CN117003541B - 一种防火隔热型憎水岩棉板及其制备方法 - Google Patents
一种防火隔热型憎水岩棉板及其制备方法 Download PDFInfo
- Publication number
- CN117003541B CN117003541B CN202311026527.7A CN202311026527A CN117003541B CN 117003541 B CN117003541 B CN 117003541B CN 202311026527 A CN202311026527 A CN 202311026527A CN 117003541 B CN117003541 B CN 117003541B
- Authority
- CN
- China
- Prior art keywords
- parts
- rock wool
- heat
- layer
- fireproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及保温技术领域，提出了一种防火隔热型憎水岩棉板及其制备方法，包括由上至下依次设置的憎水防火层、粘结层和隔热保温层，所述憎水防火层包括以下重量份的组分：岩棉30~50份，有机硅改性脂环族环氧树脂10~15份，聚磷酸三聚氰胺5~10份，有机硅憎水剂3~5份，硅酸钠3~5份；所述粘结层包括以下重量份的组分：环氧树脂5~25份，硅酸钠5~25份，水50~90份；所述隔热保温层包括以下重量份的组分：岩棉50~70份，膨胀石墨20~30份，填料10~15份，硅酸钠3~5份。通过上述技术方案，解决了相关技术中岩棉板拉拔强度低、吸水率高的问题。
Description
技术领域
本发明涉及保温材料技术领域，具体的，涉及一种防火隔热型憎水岩棉板及其制备方法。
背景技术
岩棉板是以天然岩石如玄武岩、辉长岩、白云石、铁矿石为主要原材料，经高温熔融加工而成的无机纤维板，因具有良好的保温、吸音、透气性能，广泛应用在石化、建筑、工矿领域。在防火方面，岩棉板属于A级不燃材料，在外墙保温领域也有良好的应用前景。
但是，与有机保温板如EPS板、XPS板、PU板等相比，市面上的岩棉板的拉拔强度低，且吸水率高，使得岩棉板在外墙保温中应用时，存在因拉拔强度低而导致无法保证抗风压安全系数、因吸水率高而导致易吸水开裂的问题。因此，开发一种拉拔强度高的防火隔热型憎水岩棉板极为必要。
发明内容
本发明提出一种防火隔热型憎水岩棉板及其制备方法，解决了相关技术中岩棉板拉拔强度低、吸水率高的问题。
本发明的技术方案如下：
本发明提出了一种防火隔热型憎水岩棉板，包括由上至下依次设置的憎水防火层、粘结层和隔热保温层，
所述憎水防火层包括以下重量份的组分：岩棉30~50份，有机硅改性脂环族环氧树脂10~15份，聚磷酸三聚氰胺5~10份，有机硅憎水剂3~5份，硅酸钠3~5份；
所述粘结层包括以下重量份的组分：环氧树脂5~25份，硅酸钠5~25份，水50~90份；
所述隔热保温层包括以下重量份的组分：岩棉50~70份，膨胀石墨20~30份，填料10~15份，硅酸钠3~5份。
作为进一步的技术方案，所述有机硅改性脂环族环氧树脂包括EPS-201、EPS-218、EPS-231中的一种或几种。
作为进一步的技术方案，所述有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比2~3:1的混合物。
作为进一步的技术方案，所述粘结层包括由上至下依次设置的第一粘结层、第二粘结层；
所述第一粘结层中环氧树脂的质量大于硅酸钠的质量；
所述第二粘结层中环氧树脂的质量小于硅酸钠的质量。
作为进一步的技术方案，所述第一粘结层中环氧树脂与硅酸钠的质量比为3~4:1，所述第二粘结层中环氧树脂与硅酸钠的质量比为1:3~4。
作为进一步的技术方案，所述第一粘结层与所述憎水防火层的厚度比为1:13~17，所述第二粘结层与所述隔热保温层的厚度比为1:15~17。
作为进一步的技术方案，所述第一粘结层与所述憎水防火层的厚度比为1:15，所述第二粘结层与所述隔热保温层的厚度比为1:16。
作为进一步的技术方案，所述填料包括高岭土、玻璃微珠、滑石粉、碳酸钙中的一种或多种。
本发明还提出了所述防火隔热型憎水岩棉板的制备方法，其特征在于，包括以下步骤：
S1、将岩棉与膨胀石墨、填料、硅酸钠混合均匀后，加水混合，得到隔热保温层浆料，压制成型，得到隔热保温层；
S2、将环氧树脂与硅酸钠和水混合均匀，涂布于隔热保温层上，干燥，得到粘结层；
S3、将岩棉与有机硅改性脂环族环氧树脂、聚磷酸三聚氰胺、有机硅憎水剂、硅酸钠混合均匀后，加水混合，得到憎水防火层浆料；将憎水防火层浆料涂布于粘结层上，烘干，得到防火隔热型憎水岩棉板。
本发明还提出了所述防火隔热型憎水岩棉板在外墙保温中的应用。
本发明的工作原理及有益效果为：
1、本发明中，岩棉板包括由上至下依次设置的憎水防火层、粘结层和隔热保温层，憎水防火层中加入有机硅改性脂环族环氧树脂和有机硅憎水剂，二者协同，显著提高了憎水性能，从而显著降低了岩棉板的吸水率，解决了岩棉板因吸水率高而导致的易吸水开裂的问题，此外，有机硅改性脂环族环氧树脂协同作用，提高了岩棉板的防火性能。隔热保温层中加入膨胀石墨，显著提高了岩棉板的拉拔强度，从而解决了岩棉板在外墙保温中应用时因拉拔强度低而导致无法保证抗风压安全系数的问题。
2、本发明中，憎水防火层中，有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比2~3:1的混合物时，进一步降低了岩棉板的吸水率。
3、本发明中，粘结层包括由上至下依次设置的第一粘结层和第二粘结层，通过对第一粘结层和第二粘结层中环氧树脂和硅酸钠的质量比进行优化设计，进一步提高了岩棉板的拉拔强度。
4、本发明中，第一粘结层中环氧树脂与硅酸钠的质量比为3~4:1、第二粘结层中环氧树脂与硅酸钠的质量比为1:3~4时，进一步提高了岩棉板的拉拔强度。
5、本发明中，通过对憎水防火层与第一粘结层的厚度比、第二粘结层与隔热保温层的厚度比进行优化设计，进一步提高了岩棉板的拉拔强度，降低了岩棉板的吸水率。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都涉及本发明保护的范围。
实施例1
一种防火隔热性憎水岩棉板，包括由上至下依次设置的憎水防火层、粘结层和隔热保温层，由以下方法制备：
S0、备料：按照以下憎水防火层、粘结层和隔热保温层的原料配方，准备各层原料：
憎水防火层原料：岩棉30份，有机硅改性脂环族环氧树脂EPS-201 10份，聚磷酸三聚氰胺5份，有机硅憎水剂SHP-60 3份，硅酸钠3份；
粘结层原料：环氧树脂E44 5份，硅酸钠5份，水50份；
隔热保温层原料：岩棉50份，膨胀石墨20份，高岭土10份，硅酸钠3份；
S1、将隔热保温层的原料混合均匀后，加入80份水混合，得到隔热保温层浆料，压制成型，得到隔热保温层；
S2、将粘结层的原料混合均匀，涂布于隔热保温层上，干燥，得到粘结层；
S3、将憎水防火层原料混合均匀，加入50份水混合，得到憎水防火层浆料；将憎水防火层浆料涂布于粘结层上，烘干，得到防火隔热型憎水岩棉板。
实施例2
一种防火隔热性憎水岩棉板，包括由上至下依次设置的憎水防火层、粘结层和隔热保温层，由以下方法制备：
S0、备料：按照以下憎水防火层、粘结层和隔热保温层的原料配方，准备各层原料：
憎水防火层原料：岩棉50份，有机硅改性脂环族环氧树脂EPS-201 15份，聚磷酸三聚氰胺10份，有机硅憎水剂SHP-60 5份，硅酸钠5份；
粘结层原料：环氧树脂E44 25份，硅酸钠25份，水90份；
隔热保温层原料：岩棉70份，膨胀石墨30份，玻璃微珠15份，硅酸钠5份；
S1、将隔热保温层的原料混合均匀后，加入100份水混合，得到隔热保温层浆料，压制成型，得到隔热保温层；
S2、将粘结层的原料混合均匀，涂布于隔热保温层上，干燥，得到粘结层；
S3、将憎水防火层原料混合均匀，加入65份水混合，得到憎水防火层浆料；将憎水防火层浆料涂布于粘结层上，烘干，得到防火隔热型憎水岩棉板。
实施例3
本实施例与实施例1的区别仅在于有机硅改性脂环族环氧树脂为EPS-218。
实施例4
本实施例与实施例1的区别仅在于有机硅改性脂环族环氧树脂为EPS-231。
实施例5
本实施例与实施例1的区别仅在于有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比4:1的混合物。
实施例6
本实施例与实施例1的区别仅在于有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比1:1的混合物。
实施例7
本实施例与实施例1的区别仅在于有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比2:1的混合物。
实施例8
本实施例与实施例1的区别仅在于有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比3:1的混合物。
实施例9
一种防火隔热性憎水岩棉板，包括由上至下依次设置的憎水防火层、第一粘结层、第二粘结层和隔热保温层，由以下方法制备：
S0、备料：按照以下憎水防火层、粘结层和隔热保温层的原料配方，准备各层原料：
憎水防火层原料：岩棉30份，有机硅改性脂环族环氧树脂EPS-201 10份，聚磷酸三聚氰胺5份，有机硅憎水剂SHP-60 3份，硅酸钠3份；
第一粘结层原料：环氧树脂E44 25份，硅酸钠5份，水50份；
第二粘结层原料：环氧树脂E44 5份，硅酸钠25份，水50份；
隔热保温层原料：岩棉50份，膨胀石墨20份，填料10份，硅酸钠3份；
S1、将隔热保温层的原料混合均匀后，加入80份水混合，得到隔热保温层浆料，压制成型，得到隔热保温层，厚度为68mm；
S2、将第二粘结层的原料混合均匀，涂布于隔热保温层上，干燥，得到第二粘结层，厚度为4mm，将第一粘结层的原料混合均匀，涂布于第二粘结层上，干燥，得到第一粘结层，厚度为2mm；
S3、将憎水防火层原料混合均匀，加入50份水混合，得到憎水防火层浆料；将憎水防火层浆料涂布于第一粘结层上，烘干，得到憎水防火层，厚度为26mm，最终得到防火隔热型憎水岩棉板。
实施例10
本实施例与实施例9的区别仅在于，
第一粘结层原料：环氧树脂E44 15份，硅酸钠10份，水50份；
第二粘结层原料：环氧树脂E44 15份，硅酸钠10份，水50份。
实施例11
本实施例与实施例9的区别仅在于，
第一粘结层原料：环氧树脂E44 15份，硅酸钠5份，水50份；
第二粘结层原料：环氧树脂E44 5份，硅酸钠15份，水50份。
实施例12
本实施例与实施例9的区别仅在于，
第一粘结层原料：环氧树脂E44 20份，硅酸钠5份，水50份；
第二粘结层原料：环氧树脂E44 5份，硅酸钠20份，水50份。
实施例13
本实施例与实施例9的区别仅在于，
憎水防火层、第一粘结层、第二粘结层和隔热保温层的厚度分别为34mm、2mm、4mm、60mm。
实施例14
本实施例与实施例9的区别仅在于，
憎水防火层、第一粘结层、第二粘结层和隔热保温层的厚度分别为30mm、2mm、4mm、64mm。
对比例1
本实施例与实施例1的区别仅在于憎水防火层中未加入有机硅改性脂环族环氧树脂。
对比例2
本实施例与实施例1的区别仅在于憎水防火层中未加入有机硅憎水剂。
对比例3
本实施例与实施例1的区别仅在于憎水防火层中未加入有机硅改性脂环族环氧树脂和有机硅憎水剂。
对比例4
本实施例与实施例1的区别仅在于隔热保温层中未加入膨胀石墨。
对实施例1~14及对比例1~4的岩棉板进行如下性能测试：
①吸水量：按照GB/T 259752010《建筑外墙外保温用岩棉制品》中附录 B中规定的方法进行测试；
②拉拔强度：按照JG192003《膨胀聚板薄抹灰外墙外保温系统》附录 D中规定的方法进行测试，试件尺寸为200 mm×200mm，厚度为100mm；
测试结果如下表所示：
表1 实施例1~14及对比例1~4的岩棉板的性能测试结果
与对比例1-4相比，实施例1-14的岩棉板的拉拔强度高至22.9~26.0kPa，吸水率低至0.007~0.022 kg/m2，说明采用本发明的实施例1~14的岩棉板的配方及制备方法，显著提高了岩棉的拉拔强度，降低了岩棉板的吸水率。
与实施例1和实施例4相比，实施例5~8的岩棉板吸水率降低，且实施例5~8中，实施例6~7的岩棉板的吸水率更低，说明憎水防火层中，有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比2~3:1的混合物时，进一步降低了岩棉板的吸水率。
与实施例1相比，实施例9~12的岩棉板的拉拔强度更高，说明将粘结层分为环氧树脂和硅酸钠质量比不同的第一粘结层和第二粘结层，进一步提高了岩棉板的拉拔强度。
与实施例9和实施例13相比，实施例14的岩棉板的吸水率更低，拉拔强度更高，说明当第一粘结层与憎水防火层的厚度比为1:15、第二粘结层与隔热保温层的厚度比为1:16时，进一步提高了岩棉板的拉拔强度，降低了岩棉板的吸水率。
与实施例1相比，对比例1~3的岩棉板的吸水率均明显提高，说明有机硅改性脂环族环氧树脂和有机硅憎水剂协同作用，进一步降低了岩棉板的吸水率。
与实施例1相比，对比例4的岩棉板的拉拔强度降低，说明隔热保温层中加入膨胀石墨，显著提高了岩棉板的拉拔强度。
以上仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (7)
1.一种防火隔热型憎水岩棉板，其特征在于，包括由上至下依次设置的憎水防火层、粘结层和隔热保温层，
所述憎水防火层包括以下重量份的组分：岩棉30~50份，有机硅改性脂环族环氧树脂10~15份，聚磷酸三聚氰胺5~10份，有机硅憎水剂3~5份，硅酸钠3~5份；
所述粘结层包括以下重量份的组分：环氧树脂5~25份，硅酸钠5~25份，水50~90份；
所述粘结层包括由上至下依次设置的第一粘结层、第二粘结层；
所述第一粘结层中环氧树脂与硅酸钠的质量比为3~4:1，所述第二粘结层中环氧树脂与硅酸钠的质量比为1:3~4；
所述隔热保温层包括以下重量份的组分：岩棉50~70份，膨胀石墨20~30份，填料10~15份，硅酸钠3~5份；
所述第一粘结层与所述憎水防火层的厚度比为1:13~17，所述第二粘结层与所述隔热保温层的厚度比为1:15~17。
2.根据权利要求1所述的一种防火隔热型憎水岩棉板，其特征在于，所述有机硅改性脂环族环氧树脂包括EPS-201、EPS-218、EPS-231中的一种或几种。
3.根据权利要求2所述的一种防火隔热型憎水岩棉板，其特征在于，所述有机硅改性脂环族环氧树脂为EPS-201和EPS-218质量比2~3:1的混合物。
4.根据权利要求1所述的一种防火隔热型憎水岩棉板，其特征在于，所述第一粘结层与所述憎水防火层的厚度比为1:15，所述第二粘结层与所述隔热保温层的厚度比为1:16。
5.根据权利要求1所述的一种防火隔热型憎水岩棉板，其特征在于，所述填料包括高岭土、玻璃微珠、滑石粉、碳酸钙中的一种或多种。
6.根据权利要求1~5任意一项所述的一种防火隔热型憎水岩棉板的制备方法，其特征在于，包括以下步骤：
S1、将岩棉与膨胀石墨、填料、硅酸钠混合均匀后，加水混合，得到隔热保温层浆料，压制成型，得到隔热保温层；
S2、将环氧树脂与硅酸钠和水混合均匀，涂布于隔热保温层上，干燥，得到粘结层；
S3、将岩棉与有机硅改性脂环族环氧树脂、聚磷酸三聚氰胺、有机硅憎水剂、硅酸钠混合均匀后，加水混合，得到憎水防火层浆料；将憎水防火层浆料涂布于粘结层上，烘干，得到防火隔热型憎水岩棉板。
7.根据权利要求1~5任意一项所述的一种防火隔热型憎水岩棉板或权利要求6所述的制备方法制得的防火隔热型憎水岩棉板在外墙保温中的应用。