CN116535773A - 一种高白度高遮盖pp钛白母粒及其制备方法 - Google Patents
一种高白度高遮盖pp钛白母粒及其制备方法 Download PDFInfo
- Publication number
- CN116535773A CN116535773A CN202310591609.XA CN202310591609A CN116535773A CN 116535773 A CN116535773 A CN 116535773A CN 202310591609 A CN202310591609 A CN 202310591609A CN 116535773 A CN116535773 A CN 116535773A
- Authority
- CN
- China
- Prior art keywords
- parts
- master batch
- coverage
- whiteness
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高白度高遮盖PP钛白母粒及其制备方法，一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉80～85份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份。一种高白度高遮盖PP钛白母粒的制备方法，包括以下步骤：步骤1，准备原料备用；步骤2，将步骤1中的原料进行混合获得混合物料；步骤3，将步骤2中获得的混合物料进行预热处理加热至75‑80摄氏度；步骤4，通过挤塑机挤出成型；步骤5，挤出成型的物料穿过水冷池进行冷却处理；步骤6，对冷却处理的物料进行风干处理清除物料表面的水分；步骤7，对物料进行切料处理获得母粒。本发明的有益效果是：具有较好的白度和遮盖力。
Description
技术领域
本发明涉及一种高白度高遮盖PP钛白母粒及其制备方法。
背景技术
PP(聚丙烯)是一种半结晶的热塑性塑料。具有较高的耐冲击性，机械性质强韧，抗多种有机溶剂和酸碱腐蚀。在工业界有广泛的应用，是平常常见的高分子材料之一。
色母粒由高比例的颜料或添加剂与热塑性树脂，经良好分散而成的塑料着色剂，其所选用的树脂对着色剂具有良好润湿和分散作用，并且与被着色材料具有良好的相容性。
PP钛白母粒是一种用于PP材料白色染色的色母粒。白色相比其他颜色配制的难度较高。尤其是其白度和遮盖力是被关注的重点。
发明内容
本发明的目的在于提供一种高白度高遮盖PP钛白母粒及其制备方法，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种高白度高遮盖PP钛白母粒，一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：
钛白粉80～85份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份；
其中复合分散剂由油酸酰胺和聚丙烯蜡组成。
作为本发明的进一步的实施方式，复合分散剂中聚丙烯蜡的含量是油酸酰胺的1.5～3倍。
作为本发明的进一步的实施方式，复合分散剂中聚丙烯蜡的含量是油酸酰胺的2倍。
作为本发明的进一步的实施方式，荧光增白剂为二苯乙烯基双苯并噁唑。
作为本发明的进一步的实施方式，抗氧化剂为三(2,4-二叔丁基苯基)亚磷酸酯，四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯，双(2.4-二叔丁基苯基)季戊四醇二亚磷酸酯中的一种或若干种的混合。
作为本发明的进一步的实施方式，所述一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉82～84份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份。
作为本发明的进一步的实施方式，所述一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉83份，PP树脂17份、荧光增白剂5份，液体石蜡2份、滑石粉1份、抗氧化剂1.6、复合分散剂2.2份。
一种高白度高遮盖PP钛白母粒的制备方法，包括以下步骤：
步骤1，准备以下重量份的原料备用，钛白粉80～85份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份；
步骤2，将步骤1中的原料进行混合获得混合物料；
步骤3，将步骤2中获得的混合物料进行预热处理加热至75-80摄氏度；
步骤4，通过挤塑机挤出成型；
步骤5，挤出成型的物料穿过水冷池进行冷却处理；
步骤6，对冷却处理的物料进行风干处理清除物料表面的水分；
步骤7，对物料进行切料处理获得母粒。
作为本发明的进一步的实施方式，对获得的母粒进行筛选获得符合长度和粒径的母粒。
作为本发明的进一步的实施方式，在步骤4中，采用双螺杆挤出机挤出成型。
本发明的有益之处在于：具有较好的白度和遮盖力。
发明的其他特点和优点将会在下面的具体实施方式、附图中详细的揭露。
附图说明
图1是本发明的一种高白度高遮盖PP钛白母粒的制备方法的流程图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
如图1所示，一种高白度高遮盖PP钛白母粒，一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉80～85份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份。其中复合分散剂由油酸酰胺和聚丙烯蜡组成。
作为一种具体的实施方式，复合分散剂中聚丙烯蜡的含量是油酸酰胺的1.5～3倍。具体而言，复合分散剂中聚丙烯蜡的含量是油酸酰胺的2倍。
作为一种具体的实施方式，荧光增白剂为二苯乙烯基双苯并噁唑。
作为一种具体的实施方式，抗氧化剂为三(2,4-二叔丁基苯基)亚磷酸酯，四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯，双(2.4-二叔丁基苯基)季戊四醇二亚磷酸酯中的一种或若干种的混合。
作为一种具体的实施方式，一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉82～84份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份。
作为本发明的高白度高遮盖PP钛白母粒的原料的第一种具体的实施例，一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉83份，PP树脂17份、荧光增白剂5份，液体石蜡2份、滑石粉1份、抗氧化剂1.6、复合分散剂2.2份。
作为本发明的高白度高遮盖PP钛白母粒的原料的第二种具体的实施例，一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉82份，PP树脂16份、荧光增白剂3份，液体石蜡1份、滑石粉0.6份、抗氧化剂0.5、复合分散剂0.5份。
作为本发明的高白度高遮盖PP钛白母粒的原料的第三种具体的实施例，一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉84份，PP树脂18份、荧光增白剂8份，液体石蜡3份、滑石粉1.5份、抗氧化剂3、复合分散剂2份。
作为本发明的高白度高遮盖PP钛白母粒的原料的第四种具体的实施例，
一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉80份，PP树脂16份、荧光增白剂3份，液体石蜡1份、滑石粉0.6份、抗氧化剂0.5、复合分散剂0.5份。其中复合分散剂由油酸酰胺和聚丙烯蜡组成。
作为本发明的高白度高遮盖PP钛白母粒的原料的第五种具体的实施例，
一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉85份，PP树脂18份、荧光增白剂8份，液体石蜡3份、滑石粉1.5份、抗氧化剂3、复合分散剂2份。其中复合分散剂由油酸酰胺和聚丙烯蜡组成。
作为本发明的高白度高遮盖PP钛白母粒的原料的第六种具体的实施例，
一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉83份，PP树脂17份、荧光增白剂5份，液体石蜡2份、滑石粉1份、抗氧化剂1.7、复合分散剂1.2份。其中复合分散剂由油酸酰胺和聚丙烯蜡组成。
一种高白度高遮盖PP钛白母粒的制备方法，包括以下步骤：
步骤1，准备以下重量份的原料备用，钛白粉80～85份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份；
步骤2，将步骤1中的原料进行混合获得混合物料；
步骤3，将步骤2中获得的混合物料进行预热处理加热至75-80摄氏度；
步骤4，通过挤塑机挤出成型；
步骤5，挤出成型的物料穿过水冷池进行冷却处理；
步骤6，对冷却处理的物料进行风干处理清除物料表面的水分；
步骤7，对物料进行切料处理获得母粒。
作为一种具体的实施方式，对获得的母粒进行筛选获得符合长度和粒径的母粒。
作为一种具体的实施方式，在步骤4中，采用双螺杆挤出机挤出成型。
作为一种具体的实施方式，一种高白度高遮盖PP钛白母粒的制备方法，包括以下步骤：
步骤1，准备上述高白度高遮盖PP钛白母粒的任意一种重量份的原料备用；
步骤2，将步骤1中的原料进行混合获得混合物料；
步骤3，将步骤2中获得的混合物料进行预热处理加热至78摄氏度；
步骤4，通过挤塑机挤出成型；
步骤5，挤出成型的物料穿过水冷池进行冷却处理；
步骤6，对冷却处理的物料进行风干处理清除物料表面的水分；
步骤7，对物料进行切料处理获得母粒。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (10)
1.一种高白度高遮盖PP钛白母粒，其特征在于，所述一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：
钛白粉80～85份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份；
其中所述复合分散剂由油酸酰胺和聚丙烯蜡组成。
2.根据权利要求1所述的一种高白度高遮盖PP钛白母粒，其特征在于，
所述复合分散剂中所述聚丙烯蜡的含量是所述油酸酰胺的1.5～3倍。
3.根据权利要求2所述的一种高白度高遮盖PP钛白母粒，其特征在于，
所述复合分散剂中所述聚丙烯蜡的含量是所述油酸酰胺的2倍。
4.根据权利要求1所述的一种高白度高遮盖PP钛白母粒，其特征在于，
所述荧光增白剂为二苯乙烯基双苯并噁唑。
5.根据权利要求1所述的一种高白度高遮盖PP钛白母粒，其特征在于，
所述抗氧化剂为三(2,4-二叔丁基苯基)亚磷酸酯，四[β-(3,5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯，双(2.4-二叔丁基苯基)季戊四醇二亚磷酸酯中的一种或若干种的混合。
6.根据权利要求1所述的一种高白度高遮盖PP钛白母粒，其特征在于，
所述一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉82～84份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份。
7.根据权利要求6所述的一种高白度高遮盖PP钛白母粒，其特征在于，
所述一种高白度高遮盖PP钛白母粒的原料包括以下重量份的材料：钛白粉83份，PP树脂17份、荧光增白剂5份，液体石蜡2份、滑石粉1份、抗氧化剂1.6、复合分散剂2.2份。
8.一种权利要求1至7任意一项所述的一种高白度高遮盖PP钛白母粒的制备方法，其特征在于，包括以下步骤：
步骤1，准备以下重量份的原料备用，钛白粉80～85份，PP树脂16～18份、荧光增白剂3～8份，液体石蜡1～3份、滑石粉0.6～1.5份、抗氧化剂0.5～3、复合分散剂0.5～2份；
步骤2，将步骤1中的原料进行混合获得混合物料；
步骤3，将步骤2中获得的混合物料进行预热处理加热至75-80摄氏度；
步骤4，通过挤塑机挤出成型；
步骤5，挤出成型的物料穿过水冷池进行冷却处理；
步骤6，对冷却处理的物料进行风干处理清除物料表面的水分；
步骤7，对物料进行切料处理获得母粒。
9.根据权利要求8所述的一种高白度高遮盖PP钛白母粒的制备方法，其特征在于，还包括以下步骤：
对获得的母粒进行筛选获得符合长度和粒径的母粒。
10.根据权利要求8所述的一种高白度高遮盖PP钛白母粒的制备方法，其特征在于，
在步骤4中，采用双螺杆挤出机挤出成型。