CN116869738A - 一种可视防水敷料 - Google Patents
一种可视防水敷料 Download PDFInfo
- Publication number
- CN116869738A CN116869738A CN202310054709.9A CN202310054709A CN116869738A CN 116869738 A CN116869738 A CN 116869738A CN 202310054709 A CN202310054709 A CN 202310054709A CN 116869738 A CN116869738 A CN 116869738A
- Authority
- CN
- China
- Prior art keywords
- layer
- dressing
- visual
- visual waterproof
- waterproof dressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可视防水敷料，包括保护层、黏胶层、敷芯层和离型层；所述黏胶层为采用预聚体法制备的水性聚氨酯膜涂布丙烯酸酯压敏胶；所述敷芯层为高吸水性聚氨酯泡沫。本发明提供的可视防水敷料结构简单，使用方便同时可直接观察创面情况。可视防水敷料由保护层，黏胶层，敷芯层，离型层。黏胶层水性聚氨酯膜涂布丙烯酸酯压敏胶，敷芯层是吸水性好的镂空蜂窝状高吸水性聚氨酯泡沫。水性聚氨酯因结构中具有极性较强，相互间能形成氢键的酯胺基(‑NHC00‑)因而具有良好的透湿透气，防水柔软等良好性能。
Description
技术领域
本发明涉及医用材料技术领域，具体涉及一种可视防水敷料。
背景技术
现代创口敷料的一个重要功能，在于替代正常皮肤保护创口，并一直作用至创口愈合。它能抵御机械因素(如脏物，碰撞等)、抵御污染和化学刺激，防止再次感染，吸收渗液，创造促进创口愈合的微环境。目前临床上使用的敷料一般都是不透明的对伤口的观察很不方便，使用敷料后，若需要观察创面的愈合情况，需要将敷料撕下后才能观察，撕下后还需要换上新的敷料，这样不仅提高了医疗成本，而且更换敷料时，会使患者疼痛，多次更换敷料会增加患者的痛苦。或是敷料透明可直接观察创口但是无吸收创口渗出液的功能。并且很多敷料固定不牢固容易移位，以及如果使用时间过长，大部分敷料因为透气性不佳，会使伤口和伤口周围的皮肤发白，变软导致细菌的继发的感染，这样就会使伤口更加的恶化，同时，对于伤口或者创面含有大面积渗液时，大部分敷料由于吸液能力不足，其渗液残留在创面表面，一方面不利于伤口或者创面愈合，另一方面形成细菌滋生的病灶。现需要一种吸收渗液能力好，阻水透气性好，并能直接观察创面的愈合情况的医用敷料。
基于上述情况，本发明提出了一种可视防水敷料，可有效解决以上问题。
发明内容
本发明的目的在于提供一种能吸收创面渗出液并且可以不用撕开直接观察创面的一种可视防水敷料。本发明提供的可视防水敷料结构简单，使用方便同时可直接观察创面情况。可视防水敷料由保护层，黏胶层，敷芯层，离型层。黏胶层水性聚氨酯膜涂布丙烯酸酯压敏胶，敷芯层是吸水性好的镂空蜂窝状高吸水性聚氨酯泡沫。水性聚氨酯因结构中具有极性较强，相互间能形成氢键的酯胺基(-NHC00-)因而具有良好的透湿透气，防水柔软等良好性能。
本发明采用的敷芯不同于无纺布，脱脂棉等传统的常见敷芯，也不同于常见的聚氨酯泡沫，本发明采用的敷芯是一种高吸水性聚氨酯泡沫。聚氨酯具有良好的生物相容性，血液相容性，性能优良稳定被广泛用于医用领域。很多亲水性聚氨酯泡沫大多采用TDI,MDI为基体制备而成，这些芳香族聚氨酯结构不稳定容易生成羰基，醌式基团进而发生黄变，影响产品外观和性能。本发明所使用的的原料是改性HDI，IPDI，并且加入了海藻酸钠。改性HDI，IPDI耐黄变耐水解性能更好，制备出来的聚氨酯泡沫不易发生黄变水解。加入的海藻酸钠结构中含有羟基(-OH)能增加聚氨酯的吸水能力，通过本方法制备出来的聚氨酯泡沫性能稳定不易黄变，同时具有高吸水能力。
为解决以上技术问题，本发明提供的技术方案是：
一种可视防水敷料，包括保护层(1)、黏胶层(2)、敷芯层(3)和离型层(4)；所述黏胶层(2)为采用预聚体法制备的水性聚氨酯膜涂布丙烯酸酯压敏胶；所述敷芯层(3)为高吸水性聚氨酯泡沫。
优选的，所述高吸水性聚氨酯泡沫由异氰酸酯、多元醇、溶剂、催化剂、发泡剂和海藻酸钠采用预聚体法制备得到。
所述异氰酸酯指分子中含有异氰酸根的有机化合物，结构式为R(NCO)n，是合成聚氨酯的主要原料。优选的，所述异氰酸酯为改性六亚甲基二异氰酸酯(改性HDI)、异佛尔酮二异氰酸酯(IPDI)、多苯基多亚甲基多异氰酸酯(PAPI)、甲苯二异氰酸酯(TDI)和二苯基甲烷二异氰酸酯(MDI)中的任意一种或多种。
所述多元醇是分子中含有羟基，是合成聚氨酯的主要原料。优选的，所述多元醇为聚乙二醇、聚丙二醇、聚四氢呋喃、三羟甲基丙烷、三羟甲基三丙烯酸酯、丙三醇、聚酯三元醇、聚醚三元醇和二羟甲基丙酸中的任意一种或多种。
所述溶剂为稳定反应体系溶剂，优选的，所述溶剂为丙酮、乙酸乙酯、乙酸丁酯、二羟甲基丙酸(DMPA)、乙二胺、三环己烷、三乙胺、甲苯和硅油中的任意一种或多种。
所述催化剂是促进反应进行的试剂，优选的，所述催化剂为三乙醇胺、二甲基胺基乙基醚、羟基对甲苯胺、甲基苯胺、二月桂酸二丁基锡、辛酸亚锡、二醋酸二丁基锡中的任意一种或多种。
所述发泡剂为合成聚氨酯泡沫的原料。优选的，所述发泡剂为十二烷基硫酸钠、二氯甲烷、氢氯氟烃、烷烃和水中的任意一种或多种。
优选的，所述高吸水性聚氨酯泡沫的制备方法为将IPDI，改性HDI，聚乙二醇加入反应器搅拌升温至80℃，保温一段时间后加入丙酮溶解过的DMPA，催化剂，海藻酸钠，发泡剂原料，在氮气保护下反应4到5小时，降温降至40℃继续反应数小时即可得到预聚体A；将预聚体A倒入模具中干燥即可得到高吸水性聚氨酯泡沫。
本发明与现有技术相比，具有以下优点及有益效果：
本发明提供的可视防水敷料结构简单，使用方便同时可直接观察创面情况。可视防水敷料由保护层，黏胶层，敷芯层，离型层。黏胶层水性聚氨酯膜涂布丙烯酸酯压敏胶，敷芯层是吸水性好的镂空蜂窝状高吸水性聚氨酯泡沫。水性聚氨酯因结构中具有极性较强，相互间能形成氢键的酯胺基(-NHC00-)因而具有良好的透湿透气，防水柔软等良好性能。
本发明黏胶层为采用预聚体法制备的水性聚氨酯膜涂布丙烯酸酯压敏胶。水性聚氨酯膜涂布丙烯酸酯压敏胶，具有良好的粘附性和剥离强度，并且具有良好的透气防水性能，阻水阻菌性能。
本发明敷芯采用的是高吸水性并且形状设计为可观察伤口的镂空蜂窝状聚氨酯泡沫。聚氨酯镂空蜂窝状敷芯具有优良的吸液性能，能吸收创面渗出液，同时不易黄变性能稳定，为创面提供优良的愈合环境，并且能在不撕开敷贴的情况下直接观察创面情况。
保护层位于黏胶层上，对黏胶层起支撑保护作用，同时具有适当的挺度，利于可视防水敷料的黏贴，保护层材质为格拉辛纸，中间切割刀切开一个切线便于患者或医护人员敷贴后将保护层撕开。
本发明的核心在于黏胶层和敷芯层，黏胶层为采用预聚体法制备的水性聚氨酯膜涂布丙烯酸酯压敏胶，敷芯采用的镂空蜂窝状的吸液性能良好的聚氨酯泡沫。水性聚氨酯具有良好的粘附性和剥离强度，并且具有良好的透气防水性能，阻水阻菌性能。高吸水性聚氨酯镂空蜂窝状敷芯不仅具有优良的吸液性能，而且性能稳定不易黄变，能很好吸收创面渗出液，为创面提供优良的愈合环境，并且能在不撕开敷贴的情况下直接观察创面情况，为使用提供了很大的便利性，同时也减少了敷贴更换的频率，降低了使用成本，增加了患者的适应性，具备很高的应用价值。
本发明的制备方法工艺简单，操作简便，节省了人力和设备成本。
附图说明
图1为本发明的结构示意图。
具体实施方式
为了使本领域的技术人员更好地理解本发明的技术方案，下面结合具体实施例对本发明的优选实施方案进行描述，但是不能理解为对本专利的限制。
下述实施例中所述试验方法或测试方法，如无特殊说明，均为常规方法；所述试剂和材料，如无特殊说明，均从常规商业途径获得，或以常规方法制备。
实施例1-5：
一种可视防水敷料，包括保护层(1)、黏胶层(2)、敷芯层(3)和离型层(4)；所述黏胶层(2)为采用预聚体法制备的水性聚氨酯膜涂布丙烯酸酯压敏胶；所述敷芯层(3)为高吸水性聚氨酯泡沫。
优选的，所述高吸水性聚氨酯泡沫由异氰酸酯、多元醇、溶剂、催化剂、发泡剂和海藻酸钠采用预聚体法制备得到。
所述异氰酸酯指分子中含有异氰酸根的有机化合物，结构式为R(NCO)n，是合成聚氨酯的主要原料。优选的，所述异氰酸酯为改性六亚甲基二异氰酸酯(改性HDI)、异佛尔酮二异氰酸酯(IPDI)、多苯基多亚甲基多异氰酸酯(PAPI)、甲苯二异氰酸酯(TDI)和二苯基甲烷二异氰酸酯(MDI)中的任意一种或多种。
所述多元醇是分子中含有羟基，是合成聚氨酯的主要原料。优选的，所述多元醇为聚乙二醇、聚丙二醇、聚四氢呋喃、三羟甲基丙烷、三羟甲基三丙烯酸酯、丙三醇、聚酯三元醇、聚醚三元醇和二羟甲基丙酸中的任意一种或多种。
所述溶剂为稳定反应体系溶剂，优选的，所述溶剂为丙酮、乙酸乙酯、乙酸丁酯、二羟甲基丙酸(DMPA)、乙二胺、三环己烷、三乙胺、甲苯和硅油中的任意一种或多种。
所述催化剂是促进反应进行的试剂，优选的，所述催化剂为三乙醇胺、二甲基胺基乙基醚、羟基对甲苯胺、甲基苯胺、二月桂酸二丁基锡、辛酸亚锡、二醋酸二丁基锡中的任意一种或多种。
所述发泡剂为合成聚氨酯泡沫的原料。优选的，所述发泡剂为十二烷基硫酸钠、二氯甲烷、氢氯氟烃、烷烃和水中的任意一种或多种。
优选的，所述高吸水性聚氨酯泡沫的制备方法为将IPDI，改性HDI，聚乙二醇加入反应器搅拌升温至80℃，保温一段时间后加入丙酮溶解过的DMPA，催化剂，海藻酸钠，发泡剂原料，在氮气保护下反应4到5小时，降温降至40℃继续反应数小时即可得到预聚体A；将预聚体A倒入模具中干燥即可得到高吸水性聚氨酯泡沫。
本发明实施例1-5中所述高吸水性聚氨酯泡沫的原料配比如表1所示：
表1实施例1-5中所述高吸水性聚氨酯泡沫的原料配比
| 成分 | 实验例1 | 实验例2 | 实验例3 | 实验例4 | 实验例5 |
| 聚乙二醇 | 90 | 100 | 105 | 110 | 115 |
| IPDI | 38 | 38 | 38 | 38 | 38 |
| 改性HDI | 12 | 8 | 8 | 8 | 8 |
| DMPA | 18 | 18 | 18 | 18 | 18 |
| 丙酮 | 6 | 6 | 6 | 6 | 6 |
| 三乙胺 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 |
| 乙二胺 | 2 | 2 | 2 | 2 | 2 |
| 海藻酸钠 | 2 | 2 | 2 | 2 | 2 |
| 硅油 | 2.3 | 2.3 | 2.3 | 2.3 | 2.3 |
| 催化剂 | 适量 | 适量 | 适量 | 适量 | 适量 |
| 发泡剂 | 适量 | 适量 | 适量 | 适量 | 适量 |
下面对本发明实施例1-5得到的可视防水敷料(聚氨酯泡沫)进行性能测试，测试结果如表2所示：
表2实验例1-5制得的聚氨酯泡沫性能表征
| 实验例 | 表观密度(kg/m3) | 吸水率(g/g) | 保湿性(％) |
| 实验例1 | 46±2 | 18±1.3 | 6±1.1 |
| 实验例2 | 43±1.8 | 20±2.1 | 8±1.2 |
| 实验例3 | 48±1.6 | 21±0.9 | 11±0.8 |
| 实验例4 | 40±1.5 | 17±1.2 | 5±1.3 |
| 实验例5 | 38±1.8 | 16±1.5 | 3±0.6 |
以上仅是本发明的优选实施方式，应当指出的是，上述优选实施方式不应视为对本发明的限制，本发明的保护范围应当以权利要求所限定的范围为准。对于本技术领域的普通技术人员来说，在不脱离本发明的精神和范围内，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (8)
1.一种可视防水敷料，其特征在于，包括保护层(1)、黏胶层(2)、敷芯层(3)和离型层(4)；所述黏胶层(2)为采用预聚体法制备的水性聚氨酯膜涂布丙烯酸酯压敏胶；所述敷芯层(3)为高吸水性聚氨酯泡沫。
2.根据权利要求1所述的可视防水敷料，其特征在于，所述高吸水性聚氨酯泡沫由异氰酸酯、多元醇、溶剂、催化剂、发泡剂和海藻酸钠采用预聚体法制备得到。
3.根据权利要求2所述的可视防水敷料，其特征在于，所述异氰酸酯为改性六亚甲基二异氰酸酯、异佛尔酮二异氰酸酯、多苯基多亚甲基多异氰酸酯、甲苯二异氰酸酯和二苯基甲烷二异氰酸酯中的任意一种或多种。
4.根据权利要求2所述的可视防水敷料，其特征在于，所述多元醇为聚乙二醇、聚丙二醇、聚四氢呋喃、三羟甲基丙烷、三羟甲基三丙烯酸酯、丙三醇、聚酯三元醇、聚醚三元醇和二羟甲基丙酸中的任意一种或多种。
5.根据权利要求2所述的可视防水敷料，其特征在于，所述溶剂为丙酮、乙酸乙酯、乙酸丁酯、二羟甲基丙酸、乙二胺、三环己烷、三乙胺、甲苯和硅油中的任意一种或多种。
6.根据权利要求2所述的可视防水敷料，其特征在于，所述催化剂为三乙醇胺、二甲基胺基乙基醚、羟基对甲苯胺、甲基苯胺、二月桂酸二丁基锡、辛酸亚锡、二醋酸二丁基锡中的任意一种或多种。
7.根据权利要求2所述的可视防水敷料，其特征在于，所述发泡剂为十二烷基硫酸钠、二氯甲烷、氢氯氟烃、烷烃和水中的任意一种或多种。
8.根据权利要求2至7任一项所述的可视防水敷料，其特征在于，所述高吸水性聚氨酯泡沫的制备方法为将IPDI，改性HDI，聚乙二醇加入反应器搅拌升温至80℃，保温一段时间后加入丙酮溶解过的DMPA，催化剂，海藻酸钠，发泡剂原料，在氮气保护下反应4到5小时，降温降至40℃继续反应数小时即可得到预聚体A；将预聚体A倒入模具中干燥即可得到高吸水性聚氨酯泡沫。