CN116411487A - 一种抗菌型墙纸及其制备方法 - Google Patents
一种抗菌型墙纸及其制备方法 Download PDFInfo
- Publication number
- CN116411487A CN116411487A CN202111656092.5A CN202111656092A CN116411487A CN 116411487 A CN116411487 A CN 116411487A CN 202111656092 A CN202111656092 A CN 202111656092A CN 116411487 A CN116411487 A CN 116411487A
- Authority
- CN
- China
- Prior art keywords
- long
- wallpaper
- antivirus
- acting antibacterial
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种具有长效抗菌杀毒功能的墙纸，由基层、面层和印花层构成，所述印花层外还复合一层具有长效抗菌杀毒能力的共聚尼龙薄膜。所述具有长效抗菌杀毒能力的共聚尼龙薄膜的共聚尼龙原料粒子中添加有无机长效抗菌剂，所述无机长效抗菌剂在所述共聚尼龙原料粒子合成的阶段添加。通过上述方式，本发明能够在有效提高传统PVC墙纸的强度和耐刮擦性能的同时，使墙纸具有良好的杀菌抗病毒作用，降低室内空气中的不良菌落总量，除此之外，所述长效抗菌杀毒能力的共聚尼龙薄膜还具有良好的水汽透过率，覆盖在印花层上不会影响墙体水汽挥发，有效消除了墙纸内面霉菌产生的条件，提高墙纸的使用寿命，特别适合应用于医院、商场和学校等公共场所。
Description
技术领域
本发明涉及装修材料领域，特别是涉及一种抗菌型墙纸及其制备方法。
背景技术
墙纸也称为壁纸，是一种用于裱糊墙面的室内装修材料，其目的主要是用来保护墙面完整性，掩盖墙体缺陷和提供特殊视觉效果，广泛用于住宅、办公室、宾馆、酒店及交通工具的室内装修等。其材质一般为纸、高分子膜材料或者二者的复合材料，其表面一般会通过印刷或者压纹等手段制作出各种图案。常用的墙纸由于其材质和结构的限制，一般强度较低，不耐刮擦，容易老化，且不易维护，尤其是墙纸基体大部分为纸基，容易吸潮，引起细菌孽生，为了提高墙纸的使用寿命，目前常用的方法是在墙纸上再覆盖一层PE或者PP透明膜层，这种方式虽然可以一定程度上提高了墙纸的强度和耐刮擦性能，但是由于PP或者PE膜层的隔水性比较高，墙纸铺设以后，墙体内的水分无法挥发，长此以往又会导致墙纸内侧产生霉菌，霉菌成熟后产生的孢子对室内人群的健康具有严重的威胁，尤其是近年来随着新冠病毒在世界范围内的流行，如何预防环境中的致病病毒的孽生和传染成为一个世界性的课题。
发明内容
本发明主要解决的技术问题是提供一种新型墙纸，能够具有良好的抗菌杀毒功能，适用于公共空间使用。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种具有长效抗菌杀毒功能的墙纸，所述具有长效抗菌杀毒功能的墙纸由基层、面层和印花层构成，所述印花层外还复合一层具有长效抗菌杀毒能力的共聚尼龙薄膜。所述具有长效抗菌杀毒能力的共聚尼龙薄膜的共聚尼龙原料粒子中添加有无机长效抗菌剂，所述无机长效抗菌剂在所述共聚尼龙原料粒子合成的阶段添加。
在本发明一个较佳实施例中，所述无机长效抗菌剂在合成阶段的添加方法包括以下内容：首先制取相应单体水溶液，然后根据工艺要求将相应含量的无机长效抗菌剂加入所述单体水溶液中搅拌均匀，最后将所述单体水溶液高温缩聚除水之后经挤出冷却切粒形成原料粒子。
在本发明一个较佳实施例中，所述无机长效抗菌剂为锌离子无机抗菌剂。所述锌离子抗菌剂包括氧化锌、己二酸锌胺、乙酸锌或砒啶硫酮锌中的一种或其组合。
在本发明一个较佳实施例中，所述共聚尼龙原料粒子在粒子的合成阶添加有含量为500~5000PPM，优选含量为所为3000~4000PPM的无机长效抗菌剂，
在本发明一个较佳实施例中，所述长效抗菌杀毒共聚尼龙薄膜的厚度为20~50微米。
在本发明一个较佳实施例中，所述具有长效抗菌杀毒能力的共聚尼龙薄膜的共聚尼龙原料粒子为PA66/6、PA66/610或者PA66/612中的一种或多种的组合。
在本发明一个较佳实施例中，所述具有长效抗菌杀毒能力的共聚尼龙薄膜的复合工艺包括热压、粘合或淋膜涂布工艺。其中热压工艺中包括压花步骤和热压复合步骤和压花成型步骤，所述压花成型步骤与热压复合步骤同步进行；其中淋膜涂布工艺中还包括淋膜涂布步骤和压花成型步骤，所述压花成型步骤设置在淋膜涂布步骤之后；其中粘合工艺中包括面层胶粘复合步骤和面层压花步骤，所述面层压花步骤设置在面层胶粘复合步骤之后。。
本发明的有益效果是：本发明的技术方案是在常用的墙纸基材上覆盖一层具有抗菌杀毒作用的尼龙共聚薄膜，通过这种方式覆膜，一方面通过PA66/6膜层可以有效提高墙纸的基础力学性能与耐刮擦特性，方便墙纸后期维护保养，延长整体使用寿命，另一方面，常见的病菌传染一般是通过飞沫或者唾液形成的小液滴在空气中流转导致，而尼龙材料本身为极性分子，对空气中悬浮态的液体具有较高的吸引作用，此类携带病毒细菌的液滴很容易就被吸附在墙纸表面，此时，在所述的尼龙共聚薄膜在原料合成阶段即添加的长效抗菌剂就会起到其杀菌消毒的作用，而且由于尼龙薄膜还具有良好的水汽透过率，吸收的小液滴会在环境中转化为气态挥发，重新进入环境中，然后空气中的小液滴会持续不断的吸附到墙纸表面，从而长久的发挥细菌和病毒的清除作用。除此之外，尼龙薄膜还具有良好的水汽透过率，不会影响墙面水汽挥发，杜绝了墙纸内面霉菌产生的可能，因此对保持环境空气洁净具有独特优势。由于上述多项优点，本发明特别适合应用与医院、商场和学校等公共开放式场所和家庭密闭空间的使用，给人们提供一个健康安全的环境，对于目前的新冠肆虐的时代尤其有现实意义。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明涉及一种具有长效抗菌杀毒功能的墙纸，所述具有长效抗菌杀毒功能的墙纸由基层、面层和印花层构成，所述印花层外还复合一层具有长效抗菌杀毒能力的共聚尼龙薄膜。通过这种方式，一方面工具尼龙薄膜具有良好的力学形质，可以很好的保护印花层的油墨图案，另一方面，可以利用其对长效抗菌杀毒能力对吸引空气中携菌液滴中的细菌病毒进行杀灭，对环境持续进行净化。所述具有长效抗菌杀毒能力的共聚尼龙薄膜的共聚尼龙原料粒子中添加有锌离子长效抗菌剂。
在本发明的实施方案中，所述锌离子抗菌剂的添加方法是在共聚尼龙合成过程中首先根据工艺制取相应的单体水溶液，然后根据工艺要求将相应含量的锌离子长效抗菌剂加入所述单体水溶液中溶解并搅拌均匀，最后将所述单体水溶液高温缩聚除水之后经挤出冷却切粒形成原料粒子。由于抗菌剂是加入在单体溶液中，所以经过搅拌溶解在整个聚合体系中的分散状态非常均匀，而且由于抗菌剂溶解，所以锌元素在水溶液中的存在方式为离子态，而当尼龙缩聚时，这种离子态的锌元素自动被聚合的大分子绞缠在一起，无法运动。这种方式处理得到的共聚尼龙粒子的抗菌杀毒功效几乎是恒定的，而且由于锌元素一直保持在离子态，杀毒效果更强，相比通过与抗菌剂共混获得抗菌杀毒能力来收，杀菌剂分布更均衡几乎无缺陷，而且用量更少，效果更好，对材料物理性能的影响更小。
其中锌离子抗菌剂包括氧化锌、己二酸锌胺、乙酸锌或砒啶硫酮锌中的一种或其组合。上述含锌化合物都具有较好的溶解特性，可以比较快速的融入聚酰胺单体的溶液中。锌离子抗菌剂在共聚尼龙原料粒子中的含量以锌元素折算在500~5000PPM之间，其中用在墙纸上时最合适的含量范围为3000~4000PPM。采用上述范围的原因是一方面，显而易见，添加含量越多，抗菌杀毒能力越强，另一方面，添加太多则会影响整体的物理性能，添加量在3000~4000PPM可以兼顾墙纸表面的保护性能和实际灭杀效果最大。
在本发明的实施方案中，所述长效抗菌杀毒共聚尼龙薄膜一般为PA66/6薄膜、PA66/610薄膜或者PA66/612薄膜，厚度为20~50微米。太薄容易刮伤，太厚会影响薄膜的水汽透过率。
在本发明的实施方案中，所述具有长效抗菌杀毒能力的共聚尼龙薄膜能够通过热压、粘合或者是淋膜涂布这三种工艺复复合在墙纸的面层上。
其中，采用热压工艺时可以在热压复合的同时对墙纸表面压花。如果采用淋膜涂布工艺复合的话，可以在淋膜步骤结束后，再对墙纸整体压花。如果采用粘合工艺复合的话，在粘合前需要涂布5~10微米厚度的胶层然后再粘合，粘合以后由烘箱烘干，最后再对墙纸整体压花。
根据上述发明内容，本发明的三个实施例包括：
实施例1
一种具有长效抗菌杀毒功能的墙纸，所述抗菌型墙纸由基纸、PVC面层和印花层构成，所述印花层外通过淋膜机采用淋膜涂布的方式直接复合一层厚度为50微米的PA66/6二元共聚长效抗菌膜，淋膜之后，所述墙纸还通过压花机压出条纹结构。所述PA66/6二元共聚长效抗菌膜的原料为奥升德公司自制的PA66/6长效抗菌杀毒粒子，所述PA66/6长效抗菌杀毒粒子在合成时，加入的锌离子杀菌剂为乙酸锌，以锌元素折算的理论添加量4000PPM为基准添加到单体溶液内,缩聚之后实测留存为3100PPM左右。
实施例2
一种具有长效抗菌杀毒功能的墙纸墙纸，所述抗菌型墙纸由基纸、PVC面层和印花层构成，所述印花层外通过热压机采用热压的方式复合一层厚度为30微米的PA66/610二元共聚长效抗菌膜，热压机热压的同时对表面压花，形成条纹结构。所述PA66/610二元共聚长效抗菌膜由PA66/610长效抗菌杀毒粒子经挤出流延成膜。所述PA66/610长效抗菌杀毒粒子由奥升德公司自制，所述PA66/610长效抗菌杀毒粒子在合成时，加入的锌离子杀菌剂为己二酸锌胺，以锌元素折算的理论添加量为4200PPM为基准添加到单体溶液中,缩聚之后实测最终留存为3600PPM左右。
实施例3
一种具有长效抗菌杀毒功能的墙纸，所述抗菌型墙纸由基纸、PVC面层和印花层构成，所述印花层外还经粘合烘干后复合一层厚度为20微米的PA66/612二元共聚长效抗菌膜，其中粘合层布胶厚度为5~10微米之间，粘合步骤结束之后，通过压花机在墙纸表面压出条纹结构。所述PA66/6112二元共聚长效抗菌膜由PA66/612长效抗菌杀毒粒子经挤出吹膜成型。所述PA66/612长效抗菌杀毒粒子为奥升德公司自制的，所述PA66/612长效抗菌杀毒粒子在缩聚前的单体溶液阶段加入，加入的锌离子杀菌剂为氧化锌，以锌元素折算的理论添加量4500PPM为基准添加到单体溶液中,缩聚之后实测最终留存量为3800PPM左右。
上述实施例1~3所述的抗菌墙纸的生化检测结果见下表：
由上述实施例的检测结果可见，实施例1~3对多种常见治病菌都具有良好的消杀抑制作用，可以有效提高环境的空气质量，减少治病因素，为房间内人员的身体健康提供有效保障。而且由于墙纸表面覆盖的是尼龙膜，由于尼龙本身具有良好的水汽透过率，可以将墙面水分有效排干，防止霉菌在墙纸背面产生。而且由于锌离子在薄膜中的存在方式，该消杀抑制作用长期有效。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (12)
1.一种具有长效抗菌杀毒功能的墙纸，所述具有长效抗菌杀毒功能的墙纸由基层、面层和印花层构成，其特征在于，所述印花层外还复合一层具有长效抗菌杀毒能力的共聚尼龙薄膜，
所述具有长效抗菌杀毒能力的共聚尼龙薄膜的共聚尼龙原料粒子中添加有无机长效抗菌剂，所述无机长效抗菌剂在所述共聚尼龙原料粒子合成的阶段添加。
2.根据权利要求1所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述无机长效抗菌剂的添加方法包括以下内容：首先制取相应单体水溶液，然后根据工艺要求将相应含量的无机长效抗菌剂加入所述单体水溶液中搅拌均匀，最后将所述单体水溶液高温缩聚除水之后经挤出冷却切粒形成原料粒子。
3.根据权利要求1所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述无机长效抗菌剂为锌离子无机抗菌剂。
4.根据权利要求3所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述锌离子抗菌剂包括氧化锌、己二酸锌胺、乙酸锌或砒啶硫酮锌中的一种或其组合。
5.根据权利要求3所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述锌离子无机抗菌剂在共聚尼龙原料粒子中以锌元素计添加量为500~5000PPM。
6.根据权利要求5所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述优选添加量为3000~4000PPM。
7.根据权利要求1所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述原料粒子为PA66/6、PA66/610或者PA66/612中的一种或多种的组合。
8.根据权利要求1所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述长效抗菌杀毒共聚尼龙薄膜的厚度为20~50微米。
9.根据权利要求1所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述具有长效抗菌杀毒能力的共聚尼龙薄膜的复合工艺包括热压、粘合或淋膜涂布工艺。
10.根据权利要求9所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述热压工艺中包括压花步骤和热压复合步骤和压花成型步骤，所述压花成型步骤与热压复合步骤同步进行。
11.根据权利要求9所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述淋膜涂布工艺中还包括淋膜涂布步骤和压花成型步骤，所述压花成型步骤设置在淋膜涂布步骤之后。
12.根据权利要求9所述的具有长效抗菌杀毒功能的墙纸，其特征在于，所述粘合工艺中包括所述粘合工艺中包括面层胶粘复合步骤和面层压花步骤，所述面层压花步骤设置在面层胶粘复合步骤之后。