CN116477921A - 一种提高酒体能量及纯化酒体的方法 - Google Patents
一种提高酒体能量及纯化酒体的方法 Download PDFInfo
- Publication number
- CN116477921A CN116477921A CN202310317890.8A CN202310317890A CN116477921A CN 116477921 A CN116477921 A CN 116477921A CN 202310317890 A CN202310317890 A CN 202310317890A CN 116477921 A CN116477921 A CN 116477921A
- Authority
- CN
- China
- Prior art keywords
- wine
- energy storage
- ceramic
- storage rod
- ceramic energy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种提高酒体能量及纯化酒体的方法，属于酒产品改良技术领域。本发明利用特定制备方法得到的陶瓷储能棒能够降低酒类产品毒性的同时保留酒类产品的芳香风味和口感。本发明能够提升酒中能量、对酒体进行纯化、增加酒中微生物和矿物质微量元素活性，加快酒的纯化反应，使之大大缩短纯化时间，口感更加纯正，以及有效祛除酒中杂质和有害物如甲醇、重金属铅等，提高酒的口感和品质，减少对人体的危害，有效补充人体能量。
Description
技术领域
本发明涉及酒产品改良技术领域，尤其涉及一种提高酒体能量及纯化酒体的方法。
背景技术
从生命的本质来看，生命就是新陈代谢，它是细胞不断分裂、生命体不断自我更新的过程，人体生命方程式的两个方程式，一是人体吸收碳水化合物与氧气反应生成二氧化碳和能量的过程；二是人体吸收氮气与氢反应生成氨基酸和能量的过程，公式如下：
ΔT＝温度+能量+有机酶+无机微量元素
通过以上完成细胞代谢的人体方程式图示可以看出：人体生命方程式完成的四大必要条件是温度、能量、有机酶和无机微量元素，如果四个必要条件同时达到发生共振的情况下，人体生命方程式反应速度加快，细胞代谢的速度也会提高若干倍。白酒，尤其是酱香型白酒含有的四大元素——温度、能量、有机酶和无机微量元素与方程式完成的四大必要条件——温度、能量、有机酶和无机微量元素不谋而和。所以说白酒含有人体细胞代谢所需的元素，又是很好的能量载体，每天适量饮用白酒不失为养生和提高人体免疫力的好方法。
酒的化学成分是乙醇，一般含有微量的甲醇、杂醇和酯类物质，是以粮食为原料经发酵酿造而成的饮品。杂醇油是酒的芳香成分之一，但含量过高，对人们有毒害作用，它的中毒和麻醉作用比乙醇强，能使神经系统充血，使人头痛，其毒性随分子量增大而加剧。杂醇油在体内的氧化速度比乙醇慢，在机体内停留时间较长。杂醇油的主要成分是异戊醇、戊醇、异丁醇、丙醇等，其中以异丁醇、异戊醇的毒性较大。原料中蛋白质含量多时，酒中杂醇油的含量也高。酒中醛类是分子大小相应的醇的氧化物，也是白酒发酵过程中产生的。低沸点的醛类有甲醛、乙醛等，高沸点的醛类有糠醛、丁醛、戊醛、己醛等。醛类的毒性大于醇类，其中毒性较大的是甲醛。糠醛对机体也有毒害，使用谷皮、玉米芯及麸糠做辅料时，蒸馏出的白酒中糠醛及其它醛类含量皆较高。果胶质多的原料来酿制白酒，酒中会含有多量的甲醇，甲醇对人体的毒性作用较大，4～10克即可引起严重中毒。尤其是甲醇的氧化物甲酸和甲醛，毒性更大于甲醇，甲酸的毒性比甲醇大6倍，而甲醛的毒性比甲醇大30倍。白酒饮用过多，甲醇在体内有积蓄作用，不易排出体外，它在体内的代谢产物是甲酸和甲醛，所以极少量的甲醇也能引起慢性中毒。
酒精对人的损害，最重要的是中枢神经系统。它使神经系统从兴奋到高度的抑制，严重地破坏神经系统的正常功能。过量的饮酒就是损害肝脏。慢性酒精中毒，则可导致酒精性肝硬化。因此，提升酒中能量和纯化技术、增加酒中微生物活性和矿物质微量元素，加快酒的纯化反应，使之大大缩短纯化时间，口感更加纯正，以及有效祛除酒中杂质和有害物如甲醇、重金属铅等，是提高酒的口感和品质，减少对人体的危害，有效补充人体能量的关键所在。
目前，现有技术中尚缺少一种能够降低酒类产品毒性的同时保留酒类产品的芳香风味及口感的方法。
发明内容
本发明的目的在于提供一种提高酒体能量及纯化酒体的方法，能够降低酒类产品毒性的同时保留酒类产品的芳香风味和口感。
为了实现上述发明目的，本发明提供以下技术方案：
本发明提供了一种陶瓷储能棒的制备方法，包括以下步骤：
将陶瓷泥和水混合，得到混合物料；
将混合物料进行塑形，得到胚体；
将胚体进行烧制，得到陶瓷载体；
将陶瓷载体放入电离设备，通入氮气，电离处理后得到陶瓷储能棒。
优选的，所述陶瓷泥包括高岭土、粘土、火山泥；
所述高岭土、粘土、火山泥和水的体积比为2.8～3.2:1.8～2.2:0.8～1.2:1.8～2.2；
所述胚体为空心管状结构。
优选的，所述烧制的温度为1000～3000℃。
优选的，所述烧制的时间为24～120h。
优选的，所述电离处理的时间为1～20s。
优选的，所述电离处理采用的参数为：20～40kW、300～500V、100～200A、电离电子温度10万-25万度。
本发明还提供了上述制备方法得到的陶瓷储能棒。
本发明还提供了上述陶瓷储能棒在提升酒类产品品质中的应用。
优选的，所述酒类产品包括白酒、黄酒、药酒、米酒、清酒、威士忌、白兰地和果酒。
优选的，将陶瓷储能棒放置在盛装酒类产品的容器中，密封放置10d以上；
所述陶瓷储能棒和酒类产品的重量体积比为1g:1.5～2.5mL。
本发明的技术效果和优点：
本发明提供的陶瓷储能棒能够提升酒中能量、对酒体进行纯化、增加酒中微生物和矿物质微量元素活性，加快酒的纯化反应，使之大大缩短纯化时间，口感更加纯正，以及有效祛除酒中杂质和有害物如甲醇、重金属铅等，是提高酒的口感和品质，减少对人体的危害，有效补充人体能量。
本发明核心就是根据惊蛰机理，春雷响，万物生机理，当万物在能量，温度，有机酶，无机矿物微量元素同时作用在细胞上发生共振时，其细胞裂变速度快速加快，生命新陈代谢就不停加快代谢。能量从哪里来，怎么储存，怎么转移，都是当今世界难题。目前雷电的能量是已有产生能量中它是最大的，一种模拟雷电技术等离子体发生器，通过氮等离子体超高电子温度，导入复合成份陶瓷储能棒，本身陶瓷储能棒在高温中烧结，已经聚集大量储能，和氮等离子体导入能量叠加。转移到可以储存能量的白酒，白酒本身就是非常高的能量，三者能量发生共振，不但使白酒能量增强，同时有效加速纯化白酒速度，减低白酒中有害物如甲醇，杂醇等，让人们饮用时降低对人体伤害，同时此发明创造的独特之处就是此白酒所储存能量通过人体肺部吸收，肺朝百脉，达到补充人体细胞所需能量，与白酒中碳水化合物酒精人体饮用后所产生温度上升，以及白酒中复合成份的储能陶瓷棒是富含多种矿物活性微量元素，及白酒尤其酱香白酒中的微生物有机酶，在人体细胞吸收后达到共振，促进细胞裂变和新陈代谢，以此达到提高人体免疫力，防治各类疾病和慢病，打通微循环，改善人们健康和延续生命的目的。
附图说明
图1为陶瓷储能棒红外性能检测结果p1；
图2为陶瓷储能棒红外性能检测结果p2；
图3为陶瓷储能棒红外性能检测结果p3；
图4为陶瓷储能棒红外性能检测结果p4；
图5为陶瓷储能棒红外性能检测结果p5；
图6为陶瓷储能棒红外性能检测结果p6；
图7为陶瓷储能棒红外性能检测结果p7；
图8为贵州省仁怀市精化白酒检测有限公司检测报告p1；
图9为贵州省仁怀市精化白酒检测有限公司检测报告p2；
图10为贵州省仁怀市精化白酒检测有限公司检测报告p3；
图11为国药健康产业研究院有限公司提供的实验报告p1；
图12为国药健康产业研究院有限公司提供的实验报告p2；
图13为国药健康产业研究院有限公司提供的实验报告p3；
图14为国药健康产业研究院有限公司提供的实验报告p4；
图15为国药健康产业研究院有限公司提供的实验报告p5。
具体实施方式
本发明提供了一种陶瓷储能棒的制备方法，包括以下步骤：将陶瓷泥和水混合，得到混合物料；将混合物料进行塑形，得到胚体；将胚体进行烧制，得到陶瓷载体；将陶瓷载体放入电离设备，通入氮气，电离处理后得到陶瓷储能棒；优选的，所述陶瓷泥包括高岭土、粘土、火山泥，所述高岭土、粘土、火山泥和水的体积比为2.8～3.2:1.8～2.2:0.8～1.2:1.8～2.2，优选为2.9～3.1:1.9～2.1:0.9～1.1:1.9～2.1。
在本发明中，所述胚体优选为空心管状结构，所述烧制的温度优选为1000～2000℃，进一步优选为2000～3000℃，所述烧制的时间优选为24～120h，进一步优选为120～240h；所述电离处理的时间优选为5～20s，进一步优选为20～100s；所述电离处理采用的参数优选为：20～40kW、300～500V、100～200A、电离电子温度10万-25万度，进一步优选为25～35kW、350～450V、130～170A、电离电子温度15万-20万度。
本发明还提供了上述制备方法得到的陶瓷储能棒。
本发明还提供了上述陶瓷储能棒在提升白酒品质中的应用，所述陶瓷储能棒优选用于提高微量元素的含量、降低有害物质的含量，优选将陶瓷储能棒放置在盛装白酒的容器中密封放置10d以上，以实现白酒品质的提升；所述陶瓷储能棒和白酒的重量体积比优选为1g:1.5～2.5mL，进一步优选为1g:1.8～2.2mL；在本发明中，所述陶瓷储能棒还同时具有红外特性，容器盛装白酒后还可连同陶瓷储能棒一起置于远红外辐射器中，进一步提升对酒体的改良。
下面结合实施例对本发明提供的技术方案进行详细的说明，但是不能把它们理解为对本发明保护范围的限定。
实施例1
第一步，将高岭土、粘土、火山泥和水按照3:2:1:2的体积比调和均匀；
第二步：将调和的原材料制成管状空心胚体，150mm高、外径45mm、内径30mm、重量250g；
第三步，制成的胚体在窑炉中通过高温1700度、24小时烧结；
第四步，将烧制好的胚体置入充能设备(东莞市微弧环保科技公司MAO—30)中，通入氮气，设置参数30KW、电压400V、电流150A、电离电子温度20万度，进行电离，时间为5s。
第五步，将陶瓷储能棒安装在500ml酒瓶中，用于盛装酒。
实施例2
第一步，将高岭土、粘土、火山泥和水按照3.2:2.2:0.8:2.2的体积比调和均匀；
第二步：将调和的原材料制成管状空心胚体，150mm高、外径45mm、内径30mm、重量250g；
第三步，制成的胚体在窑炉中通过高温1800度、36小时烧结；
第四步，将烧制好的胚体置入充能设备(东莞市微弧环保科技公司MAO—30)中，通入氮气，设置参数20KW、电压300V、电流100A、电离电子温度10万度，进行电离，时间为5s。
第五步，将陶瓷储能棒安装在500ml酒瓶中，用于盛装酒。
实施例3
第一步，将高岭土、粘土、火山泥和水按照2.8:1.8:1.2:1.8的体积比调和均匀；
第二步：将调和的原材料制成管状空心胚体，150mm高、外径45mm、内径30mm、重量250g；
第三步，制成的胚体在窑炉中通过高温1900度、72小时烧结；
第四步，将烧制好的胚体置入充能设备(东莞市微弧环保科技公司MAO—30)中，通入氮气，设置参数40KW、电压500V、电流200A、电离电子温度25万度，进行电离，时间为5s。
第五步，将陶瓷储能棒安装在500ml酒瓶中，用于盛装酒。
实验例1
委托武汉产品质量监督检验所对本发明制备的陶瓷储能棒的红外性能进行检测(为方便检测提供样品为圆柱体，实际中采用空心管状，并不会影响其远红外性能)，检验结果如图1～7所示。
结果显示，陶瓷储能棒法的全发射率为0.89，大于国家标准0.83，且具有较广的红外辐射波长范围。
实验例2
取白酒分为两份，一份盛装在实施例1中安装有陶瓷储能棒的酒瓶中，作为实验组，另一份盛装在未安装陶瓷储能棒的酒瓶中，作为对照组。
相同条件下放置30天后，由10名具有品评经验的人员对样品的柔和程度、气味、综合性质进行评分(每项总分100)，统计评价结果，计算平均分值，0～50记为较差，51～80记为一般，81～100记为优良，结果如下表1所示：
表1酒品感官品质评价结果
| 项目 | 对照组 | 实验组 |
| 柔和程度 | 一般 | 优良 |
| 气味 | 一般 | 优良 |
| 综合性质 | 一般 | 优良 |
在感官品质评价的同时，将样品委托检测机构对甲醇指标进行检测，结果如下表2所示：
表2酒品甲醇含量检测结果
| 项目 | 国家标准 | 对照组 | 实验组 |
| 甲醇 | ≤0.6g/L | 0.25g/L | ＜0.025g/L(限定量) |
注：限定量表示测量的最小限度，真实数据小于此数值
实验结果说明，采用本发明安装有陶瓷储能棒的酒瓶放置后的酒体，其中的有害物质甲醇含量大大降低，且感官品质更优。
实验例3
利用本发明实施例1盛装放置30d后的酒品，其产品名为白金全球鹰酒，分别取样送检至贵州省仁怀市精化白酒检测有限公司和国药健康产业研究院有限公司。
通过贵州省仁怀市精化白酒检测有限公司检测证明本发明白酒，甲醇和重金属铅的含量几乎为零，氯化物也大大减少，说明本发明提供的陶瓷储能棒有祛除酒中有甲醇、重金属有害物质，纯化酒体的作用，口感纯正，不呛不辣，不容易过敏，检测报告见图8～10。
通过国药健康产业研究院有限公司提供的《白金全球鹰酒、财江天下酒、五粮液白酒及中药枳椇子对小鼠醉酒影响》实验报告可知，本发明提供的陶瓷储能棒处理后的白酒对人体伤害大大减少，实验报告见图11～15。
由上可知，本发明采用特殊陶土材质，富含矿物质微量元素，能够提升酒水中微量元素；具有很强的吸附性，能够吸附和分解酒体中的一些有害物质，如甲醇，重金属铅等，从而使酒的品质得到上升；远红外能量波帮助酒体微生物活化，加快酒体中微生物活化过程，有利于酒体的纯化，让酒体越来越饱满，具有很好的保存收藏价值；酒本身是很好的能量载体，全球鹰酒把酒体杂质祛除，再通过远红外能量波，以及在特殊气体的等离子体中进一步补充能量，使之与酒体分子产生共振，使之能量加强；该复合成份陶瓷储能棒还能够调节酒的酸碱性和矿化水质的作用。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种陶瓷储能棒的制备方法，其特征在于，包括以下步骤：
将陶瓷泥和水混合，得到混合物料；
将混合物料进行塑形，得到胚体；
将胚体进行烧制，得到陶瓷载体；
将陶瓷载体放入电离设备，通入氮气，电离处理后得到陶瓷储能棒。
2.根据权利要求1所述的陶瓷储能棒的制备方法，其特征在于，所述陶瓷泥包括高岭土、粘土、火山泥；
所述高岭土、粘土、火山泥和水的体积比为2.8～3.2:1.8～2.2:0.8～1.2:1.8～2.2；
所述胚体为空心管状结构。
3.根据权利要求2所述的陶瓷储能棒的制备方法，其特征在于，所述烧制的温度为1000～3000℃。
4.根据权利要求3所述的陶瓷储能棒的制备方法，其特征在于，所述烧制的时间为24～120h。
5.根据权利要求4所述的陶瓷储能棒的制备方法，其特征在于，所述电离处理的时间为1～20s。
6.根据权利要求5所述的陶瓷储能棒的制备方法，其特征在于，所述电离处理采用的参数为：20～40kW、300～500V、100～200A、电离电子温度10万-25万度。
7.权利要求1～6任一项所述的制备方法得到的陶瓷储能棒。
8.权利要求7所述的陶瓷储能棒在提升酒类产品品质中的应用。
9.根据权利要求8所述的陶瓷储能棒在提升酒类产品品质中的应用，其特征在于，所述酒类产品包括白酒、黄酒、药酒、米酒、清酒、威士忌、白兰地、果酒。
10.根据权利要求8或9所述的陶瓷储能棒在提升酒类产品品质中的应用，其特征在于，将陶瓷储能棒放置在盛装酒类产品的容器中，密封放置10d以上；
所述陶瓷储能棒和酒类产品的重量体积比为1g:1.5～2.5mL。