CN116496670A - 一种长效玻璃防霉粉及其制备方法 - Google Patents
一种长效玻璃防霉粉及其制备方法 Download PDFInfo
- Publication number
- CN116496670A CN116496670A CN202310549985.2A CN202310549985A CN116496670A CN 116496670 A CN116496670 A CN 116496670A CN 202310549985 A CN202310549985 A CN 202310549985A CN 116496670 A CN116496670 A CN 116496670A
- Authority
- CN
- China
- Prior art keywords
- mildew
- powder
- long
- proof
- acting glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种长效玻璃防霉粉及其制备方法，属于涂料技术领域，本发明的印刷方法包括羧甲基壳聚糖、气相二氧化硅、艾草粉、丙烯酸树脂、无机抑霉剂、磷酸钙和苯甲酸钠，其中气相二氧化硅作为支撑材料包裹防霉材料对防霉物质进行缓释，达到长久防霉的效果。其次，本发明的配方体系中羧甲基壳聚糖和艾草粉既作为本发明长效玻璃防霉粉的支撑材料也作为本发明长效玻璃防霉粉的防霉材料，将支撑与防霉的功能融为一身，配合丙烯酸树脂、无机抑霉剂、磷酸钙和苯甲酸钠能实现很好的玻璃防霉功能。
Description
技术领域
本发明涉及涂料技术领域，尤其涉及一种长效玻璃防霉粉及其制备方法。
背景技术
平板玻璃储运过程中，在一定的温度、湿度、化学气氛影响下，会发生物理、化学、物理化学、生物化学和其它污诱型霉变；在外力影响下，玻璃还会发生擦伤。据有关资料显示，霉变或擦伤的玻璃损失量，有时可高达10％。玻璃的霉变极大地影响了玻璃的质量。为此，需采用防护材料(如玻璃防霉纸、防霉液、防霉粉或塑料等)对其进行包装保护。由于喷洒防霉液的玻璃表面会留下雾迹，玻璃企业及用户不易接受这种防护方法。随着“白色革命”而产生的塑料薄膜，特别是“防霉化”的薄膜，对玻璃的包装防护作用较好。但由于其价格高等原因，薄膜多用在箱架的玻璃整体或深加工玻璃的包装上。而玻璃防霉纸、防霉粉自然成了玻璃防护包装的主角材料。长期以来，玻璃防护材料为玻璃应用质量保驾护航，浮法玻璃在发展应用中壮大，玻璃防护材料也在创新中发展。玻璃防霉隔离粉用在玻璃夹层中可以杀死或抑制霉菌的生长，并且具有防霉、防潮、耐腐蚀的作用，同时还能减少玻璃之间的摩擦以保护玻璃表面不受损，与传统的隔离纸方法比较，防霉隔离粉具有成本低、有效和环保的优点。
现有技术中的玻璃防霉粉存在菌防霉效果不好，时间短的问题，影响其实际使用价值。
发明内容
本发明提供一种长效玻璃防霉粉及其制备方法，以解决现有技术防霉效果不好，时间短的的技术问题，本发明的内容如下：
本发明的第一个目的在于提供一种长效玻璃防霉粉，其技术点在于，按照重量份数计，包括15-35重量份的羧甲基壳聚糖、30-40重量份的气相二氧化硅、30-65重量份的艾草粉、15-35重量份的丙烯酸树脂、0.2-0.45重量份的无机抑霉剂、0.2-0.45重量份的磷酸钙和0.2-0.4重量份的苯甲酸钠。
为了更好的实现上述技术方案，本发明的长效玻璃防霉粉的配方体系中羧甲基壳聚糖的脱乙酰度≥90％，羧基取代度≥80％，粘均分子量5-10万。
为了更好的实现上述技术方案，本发明的长效玻璃防霉粉的配方体系中气相二氧化硅的粒径为2-10nm。
为了更好的实现上述技术方案，本发明的长效玻璃防霉粉的配方体系中艾草粉采用自然风干的艾草研磨而成，且艾草粉的目数在700目以上。
为了更好的实现上述技术方案，本发明的长效玻璃防霉粉的配方体系中丙烯酸树脂为水溶性丙烯酸树脂。
为了更好的实现上述技术方案，本发明的长效玻璃防霉粉的配方体系中无机抑霉剂为纳米二氧化钛和纳米银粉中的至少一种。
为了更好的实现上述技术方案，本发明的长效玻璃防霉粉的配方体系中磷酸钙的粒径4.5-5.0μm。
为了更好的实现上述技术方案，本发明的长效玻璃防霉粉的配方体系中苯甲酸中的有效物质含量≥99.5wt％。
本发明的第二个目的在于提供一种长效玻璃防霉粉的制备方法，其技术点在于，包括以下步骤：
步骤一，按权利要求1所述的原料配比备料；将干燥的羧甲基壳聚糖、气相二氧化硅和艾草粉进行混合，得混合物A；
步骤二，将丙烯酸树脂和无机抑霉剂加入到所述混合物A中，混合均匀后加入磷酸钙和苯甲酸钠，搅拌均匀后得混合物B；
步骤三，将步骤二中得到的混合物B先切碎为若干小块，再进行研磨处理，最后放入球磨机中进行球磨，所得粉末即为所述长效玻璃防霉粉。
与现有技术相比，本发明的长效玻璃防霉粉及其制备方法的技术方案能够达到以下有益效果：
本发明的长效玻璃防霉粉包括羧甲基壳聚糖、气相二氧化硅、艾草粉、丙烯酸树脂、无机抑霉剂、磷酸钙和苯甲酸钠，其中气相二氧化硅作为支撑材料包裹防霉材料对防霉物质进行缓释，达到长久防霉的效果。其次，本发明的配方体系中羧甲基壳聚糖和艾草粉既作为本发明长效玻璃防霉粉的支撑材料也作为本发明长效玻璃防霉粉的防霉材料，将支撑与防霉的功能融为一身，配合丙烯酸树脂、无机抑霉剂、磷酸钙和苯甲酸钠能实现很好的玻璃防霉功能。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将结合本发明具体实施例对本发明技术方案进行清楚、完整地描述。显然，所描述的实施例仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种长效玻璃防霉粉包括25kg的羧甲基壳聚糖、35kg的气相二氧化硅、47.5kg的艾草粉、25kg的丙烯酸树脂、0.3kg的无机抑霉剂、0.3kg的磷酸钙和0.3kg的苯甲酸钠。
进一步的，本发明的长效玻璃防霉粉的配方体系中羧甲基壳聚糖的脱乙酰度≥90％，羧基取代度≥80％，粘均分子量7.5万。
进一步的，本发明的长效玻璃防霉粉的配方体系中气相二氧化硅的粒径为6nm。
进一步的，本发明的长效玻璃防霉粉的配方体系中艾草粉采用自然风干的艾草研磨而成，且艾草粉的目数在700目以上。
进一步的，本发明的长效玻璃防霉粉的配方体系中丙烯酸树脂为水溶性丙烯酸树脂。
进一步的，本发明的长效玻璃防霉粉的配方体系中无机抑霉剂为纳米二氧化钛。
进一步的，本发明的长效玻璃防霉粉的配方体系中磷酸钙的粒径4.25μm。
进一步的，本发明的长效玻璃防霉粉的配方体系中苯甲酸中的有效物质含量≥99.5wt％。
按照上述配方，本实施例的一种长效玻璃防霉粉的制备方法包括以下步骤：
步骤一，按权利要求1所述的原料配比备料；将干燥的羧甲基壳聚糖、气相二氧化硅和艾草粉进行混合，得混合物A；
步骤二，将丙烯酸树脂和无机抑霉剂加入到所述混合物A中，混合均匀后加入磷酸钙和苯甲酸钠，搅拌均匀后得混合物B；
步骤三，将步骤二中得到的混合物B先切碎为若干小块，再进行研磨处理，最后放入球磨机中进行球磨，所得粉末即为所述长效玻璃防霉粉。
实施例2
一种长效玻璃防霉粉包括15kg的羧甲基壳聚糖、30kg的气相二氧化硅、30kg的艾草粉、15kg的丙烯酸树脂、0.2kg的无机抑霉剂、0.2kg的磷酸钙和0.2kg的苯甲酸钠。
进一步的，本发明的长效玻璃防霉粉的配方体系中羧甲基壳聚糖的脱乙酰度≥90％，羧基取代度≥80％，粘均分子量5万。
进一步的，本发明的长效玻璃防霉粉的配方体系中气相二氧化硅的粒径为2nm。
进一步的，本发明的长效玻璃防霉粉的配方体系中艾草粉采用自然风干的艾草研磨而成，且艾草粉的目数在700目以上。
进一步的，本发明的长效玻璃防霉粉的配方体系中丙烯酸树脂为水溶性丙烯酸树脂。
进一步的，本发明的长效玻璃防霉粉的配方体系中无机抑霉剂为纳米银粉。
进一步的，本发明的长效玻璃防霉粉的配方体系中磷酸钙的粒径4.5-5.0μm。
进一步的，本发明的长效玻璃防霉粉的配方体系中苯甲酸中的有效物质含量≥99.5wt％。
按照上述配方，本实施例的一种长效玻璃防霉粉的制备方法包括以下步骤：
步骤一，按权利要求1所述的原料配比备料；将干燥的羧甲基壳聚糖、气相二氧化硅和艾草粉进行混合，得混合物A；
步骤二，将丙烯酸树脂和无机抑霉剂加入到所述混合物A中，混合均匀后加入磷酸钙和苯甲酸钠，搅拌均匀后得混合物B；
步骤三，将步骤二中得到的混合物B先切碎为若干小块，再进行研磨处理，最后放入球磨机中进行球磨，所得粉末即为所述长效玻璃防霉粉。
实施例3
一种长效玻璃防霉粉包括35kg的羧甲基壳聚糖、40kg的气相二氧化硅、65kg的艾草粉、35kg的丙烯酸树脂、0.45kg的无机抑霉剂、0.45kg的磷酸钙和0.4kg的苯甲酸钠。
进一步的，本发明的长效玻璃防霉粉的配方体系中羧甲基壳聚糖的脱乙酰度≥90％，羧基取代度≥80％，粘均分子量10万。
进一步的，本发明的长效玻璃防霉粉的配方体系中气相二氧化硅的粒径为10nm。
进一步的，本发明的长效玻璃防霉粉的配方体系中艾草粉采用自然风干的艾草研磨而成，且艾草粉的目数在700目以上。
进一步的，本发明的长效玻璃防霉粉的配方体系中丙烯酸树脂为水溶性丙烯酸树脂。
进一步的，本发明的长效玻璃防霉粉的配方体系中无机抑霉剂为纳米二氧化钛和纳米银粉的混合物，其中纳米二氧化钛和纳米银粉重量比为1：1。
进一步的，本发明的长效玻璃防霉粉的配方体系中磷酸钙的粒径5.0μm。
进一步的，本发明的长效玻璃防霉粉的配方体系中苯甲酸中的有效物质含量≥99.5wt％。
按照上述配方，本实施例的一种长效玻璃防霉粉的制备方法包括以下步骤：
步骤一，按权利要求1所述的原料配比备料；将干燥的羧甲基壳聚糖、气相二氧化硅和艾草粉进行混合，得混合物A；
步骤二，将丙烯酸树脂和无机抑霉剂加入到所述混合物A中，混合均匀后加入磷酸钙和苯甲酸钠，搅拌均匀后得混合物B；
步骤三，将步骤二中得到的混合物B先切碎为若干小块，再进行研磨处理，最后放入球磨机中进行球磨，所得粉末即为所述长效玻璃防霉粉。
试验例
将实施例1-3制备得到的长效玻璃防霉粉试验进行防霉试验(抑曲霉菌斑试验)，试验结果见表1：
表1防霉试验结果
以上所述仅为本发明的实施例而已，并不用于限制本发明。对于本领域技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原理之内所作的任何修改、等同替换、改进等，均应包含在本发明的权利要求范围之内。
Claims (9)
1.一种长效玻璃防霉粉，其特征在于，按照重量份数计，包括15-35重量份的羧甲基壳聚糖、30-40重量份的气相二氧化硅、30-65重量份的艾草粉、15-35重量份的丙烯酸树脂、0.2-0.45重量份的无机抑霉剂、0.2-0.45重量份的磷酸钙和0.2-0.4重量份的苯甲酸钠。
2.根据权利要求1所述的一种长效玻璃防霉粉，其特征在于，所述羧甲基壳聚糖的脱乙酰度≥90％，羧基取代度≥80％，粘均分子量5-10万。
3.根据权利要求1所述的一种长效玻璃防霉粉，其特征在于，所述气相二氧化硅的粒径为2-10nm。
4.根据权利要求1所述的一种长效玻璃防霉粉，其特征在于，所述艾草粉采用自然风干的艾草研磨而成，且艾草粉的目数在700目以上。
5.根据权利要求1所述的一种长效玻璃防霉粉，其特征在于，所述丙烯酸树脂为水溶性丙烯酸树脂。
6.根据权利要求1所述的一种长效玻璃防霉粉，其特征在于，所述无机抑霉剂为纳米二氧化钛和纳米银粉中的至少一种。
7.根据权利要求1所述的一种长效玻璃防霉粉，其特征在于，所述磷酸钙的粒径4.5-5.0μm。
8.根据权利要求1所述的一种长效玻璃防霉粉，其特征在于，所述苯甲酸中的有效物质含量≥99.5wt％。
9.一种长效玻璃防霉粉的制备方法，其特征在于，包括以下步骤：
步骤一，按权利要求1所述的原料配比备料；将干燥的羧甲基壳聚糖、气相二氧化硅和艾草粉进行混合，得混合物A；
步骤二，将丙烯酸树脂和无机抑霉剂加入到所述混合物A中，混合均匀后加入磷酸钙和苯甲酸钠，搅拌均匀后得混合物B；
步骤三，将步骤二中得到的混合物B先切碎为若干小块，再进行研磨处理，最后放入球磨机中进行球磨，所得粉末即为所述长效玻璃防霉粉。