758029A CN 117511276 A CN117511276 A CN 117511276A
- Authority
- CN
- China
- Prior art keywords
- interior wall
- parts
- preservative
- environment
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于涂料技术领域，具体涉及一种绿色环保建筑内墙防腐涂料。一种防腐剂，所述防腐剂的有效成分由苄索氯铵和多菌灵按1‑9：3的质量比混合而成。本发明的防腐剂对抑制多种霉菌表现出增效作用，可以提高对霉菌的抑制效果，基于此可以减少防腐剂的添加量，降低成本。本发明的绿色环保建筑内墙防腐涂料中添加的所述防腐剂成分，可以抵御微生物对涂料的干扰，进而有利于延长涂料的贮藏时间。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种绿色环保建筑内墙防腐涂料。
背景技术
防腐涂料中含有有机物质，这些有机物质为微生物的生长繁殖提供了基本条件。在适宜的条件下，会促进微生物的大量生长繁殖，在此过程中，微生物产生的酶和有机酸等代谢产物会引起涂料气味、颜色和黏度等发生变化，造成产品变质。防腐剂可以抑制微生物生长，在产品中添加适量且合适的防腐剂可以有效防止微生物的侵害，保证涂料生产和贮存过程中不产生腐败变质。
苄索氯铵，易溶于水形成泡沫状肥皂水样溶液，溶于乙醇、丙酮和氯仿。用于杀菌消毒剂，具有较好的表面活性，广泛用于日化和医疗等领域作为防腐、杀菌剂。但使用单一成分苄索氯铵作为防腐剂，效果有限，且长期使用容易导致霉菌对其产生抗药性，导致防腐效果降低。
现有技术CN201010604560.X的专利公开了一种含苄索氯铵的杀菌防腐组合物及用途，在该专利中公开了苄索氯铵与对羟基苯甲酸酯和/或3-碘-2-丙炔基丁基氨基甲酸酯等抗真菌剂组合使用，不仅可以提高苄索氯铵对细菌的抗菌性能，同时对真菌的抑菌能力也明显提高，杀菌谱广，效果稳定。可广泛用于化妆品、湿巾、护理洗液和洗手液等个人护理品种作为防腐杀菌剂使用。但目前还未见到苄索氯铵和多菌灵组合使用的相关报道。
公开于该背景技术部分的信息仅仅旨在增加对本发明的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
发明内容
本发明的目的在于提供一种绿色环保建筑内墙防腐涂料，以解决背景技术中使用单一成分苄索氯铵作为防腐剂时存在的问题。
为实现上述目的，本发明提供了如下技术方案：
一种防腐剂，所述防腐剂的有效成分由苄索氯铵和多菌灵按1-9：2-1的质量比混合而成。
本发明还提供了包括所述防腐剂的绿色环保建筑内墙防腐涂料，以重量份计由以下成分制备而成：水性丙烯酸乳液30-60份、成膜助剂3-6份、分散剂2-5份、填料20-40份、增稠剂6-8份、消泡剂1-2份、pH调节剂0.2-0.3份、所述防腐剂1-2份及去离子水25-30份。
作为优选，所述成膜助剂为伊斯曼十二碳醇酯。
作为优选，所述分散剂为BYK 163。
作为优选，所述填料为煅烧高岭土。
作为优选，所述增稠剂为WT-105A缔合型聚氨酯。
作为优选，所述消泡剂为AFE-3168消泡剂。
作为优选，所述pH调节剂为二甲基乙醇胺。
本发明还提供了所述绿色环保建筑内墙防腐涂料的制备方法，具体为：将水性丙烯酸乳液、填料、1/2的分散剂、1/2的消泡剂和去离子水混合均匀，800转/min下搅拌30min后利用研磨机进行研磨，过150-200目筛；然后加入成膜助剂、1/2的分散剂、1/2的消泡剂、pH调节剂、增稠剂和防腐剂，混合均匀后1200转/min下搅拌40min，即得到所述所述绿色环保建筑内墙防腐涂料。
与现有技术相比，本发明具有如下有益效果：
本发明的防腐剂对抑制多种霉菌表现出增效作用，可以提高对霉菌的抑制效果，基于此可以减少防腐剂的添加量，降低成本。本发明的绿色环保建筑内墙防腐涂料中添加的所述防腐剂成分，可以抵御微生物对涂料的干扰，进而有利于延长涂料的贮藏时间。
具体实施方式
下面对本发明专利的技术方案进行清楚、完整的描述，显然，所描述的实施例是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域所属的技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
1.供试霉菌
详见表1。
表1供试霉菌
2.试验药剂
99％苄索氯铵原药、98％多菌灵原药
用DMSO溶解，然后用0.1％吐温-80水溶液分别配制成单剂母液，设置多组配比，各单剂和每组配比再用0.1％吐温-80水溶液按照等比方法稀释成5个质量浓度梯度，备用。
3.试验方法
3.1真菌类
菌丝生长速率法。将1mL试验药剂与9mL融化的PDA培养基混匀，倒入无菌培养皿中制成含药平板。待培养基凝固后，在含药平板中央放入1个霉菌菌饼(直径5mm)，以0.1％吐温-80水溶液为对照，每个处理设置3次重复。放入培养箱中，28±1℃下培养3d后，用十字交叉法测量霉菌菌落生长直径，计算抑制率。
4.数据分析
用DPS软件对试验药剂浓度对数值和菌丝生长抑制率几率值进行回归分析，计算各处理药剂的EC50，并根据Wadlley法评价增效作用。
SR≥1.5表示具有增效作用；SR≤0.5表示具有拮抗作用；0.5＜SR＜1.5表示具有相加作用，结果见表1-3。
表1苄索氯铵(A)和多菌灵(B)复配对变色曲霉的毒力
从表1可以看出，苄索氯铵和多菌灵在1-9：2-1的质量比范围内对变色曲霉的增效系数均大于1.5，表现出增效作用。
表2苄索氯铵(A)和多菌灵(B)复配对产紫青霉的毒力
从表2可以看出，苄索氯铵和多菌灵在1-9：2-1的质量比范围内对产紫青霉的增效系数均大于1.5，表现出增效作用。
表3苄索氯铵(A)和多菌灵(B)复配对黑曲霉的毒力
从表3可以看出，苄索氯铵和多菌灵在1-9：2-1的质量比范围内对黑曲霉的增效系数均大于1.5，表现出增效作用。
实施例2
一种绿色环保建筑内墙防腐涂料，由以下成分制备而成：水性丙烯酸乳液42kg、伊斯曼十二碳醇酯5kg、BYK 163分散剂4.5kg、煅烧高岭土24kg、WT-105A缔合型聚氨酯7kg、AFE-3168消泡剂2kg、二甲基乙醇胺0.3kg、防腐剂1.4kg及去离子水30kg；其中，防腐剂由苄索氯铵和多菌灵按3：1的质量比混合而成。
上述涂料的制备方法为：将水性丙烯酸乳液、煅烧高岭土、1/2的BYK 163分散剂、1/2的AFE-3168消泡剂和去离子水混合均匀，800转/min下搅拌30min后利用研磨机进行研磨，过180目筛；然后加入伊斯曼十二碳醇酯、二甲基乙醇胺、1/2的BYK 163分散剂、1/2的AFE-3168消泡剂、防腐剂和WT-105A缔合型聚氨酯，混合均匀后1200转/min下搅拌40min，即得到所述所述绿色环保建筑内墙防腐涂料。
前述对本发明的具体示例性实施方案的描述是为了说明和例证的目的。这些描述并非想将本发明限定为所公开的精确形式，并且很显然，根据上述教导，可以进行很多改变和变化。对示例性实施例进行选择和描述的目的在于解释本发明的特定原理及其实际应用，从而使得本领域的技术人员能够实现并利用本发明的各种不同的示例性实施方案以及各种不同的选择和改变。本发明的范围意在由权利要求书及其等同形式所限定。
Claims (9)
1.一种防腐剂，其特征在于，所述防腐剂的有效成分由苄索氯铵和多菌灵按1-9：2-1的质量比混合而成。
2.一种包括权利要求1所述防腐剂的绿色环保建筑内墙防腐涂料，其特征在于，以重量份计由以下成分制备而成：水性丙烯酸乳液30-60份、成膜助剂3-6份、分散剂2-5份、填料20-40份、增稠剂6-8份、消泡剂1-2份、pH调节剂0.2-0.3份、所述防腐剂1-2份及去离子水25-30份。
3.根据权利要求2所述的绿色环保建筑内墙防腐涂料，其特征在于，所述成膜助剂为伊斯曼十二碳醇酯。
4.根据权利要求2所述的绿色环保建筑内墙防腐涂料，其特征在于，所述分散剂为BYK163。
5.根据权利要求2所述的绿色环保建筑内墙防腐涂料，其特征在于，所述填料为煅烧高岭土。
6.根据权利要求2所述的绿色环保建筑内墙防腐涂料，其特征在于，所述增稠剂为WT-105A缔合型聚氨酯。
7.根据权利要求2所述的绿色环保建筑内墙防腐涂料，其特征在于，所述消泡剂为AFE-3168消泡剂。
8.根据权利要求2所述的绿色环保建筑内墙防腐涂料，其特征在于，所述pH调节剂为二甲基乙醇胺。
9.一种权利要求2-8任一项所述绿色环保建筑内墙防腐涂料的制备方法，其特征在于，具体为：将水性丙烯酸乳液、填料、1/2的分散剂、1/2的消泡剂和去离子水混合均匀，800转/min下搅拌30min后利用研磨机进行研磨，过150-200目筛；然后加入成膜助剂、1/2的分散剂、1/2的消泡剂、pH调节剂、增稠剂和防腐剂，混合均匀后1200转/min下搅拌40min，即得到所述所述绿色环保建筑内墙防腐涂料。