CN1164515C - 永久性自洁净纳米陶瓷釉 - Google Patents
永久性自洁净纳米陶瓷釉 Download PDFInfo
- Publication number
- CN1164515C CN1164515C CNB02115404XA CN02115404A CN1164515C CN 1164515 C CN1164515 C CN 1164515C CN B02115404X A CNB02115404X A CN B02115404XA CN 02115404 A CN02115404 A CN 02115404A CN 1164515 C CN1164515 C CN 1164515C
- Authority
- CN
- China
- Prior art keywords
- ceramic
- cleaning
- ceramic glaze
- glaze
- dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种永久性自洁净纳米陶瓷釉,它是在普通陶瓷釉中添加进多种纳米氧化物材料,改变传统陶瓷釉配方,使用传统的陶瓷类产品制备工艺烧结,使新陶瓷类产品陶瓷釉表面有纳米结构,因此具有疏水和永久性自洁净功能。该陶瓷釉主要用于电力瓷瓶、瓷棒、建筑和家用等自洁净陶瓷类产品中。本发明的陶瓷釉制备工艺简单;成本低;不改变陶瓷产品的生产工艺;耐温范围大;耐酸碱性好。
Description
技术领域
本发明涉及工业、民用陶瓷釉材料,特别涉及永久性自洁净纳米陶瓷釉材料。
背景技术
普通陶瓷釉,尤其是用于电力瓷瓶、瓷棒、建筑和家和陶瓷的釉表面,疏水和自洁净性能差,易污染。目前尚没有发现制备永久性自洁净纳米高压瓷瓶的报道和介绍,也没发现任何相关永久性自洁净纳米陶瓷釉及其在陶瓷产品表面的应用的报导和实际应用产品。陶瓷产品生产和应用厂家渴望有自洁净纳米陶瓷釉及自洁净陶瓷类产品。
发明内容
本发明的目的是提供一种永久性自洁净纳米陶瓷釉,通过纳米技术改变陶瓷釉表面的结构,使其具有永久性疏水、自洁净的性能。
实现本发明目的的永久性自洁净纳米陶瓷釉是在普通陶瓷釉中添加一氧化锌(ZnO)、三氧化二铋(Bi2O3)、三氧化二锑(Sb2O3)、二氧化锰(MnO2)、三氧化二钴(Co2O3)、三氧化二铬(Cr2O3)、一氧化镍(NiO)、二氧化硅(SiO2)、三氧化二硼(B2O3)、九水硝酸铝(Al(NO3)3·9H2O)无机纳米材料,其中各材料的重量配比为:普通陶瓷釉200份,一氧化锌0~10份,三氧化二铋0.7~1.0份,三氧化二锑1.5~1.8份,二氧化锰0.7~1.0份,三氧化二钴1.5~1.8份,三氧化二铬0.7~1.0份,一氧化镍1.5~1.8份,二氧化硅2~2.8份,三氧化二硼0.15~0.2份,九水硝酸铝0~0.2份。
所述永久性自洁净纳米陶瓷釉的配制方法,其步骤是:
(1)将纳米级三氧化二铋、三氧化二锑、二氧化锰、三氧化二钴、三氧化二铬、一氧化镍、二氧化硅、三氧化二硼、九水硝酸铝按0.5∶1∶0.5∶1∶0.5∶1∶1.5∶0.1∶0~0.1的重量比混合均匀;
(2)将步骤(1)的混合物与氧化锌按2∶0~5重量比混合;
(3)将步骤(2)所得到的混合物和普通陶瓷釉按8~20∶200重量比(8~20克混合物和200毫升普通陶瓷釉)混合均匀即得。
按本发明混合制成的永久性自洁净纳米陶瓷釉产品,涂敷在陶瓷土坯表面,经传统陶瓷烧制工艺制备出的陶瓷表面有纳米结构,在瓷釉表面与水珠之间形成一层气膜,使其有永久性疏水、自洁净的性能。
本发明与现有相关技术相比有如下优点和积极效果:永久性疏水、自洁净性能;制备工艺简单;成本低;不改变陶瓷产品的传统烧结工艺;耐温范围大;耐酸碱性好。
具体实施方式
实施例1
普通陶瓷釉中添加纳米级三氧化二铋(Bi2O3)、三氧化二锑(Sb2O3)、二氧化锰(MnO2)、三氧化二钴(Co2O3)、三氧化二铬(Cr2O3)、一氧化镍(NiO)、二氧化硅(SiO2)、三氧化二硼(B2O3)氧化物,具体比例为0.5∶1∶0.5∶1∶0.5∶1∶1.5∶0.1。将这些纳米材料混合均匀后,其与普通瓷釉的比例为10克纳米材料与200毫升(约200克)普通瓷釉。实例中使用的普通瓷釉和瓷土坯是普通的瓷釉和瓷土坯的产品。烧结工艺为从室温开始经过1个半小时的匀速加温,达到300度,在300度保温1个半小时;在300度的基础上,再经过1个半小时的匀速加温,达到600度,600度保温1小时;在600长基础上经过1个半小时的匀速加温,达到900度,在900度保温1个半小时;在900度基础上,经过1个半小时保温,达到1100度,在1100度保温1小时;在1100度基础上,经过1个半小时的匀速加温,达到1280度,1280度保温2小时;最后关掉电源,使其自然冷却到室温,得到永久性疏水、自洁净的纳米瓷釉表面,疏水角达到120度。
实施例2 普通陶瓷釉中添加纳米级三氧化二铋(Bi2O3)、三氧化二锑(Sb2O3)、二氧化锰(MnO2)、三氧化二钴(Co2O3)、三氧化二铬(Cr2O3)、一氧化镍(NiO)、二氧化硅(SiO2)、三氧化二硼(B2O3)氧化物和九水硝酸铝(Al(NO3)3·9H2O),具体比例为0.5∶1∶0.5∶1∶0.5∶1∶1.5∶0.1∶0.1。将这些纳米材料混合均匀后,再与氧化锌按照2∶5的比例混合,将混合物与普通瓷釉的比例为10克纳米材料配200毫升(200克)普通瓷釉。本例使用的普通瓷釉和瓷土坯及烧结工艺同实施例1,得到永久性疏水、自洁净的纳米瓷釉表面,疏水角达到125度。
Claims (2)
1、一种自洁净纳米陶瓷釉,包含普通陶瓷釉,其特征在于还包含一氧化锌(ZnO)、三氧化二铋(Bi2O3)、三氧化二锑(Sb2O3)、二氧化锰(MnO2)、三氧化二钴(Co2O3)、三氧化二铬(Cr2O3)、一氧化镍(NiO)、二氧化硅(SiO2)、三氧化二硼(B2O3)、九水硝酸铝(Al(NO3)3·9H2O)无机纳米材料,各材料的重量配比为:200份普通陶瓷釉,加一氧化锌0~10份、三氧化二铋0.7~1.0份、三氧化二锑1.5~1.8份、二氧化锰0.7~1.0份、三氧化二钴1.5~1.8份、三氧化二铬0.7~1.0份、一氧化镍1.5~1.8份、二氧化硅2~2.8份、三氧化二硼0.15~0.2份、九水硝酸铝0~0.2份。
2、权利要求1所述的纳米陶瓷釉的配制方法,其步骤是:
(1)将纳米级三氧化二铋、三氧化二锑、二氧化锰、三氧化二钴、三氧化二铬、一氧化镍、二氧化硅、三氧化二硼、九水硝酸铝按0.5∶1∶0.5∶1∶0.5∶1∶1.5∶0.1∶0~0.1的重量比混合均匀;
(2)将步骤(1)的混合物与氧化锌按2∶0~5重量比混合;
(3)将步骤(2)所得到的混合物和普通陶瓷釉按8~20∶200重量比混合均匀即得。