CN116656203A - 一种具有防霉抗菌性能的涂料组合物及其制备方法 - Google Patents
一种具有防霉抗菌性能的涂料组合物及其制备方法 Download PDFInfo
- Publication number
- CN116656203A CN116656203A CN202310961752.3A CN202310961752A CN116656203A CN 116656203 A CN116656203 A CN 116656203A CN 202310961752 A CN202310961752 A CN 202310961752A CN 116656203 A CN116656203 A CN 116656203A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- agent
- mildew
- silicone oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及涂料技术领域，公开了一种具有防霉抗菌性能的涂料组合物及其制备方法，该涂料组合物包括以下原料：丙烯酸树脂乳液、固化剂、成膜助剂、消泡剂、流平剂，其中，丙烯酸树脂乳液是由丙烯酸酯类单体、交联剂和含氟硅油，在引发剂作用下，经自由基聚合制得，交联剂结构中的双子季铵盐官能团可以使涂料具有良好的防霉抗菌作用，醚键的存在可以使涂料具有更好的附着力，而含氟硅油的存在可以使涂料固化形成的涂膜具有超疏水表面，不仅避免表面潮湿促进细菌生长和繁殖，还能赋予涂料防污自清洁效果，此外，硅油中的硅氧键可以有效提高涂料的耐热性，有利于其在室内装修中的进一步应用。
Description
技术领域
本发明涉及涂料技术领域，具体涉及一种具有防霉抗菌性能的涂料组合物及其制备方法。
背景技术
随着建筑业的不断发展，室内装修成为重中之重，其中，厨房是每个家庭必不可少的，目前，厨房墙面装饰大多采用瓷砖、强化玻璃和涂料等，而吊顶材料一般采用塑材，由于厨房长期处于特殊的湿热环境，易导致塑材发生老化，失去原有装饰作用，因此，在实际应用中，往往通过在塑料表面涂覆有机高分子涂料，涂料经固化后可形成涂膜，进而对塑材进行保护，起到延缓塑材老化的作用。
目前，市面上使用的有机高分子涂料主要为环氧树脂类、聚氨酯类和丙烯酸酯类，其中，丙烯酸酯类涂料具有保光保色性优良、光泽柔和、附着力较高等优点，广泛应用于室内装修中，但是，丙烯酸酯类涂料在湿热的环境中，容易滋生细菌，而且这种湿热的环境有利于细菌的生长和繁殖，从而导致涂料固化形成的涂膜发生霉变，不仅会使涂膜失去原有的保护作用，同时还会引起卫生健康问题。此外，丙烯酸树脂类涂料的耐热性较差，在湿热的环境中会发生分解、老化黄变等现象，引起涂膜脱落，失去保护的作用，因此，将丙烯酸酯类涂料应用在厨房中，还需克服以上缺陷。
申请号为CN201410020505.4的发明专利公开了一种可用于墙体、木器和金属器材的环保、抗菌性丙烯酸酯类树脂涂料的制备方法，利用改性的脂质体对艾蒿油进行包覆，形成艾蒿油包覆液，在丙烯酸酯类树脂制备过程中加入上述包覆液，可提高丙烯酸酯类树脂的抗菌持久性，但是，艾蒿油稳定性较差，且简单物理混合很容易发生抗菌剂的析出现象，因此实际上很难保障丙烯酸酯类树脂的持久抗菌效果。
发明内容
本发明的目的在于提供一种具有防霉抗菌性能的涂料组合物及其制备方法，解决了丙烯酸酯类涂料防霉抗菌性能和耐热性较差的问题。
本发明的目的可以通过以下技术方案实现：
一种具有防霉抗菌性能的涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液35-45份、固化剂2-3份、成膜助剂1.5-2份、消泡剂1-2份、流平剂0.2-0.5份；
所述丙烯酸树脂乳液包括以下重量份的原料：甲基丙烯酸甲酯10-25份、丙烯酸乙酯5-15份、丙烯酸1-3份、甲基丙烯酸缩水甘油酯2-3.5份、交联剂1-2份、含氟硅油2-6份、引发剂0.1-0.3份、乳化剂1-2份、纯化水20-35份；
所述丙烯酸树脂乳液的制备方法具体为：
将重量份的甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸、甲基丙烯酸缩水甘油酯、乳化剂与纯化水混合，搅拌均匀后，升高温度至80-90℃，继续加入重量份的交联剂和含氟硅油混合，加入引发剂，加毕，保温搅拌6-9h后，降温出料，即可；
所述交联剂为结构中含有双子季铵盐抗菌官能团的端乙烯基聚乙二醇型交联剂；
所述含氟硅油为接枝了含氟疏水基团的硅油衍生物。
在上述技术方案中，在引发剂作用下，甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸、甲基丙烯酸缩水甘油酯、交联剂和含氟硅油结构中的不饱和烯基可发生自由基聚合反应，在乳化剂作用下，可制得丙烯酸树脂乳液。
进一步地，所述固化剂为氮丙啶；所述成膜助剂为丙二醇甲醚或者乙二醇丁醚中的任意一种；消泡剂为脂肪醇聚氧乙烯醚或者烷基酚聚氧乙烯醚中的任意一种；所述流平剂为聚丙烯酸钠；所述引发剂为偶氮二异丁基眯盐酸盐或者偶氮二氰基戊酸中的任意一种；所述乳化剂为十二烷基硫酸钠或者十二烷基苯磺酸钠中的任意一种。
进一步地，所述交联剂的制备方法具体包括以下步骤：
第一步：将聚乙二醇二缩水甘油醚、叔胺单体与乙醇混合，搅拌均匀后，通氮气保护，升高温度至60-65℃，搅拌2-3h后，滴加冰醋酸调节pH值至6-7，继续搅拌6-8h后，蒸发溶剂，去除未反应物，获得交联中间体；
第二步：将交联中间体、丙烯酸异氰酸酯和甲苯混合，搅拌均匀，通入氮气，投入催化剂，开启搅拌，70-75℃下搅拌6-12h，蒸发溶剂，去除未反应物，降温出料，获得交联剂。
进一步地，第一步中，所述叔胺单体为N,N-二甲基己胺、N,N-二甲基正辛胺、N,N-二甲基十二烷基胺或者十六烷基二甲基叔胺中的任意一种。
进一步地，第二步中，所述丙烯酸异氰酸酯为甲基丙烯酸异氰基乙酯或者异氰酸酯丙烯酸乙酯中的任意一种。
进一步地，第二步中，所述催化剂为二月桂酸二丁基锡或者辛酸亚锡中的任意一种。
在上述技术方案中，聚乙二醇二缩水甘油醚分子链末端含有活性环氧基团，可以与叔胺单体发生季铵化开环反应，形成分子链末端为长链季铵盐官能团的交联中间体，由于在开环反应过程中会产生活性羟基，在催化剂的作用下，可以与丙烯酸异氰酸酯结构中的异氰酸酯基团发生胺酯化反应，从而制得结构中含有双子季铵盐抗菌官能团的端乙烯基聚乙二醇型交联剂。
进一步地，所述含氟硅油的制备方法具体为：
将羟基乙烯基硅油和四氢呋喃混合，搅拌至形成均匀溶液，继续加入含氟羧酸、二环己基碳二亚胺和4-二甲氨基吡啶，通氮气，室温搅拌4-8h后，蒸发溶剂，去除未反应物，出料，获得含氟硅油。
进一步地，所述羟基乙烯基硅油的乙烯基含量为10%，羟基含量为8%。
进一步地，所述含氟羧酸为三氟丁酸或者5,5,5-三氟戊酸中的任意一种。
在上述技术方案中，羟基乙烯基硅油结构中含有活性羟基，可以在二环己基碳二亚胺和4-二甲氨基吡啶的共同作用下，与含氟羧酸结构中的羧基发生酯化缩合，从而在羟基乙烯基硅油结构中引入含氟疏水链段，制得含氟硅油。
一种具有防霉抗菌性能的涂料组合物的制备方法，包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂、消泡剂和流平剂，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂与预混料搅拌混合，形成均匀物料，室温保存，即可。
本发明的有益效果：
（1）本发明通过制备结构中含有双子季铵盐抗菌官能团的端乙烯基聚乙二醇型交联剂，参与丙烯酸树脂乳液的制备过程，从而在丙烯酸树脂结构中引入聚乙二醇链段，聚乙二醇链段中富含的醚键可以与被粘基体产生更多的氢键，并且经交联后的丙烯酸树脂分子链的内聚力更大，可有效提高涂料与被粘基材之间的附着力。同时，交联剂结构中还含有双子季铵盐抗菌基团，由于季铵盐官能团具有广谱抗菌作用，因此将双子季铵盐抗菌基团引入丙烯酸树脂结构中后，可赋予涂料良好的抗菌防霉效果。此外，由于抗菌剂是以自由基聚合的方式，接枝在丙烯酸树脂分子链中，可避免抗菌剂的析出问题。
（2）本发明通过制备含氟硅油，参与丙烯酸树脂乳液的制备，修饰了含氟基团的硅油表面能极低，可在涂料固化阶段游离到涂料表面，利用含氟基团和硅油的强疏水性，使涂料形成超疏水表面，进而起到隔绝水汽的作用，使涂料表面处于干燥环境，避免为细菌的生产和繁殖提供有利的潮湿环境，从侧面使涂料达到防霉抗菌的效果，同时，超疏水表面还能使涂料产生防污自清洁效果。此外，硅油中的硅氧键键能较高，可以提高丙烯酸树脂的耐热性，从而减少了涂料在较高温度下发生分解和黄变现象，有利于提高涂料的使用寿命。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例描述所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1为本发明实施例1中制备的交联剂的红外谱图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例一
一种具有防霉抗菌性能的涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液35份、固化剂氮丙啶2份、成膜助剂丙二醇甲醚1.5份、消泡剂脂肪醇聚氧乙烯醚1份、流平剂聚丙烯酸钠0.2份；
该涂料组合物的制备方法包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂丙二醇甲醚、消泡剂脂肪醇聚氧乙烯醚和流平剂聚丙烯酸钠，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂氮丙啶与预混料搅拌混合，形成均匀物料，室温保存，即可。
其中丙烯酸树脂乳液的制备方法具体为：
将10份甲基丙烯酸甲酯、5份丙烯酸乙酯、1份丙烯酸、2份甲基丙烯酸缩水甘油酯、1份乳化剂十二烷基硫酸钠与20份纯化水混合，搅拌均匀后，升高温度至80℃，继续加入1份交联剂和2份含氟硅油混合，加入0.1份引发剂偶氮二异丁基眯盐酸盐，加毕，保温搅拌6h后，降温出料，即可。
其中交联剂的制备方法具体包括以下步骤：
第一步：将2.4g聚乙二醇二缩水甘油醚、2g的N,N-二甲基十二烷基胺与乙醇混合，搅拌均匀后，通氮气保护，升高温度至65℃，搅拌3h后，滴加冰醋酸调节pH值至7，继续搅拌6h后，蒸发溶剂，去除未反应物，获得交联中间体；
第二步：将1.6g交联中间体、0.55g甲基丙烯酸异氰基乙酯和甲苯混合，搅拌均匀，通入氮气，投入0.1g二月桂酸二丁基锡，开启搅拌，70℃下搅拌9h，蒸发溶剂，去除未反应物，降温出料，获得交联剂。
交联剂的红外测试图如图1所示，其中3054cm-1处为碳碳双键中C-H伸缩振动峰，2943cm-1处为甲基中C-H伸缩振动峰，2864cm-1为亚甲基中C-H伸缩振动峰，1721cm-1为酰胺基中C=O特征吸收峰，1409cm-1为季铵盐官能团中C-N特征吸收峰，并且在1165cm-1出现醚键C-O-C特征吸收峰。
其中含氟硅油的制备方法具体为：
将1.8g乙烯基含量为10%，羟基含量为8%的羟基乙烯基硅油和四氢呋喃混合，搅拌至形成均匀溶液，继续加入0.26g三氟丁酸、0.4g二环己基碳二亚胺和0.1g的4-二甲氨基吡啶，通氮气，室温搅拌6h后，蒸发溶剂，去除未反应物，出料，获得含氟硅油。
使用皂返滴定法测试含氟硅油结构中的酯基含量，经测试，含氟硅油中酯基的含量为2.36mmol/g，该酯基是羟基乙烯基硅油结构中的羟基与三氟丁酸结构中的羧基发生酯化缩合反应导致。
实施例二
一种具有防霉抗菌性能的涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液42份、固化剂氮丙啶3份、成膜助剂乙二醇丁醚1.6份、消泡剂烷基酚聚氧乙烯醚1.5份、流平剂聚丙烯酸钠0.3份；
该涂料组合物的制备方法包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂乙二醇丁醚、消泡剂烷基酚聚氧乙烯醚和流平剂聚丙烯酸钠，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂氮丙啶与预混料搅拌混合，形成均匀物料，室温保存，即可。
其中丙烯酸树脂乳液的制备方法具体为：
将20份甲基丙烯酸甲酯、6份丙烯酸乙酯、2份丙烯酸、3份甲基丙烯酸缩水甘油酯、1.5份乳化剂十二烷基苯磺酸钠与25份纯化水混合，搅拌均匀后，升高温度至85℃，继续加入2份交联剂和5份含氟硅油混合，加入0.2份引发剂偶氮二氰基戊酸，加毕，保温搅拌8h后，降温出料，即可。
其中交联剂和含氟硅油的制备方法与实施例1相同。
实施例三
一种具有防霉抗菌性能的涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液45份、固化剂氮丙啶3份、成膜助剂丙二醇甲醚2份、消泡剂脂肪醇聚氧乙烯醚2份、流平剂聚丙烯酸钠0.5份；
该涂料组合物的制备方法包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂丙二醇甲醚、消泡剂脂肪醇聚氧乙烯醚和流平剂聚丙烯酸钠，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂氮丙啶与预混料搅拌混合，形成均匀物料，室温保存，即可。
其中丙烯酸树脂乳液的制备方法具体为：
将25份甲基丙烯酸甲酯、15份丙烯酸乙酯、3份丙烯酸、3.5份甲基丙烯酸缩水甘油酯、2份乳化剂十二烷基硫酸钠与35份纯化水混合，搅拌均匀后，升高温度至90℃，继续加入2份交联剂和6份含氟硅油混合，加入0.3份引发剂偶氮二异丁基眯盐酸盐，加毕，保温搅拌9h后，降温出料，即可。
其中交联剂和含氟硅油的制备方法与实施例1相同。
对比例1
一种涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液42份、固化剂氮丙啶3份、成膜助剂乙二醇丁醚1.6份、消泡剂烷基酚聚氧乙烯醚1.5份、流平剂聚丙烯酸钠0.3份；
该涂料组合物的制备方法包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂乙二醇丁醚、消泡剂烷基酚聚氧乙烯醚和流平剂聚丙烯酸钠，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂氮丙啶与预混料搅拌混合，形成均匀物料，室温保存，即可。
其中丙烯酸树脂乳液的制备方法具体为：
将20份甲基丙烯酸甲酯、6份丙烯酸乙酯、2份丙烯酸、3份甲基丙烯酸缩水甘油酯、1.5份乳化剂十二烷基苯磺酸钠与25份纯化水混合，搅拌均匀后，升高温度至85℃，继续加入5份含氟硅油混合，加入0.2份引发剂偶氮二氰基戊酸，加毕，保温搅拌8h后，降温出料，即可。
其中含氟硅油的制备方法与实施例1相同。
对比例2
一种涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液42份、固化剂氮丙啶3份、成膜助剂乙二醇丁醚1.6份、消泡剂烷基酚聚氧乙烯醚1.5份、流平剂聚丙烯酸钠0.3份；
该涂料组合物的制备方法包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂乙二醇丁醚、消泡剂烷基酚聚氧乙烯醚和流平剂聚丙烯酸钠，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂氮丙啶与预混料搅拌混合，形成均匀物料，室温保存，即可。
其中丙烯酸树脂乳液的制备方法具体为：
将20份甲基丙烯酸甲酯、6份丙烯酸乙酯、2份丙烯酸、3份甲基丙烯酸缩水甘油酯、1.5份乳化剂十二烷基苯磺酸钠与25份纯化水混合，搅拌均匀后，升高温度至85℃，继续加入2份交联剂和5份羟基乙烯基硅油混合，加入0.2份引发剂偶氮二氰基戊酸，加毕，保温搅拌8h后，降温出料，即可。
其中交联剂的制备方法与实施例1相同。
对比例3
一种涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液42份、固化剂氮丙啶3份、成膜助剂乙二醇丁醚1.6份、消泡剂烷基酚聚氧乙烯醚1.5份、流平剂聚丙烯酸钠0.3份；
该涂料组合物的制备方法包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂乙二醇丁醚、消泡剂烷基酚聚氧乙烯醚和流平剂聚丙烯酸钠，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂氮丙啶与预混料搅拌混合，形成均匀物料，室温保存，即可。
其中丙烯酸树脂乳液的制备方法具体为：
将20份甲基丙烯酸甲酯、6份丙烯酸乙酯、2份丙烯酸、3份甲基丙烯酸缩水甘油酯、1.5份乳化剂十二烷基苯磺酸钠与25份纯化水混合，搅拌均匀后，升高温度至85℃，继续加入2份交联剂混合，加入0.2份引发剂偶氮二氰基戊酸，加毕，保温搅拌8h后，降温出料，即可。
其中交联剂的制备方法与实施例1相同。
对比例4
一种涂料组合物，按重量份计，包括以下原料：丙烯酸树脂乳液42份、固化剂氮丙啶3份、成膜助剂乙二醇丁醚1.6份、消泡剂烷基酚聚氧乙烯醚1.5份、流平剂聚丙烯酸钠0.3份；
该涂料组合物的制备方法包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂乙二醇丁醚、消泡剂烷基酚聚氧乙烯醚和流平剂聚丙烯酸钠，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂氮丙啶与预混料搅拌混合，形成均匀物料，室温保存，即可。
其中丙烯酸树脂乳液的制备方法具体为：
将20份甲基丙烯酸甲酯、6份丙烯酸乙酯、2份丙烯酸、3份甲基丙烯酸缩水甘油酯、1.5份乳化剂十二烷基苯磺酸钠与25份纯化水混合，搅拌均匀后，升高温度至85℃，加入0.2份引发剂偶氮二氰基戊酸，加毕，保温搅拌8h后，降温出料，即可。
将本发明实施例1-实施例3以及对比例1-对比例4制备的涂料组合物均匀涂覆在马口铁表面，置于120℃的烘箱中干燥固化，形成涂膜后，制作成符合测试规格的各组实验样品，进行以下性能测试：
参考国家标准GB/T 9286-2021，进行附着力测试；参考国家标准GB/T 21866-2008，进行抑菌率测试，测试菌种为金黄色葡萄球菌；使用PZ-200SD型接触角测定仪，进行水接触角测试；将样品放置于180℃的烘箱中，24h后取出，观察涂膜是否出现脱落、起泡、发黄等现象，对涂料的耐热性进行评价，测试结果记录在下表中：
；
由上表可知，本发明实施例1-实施例3制备的涂料附着力强，抑菌率高，耐热性好，且水接触角均大于150°，具有超疏水表面。
对比例1在制备丙烯酸树脂乳液的过程中，未使用交联剂，因此制备的丙烯酸树脂结构中不含聚乙二醇链段和双子季铵盐抗菌基团，因此导致涂料的附着力和抗菌性能表现较差。
对比例2在制备丙烯酸树脂乳液的过程中，使用不含氟的硅油参与反应，结构中仅有硅油具有疏水性，涂膜的水接触角小于150°，因此对比例2制备的涂料达不到超疏水的要求。
对比例3制备丙烯酸树脂乳液的过程中，没有使用硅油参与反应，结构中不含硅氧键和含氟疏水链段，因此对比例3制备的涂料疏水性和耐热性均表现较差。
对比例4制备丙烯酸树脂乳液过程中，未使用交联剂和硅油参与聚合反应，结构中不含聚乙二醇链段、双子季铵盐抗菌基团以及不含硅氧键和含氟疏水链段，因此对比例4制备的涂料各项性能表现均为最差。
以上内容仅仅是对本发明的构思所作的举例和说明，所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离发明的构思或者超越本权利要求书所定义的范围，均应属于本发明的保护范围。
Claims (10)
1.一种具有防霉抗菌性能的涂料组合物，其特征在于，按重量份计，包括以下原料：丙烯酸树脂乳液35-45份、固化剂2-3份、成膜助剂1.5-2份、消泡剂1-2份、流平剂0.2-0.5份；
所述丙烯酸树脂乳液包括以下重量份的原料：甲基丙烯酸甲酯10-25份、丙烯酸乙酯5-15份、丙烯酸1-3份、甲基丙烯酸缩水甘油酯2-3.5份、交联剂1-2份、含氟硅油2-6份、引发剂0.1-0.3份、乳化剂1-2份、纯化水20-35份；
所述丙烯酸树脂乳液的制备方法具体为：
将重量份的甲基丙烯酸甲酯、丙烯酸乙酯、丙烯酸、甲基丙烯酸缩水甘油酯、乳化剂与纯化水混合，搅拌均匀后，升高温度至80-90℃，继续加入重量份的交联剂和含氟硅油混合，加入引发剂，加毕，保温搅拌6-9h后，降温出料，即可；
所述交联剂为结构中含有双子季铵盐抗菌官能团的端乙烯基聚乙二醇型交联剂；
所述含氟硅油为接枝了含氟疏水基团的硅油衍生物。
2.根据权利要求1所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，所述固化剂为氮丙啶；所述成膜助剂为丙二醇甲醚或者乙二醇丁醚中的任意一种；消泡剂为脂肪醇聚氧乙烯醚或者烷基酚聚氧乙烯醚中的任意一种；所述流平剂为聚丙烯酸钠；所述引发剂为偶氮二异丁基眯盐酸盐或者偶氮二氰基戊酸中的任意一种；所述乳化剂为十二烷基硫酸钠或者十二烷基苯磺酸钠中的任意一种。
3.根据权利要求1所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，所述交联剂的制备方法具体包括以下步骤：
第一步：将聚乙二醇二缩水甘油醚、叔胺单体与乙醇混合，搅拌均匀后，通氮气保护，升高温度至60-65℃，搅拌2-3h后，滴加冰醋酸调节pH值至6-7，继续搅拌6-8h后，蒸发溶剂，去除未反应物，获得交联中间体；
第二步：将交联中间体、丙烯酸异氰酸酯和甲苯混合，搅拌均匀，通入氮气，投入催化剂，开启搅拌，70-75℃下搅拌6-12h，蒸发溶剂，去除未反应物，降温出料，获得交联剂。
4.根据权利要求3所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，第一步中，所述叔胺单体为N,N-二甲基己胺、N,N-二甲基正辛胺、N,N-二甲基十二烷基胺或者十六烷基二甲基叔胺中的任意一种。
5.根据权利要求3所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，第二步中，所述丙烯酸异氰酸酯为甲基丙烯酸异氰基乙酯或者异氰酸酯丙烯酸乙酯中的任意一种。
6.根据权利要求3所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，第二步中，所述催化剂为二月桂酸二丁基锡或者辛酸亚锡中的任意一种。
7.根据权利要求1所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，所述含氟硅油的制备方法具体为：
将羟基乙烯基硅油和四氢呋喃混合，搅拌至形成均匀溶液，继续加入含氟羧酸、二环己基碳二亚胺和4-二甲氨基吡啶，通氮气，室温搅拌4-8h后，蒸发溶剂，去除未反应物，出料，获得含氟硅油。
8.根据权利要求7所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，所述羟基乙烯基硅油的乙烯基含量为10%，羟基含量为8%。
9.根据权利要求7所述的一种具有防霉抗菌性能的涂料组合物，其特征在于，所述含氟羧酸为三氟丁酸或者5,5,5-三氟戊酸中的任意一种。
10.如权利要求1所述的一种具有防霉抗菌性能的涂料组合物的制备方法，其特征在于，包括以下步骤：
步骤一：取重量份的丙烯酸树脂乳液、成膜助剂、消泡剂和流平剂，倒入混料机中，搅拌混合均匀后，静置消泡，形成预混料；
步骤二：将重量份的固化剂与预混料搅拌混合，形成均匀物料，室温保存，即可。