CN116463020A - Colorful imitation marble paint and preparation process thereof - Google Patents
Colorful imitation marble paint and preparation process thereof Download PDFInfo
- Publication number
- CN116463020A CN116463020A CN202310485834.5A CN202310485834A CN116463020A CN 116463020 A CN116463020 A CN 116463020A CN 202310485834 A CN202310485834 A CN 202310485834A CN 116463020 A CN116463020 A CN 116463020A
- Authority
- CN
- China
- Prior art keywords
- stirring
- paint
- imitation marble
- bactericide
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a colorful imitation marble paint and a preparation process, which belongs to the technical field of paint, and aims at the problems of easy layering and precipitation stability and higher flushing resistance of imitation marble paint.
Description
Technical Field
The invention belongs to the technical field of paint, and particularly relates to a colorful imitation marble paint and a preparation process thereof.
Background
The marble-like coating adopts natural minerals, has high weather resistance, water resistance, moisture resistance and lasting color, has the texture, luster and texture of natural marble, can be compared with natural marble in fidelity, and is widely applied to the aspect of building decoration.
The existing imitation marble paint is generally used for protecting and decorating an outer wall body, is subjected to wind blowing, sun drying and rain spraying all the year round, and changes color and falls off after being used for a period of time, natural ore is added into the imitation marble paint, the specific gravity is larger than that of emulsion, the imitation marble paint can sink after being placed for a certain period of time, the layering phenomenon of 'upper thin and lower thick' is caused, and the imitation marble paint needs to be fully shaken and stirred manually during construction, so that the imitation marble paint is uniformly distributed, the labor intensity of constructors is increased, and the construction efficiency is influenced.
Disclosure of Invention
The invention aims to provide a colorful imitation marble paint which can enhance the flushing resistance and the storage stability of the paint.
In order to solve the technical problems, the following technical scheme is provided:
a colorful imitation marble paint is composed of the following raw materials in parts by weight:
0.12 to 0.18 percent of normal temperature bactericide
Anti-settling agent (a bright nest partner) 0.8-1.2
Dispersion stabilizer (Brilliant nest guard) 16.16-24.24
0.08 to 0.12 percent of high-temperature bactericide
Pure acrylic emulsion 9.6-14.4
Film forming auxiliary agent 0.72-10.8
0.4 to 0.6 of glycol
0.08-0.12 of multifunctional auxiliary agent
3.2 to 4.8 portions of fluorite
Coarse sand 22.4-33.6
Fine sand 22.4-33.6
Thickening agents 4-6
Defoaming agent 0.04-0.06
Further, the normal temperature bactericide is isothiazolinone.
Further, the anti-settling agent is a nano-mineral material.
Further, the stabilizer is a mixture of bentonite powder and water, wherein the ratio of the powder to the water is 1:74, and the stabilizer is prepared by stirring.
Further, the high-temperature bactericide is benzisothiazolinone.
Further, the film forming auxiliary agent is an alcohol ester compound.
Further, the multifunctional auxiliary agent is 2-amino-2-methyl-1-propanol containing 5% of water.
Further, the size of the coarse sand particles is 40-80 meshes, and the size of the fine sand particles is 80-120 meshes.
Further, the thickener is formed by mixing 1 part of raw pulp with the model RD-180 with 19 parts of water.
Another object of the present invention is to provide a process for preparing a multicolor marbleized paint, comprising the steps of:
step one, stirring for the first time: adding normal temperature bactericide, precipitant (Brilliant nest partner), stabilizer (Brilliant nest guard), high temperature bactericide and pure acrylic emulsion into the stirrer in turn according to a specified proportion, stirring for 4-6 min at a rotation speed of 500r/min.
Step two, stirring for the second time: sequentially adding the film forming additive, the ethylene glycol and the multifunctional additive into the mixed solution which is stirred for the first time according to a specified proportion, and continuously stirring for 35-45 minutes at the rotating speed of 500r/min.
And thirdly, adjusting the pH value, and adjusting the pH value of the mixed emulsion after the second stirring to 9.
Step four, base material is put in: a 5mm x 5mm screen is arranged at a feed inlet of the stirrer, and fluorite (powder and granular proportion is 1:3) with a specified proportion, coarse sand with 40-80 meshes and fine sand with 80-120 meshes are sequentially added and stirred uniformly.
And fifthly, thickening, namely putting the prepared thickening agent (the ratio of primary pulp to water is 1:19) into the emulsion after the step four, and uniformly stirring.
Step six, defoaming: and (3) adding an antifoaming agent into the thickened emulsion to eliminate foam generated in the step (V).
Compared with the prior art, the colorful imitation marble paint provided by the invention has outstanding storage stability and flushing resistance.
Description of the embodiments
In an embodiment, the model number and merchant of each component used is as follows:
normal temperature bactericide: isothiazolinone, CAS#, CMIT 26172-55-4 Shanghai dry chemical technology Co., ltd
Anti-settling agent: a bright nest partner; shanghai Huang nest Utility Co., ltd
Stabilizing agent: the brilliant nest guard No. 1; shanghai Huang nest Utility Co., ltd
High-temperature bactericide: benzisothiazolinone: CAS#,2634-33-5, shanghai daily Dry chemical technology Co., ltd
Pure acrylic emulsion: jiangsu Japanese chemical Co Ltd
Film forming auxiliary agent: alcohol ester twelve; ji Luyi Shiman Fine chemical Co., ltd
Multifunctional auxiliary agent: 2-amino-2-methyl-1-propanol; ceramic AMP-95; tuo chemical Shanghai Co Ltd
And (3) a thickening agent: RD-180 Qingdao sea-Lyen chemical technology Co.Ltd
Defoaming agent: MING XIANG MX-68 Ming Xiang chemical technology group Co., ltd
Example 1
Adding isothiazolinone 0.15kg, anti-settling agent (Brilliant nest partner) 1kg, stabilizer (Brilliant nest guard) 20.2kg, high-temperature bactericide 0.1kg, and pure acrylic emulsion 12kg into a stirrer, stirring for 5min at 500r/min.
The isothiazolinone can kill bacteria, fungi and other microbes in water effectively to prevent paint from deteriorating, and the anti-precipitant can prevent paint from layering and depositing solid matter, increase the transparency of paint and improve construction effect. The stabilizer is mainly composed of montmorillonite, has covering power and adhesive force, has extremely strong water absorbability and dispersibility, and plays a role of a dispersing agent in the paint, so that the paint is kept uniform. The benzisothiazolinone has the functions of corrosion resistance, mildew resistance, deterioration resistance, demulsification resistance and the like. The pure acrylic emulsion is an emulsion formed by copolymerization of various acrylic acid, methacrylic acid, methyl methacrylate, acrylic esters and functional additives through an optimized process, has no toxicity, no corrosiveness and no combustion, has high safety and environmental protection, is a base part of a coating, and is also a carrier of main coating additives such as sand stone, fluorite and the like.
0.9kg of film-forming additive, 0.5kg of ethylene glycol and 0.1kg of multifunctional additive are added into the mixed emulsion after the steps are completed, and stirring is continued for 40 minutes at the rotating speed of 500r/min.
The film forming additive is an alcohol ester compound, which is also called as a coalescing additive. Can promote the plastic flow and elastic deformation of high molecular compound, improve the coalescence property, and can form a film in a wider construction temperature range, and is a fugitive plasticizer. The general emulsion has a film forming temperature, when the ambient temperature is lower than the film forming temperature of the emulsion, the emulsion is not easy to form a film, and the film forming auxiliary agent can improve the film forming mechanism of the emulsion and help to form a film. The film forming auxiliary agent volatilizes after film forming, and the characteristic of the coating film is not affected. The glycol has hygroscopicity at the freezing point of-12.6 ℃, plays a role in preventing freezing in the paint and has a slow drying effect in construction. The multifunctional auxiliary agent is 2 amino-2-methyl-1-propanol, and has the functions of improving pigment dispersibility of the paint, improving the gloss of a paint film, regulating and stabilizing the PH value of the paint, improving the performance of a thickener and the like. The film forming additive, glycol and multifunctional additive are all paint additives for improving and improving the performance of paint.
And adjusting the pH value to 9.
The pH value of the emulsion is regulated by using a multifunctional auxiliary agent, and the emulsion is regulated by using a small amount of multiple principles.
The base material is put in, a 5mm sieve is arranged at a feed inlet of the stirrer, 4kg of fluorite (the ratio of powder to granular is 1:3) with a specified ratio, 28kg of coarse sand with 40-80 meshes and 28kg of fine sand with 80-120 meshes are sequentially put in, and the stirring is uniform.
The emulsion is prepared, so that the fluorite powder can be put in, the fluorite powder is bright in color and mixed into the emulsion, the fluorite powder is a key component of the marble-like coating, coarse sand and fine sand not only increase the hardness of the coating after construction, but also have the texture of natural stone, and can be combined with the fluorite, so that the fluorite powder can be compared with the natural marble, and the decorative effect is much better than that of the common coating.
Thickening, namely 5kg of a prepared thickening agent RD-180 (the ratio of raw pulp to water is 1:19) is put into the emulsion after the step four, and the mixture is stirred uniformly.
Defoaming, namely adding 0.05kg of defoaming agent into the thickened emulsion, stirring, eliminating foam generated in the step five, adding the defoaming agent in batches, and observing the state of the coating to obtain the skin lotion.
After the marbleized coating product is prepared according to the steps, the quality characteristics of the marbleized coating product are detected.
Example two
The procedure of example one was repeated by adjusting the amounts of the components used in example one.
Stirring for the first time, adding 0.12kg of normal temperature bactericide, 0.8 of anti-settling agent (a bright nest partner), 24.24 of stabilizer (a bright nest guard), 0.12 of high temperature bactericide and 9.6 of pure acrylic emulsion into a stirrer according to a specified proportion, and stirring for 4 minutes at a rotating speed of 500r/min.
And stirring for the second time, sequentially adding 0.72 of film forming additive, 0.4 of ethylene glycol and 0.08 of multifunctional additive into the mixed solution after the first stirring according to a specified proportion, and continuing stirring for 35 minutes at the rotating speed of 500r/min.
And adjusting the pH value to 9.
The base material is put in, a 5mm sieve is arranged at a feed inlet of the stirrer, 3.2kg of fluorite (the ratio of powder to granule is 1:3) with a specified ratio, 23.08kg of coarse sand with 40-80 meshes and 33.6kg of fine sand with 80-120 meshes are sequentially put in, and the stirring is uniform.
4kg of a prepared thickener (the ratio of raw pulp to water is 1:19) is put into the emulsion after the step is finished, and the mixture is stirred uniformly.
Defoaming, namely adding 0.04kg of defoaming agent into the thickened emulsion to eliminate foam generated in the step five.
Example III
The procedure of example one was repeated by adjusting the amounts of the components used in example one.
Stirring for the first time, adding 0.18kg of normal temperature bactericide, 1.2kg of anti-settling agent (a bright nest partner), 16.15kg of stabilizer (a bright nest guard), 0.08kg of high temperature bactericide and 14.3 kg of pure acrylic emulsion into a stirrer according to a specified proportion, and stirring for 6 minutes at a rotating speed of 500r/min.
And (3) stirring for the second time, sequentially adding 1.08kg of film forming additive, 0.6kg of ethylene glycol and 0.12kg of multifunctional additive into the mixed solution subjected to the first stirring according to a specified proportion, and continuing stirring for 45 minutes at the rotating speed of 500r/min.
And adjusting the pH value to 9.
The base material is put in, a 5mm sieve is arranged at a feed inlet of the stirrer, 4.8kg of fluorite (the ratio of powder to granule is 1:3) with a specified ratio, 33.03kg of coarse sand with 40-80 meshes and 22.4kg of fine sand with 80-120 meshes are sequentially put in, and the stirring is uniform.
And (3) thickening, namely, 6kg of prepared thickening agent (the ratio of raw pulp to water is 1:19) is put into the emulsion after the step four, and the mixture is stirred uniformly. Comparative example
Defoaming, namely adding 0.06kg of defoaming agent into the thickened emulsion to eliminate foam generated in the step five.
Comparative example
CN 101967329A discloses an invention patent: the quality detection results of the water-based multicolor marble-like paint prepared according to the embodiment of the invention are shown in the table I.
(1) Preparing color particle component (single color): weighing 35 parts of 7104 acrylic emulsion, 25 parts of deionized water, 0.3 part of auxiliary agent (comprising 0.3 part of cellulose, 0.6 part of dispersing agent and 3 parts of antifreeze agent), 0.3 part of xanthan gum and 30 parts of pigment and filler, adding the auxiliary agent consisting of dispersing agent, cellulose and antifreeze agent and xanthan gum into water under low-speed (400 r/min) stirring, stirring for 5min-10min, regulating the speed to medium speed (600 r/min), slowly and uniformly adding pigment and filler, dispersing for 45 min at high speed (1200 r/min-1500 r/min), grinding to fineness of less than 45 mu m by using a grinder, adding the metered 7104 acrylic emulsion, and stirring uniformly to obtain a single-color particle base material for later use.
(2) Preparing protective colloid, namely weighing 0.8 part of suspending agent, 30 parts of deionized water, 1 part of ionic compound, 60 parts of 7104 acrylic emulsion and 4.5 parts of functional dispersing agent by weight, during production, firstly dispersing and dissolving the weighed suspending agent at a high speed (1200 r/min) by using the weighed deionized water, and then adding the 7104 acrylic emulsion and the functional dispersing agent into the prepared pre-gel liquid under stirring at a medium speed (600 r/min-800 r/min) to obtain a protective colloid material for later use.
(3) And (3) granulating and surface curing, namely adding the various color particle base materials obtained in the step (1) and the protective colloid materials obtained in the step (2) into a self-made shearing stirring device according to the weight ratio of 2:1, stirring and shearing at a low speed to achieve the color particle size specification required by the requirement, and adding an ionic compound to carry out surface gelatinization treatment to obtain the monochromatic water-based multicolor particles with the required hardness.
(4) Mixing, painting, and proportionally mixing several monochromatic color particles according to the requirements of real objects or standard samples to obtain the final product.
Table I A comparison table of quality test results of examples and comparative examples
From the test data in Table I, it can be seen that the marbleized multicolor paint provided by the invention has outstanding advantages in both storage stability and wash fastness.
Claims (10)
1. The colorful imitation marble paint is characterized by comprising the following raw materials in percentage by weight:
0.12 to 0.18 percent of normal temperature bactericide
0.8 to 1.2 percent of anti-settling agent
Stabilizers 16.16-24.24
0.08 to 0.12 percent of high-temperature bactericide
Pure acrylic emulsion 9.6-14.4
Film forming auxiliary agent 0.72-10.8
0.4 to 0.6 of glycol
0.08-0.12 of multifunctional auxiliary agent
3.2 to 4.8 portions of fluorite
Coarse sand 22.4-33.6
Fine sand 22.4-33.6
Thickening agents 4-6
0.04-0.06 part of defoaming agent.
2. The multi-color imitation marble paint of claim 1, wherein the room temperature bactericide is isothiazolinone.
3. The multi-color imitation marble coating of claim 1, wherein the anti-settling agent is a nano-mineral material.
4. The colorful simulated marble paint of claim 1, wherein the stabilizer is a mixture of bentonite powder and water, the ratio of powder to water is 1:74, and the paint is obtained by stirring.
5. The multi-color imitation marble paint of claim 1, wherein the high-temperature bactericide is benzisothiazolinone.
6. The multi-color imitation marble coating of claim 1, wherein the film-forming aid is an alcohol ester compound.
7. The multi-color imitation marble paint of claim 1, wherein the multifunctional auxiliary agent is 2 amino-2-methyl-1-propanol containing 5% water.
8. The multi-color imitation marble paint of claim 1, wherein the coarse sand grain size is 40-80 mesh and the fine sand grain size is 80-120 mesh.
9. The multi-color imitation marble paint of claim 1, wherein the thickener is mixed with 19 parts of water from 1 part of model RD-180 virgin pulp.
10. A preparation process of a colorful imitation marble paint comprises the following steps:
step one, stirring for the first time: adding a normal temperature bactericide, a precipitator (a brilliant nest partner), a stabilizer (a brilliant nest guard), a high-temperature bactericide and a pure acrylic emulsion into a stirrer in turn according to a specified proportion, and stirring for 4-6 minutes at a rotating speed of 500r/min;
step two, stirring for the second time: sequentially adding the film forming additive, the ethylene glycol and the multifunctional additive into the mixed solution which is stirred for the first time according to a specified proportion, and continuously stirring for 35-45 minutes at the rotating speed of 500r/min;
step three, regulating the pH value, and regulating the pH value of the mixed emulsion after the second stirring to 9;
step four, base material is put in: arranging a 5 mm-5 mm screen at a feed inlet of a stirrer, sequentially adding fluorite (powder and granular proportion is 1:3), 40-80 mesh coarse sand and 80-120 mesh fine sand in a specified proportion, and uniformly stirring;
step five, thickening, namely putting the prepared thickening agent (the ratio of primary pulp to water is 1:19) into the emulsion after the step four, and uniformly stirring;
step six, defoaming: and (3) adding an antifoaming agent into the thickened emulsion to eliminate foam generated in the step (V).