CN117100338A - 一种全缝线锚钉 - Google Patents
一种全缝线锚钉 Download PDFInfo
- Publication number
- CN117100338A CN117100338A CN202310970688.5A CN202310970688A CN117100338A CN 117100338 A CN117100338 A CN 117100338A CN 202310970688 A CN202310970688 A CN 202310970688A CN 117100338 A CN117100338 A CN 117100338A
- Authority
- CN
- China
- Prior art keywords
- flat belt
- full
- absorbable
- suture anchor
- braiding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种全缝线锚钉，包括由可吸收纱线制成的牵拉芯线和编织扁带，牵拉芯线和编织扁带一体编织成型，且牵拉芯线被配置为可活动抽拉地交错穿插于编织扁带上，可吸收纱线被配置为具有可释放的促骨生长成分。本发明的全缝线锚钉整体是由包含有促骨生长成分的可吸收纱线制成的，锚固后，随着组织重建，可吸收纱线逐渐降解，同时可吸收纱线释放促骨生长成分从而促进骨骼再生，待组织重建成功，可吸收性纱线完全降解成小分子并被机体吸收，从而为组织修复减少了炎症、瘢痕组织甚至引发癌症的风险。
Description
技术领域
本发明涉及医疗器械技术领域，具体涉及一种全缝线锚钉。
背景技术
机体运动软组织主要包括维持肌肉骨骼系统的各种肌腱、韧带等，因具有细胞含量低、成血管能力弱的缺陷，导致其一旦断裂，自愈的概率很小。因此肌腱/韧带损伤治疗一直是运动医学领域内的研究热点，其最大的难点在于将断裂组织与骨头重新桥接以达到组织重建。现在普遍使用的手术治疗方式是带线锚钉锚固骨头，再用缝线将受损组织连接到骨头上，以此达到桥接的目的。近些年来，带线锚钉由硬质的锚钉过渡到软质的全缝线锚钉，硬质锚钉主要包括钛合金类、聚醚醚酮(PEEK)类等刚度大且耐腐蚀的材料，但其长期植入易引发炎症反应或需进行二次手术取出会造成机体二次伤害。全缝线锚钉一般由线锚和缝线组成，因线锚是具有松软性能的编织物，其材料及结构具有松软性、易于植入骨中，且缝线拉紧后锚钉收缩团聚因具有一定的刚度即可稳定地锚固在骨道中，从而减少了对骨的伤害。但是，现在市面上的全缝线锚钉都是将线锚和缝线各自编织出来后再经二次组装而成，具有不易操作且易损伤线锚、缝线的缺陷。此外，市面上的全缝线锚钉所编织用的纱线一般为聚酯(PET)、超高分子量聚乙烯(UHMWPE)、聚丙烯(PP)、碳纤维(C)等不可降解的高分子材料，植入体内后，因不可降解、不可吸收而具有潜在的风险，易引发异物排斥导致炎症反应，长期存在甚至可能导致癌变等。
发明内容
针对现有技术的不足，本发明提供了一种全缝线锚钉，其主要解决的是现有全缝线锚钉由不可吸收材料制成，易引发异物排斥导致炎症反应的技术问题。
为达到上述目的，本发明是通过以下技术方案实现的：
一种全缝线锚钉，包括由可吸收纱线制成的牵拉芯线和编织扁带，牵拉芯线和编织扁带一体编织成型，且牵拉芯线被配置为可活动抽拉地交错穿插于编织扁带上，可吸收纱线被配置为具有可释放的促骨生长成分。
进一步，可吸收纱线由可吸收材料制成，可吸收材料包括聚乳酸、聚羟基乙酸、聚己内酯、羟基乙酸-乳酸共聚物、聚对二氧环己酮、聚羟基丁酸酯、聚羟基丁酸、海藻酸盐、丝素蛋白、胶原、明胶、甲壳素、纤维素纤维中的一种或多种。
进一步，与可吸收纱线结合的促骨生长成分包括无机磷酸钙、生长因子、糖胺聚糖中的一种或多种。
进一步，无机磷酸钙为羟基磷灰石或β-磷酸三钙；生长因子为骨形态发生蛋白-2或胰岛素样生长因子-1；糖胺聚糖为硫酸软骨素。
进一步，促骨生长成分通过掺杂或交联的方式与可吸收材料混合制成可吸收纱线，或促骨生长成分通过涂层或包覆的方式与由可吸收材料预制的可吸收纱线结合在一起。
进一步，编织扁带由若干可吸收纱线通过编织机进行交叉编织成型，且在编织扁带编织成型的过程中，牵拉芯线可活动抽拉地交错穿插连接在编织扁带中。
进一步，编织扁带中交错穿插连接有若干与牵拉芯线平行设置的芯纱，芯纱由所述可吸收纱线制成，且牵拉芯线、编织扁带和芯纱一体编织成型在一起。
进一步，编织扁带呈长条状，编织扁带的长度为200mm～500mm，宽度为10mm～50mm，在编织扁带的两端分别预留一段100mm～1000mm长的牵拉芯线。
进一步，编织扁带上交错穿插连接有两根牵拉芯线。
进一步，编织扁带呈两头宽、中间窄的沙漏状结构。
上述技术方案具有如下优点或有益效果：
本发明所述的全缝线锚钉中，全缝线锚钉整体是由包含有促骨生长成分的可吸收纱线制成的，锚固后，随着组织重建，可吸收纱线逐渐降解，同时可吸收纱线释放促骨生长成分从而促进骨骼再生，待组织重建成功，可吸收性纱线完全降解成小分子并被机体吸收，从而为组织修复减少了炎症、瘢痕组织甚至引发癌症的风险。此外，本实施例的全缝线锚钉的牵拉芯线和编织扁带是利用编织机一体编织成型在一起的，无需像现有技术的那般将线锚和缝线各自编织出来后再经二次组装，便于生产和使用，避免了线锚和缝线在二次组装时而导致的损伤问题。
附图说明
图1是本发明实施例一的全缝线锚钉的立体结构示意图。
图2是本发明实施例一的全缝线锚钉的平面结构示意图。
图3是本发明实施例一的全缝线锚钉的半对折状态示意图。
图4是本发明实施例一的全缝线锚钉的全对折状态示意图。
图5是本发明实施例二的全缝线锚钉的平面结构示意图。
标号说明：
1、牵拉芯线，2、编织扁带，3、芯纱。
具体实施方式
下面结合附图及实施例对本发明作进一步描述。
在本发明的描述中，需要理解的是，术语“上”、“下”、“前”、“后”、“左”、“右”、“顶”、“底”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
实施例一
请参照附图1至附图4，本发明的一种实施例提供一种全缝线锚钉，包括由可吸收纱线制成的牵拉芯线1(相当于缝线)和编织扁带2(相当于线锚)，牵拉芯线1和编织扁带2一体编织成型，且牵拉芯线1被配置为可活动抽拉地交错穿插于编织扁带2上，可吸收纱线被配置为具有可释放的促骨生长成分。可以理解的是，本实施例中，该全缝线锚钉的编织扁带2对折后通过插入器顶着插入到预制的骨道内，对折的编织扁带2依靠与骨道内壁的摩擦力保持在骨道内，而后抽拉牵拉芯线1的两端，编织扁带2将产生收缩、折叠等运动进而形成花簇/球团状结构从而锚固在骨道内，由于编织扁带2材质松软，对骨头的损伤较小，且全缝线锚钉整体是由包含有促骨生长成分的可吸收纱线制成的，锚固后，随着组织重建，可吸收纱线逐渐降解，同时可吸收纱线释放促骨生长成分从而促进骨骼再生，待组织重建成功，可吸收性纱线完全降解成小分子并被机体吸收，从而为组织修复减少了炎症、瘢痕组织甚至引发癌症的风险。此外，本实施例的全缝线锚钉的牵拉芯线1和编织扁带2是利用编织机一体编织成型在一起的，无需像现有技术的那般将线锚和缝线各自编织出来后再经二次组装，便于生产和使用，避免了线锚和缝线在二次组装时而导致的损伤问题。
请参照附图1至附图4，其中一种较优实施例中，可吸收纱线由可吸收材料制成，可吸收材料包括聚乳酸(PLA)、聚羟基乙酸(PGA)、聚己内酯(PCL)、羟基乙酸-乳酸共聚物(PLGA)、聚对二氧环己酮(PPDO)、聚羟基丁酸酯(PHA)、聚羟基丁酸(PHB)、海藻酸盐(SA)、丝素蛋白(SF)、胶原(COL)、明胶(HA)、甲壳素(CH)、纤维素纤维(CL)中的一种或多种。其中一种较优实施例中，与可吸收纱线结合的促骨生长成分包括无机磷酸钙、生长因子、糖胺聚糖中的一种或多种。本实施例中，优选地，无机磷酸钙为羟基磷灰石(HA)或β-磷酸三钙(β-TCP)；生长因子为骨形态发生蛋白-2(BMP-2或胰岛素样生长因子-1(IGF－1)；糖胺聚糖为硫酸软骨素(CS)。进一步地，促骨生长成分通过掺杂或交联的方式与可吸收材料混合制成可吸收纱线，或促骨生长成分通过涂层、包覆的方式与由可吸收材料预制的可吸收纱线结合在一起。
请参照附图1至附图4，其中一种较优实施例中，编织扁带2由若干可吸收纱线通过编织机进行交叉编织成型，且在编织扁带2编织成型的过程中，牵拉芯线1可活动抽拉地交错穿插连接在编织扁带2中。其中一种较优实施例中，优选地，编织扁带2中交错穿插连接有若干与牵拉芯线1平行设置的芯纱3，芯纱3由所述可吸收纱线制成，且牵拉芯线1、编织扁带2和芯纱3一体编织成型在一起。可以理解的是，本实施例中，通过增加若干平行于牵拉芯线1且交错穿插连接在编织扁带2中的芯纱3，可以增强编织扁带2在使用过程中收缩成团后后的整体强度，进而提高收缩成团后的编织扁带2与骨道内壁之间的锚固稳定性。
请参照附图1至附图4，其中一种较优实施例中，编织扁带2呈长条状，编织扁带2的长度为200mm～500mm，宽度为10mm～50mm，在编织扁带2的两端分别预留一段100mm～1000mm长的牵拉芯线1。可以理解的是，在安装过程中，待对折的编织扁带2通过插入器(对折的编织扁带2对称贴合于插入器两侧，且插入器端部抵压着编织扁带2的中间部位)插入到骨道内部之后，通过牵拉预留出来的牵拉芯线1可以使对折的编织扁带2收缩成团进而锚固在骨道内部，而后，牵拉芯线1可以用于断裂软组织的桥接、缝合等。
请参照附图1至附图4，其中一种较优实施例中，编织扁带2上交错穿插连接有两根牵拉芯线1。本实施例中，牵拉芯线1可以是中空结构或芯鞘结构。
实施例二
请参照附图5，本实施例与实施例一的区别在于，编织扁带2呈两头宽、中间窄的沙漏状结构。可以理解的是，本实施例中，通过将编织扁带2配置为呈两头宽、中间窄的沙漏状结构，使得编织扁带2可以更好地进行对折以便通过插入器将其插入到骨道内。
以上所述，实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述实施例所记载的技术方案进行修改，或者对其中的部分技术特征进行等同替换；而这些修改或替换，并不使相应技术方案脱离本发明实施例技术方案的精神和范围，因此本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明的保护范围。
Claims (10)
1.一种全缝线锚钉，其特征在于：包括由可吸收纱线制成的牵拉芯线(1)和编织扁带(2)，牵拉芯线(1)和编织扁带(2)一体编织成型，且牵拉芯线(1)被配置为可活动抽拉地交错穿插于编织扁带(2)上，可吸收纱线被配置为具有可释放的促骨生长成分。
2.根据权利要求1所述的全缝线锚钉，其特征在于：可吸收纱线由可吸收材料制成，可吸收材料包括聚乳酸、聚羟基乙酸、聚己内酯、羟基乙酸-乳酸共聚物、聚对二氧环己酮、聚羟基丁酸酯、聚羟基丁酸、海藻酸盐、丝素蛋白、胶原、明胶、甲壳素、纤维素纤维中的一种或多种。
3.根据权利要求1所述的全缝线锚钉，其特征在于：与可吸收纱线结合的促骨生长成分包括无机磷酸钙、生长因子、糖胺聚糖中的一种或多种。
4.根据权利要求3所述的全缝线锚钉，其特征在于：无机磷酸钙为羟基磷灰石或β-磷酸三钙；生长因子为骨形态发生蛋白-2或胰岛素样生长因子-1；糖胺聚糖为硫酸软骨素。
5.根据权利要求1所述的全缝线锚钉，其特征在于：促骨生长成分通过掺杂或交联的方式与可吸收材料混合制成可吸收纱线，或促骨生长成分通过涂层或包覆的方式与由可吸收材料预制的可吸收纱线结合在一起。
6.根据权利要求1所述的全缝线锚钉，其特征在于：编织扁带(2)由若干可吸收纱线通过编织机进行交叉编织成型，且在编织扁带(2)编织成型的过程中，牵拉芯线(1)可活动抽拉地交错穿插连接在编织扁带(2)中。
7.根据权利要求6所述的全缝线锚钉，其特征在于：编织扁带(2)中交错穿插连接有若干与牵拉芯线(1)平行设置的芯纱(3)，芯纱(3)由所述可吸收纱线制成，且牵拉芯线(1)、编织扁带(2)和芯纱(3)一体编织成型在一起。
8.根据权利要求1所述的全缝线锚钉，其特征在于：编织扁带(2)呈长条状，编织扁带(2)的长度为200mm～500mm，宽度为10mm～50mm，在编织扁带(2)的两端分别预留一段100mm～1000mm长的牵拉芯线(1)。
9.根据权利要求1所述的全缝线锚钉，其特征在于：编织扁带(2)上交错穿插连接有两根牵拉芯线(1)。
10.根据权利要求1至9任一项所述的全缝线锚钉，其特征在于：编织扁带(2)呈两头宽、中间窄的沙漏状结构。