CN116947470B - 具有仿旧和黑云印记效果的剃花纹陶瓷及其制备方法 - Google Patents
具有仿旧和黑云印记效果的剃花纹陶瓷及其制备方法 Download PDFInfo
- Publication number
- CN116947470B CN116947470B CN202311046610.0A CN202311046610A CN116947470B CN 116947470 B CN116947470 B CN 116947470B CN 202311046610 A CN202311046610 A CN 202311046610A CN 116947470 B CN116947470 B CN 116947470B
- Authority
- CN
- China
- Prior art keywords
- parts
- soil
- old
- matte white
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及陶瓷领域，具体涉及一种具有仿旧和黑云印记效果的剃花纹陶瓷及其制备方法，坯体的表面覆盖有仿旧装饰层，仿旧装饰层包括多层的、交替设置的黑云浆土和哑光白装饰土。坯体在烧成后能够形成致密的釉面效果，其与表面具有孔隙的化妆土形成紧密结合，因此坯体与仿旧装饰层的结合强度高，且坯体自带的釉面效果与表面的仿旧装饰层效果均通过一次烧成，整体的烧成工艺简单；哑光白装饰土的孔隙率高，且越往里层的哑光白装饰土的孔隙率越高，因此黑云浆土能够透过哑光白装饰土向外渗透，黑云浆土在哑光白装饰土上根据需求自由分布，烧成后在哑光白装饰土上形成仿黑云的印记，且由于不同部位黑云浆土叠加和覆盖的程度不同，因此印记的深浅不一；从仿旧装饰层的剃花纹透露出的坯体呈现自身光亮橙红色的釉面效果，而仿旧装饰层本身以白色为底色、其中透着黑云般的、深浅不一的仿旧印记，具有古旧的美感。
Description
技术领域
本发明涉及陶瓷领域，具体的涉及具有仿旧和黑云印记效果的剃花纹陶瓷及其制备方法。
背景技术
化妆土是一种常用的陶瓷装饰材料。化妆土具有质地细腻、色泽均匀、遮盖力较强、耐火度高、表现力丰富等特性。化妆土装饰，就是使用化妆土来改变器皿外观的一种装饰形式。运用化妆土，可以改变坯体表面的颜色；掩盖坯体的粗糙及缺陷；使坯体表面更光滑，更易于着色；作为釉底料使用，可以使色釉显得更加鲜明；运用于不同的工艺，能够以有限的材料表现丰富多彩的装饰效果。最早的化妆土装饰大都以陶衣或釉底料的形式出现，功能性多于装饰性，随着制陶技术的发展，各种各样的化妆土装饰技法相继形成。现有的化妆土装饰效果较为单一，多以呈现某种单一色彩为目的，无法形成丰富的釉面效果，有鉴于此，本案由此产生。
发明内容
本发明的一个目的是通过具有仿旧和黑云印记效果的剃花纹陶瓷及其制备方法解决至少上述问题。
为解决上述技术问题，本发明采用的技术方案如下：具有仿旧和黑云印记效果的剃花纹陶瓷，包括坯体，所述坯体的表面覆盖有仿旧装饰层，所述仿旧装饰层包括多层的、交替设置的黑云浆土和哑光白装饰土。
优选的，所述坯体的原料以重量份计，包括如下组分：高岭土10-15份、石英30-35份、长石8-12份、膨润土3-5份、滑石5-8份、精赤陶泥8-12份、工业氧化铁粉末3-5份，所述精赤陶泥的粒径为300-400目。
优选的，所述黑云浆土的原料以重量份计，包括如下组分：氧化铜10-12、氧化钴15-16份、氧化铁10-12份，透明釉20-30份、碳粉10-12份。
优选的，所述哑光白装饰土的原料以重量份计，包括如下组分：牛骨5-8份、白陶土40-45份、石英15-17份、长石30-35份、膨润土5-7份、阿拉伯树胶4-5份、聚乙烯醇4-5份。
优选的，所述仿旧装饰层的哑光白装饰土设有三层，从内往外的哑光白装饰土的原料依次还分别添加有：高分子混合物15-18份、淀粉18-20份、碳粉20-25份。
优选的，所述高分子混合物的原料以重量份计，包括如下组分：草酸铵5-10份、聚甲基丙烯酸甲酯5-10份、聚苯乙烯8-12份。
根据上述的具有仿旧和黑云印记效果的剃花纹陶瓷的制备方法，包括如下步骤：
步骤a、坯体成型，烘干；
步骤b、在坯体表面交替施加黑云浆土和哑光白装饰土，干燥；
步骤c、在仿旧装饰层上用笔勾画出装饰图案，用工具剃除仿旧装饰层上事先勾勒的图案的部分，直到露出坯体的本色为止；
步骤d、入窑炉烧成，哑光白装饰土内部的造孔剂在燃烧过程中产生孔隙，黑云浆土透过哑光白装饰土的孔隙向外渗透，在哑光白装饰土呈现深浅不一的黑色印记。
优选的，所述哑光白装饰土的制备方法如下：将哑光白装饰土的基体配料添加不同的造孔剂，研磨40-50min，之后添加阿拉伯树胶和聚乙烯醇，并继续研磨混合30-40min。
优选的，所述哑光白装饰土的基体材料和造孔剂的粒度为300目。
优选的，所述步骤d中，2小时内快速升温至600-800摄氏度，并保温2小时，哑光白装饰土内的造孔剂燃烧干净，之后5-6小时内升温至1250-1300摄氏度，保温6-8小时，然后自然降温。
由上述描述可知，本发明提供的具有仿旧和黑云印记效果的剃花纹陶瓷及其制备方法具有如下有益效果：坯体在烧成后能够形成致密的釉面效果，其与表面具有孔隙的化妆土形成紧密结合，因此坯体与仿旧装饰层的结合强度高，且坯体自带的釉面效果与表面的仿旧装饰层效果均通过一次烧成，整体的烧成工艺简单；哑光白装饰土的孔隙率高，且越往里层的哑光白装饰土的孔隙率越高，因此黑云浆土能够透过哑光白装饰土向外渗透，黑云浆土在哑光白装饰土上根据需求自由分布，烧成后在哑光白装饰土上形成仿黑云的印记，且由于不同部位黑云浆土叠加和覆盖的程度不同，因此印记的深浅不一；从仿旧装饰层的剃花纹透露出的坯体呈现自身光亮橙红色的釉面效果，而仿旧装饰层本身以白色为底色、其中透着黑云般的、深浅不一的仿旧印记，具有古旧的美感。
具体实施方式
以下通过具体实施方式对本发明作进一步的描述。
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
本发明的具有仿旧和黑云印记效果的剃花纹陶瓷，包括坯体，坯体的表面覆盖有仿旧装饰层，仿旧装饰层包括多层的、交替设置的黑云浆土和哑光白装饰土。
坯体的原料以重量份计，包括如下组分：高岭土10-15份、石英30-35份、长石8-12份、膨润土3-5份、滑石5-8份、精赤陶泥8-12份、工业氧化铁粉末3-5份，精赤陶泥的粒径为300-400目。坯体在釉烧过程中形成致密化合物，较传统坯体而言致密度更高，烧成后其表面自身具有橙红色釉面效果，如果采用普通坯料，剃花纹内部的坯体不好单独上釉，只能展示坯体的粗糙面，而本发明中坯体的原料在烧成后能够形成具有光亮的釉面效果，因此雕刻的剃花纹呈现坯体底色的光亮橙红色，而表面则为粗糙面的白色哑光化妆土，并带有黑云印记和具有仿旧效果，两者具有强烈的对比和冲突，独具美感；并且由于坯体的石英石含量高，在烧成过程中能够与其表面的带孔隙的仿旧装饰层紧密结合，使得仿旧装饰层不易脱落；坯体自带的釉面效果与表面的装饰层效果通过一次烧成，烧成工艺简单。
黑云浆土的原料以重量份计，包括如下组分：氧化铜10-12、氧化钴15-16份、氧化铁10-12份，透明釉20-30份、碳粉10-12份。黑云浆土中的多种氧化物为仿旧装饰层黑化的来源，氧化物渗透哑光白装饰土形成仿黑云的印记，碳粉在釉烧过程中燃烧产生气体，外溢的气体可以进一步带动氧化物向外渗透。
哑光白装饰土的原料以重量份计，包括如下组分：牛骨5-8份、白陶土40-45份、石英15-17份、长石30-35份、膨润土5-7份、阿拉伯树胶4-5份、聚乙烯醇4-5份。哑光白装饰土整体呈哑光白色，其中添加造孔剂，使其表面粗糙且具有孔隙，阿拉伯树胶、聚乙烯醇能提高其与坯体的粘结度。
仿旧装饰层的哑光白装饰土设有三层，从内往外的哑光白装饰土的原料依次还分别添加有：高分子混合物15-18份、淀粉18-20份、碳粉20-25份。从内往外的各层哑光白装饰土中添加不同的造孔剂，其造孔效果为：高分子混合物大于淀粉大于碳粉，具体的，最内层的哑光白装饰土的烧成后孔隙率为25-30％，中间层的哑光白装饰土的烧成后孔隙率为18-25％，最外层的哑光白装饰土的烧成后孔隙率为15-18％，因此烧成后从内往外孔隙率逐渐减小，因此最内层哑光白装饰土孔隙率高、黑云浆土能够渗透至外部，而最外层的哑光白装饰土的孔隙率低、能够兼顾黑云浆土的渗透性和保持装饰土本身强度，由于不同层的黑云浆土施加的区域可能不同，有的部位三层的黑云浆土渗透叠加，黑云浆土依次从各层的哑光白装饰土向外渗透，其形成的黑云印记颜色深且有层次、呈深灰色或黑色，有的部位只有一层或两层的黑云浆土相叠加，其形成的黑云印记颜色浅、呈浅灰色，表现到仿旧装饰层整体表面形成深浅不一的黑色仿旧印记，具有独特的仿旧效果。
高分子混合物的原料以重量份计，包括如下组分：草酸铵5-10份、聚甲基丙烯酸甲酯5-10份、聚苯乙烯8-12份。
具有仿旧和黑云印记效果的剃花纹陶瓷的制备方法，包括如下步骤：
步骤a、坯体成型，烘干；
步骤b、在坯体表面交替施加黑云浆土和哑光白装饰土，干燥；
步骤c、在仿旧装饰层上用笔勾画出装饰图案，用工具剃除仿旧装饰层上事先勾勒的图案的部分，直到露出坯体的本色为止；
步骤d、入窑炉烧成，哑光白装饰土内部的造孔剂在燃烧过程中产生孔隙，黑云浆土透过哑光白装饰土的孔隙向外渗透，在哑光白装饰土呈现深浅不一的黑色印记。坯体在烧成后能够形成致密的釉面效果，其与表面具有孔隙的化妆土形成紧密结合，因此坯体与仿旧装饰层的结合强度高，且坯体自带的釉面效果与表面的仿旧装饰层效果均通过一次烧成，整体的烧成工艺简单；哑光白装饰土的孔隙率高，且越往里层的哑光白装饰土的孔隙率越高，因此黑云浆土能够透过哑光白装饰土向外渗透，黑云浆土在哑光白装饰土上根据需求自由分布，烧成后在哑光白装饰土上形成仿黑云的印记，且由于不同部位黑云浆土叠加和覆盖的程度不同，因此印记的深浅不一；从仿旧装饰层的剃花纹透露出的坯体呈现自身光亮橙红色的釉面效果，而仿旧装饰层本身以白色为底色、其中透着黑云般的、深浅不一的仿旧印记，具有古旧的美感。
哑光白装饰土的制备方法如下：将哑光白装饰土的基体配料添加不同的造孔剂，研磨40-50min，之后添加阿拉伯树胶和聚乙烯醇，并继续研磨混合30-40min。
哑光白装饰土的基体材料和造孔剂的粒度为300目。
步骤d中，2小时内快速升温至600-800摄氏度，并保温2小时，哑光白装饰土内的造孔剂燃烧干净，之后5-6小时内升温至1250-1300摄氏度，保温6-8小时，然后自然降温。
上述仅为本发明的若干具体实施方式，但本发明的设计构思并不局限于此，凡利用此构思对本发明进行非实质性的改动，均应属于侵犯本发明保护范围的行为。
Claims (5)
1.具有仿旧和黑云印记效果的剃花纹陶瓷，其特征在于：包括坯体，所述坯体的表面覆盖有仿旧装饰层，所述仿旧装饰层包括多层的、交替设置的黑云浆土和哑光白装饰土；
所述坯体的原料以重量份计，包括如下组分：高岭土10-15份、石英30-35份、长石8-12份、膨润土3-5份、滑石5-8份、精赤陶泥8-12份、工业氧化铁粉末3-5份，所述精赤陶泥的粒径为300-400目；
所述黑云浆土的原料以重量份计，包括如下组分：氧化铜10-12份、氧化钴15-16份、氧化铁10-12份，透明釉20-30份、碳粉10-12份；
所述哑光白装饰土的原料以重量份计，包括如下组分：牛骨5-8份、白陶土40-45份、石英15-17份、长石30-35份、膨润土5-7份、阿拉伯树胶4-5份、聚乙烯醇4-5份；
所述仿旧装饰层的哑光白装饰土设有三层，从内往外的哑光白装饰土的原料依次还分别添加有：高分子混合物15-18份、淀粉18-20份、碳粉20-25份；
所述高分子混合物的原料以重量份计，包括如下组分：草酸铵5-10份、聚甲基丙烯酸甲酯5-10份、聚苯乙烯8-12份。
2.根据权利要求1所述的具有仿旧和黑云印记效果的剃花纹陶瓷的制备方法，其特征在于：包括如下步骤：
步骤a、坯体成型，烘干；
步骤b、在坯体表面交替施加黑云浆土和哑光白装饰土，干燥；
步骤c、在仿旧装饰层上用笔勾画出装饰图案，用工具剃除仿旧装饰层上事先勾勒的图案的部分，直到露出坯体的本色为止；
步骤d、入窑炉烧成，哑光白装饰土内部的造孔剂在燃烧过程中产生孔隙，黑云浆土透过哑光白装饰土的孔隙向外渗透，在哑光白装饰土呈现深浅不一的黑色印记。
3.根据权利要求2所述的具有仿旧和黑云印记效果的剃花纹陶瓷的制备方法，其特征在于：所述哑光白装饰土的制备方法如下：将哑光白装饰土的基体配料添加不同的造孔剂，研磨40-50min，之后添加阿拉伯树胶和聚乙烯醇，并继续研磨混合30-40min。
4.根据权利要求3所述的具有仿旧和黑云印记效果的剃花纹陶瓷的制备方法，其特征在于：所述哑光白装饰土的基体配料和造孔剂的粒度为300目。
5.根据权利要求2所述的具有仿旧和黑云印记效果的剃花纹陶瓷的制备方法，其特征在于：所述步骤d中，2小时内快速升温至600-800摄氏度，并保温2小时，哑光白装饰土内的造孔剂燃烧干净，之后5-6小时内升温至1250-1300摄氏度，保温6-8小时，然后自然降温。