CN1165487C - 一步碳化制备尺寸为80-100nm的立方体碳酸钙的方法 - Google Patents
一步碳化制备尺寸为80-100nm的立方体碳酸钙的方法 Download PDFInfo
- Publication number
- CN1165487C CN1165487C CNB021147698A CN02114769A CN1165487C CN 1165487 C CN1165487 C CN 1165487C CN B021147698 A CNB021147698 A CN B021147698A CN 02114769 A CN02114769 A CN 02114769A CN 1165487 C CN1165487 C CN 1165487C
- Authority
- CN
- China
- Prior art keywords
- carbonization
- calcium carbonate
- calcium hydroxide
- control agent
- crystal control
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
Claims (3)