CN116855138A - 一种驱蚊组合物、墙体驱蚊涂料、制备方法及其用途 - Google Patents
一种驱蚊组合物、墙体驱蚊涂料、制备方法及其用途 Download PDFInfo
- Publication number
- CN116855138A CN116855138A CN202310819013.0A CN202310819013A CN116855138A CN 116855138 A CN116855138 A CN 116855138A CN 202310819013 A CN202310819013 A CN 202310819013A CN 116855138 A CN116855138 A CN 116855138A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- mosquito
- byk
- mosquito repellent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种驱蚊组合物、墙体驱蚊涂料、制备方法及其用途;驱蚊组合物,包括组分A和组分B;组分A与组分B按质量比为1:(1‑10)混合;组分A,其原料包括:硅藻土、氯菊酯、右旋反式氯丙炔菊酯、有机硅表面助剂Byk‑375、不饱和多元胺酰胺盐Byk‑P104S、聚合物溶液Byk‑80、聚醚改性聚硅氧烷溶液Byk‑20、流平剂Byk‑333和水;组分B,其原料包括:BA101钛白粉、滑石粉、碳酸钙、甲基纤维素浆、醇酯‑12成膜助剂、98A丙烯酸乳液、增稠剂、表面助剂和水。制备方法,用于制备上述的一种驱蚊组合物。本方案解决了现有涂料中驱蚊效果不够或驱蚊持久性差的问题。
Description
技术领域
本发明涉及驱蚊涂料技术领域,尤其涉及一种驱蚊组合物、墙体驱蚊涂料、制备方法及其用途。
背景技术
对于厨房或卫生间的墙体,环境中的积水容易滋生蚊虫,而用户一般使用蚊香、杀虫剂、灭蚊灯等方式进行处理;但驱蚊效果差;现有技术是直接将驱蚊剂添加至涂料中,再将涂料布施于瓷砖表面,但涂料的驱蚊效果下降;尤其是涂料对驱蚊剂的附着效果不足,驱蚊剂的驱蚊持久性差,不适用于长期驱蚊。
发明内容
本发明的目的在于提出一种驱蚊组合物,其通过将组分A和组分B组合使用,组分A中的氯菊酯和右旋反式氯丙炔菊酯作为主要驱蚊组分,再将有机硅表面助剂Byk-375与组分B的98A丙烯酸乳液固化反应形成将驱蚊组分结合在聚合物结构中,配合组合物中的硅藻土和无机材料,从而使驱蚊组合物具有优异的驱蚊效果和驱蚊持久性。
本发明还提出一种驱蚊组合物的制备方法,用于制备上述的一种驱蚊组合物。
本发明还提出一种墙体驱蚊涂料,使用上述的一种驱蚊组合物。
本发明还提出一种组合物在制备墙体驱蚊涂料中的用途。
为达此目的,本发明采用以下技术方案:
一种驱蚊组合物,包括组分A和组分B;
所述组分A与组分B按质量比为1:(1-10)混合;
所述组分A,按质量份数,其原料包括:20-40份的硅藻土、0.1-2份的氯菊酯、0.1-2份的右旋反式氯丙炔菊酯、0.1-2份的有机硅表面助剂Byk-375、0.1-2份的不饱和多元胺酰胺盐Byk-P104S、0.1-2份的聚合物溶液Byk-80、0.1-2份的聚醚改性聚硅氧烷溶液Byk-20、0.1-2份的流平剂Byk-333和50-100份的水;
所述组分B,按质量份数,其原料包括:2-10份的BA101钛白粉、1-5份的滑石粉、10-30份的碳酸钙、2-8份的甲基纤维素浆、0.1-1.5份的醇酯-12成膜助剂、10-20份的98A丙烯酸乳液、0.1-0.5份的增稠剂、0.1-0.5份的表面助剂和20-50份的水。
优选地,所述组分B中,所述表面助剂包括SN 5040分散剂、NX2消泡剂和AMP-95pH调节剂中的至少一种或两种以上的组合。
一种驱蚊组合物的制备方法,用于制备上述的一种驱蚊组合物,其特征在于,将组分A与组分B按比例搅拌混合;
组分A的制备方法,按组分A的原料放入反应釜后先搅拌均匀,再添加占总质量0.1–5%乳化剂,设定反应釜转数300-600转/分钟,乳化时间5-20min;
组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
一种墙体驱蚊涂料,使用上述的一种驱蚊组合物。
一种组合物在制备墙体驱蚊涂料中的用途,所述组合物为上述的一种驱蚊组合物。
本发明提供的技术方案可以包括以下有益效果:
本方案提供一种驱蚊组合物,其通过将组分A和组分B组合使用,组分A中的氯菊酯和右旋反式氯丙炔菊酯作为主要驱蚊组分,再将有机硅表面助剂Byk-375与组分B的98A丙烯酸乳液固化反应形成将驱蚊组分结合在聚合物结构中,配合组合物中的硅藻土和无机材料,从而使驱蚊组合物具有优异的驱蚊效果和驱蚊持久性,驱蚊率达75%,解决了现有涂料中驱蚊效果不够或驱蚊持久性差的问题。
具体实施方式
下面通过具体实施方式来进一步说明本方案的技术方案。
一种驱蚊组合物,包括组分A和组分B;
所述组分A与组分B按质量比为1:(1-10)混合;
所述组分A,按质量份数,其原料包括:20-40份的硅藻土、0.1-2份的氯菊酯、0.1-2份的右旋反式氯丙炔菊酯、0.1-2份的有机硅表面助剂Byk-375、0.1-2份的不饱和多元胺酰胺盐Byk-P104S、0.1-2份的聚合物溶液Byk-80、0.1-2份的聚醚改性聚硅氧烷溶液Byk-20、0.1-2份的流平剂Byk-333和50-100份的水;
所述组分B,按质量份数,其原料包括:2-10份的BA101钛白粉、1-5份的滑石粉、10-30份的碳酸钙、2-8份的甲基纤维素浆、0.1-1.5份的醇酯-12成膜助剂、10-20份的98A丙烯酸乳液、0.1-0.5份的增稠剂、0.1-0.5份的表面助剂和20-50份的水。
本方案提供一种驱蚊组合物,其通过将组分A和组分B组合使用,组分A中的氯菊酯和右旋反式氯丙炔菊酯作为主要驱蚊组分,再将有机硅表面助剂Byk-375与组分B的98A丙烯酸乳液固化反应形成将驱蚊组分结合在聚合物结构中,配合组合物中的硅藻土和无机材料,从而使驱蚊组合物具有优异的驱蚊效果和驱蚊持久性,驱蚊率达75%,解决了现有涂料中驱蚊效果不够或驱蚊持久性差的问题。
优选地,所述组分B中,所述表面助剂包括SN 5040分散剂、NX2消泡剂和AMP-95pH调节剂中的至少一种或两种以上的组合。
一种驱蚊组合物的制备方法,用于制备上述的一种驱蚊组合物,其特征在于,将组分A与组分B按比例搅拌混合;
组分A的制备方法,按组分A配比称料,放入反应釜后先搅拌均匀,再添加占总质量1%乳化剂,设定反应釜转数400转/分钟,乳化时间5-20min;
组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
一种墙体驱蚊涂料,使用上述的一种驱蚊组合物。
一种组合物在制备墙体驱蚊涂料中的用途,所述组合物为上述的一种驱蚊组合物。
性能测试:
驱避率:自制有机玻璃检测设备,放入活蚊子,设备中间分隔成左右独立空间,两个独立空间中间开一条相互连通的通道;测试前在其中一个独立空间放入驱蚊产品,同时放入活动的蚊子;经过一天后观察驱蚊产品里面的剩余蚊子数量,计算出蚊子的趋避率。
驱避等级:根据国家标准《GB/T13917-9-2009》中,农药登记用卫生杀虫剂室内药效试验及评价第9部分进行测试。
驱蚊持久性:将驱蚊组合物涂在暴露于空气的板体,每10天测试驱蚊率,记录驱蚊率在50%以下所需要的天数。
实施例A,包括实施例A1-A4;
实施例A中,将组分A与组分B按表1的质量进行搅拌混合;
组分A,按质量份数,其原料包括:38.15份的硅藻土、0.8份的氯菊酯、0.25份的右旋反式氯丙炔菊酯、0.2份的有机硅表面助剂Byk-375、0.2份的不饱和多元胺酰胺盐Byk-P104S、0.1份的聚合物溶液Byk-80、0.1份的聚醚改性聚硅氧烷溶液Byk-20、0.1份的流平剂Byk-333和60份的水;
组分A的制备方法,按组分A配比称料,放入反应釜后先搅拌均匀,再添加占总质量1%乳化剂,设定反应釜转数400转/分钟,乳化时间5min;
组分B,按质量份数,其原料包括:8份的BA101钛白粉、5份的滑石粉、20份的碳酸钙、6份的甲基纤维素浆、1份的醇酯-12成膜助剂、15份的98A丙烯酸乳液、0.5份的增稠剂、0.5份的表面助剂和35份的水;表面助剂中,SN 5040分散剂、NX2消泡剂和AMP-95pH调节剂按质量比为1:2:2配料;
组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
将实施例A进行性能测试,结果如表2所示。
表1-实施例A的组分A和组分B配比
组分 | 实施例A1 | 实施例A2 | 实施例A3 | 实施例A4 |
组分A(kg) | 0.1 | 0.1 | 0.1 | 0 |
组分B(kg) | 1 | 0.4 | 0.1 | 1 |
表2-实施例A的性能对比
检测项目 | 实施例A1 | 实施例A2 | 实施例A3 | 实施例A4 |
驱蚊率(%) | 70 | 75 | 70 | 0 |
国标等级 | A级 | A级 | A级 | 不合格 |
驱蚊持久性(天) | >180 | >180 | >180 | 0 |
说明:
1、由实施例A1-A3对比可知,实施例A1中组分A与组分B的质量比为1:10,实施例A2中组分A与组分B的质量比为1:4,实施例A3中组分A与组分B的质量比为1:1,实施例A1-A3的质量比都在1:(1-10),驱蚊率都稳定在70-75%,国标等级为A级,驱蚊持久性都可以大于180天,说明将组分A与组分B的质量比控制在1:(1-10)可以确保驱蚊率和驱蚊持久性。
2、由实施例A1和实施例A4对比可知,实施例A4没有添加组分A,而组分A中包含了以氯菊酯和右旋反式氯丙炔菊酯作为的驱蚊活性成分,以及有机硅表面助剂Byk-375,机硅表面助剂Byk-375能在涂层固化反应过程中与B组分中丙烯酸乳液起到内交粘反应,使得有效驱蚊组分结合在聚合物结构中,使得驱蚊效率得到提高,持久性增强。并且同时,硅藻土具有一定的多孔性结构,能增大了材料的比表面积,能更好的吸附住驱蚊成分。因而实施例A4不具有驱蚊效果和驱蚊持久性。
实施例B,包括实施例B1-B5;
实施例B中,将组分A与组分B按质量比为1:4进行搅拌混合;
组分A的制备方法,组分A的制备方法,按组分A配比称料,放入反应釜后先搅拌均匀,再添加占总质量5%乳化剂,设定反应釜转数500转/分钟,乳化时间10min;组分A的的配料如表3所示;
组分B,按质量份数,其原料包括:8份的BA101钛白粉、5份的滑石粉、20份的碳酸钙、6份的甲基纤维素浆、1份的醇酯-12成膜助剂、15份的98A丙烯酸乳液、0.5份的增稠剂、0.5份的表面助剂和20份的水。表面助剂中,SN 5040分散剂和AMP-95pH调节剂按质量比为3:2配料;
组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
表3-实施例B的组分A配料
注:此表中的原料使用牌号作为缩写。
将实施例B1-B5进行性能测试,结果如表4所示。
表4-实施例B的性能测试
检测项目 | 实施例B1 | 实施例B2 | 实施例B3 | 实施例B4 | 实施例B5 |
驱蚊率(%) | 75 | 55 | 60 | 60 | 70 |
国标等级 | A级 | B级 | B级 | B级 | A级 |
驱蚊持久性(天) | >180 | 30 | 50 | 50 | 30 |
说明:
1、由实施例B1、实施例B2和实施例B3对比可知,实施例B2没有添加氯菊酯,其导致了实施例B2的驱蚊率仅为55%,国标等级为B级;且由于其本身驱蚊率基数较低,自身驱蚊持久性不足。实施例B3没有添加右旋反式氯丙炔菊酯,其导致了实施例B3的驱蚊率为60%,国标等级为B级;而实施例B1将氯菊酯和右旋反式氯丙炔菊酯进行组合使用,并通过其加入的有机硅表面助剂与B组分的98A丙烯酸乳液配合,氯菊酯和右旋反式氯丙炔菊酯在涂层固化反应过程中与B组分中丙乳乳液起到内交粘反应,使得有效驱蚊组分结合在聚合物结构中,使得驱蚊效率得到提高,持久性增强。因而实施例B1的驱蚊率可达75%,国标等级为A级,驱蚊持久性>180天。其说明了,氯菊酯和右旋反式氯丙炔菊酯两者通过与有机硅表面助剂与B组分的98A丙烯酸乳液配合,可以进一步地提高了驱蚊率和驱蚊持久性。
2、由实施例B1与实施例B4对比可知,实施例B4没有添加Byk-375,此处的Byk-375为有机硅表面助剂Byk-375,有机硅表面助剂Byk-375能有效地与B组分的98A丙烯酸乳液配合,从而提高氯菊酯和右旋反式氯丙炔菊酯两者的驱蚊率及驱蚊持久性;而实施例B4没有添加Byk-375,导致实施例B4的驱蚊率下降至60%,及驱蚊持久性只有50天。
3、由实施例B1与实施例B5对比可知,实施例B5没有添加Byk-P104S、Byk-80和Byk-20,其分别为不饱和多元胺酰胺盐Byk-P104S、不饱和多元胺酰胺盐Byk-P104S和聚醚改性聚硅氧烷溶液Byk-20,三者能辅助氯菊酯和右旋反式氯丙炔菊酯进行乳化并分散在组分B的水中,组分A和组分B制成涂层后能将分散的氯菊酯和右旋反式氯丙炔菊酯固定在物体的外表面,氯菊酯和右旋反式氯丙炔菊酯能被缓慢释放出来,从而提高驱蚊持久性。而实施例B5虽然具有驱蚊效果达到70%,但其驱蚊持久性下降。
实施例C:
实施例C中,将组分A与组分B按质量比为1:5进行搅拌混合;
组分A,按质量份数,其原料包括:38.15份的硅藻土、0.8份的氯菊酯、0.25份的右旋反式氯丙炔菊酯、0.2份的有机硅表面助剂Byk-375、0.2份的不饱和多元胺酰胺盐Byk-P104S、0.1份的聚合物溶液Byk-80、0.1份的聚醚改性聚硅氧烷溶液Byk-20、0.1份的流平剂Byk-333和80份的水;
组分A的制备方法,按组分A配比称料,放入反应釜后先搅拌均匀,再添加占总质量1%乳化剂,设定反应釜转数600转/分钟,乳化时间10min;
组分B的的配料如表5所示;组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;表面助剂为NX2消泡剂;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
表5-实施例C的组分B配料
组分(份) | 实施例C1 | 实施例C2 | 实施例C3 |
BA101钛白粉 | 8 | 8 | 0 |
滑石粉 | 5 | 5 | 0 |
碳酸钙 | 20 | 20 | 0 |
甲基纤维素浆 | 6 | 6 | 6 |
醇酯-12成膜助剂 | 1 | 1 | 1 |
98A丙烯酸乳液 | 15 | 0 | 15 |
增稠剂 | 0.5 | 0.5 | 0.5 |
表面助剂 | 0.5 | 0.5 | 0.5 |
水 | 30 | 45 | 30 |
将实施例C进行性能测试,结果如表6所示。
表6-实施例C的性能测试
检测项目 | 实施例C1 | 实施例C2 | 实施例C3 |
驱蚊率(%) | 75 | 60 | 70 |
国标等级 | A级 | B级 | A级 |
驱蚊持久性(天) | >180 | 50 | 50 |
说明:
1、由实施例C1与实施例C2对比可知,实施例C2没有添加98A丙烯酸乳液,通过15份水代替实施例C1的98A丙烯酸乳液;而本方案中,有机硅表面助剂Byk-375在涂层固化反应过程中与98A丙烯酸乳液起到内交粘反应,使得有效驱蚊组分结合在聚合物结构中,使得驱蚊效率得到提高,持久性增强。因而实施例C2没有形成内交粘结构,导致有效驱蚊组分未能与聚合物结构结合,对有效驱蚊组分附着效果不足,一方面容易脱落,影响了驱蚊效果和驱蚊持久性;另一方面由于98A丙烯酸乳液在水分蒸发后表面形成多个微孔结构,可以与硅藻土配合提高对有效驱蚊组分的缓释效果。
2、由实施例C1和C3对比可知,实施例C3没有添加BA101钛白粉、滑石粉和碳酸钙作为无机材料,而无机材料在本申请中具有增加白度和粘度的功能,可以更便于施工,又能与硅藻土结合,对驱蚊有效剂起到物理吸附,进而提高驱蚊剂的使用寿命。因而实施例C3的驱蚊持久性下降,说明加入BA101钛白粉、滑石粉和碳酸钙作为无机材料可以提高驱蚊剂的持久性。
实施例D:
实施例D中,将组分A与组分B按质量比为1:4进行搅拌混合;
组分A,按质量份数,其原料包括:20份的硅藻土、2份的氯菊酯、2份的右旋反式氯丙炔菊酯、2份的有机硅表面助剂Byk-375、2份的不饱和多元胺酰胺盐Byk-P104S、2份的聚合物溶液Byk-80、2份的聚醚改性聚硅氧烷溶液Byk-20、2份的流平剂Byk-333和100份的水;
组分A的制备方法,按组分A配比称料,放入反应釜后先搅拌均匀,再添加占总质量1%乳化剂,设定反应釜转数300转/分钟,乳化时间5min;
组分B,按质量份数,其原料包括:2份的BA101钛白粉、1份的滑石粉、30份的碳酸钙、2份的甲基纤维素浆、0.1份的醇酯-12成膜助剂、20份的98A丙烯酸乳液、0.1份的增稠剂、0.1份的表面助剂和35份的水;表面助剂中,SN 5040分散剂、NX2消泡剂和AMP-95pH调节剂按质量比为1:1:3配料;
组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
实施例E:
实施例E中,将组分A与组分B按质量比为1:5进行搅拌混合;
组分A,按质量份数,其原料包括:40份的硅藻土、0.1份的氯菊酯、0.1份的右旋反式氯丙炔菊酯、2份的有机硅表面助剂Byk-375、0.1份的不饱和多元胺酰胺盐Byk-P104S、2份的聚合物溶液Byk-80、0.1份的聚醚改性聚硅氧烷溶液Byk-20、0.1份的流平剂Byk-333和50份的水;
组分A的制备方法,按组分A配比称料,放入反应釜后先搅拌均匀,再添加占总质量3%乳化剂,设定反应釜转数600转/分钟,乳化时间5min;
组分B,按质量份数,其原料包括:10份的BA101钛白粉、5份的滑石粉、10份的碳酸钙、8份的甲基纤维素浆、1.5份的醇酯-12成膜助剂、10份的98A丙烯酸乳液、0.5份的增稠剂、0.5份的表面助剂和50份的水;表面助剂中,SN 5040分散剂、NX2消泡剂和AMP-95pH调节剂按质量比为0.5:1.5:3配料;
组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
将实施例D和E进行性能测试,结果如表7所示。
表7-实施例D和E的性能测试
检测项目 | 实施例D | 实施例E |
驱蚊率(%) | 71 | 73 |
国标等级 | A级 | A级 |
驱蚊持久性(天) | >180 | >180 |
以上结合具体实施例描述了本方案的技术原理。这些描述只是为了解释本方案的原理,而不能以任何方式解释为对本方案保护范围的限制。基于此处的解释,本领域的技术人员不需要付出创造性的劳动即可联想到本方案的其它具体实施方式,这些方式都将落入本方案的保护范围之内。
Claims (5)
1.一种驱蚊组合物,其特征在于,包括组分A和组分B;
所述组分A与组分B按质量比为1:(1-10)混合;
所述组分A,按质量份数,其原料包括:20-40份的硅藻土、0.1-2份的氯菊酯、0.1-2份的右旋反式氯丙炔菊酯、0.1-2份的有机硅表面助剂Byk-375、0.1-2份的不饱和多元胺酰胺盐Byk-P104S、0.1-2份的聚合物溶液Byk-80、0.1-2份的聚醚改性聚硅氧烷溶液Byk-20、0.1-2份的流平剂Byk-333和50-100份的水;
所述组分B,按质量份数,其原料包括:2-10份的BA101钛白粉、1-5份的滑石粉、10-30份的碳酸钙、2-8份的甲基纤维素浆、0.1-1.5份的醇酯-12成膜助剂、10-20份的98A丙烯酸乳液、0.1-0.5份的增稠剂、0.1-0.5份的表面助剂和20-50份的水。
2.根据权利要求1所述的一种驱蚊组合物,其特征在于,所述组分B中,所述表面助剂包括SN 5040分散剂、NX2消泡剂和AMP-95pH调节剂中的至少一种或两种以上的组合。
3.一种驱蚊组合物的制备方法,用于制备权利要求1或2所述的一种驱蚊组合物,其特征在于,将组分A与组分B按比例搅拌混合;
组分A的制备方法,按组分A的原料放入反应釜后先搅拌均匀,再添加占总质量0.1–5%乳化剂,设定反应釜转数300-600转/分钟,乳化完成后制得;
组分B的制备方法包括以下步骤:
(1)将BA101钛白粉、滑石粉、碳酸钙和部分表面助剂加水混合,混合均匀后砂磨,使细度<60μm;
(2)搅拌条件下加入部分表面助剂、甲基纤维素浆和水;
(3)搅拌条件下加入醇酯-12成膜助剂;
(4)搅拌条件下加入98A丙烯酸乳液;
(5)加入增稠剂和水调节粘度。
4.一种墙体驱蚊涂料,其特征在于,使用权利要求1-2任意一项所述的一种驱蚊组合物。
5.一种组合物在制备墙体驱蚊涂料中的用途,其特征在于,所述组合物为权利要求1或2所述的一种驱蚊组合物。