CN116333429A - 聚合物组合物、聚合物母料组合物以及包含其或由其制备的板材 - Google Patents
聚合物组合物、聚合物母料组合物以及包含其或由其制备的板材 Download PDFInfo
- Publication number
- CN116333429A CN116333429A CN202111604740.2A CN202111604740A CN116333429A CN 116333429 A CN116333429 A CN 116333429A CN 202111604740 A CN202111604740 A CN 202111604740A CN 116333429 A CN116333429 A CN 116333429A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- antioxidant
- polymer
- polymer composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了聚合物组合物、聚合物母料组合物以及包含其或由其制备的板材。该聚合物组合物包含:90重量份至99重量份的聚合物基体;1重量份至10重量份的阻燃剂;0.1重量份至0.5重量份的缚酸剂;0.1重量份至0.5重量份的抗氧剂;以及0.2重量份至5重量份的协效剂,上述重量份均基于100重量份的所述聚合物组合物的总重量。通过应用本发明的聚合物组合物、聚合物母料组合物以及包含其或由其制备的板材,实现了在高温下稳定性能的提高,以及阻燃性和机械性能的平衡。
Description
技术领域
本发明涉及聚合物加工领域,具体而言,涉及一种聚合物组合物、聚合物母料组合物以及包含其或由其制备的板材。
背景技术
聚合物表现出金属或陶瓷通常不具备的一些独特性质,这些性质包括低密度、高韧性和耐冲击性以及光学透明度。但是具备优异特性的聚合物的缺点之一是它们缺少阻燃性。现有技术中,通过向聚合物中加入阻燃剂来实现阻燃性。
为了使聚合物实现阻燃效果,通常使用小分子六溴环十二烷(HBCD)作为阻燃剂添加到聚合物中。然而,在大量应用和实验中发现,HBCD具有一定的生物毒性,其能够在生物体内进行累积,并且是环境不可降解的。因此,为了降低环境污染与生物污染,在聚合物行业中开发了多种新型大分子(聚合型)阻燃剂,例如朗盛化学的Emerald Innovation 3000(简称EI3000)型阻燃剂。聚合型阻燃剂具有较高的分子量,增加了抗迁移、萃取、蒸发性,从而减少了阻燃剂从聚合物中释放到环境中的风险。此外,聚合型阻燃剂具有相对于小分子阻燃剂更高的分子量,因此其不容易被消化道分解和吸收,减少了生物对其的可获得性、以及对生态环境的不利影响。
然而,在使用聚合型阻燃剂的情况下发现,其在190℃的温度下会发生降解,从而会不利地影响其阻燃性能。此外,由于在聚合型阻燃剂的降解过程中会产生酸性物质,聚合物产品的力学性能也将会受其影响。因此,仍需开发具有高温下稳定性且能够平衡聚合物产品的阻燃性能和机械性能的聚合物组合物。
发明内容
本发明的主要目的在于提供一种聚合物组合物、聚合物母料组合物以及包含其或由其制备的板材,以解决现有技术中的聚合物组合物在高温下不稳定的问题。
为了实现上述目的,根据本发明的一个方面,提供了一种聚合物组合物,包含:聚合物基体,90重量份至99重量份;阻燃剂,1重量份至10重量份;缚酸剂,0.1重量份至0.5重量份;抗氧剂,0.1重量份至0.5重量份;以及协效剂,0.2重量份至5重量份,上述重量份均基于100重量份的聚合物组合物的总重量。
进一步地,在上述聚合物组合物中,缚酸剂包括氧化锡类缚酸剂、水滑石类缚酸剂或它们的组合。
进一步地,在上述聚合物组合物中,抗氧剂包括主抗氧剂和辅抗氧剂,并且其中主抗氧剂包含受阻酚类抗氧剂、胺类抗氧剂、硫醚类抗氧剂、三嗪类抗氧剂、或它们两种以上的任意组合,辅抗氧剂包含亚磷酸酯类抗氧剂、三嗪类抗氧剂、或它们的组合。
进一步地,在上述聚合物组合物中,协效剂包含锌化合物、膨胀石墨、联枯(即,2,3-二甲基-2,3-二苯基丁烷)、或它们两种以上的任意组合。
进一步地,在上述聚合物组合物中,阻燃剂为溴化丁二烯-苯乙烯嵌段共聚物,并且其中溴化丁二烯-苯乙烯嵌段共聚物包含溴化1,2-丁二烯嵌段、溴化1,4-丁二烯嵌段、或它们的组合;基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中的溴化丁二烯嵌段,溴化1,2-丁二烯嵌段的量在50重量份至90重量份的范围内,并且溴化1,4-丁二烯嵌段的量在10重量份至50重量份的范围内。
进一步地,在上述聚合物组合物中,阻燃剂与协效剂的重量比例在1:1至10:1的范围内。
进一步地,在上述聚合物组合物中,缚酸剂与抗氧剂的重量比在0.5:1至5:1的范围内。
根据本发明的另一个方面,提供了一种聚合物母料组合物,其特征在于,包含:第一母料,基于100重量份的第一母料的总重量包含5重量份至20重量份的协效剂,和80重量份至95重量份的聚合物基体;第二母料,基于100重量份的第二母料的总重量包含40重量份至60重量份的阻燃剂,2重量份至5重量份的缚酸剂,2重量份至3.75重量份的抗氧剂,和30重量份至60重量份的聚合物基体,第一母料与第二母料的重量比在1:2至1:4的范围内。
根据本发明的另一个方面,提供了一种包含前文描述的聚合物组合物的板材。
根据本发明的另一个方面,提供了一种由前文描述的聚合物组合物或前文描述的聚合物母料组合物制备的板材。
通过应用本发明的聚合物组合物、聚合物母料组合物以及包含其或由其制备的板材,实现了在高温下稳定性能的提高,以及阻燃性和机械性能的平衡。
具体实施方式
需要说明的是,在不冲突的情况下,本申请中的实施例及各个实施例中的特征可以相互组合。下面将结合实施例来详细说明本发明。以下的实施例仅为示例性的,并不构成对于本发明保护范围的限制。
如背景技术中所说明的,现有技术中的聚合物组合物具有高温下不稳定、易分解且对成品聚合物产品产生不利影响。针对现有技术中的问题,本发明的一个典型实施方式提供了一种聚合物组合物,包含:90重量份至99重量份的聚合物基体;1重量份至10重量份的阻燃剂;0.1重量份至0.5重量份的缚酸剂;0.1重量份至0.5重量份的抗氧剂;以及0.2重量份至5重量份的协效剂,上述重量份均基于100重量份的聚合物组合物的总重量。
在本发明的发明人进行大量实验之后惊奇地发现,在将1重量份至10重量份的阻燃剂与0.2重量份至5重量份的协效剂同时加入到聚合物组合物中时,可以有效地提高聚合物体系的氧指数。发明人发现,在将阻燃剂与协效剂以上述重量份添加到聚合物体系中时,协效剂可以有效地与阻燃剂在高温下分解形成的物质发生反应,例如在使用含卤素化合物作为阻燃剂时,协效剂将与高温下生成的卤化氢或活性卤素元素反应,从而减少易挥发的可燃气体的产生,并且产生能够隔绝热量并起到屏蔽作用的碳化物,保护了聚合物体系的进一步受热分解。在通过ASTM D 2863-97进行极限氧指数(LOI指数)测试之后发现,在使用本申请的聚合物组合物情况下,与不使用任何阻燃剂和协效剂的聚合物体系相比,LOI指数升高了至少5%。
在现有技术中,一些阻燃剂虽然可以有效地使成品聚合物具有所期望的阻燃性,但是仅包含阻燃剂的聚合物体系通常表现出不尽如人意的机械性能和导热性能,例如热导率和压缩性能的下降。然而,在使用本发明的聚合物组合物的情况下,可以使得聚合物成品的阻燃性能和机械性能得到有效的平衡,在提高成品阻燃性的情况下,仍然能够保持成品具有良好的导热率和压缩性能。
在本发明的一些实施方式中,缚酸剂包含氧化锡类缚酸剂、水滑石类缚酸剂或它们的组合。在本发明的实施方式中,选择前文描述的特征的缚酸剂,用以有效实现中和聚合物体系中酸性物质(溴化氢)的效果,从而抑制溴化丁二烯-苯乙烯嵌段共聚物的自催化分解作用。在上述缚酸剂中,优选的缚酸剂为水滑石类缚酸剂。优选地,本发明中所使用的缚酸剂包含单丁基氧化锡、二丁基氧化锡、三丁基氧化锡、二戊基氧化锡、二辛基氧化锡、Al2O3·6MgO·CO2·12H2O、Mg4.5Al2(OH)13·CO3·3.5H2O、4MgO·Al2O3·CO2·9H2O、4MgO·Al2O3·CO2·6H2O、ZnO·3MgO·Al2O3·CO2·8H2O、ZnO·3MgO·Al2O3·CO2·5H2O、Mg4.5Al2(OH)13·CO3、Mg4.5Al2(OH)13·CO3·3H2O、Mg4.5Al2(OH)13·O0.2·(CO3)0.8以及它们的任意组合。在本发明的具体实施例中可以使用的缚酸剂包括但不限于:商购自西格玛奥德里奇(上海)的货号为652288的合成水滑石;商购自麦克林(上海)的货号为H875432的合成水滑石;商购自南通艾德旺的货号为HT-33PL、HT-33PL、HT-22、HT-37的铝镁水滑石和铝镁无水水滑石;商购自克莱恩化工的货号为KLE713的水和铝碳酸镁商购自南通艾德旺的货号为MBTO的单丁基氧化锡;商购自南通艾德旺的货号为DBTO的二丁基氧化锡;商购自北京百灵威的三丁基氧化锡,CAS:56-35-9;商购自Achemica(瑞士)的二戊基氧化锡,CAS:2273-46-3;以及商购自南通艾德旺的货号为DOTO的二辛基氧化锡。
在本发明的一些实施方式中,抗氧剂包括主抗氧剂和辅抗氧剂,并且其中主抗氧剂包含受阻酚类抗氧剂、胺类抗氧剂、硫醚类抗氧剂、三嗪类抗氧剂、或它们两种以上的任意组合,辅抗氧剂包含亚磷酸酯类抗氧剂、三嗪类抗氧剂、或它们的组合。在一些实施方式中,本发明的阻燃剂组合物可以仅包含单一种类的抗氧剂,例如受阻酚类抗氧剂、胺类抗氧剂、亚磷酸酯类抗氧剂、硫醚类抗氧剂、或三嗪类抗氧剂。在优选的实施方式中,本发明的阻燃剂组合物仅包含三嗪类抗氧剂。在另一些实施方式中,本发明的阻燃剂组合物包含主抗氧剂和辅抗氧剂的组合。在使用两种以上抗氧剂的情况下,优选使用受阻酚类抗氧剂作为主抗氧剂,使用亚磷酸酯类抗氧剂作为辅抗氧剂的组合。
在本发明的一些特定实施方式中,主抗氧剂包含四[β-(3.5-二叔丁基,4-羟基苯基)丙酸]季戊四酯醇、四(3,5-二叔丁基-4-羟基)苯丙酸季戊四醇酯、2,6-二叔丁基对甲苯酚、4-羟甲基-2,6-二叔丁基苯酚、2,6-二叔丁基-α-二甲氨基苯酚、N-环己基-N’-苯基对苯二胺、N,N’-二苯基对苯二胺、硫代二丙酸二月桂酸酯、2,4-二(十二烷基硫甲基)-6-甲基苯酚、6-(4-羟基-3,5-二叔丁基苯胺基)-2,4-双(辛基硫基)-1,3,5-三嗪、2-正辛基硫代-4,6-双(4’-羟基-3,5-二叔丁基苯氧基)-1,3,5-三嗪、或它们两种以上的任意组合。
在本发明的一些特定实施方式中,辅抗氧剂包含亚磷酸三(2,4-二叔丁基苯基)酯、二(2,4-二-丁基苯)季戊四醇二磷酸酯、亚磷酸双酚A酯、亚磷酸三丁酯、6-(4-羟基-3,5-二叔丁基苯胺基)-2,4-双(辛基硫基)-1,3,5-三嗪、2-正辛基硫代-4,6-双(4’-羟基-3,5-二叔丁基苯氧基)-1,3,5-三嗪、或它们两种以上的任意组合。
在本发明的一些特定实施方式中,本申请的聚合物组合物中的协效剂包含锌化合物、膨胀石墨、联枯(即,2,3-二甲基-2,3-二苯基丁烷)、或它们两种以上的任意组合。在进一步优选的实施方式中,协效剂包含膨胀石墨、锡酸锌、硼酸锌、氧化锌、联枯(即,2,3-二甲基-2,3-二苯基丁烷)、或它们两种以上的任意组合。在使用上述协效剂的情况下,能够与阻燃剂发生协效作用,从而有效提高聚合物组合物的氧指数。
在本发明的一些实施方式中,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物,溴化丁二烯-苯乙烯嵌段共聚物包含10至40重量份的苯乙烯嵌段以及60至90重量份的溴化丁二烯嵌段。在优选实施方式中,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物,溴化丁二烯-苯乙烯嵌段共聚物包含15重量份至35重量份的苯乙烯嵌段以及65重量份至85重量份的溴化丁二烯嵌段。具体地,在本发明的一些实施例中,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物,苯乙烯嵌段的最小值应大于10重量份、11重量份、12重量份、13重量份、14重量份、15重量份、16重量份、17重量份、18重量份、19重量份或20重量份,并且其最大值应小于40重量份、39重量份、38重量份、37重量份、36重量份、35重量份、34重量份、33重量份、32重量份、31重量份或30重量份。并且在一些实施例中,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物,溴化丁二烯嵌段的最小值应大于60重量份、61重量份、62重量份、63重量份、64重量份、65重量份、66重量份、67重量份、68重量份、69重量份、70重量份、71重量份、72重量份、73重量份、74重量份或75重量份,并且其最大值应小于90重量份、89重量份、88重量份、87重量份、86重量份、85重量份、84重量份、83重量份、82重量份、81重量份、80重量份、79重量份、78重量份、77重量份或76重量份。
具体而言,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物,苯乙烯嵌段的量可以在以下范围内:10重量份至40重量份、11重量份至39重量份、12重量份至38重量份、13重量份至37重量份、14重量份至36重量份、15重量份至35重量份、16重量份至34重量份、17重量份至33重量份、18重量份至32重量份、19重量份至31重量份、20重量份至30重量份、10重量份至20重量份、10重量份至30重量份、20重量份至40重量份或30重量份至40重量份。并且基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物,溴化丁二烯嵌段的量可以在以下范围内:60重量份至90重量份、61重量份至89重量份、62重量份至88重量份、63重量份至87重量份、64重量份至86重量份、65重量份至85重量份、66重量份至84重量份、67重量份至83重量份、68重量份至82重量份、69重量份至81重量份、70重量份至80重量份、70重量份至90重量份、80重量份至90重量份、60重量份至80重量份或60重量份至70重量份。
在本发明的一些实施方式中,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中的溴化丁二烯嵌段,溴化1,2-丁二烯嵌段的量在50重量份至90重量份的范围内,并且溴化1,4-丁二烯嵌段的量在10重量份至50重量份的范围内。
在本发明的一些实施方式中,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中的溴化丁二烯嵌段,溴化1,2-丁二烯嵌段的量在60重量份至85重量份的范围内,并且溴化1,4-丁二烯嵌段的量在15重量份至40重量份的范围内。在本发明的一些实施方式中,如前文的描述,溴化丁二烯-苯乙烯嵌段共聚物可以同时包含溴化1,2-丁二烯嵌段和溴化1,4-丁二烯嵌段,例如苯乙烯-溴化1,2-丁二烯-溴化1,4-丁二烯三元嵌段共聚物、苯乙烯-溴化1,2-丁二烯-溴化1,4-丁二烯-苯乙烯四元嵌段共聚物。在一些实施例中,在同时包含溴化1,2-丁二烯嵌段和溴化1,4-丁二烯嵌段的情况下,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中的溴化丁二烯嵌段,溴化1,2-丁二烯嵌段的最小值应大于60重量份、大于61重量份、大于62重量份、大于63重量份、大于64重量份、大于65重量份、大于66重量份、大于67重量份、大于68重量份、大于69重量份或大于70重量份,并且其最大值应小于85重量份、小于84重量份、小于83重量份、小于82重量份、小于81重量份、小于80重量份、小于79重量份、小于78重量份、小于77重量份、小于76重量份或小于75重量份。并且在一些实施例中,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中溴化丁二烯嵌段,溴化1,4-丁二烯嵌段的最小值应大于15重量份、大于16重量份、大于17重量份、大于18重量份、大于19重量份、大于20重量份、大于21重量份、大于22重量份、大于23重量份、大于24重量份或大于25重量份,并且其最大值应小于40重量份、小于39重量份、小于38重量份、小于37重量份、小于36重量份、小于35重量份、小于34重量份、小于33重量份、小于32重量份、小于31重量份或小于30重量份。
具体而言,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中的溴化丁二烯嵌段,溴化1,2-丁二烯嵌段的量在以下范围内:60重量份至85重量份的范围内、61重量份至84重量份的范围内、62重量份至83重量份的范围内、63重量份至82重量份的范围内、64重量份至81重量份的范围内、65重量份至80重量份的范围内、66重量份至79重量份的范围内、67重量份至78重量份的范围内、68重量份至77重量份的范围内、69重量份至76重量份的范围内、70重量份至75重量份的范围内、60重量份至80重量份的范围内、60重量份至75重量份的范围内、60重量份至70重量份的范围内、60重量份至65重量份的范围内、65重量份至85重量份的范围内、70重量份至85重量份的范围内、75重量份至85重量份的范围内或80重量份至85重量份的范围内。并且基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中的溴化丁二烯嵌段,溴化1,4-丁二烯嵌段的量在以下范围内:15重量份至40重量份的范围内、16重量份至39重量份的范围内、17重量份至38重量份的范围内、18重量份至37重量份的范围内、19重量份至36重量份的范围内、20重量份至35重量份的范围内、21重量份至34重量份的范围内、22重量份至33重量份的范围内、23重量份至32重量份的范围内、24重量份至31重量份的范围内、25重量份至30重量份的范围内、20重量份至40重量份的范围内、25重量份至40重量份的范围内、30重量份至40重量份的范围内、35重量份至40重量份的范围内、15重量份至35重量份的范围内、15重量份至30重量份的范围内、15重量份至25重量份的范围内或15重量份至20重量份的范围内。
在本发明的一些实施方式中,溴化丁二烯-苯乙烯嵌段共聚物具有使用双酚A均聚碳酸酯标准品通过凝胶渗透色谱(GPC)测量的100,000到160,000克/摩尔的重均分子量。优选地,溴化丁二烯-苯乙烯嵌段共聚物具有120,000至150,000克/摩尔的重均分子量。在本发明的一些实施例中,不考虑具体结构,溴化丁二烯-苯乙烯嵌段共聚物的重均分子量可以大于或等于100,000克/摩尔大于或等于110,000克/摩尔、大于或等于120,000克/摩尔、大于或等于130,000克/摩尔、大于或等于140,000克/摩尔或大于或等于150,000克/摩尔并且小于或等于160,000克/摩尔、小于或等于150,000克/摩尔、小于或等于140,000克/摩尔、小于或等于130,000克/摩尔或小于或等于120,000克/摩尔。在本发明的一些实施方式中,也可以根据ASTM D5296-11,使用聚苯乙烯标准品,通过凝胶渗透色谱法(GPC)确定分子量。在一些实施方式中,可以在220℃使用1-氯萘作为溶剂,使用高温GPC法,例如根据ASTMD6474-11进行测定。
在本发明的一些实施方式中,本发明的聚合物组合物中,阻燃剂与协效剂的重量比例在1:1至10:1的范围内。在优选实施方式中,阻燃剂与协效剂的重量比例在3:1至7:1的范围内。当阻燃剂与协效剂的重量比例小于1:1时,由于阻燃剂含量过少,从而不能有效地实现阻燃效果。当阻燃剂与协效剂的重量比例大于10:1,阻燃剂含量过多,使得协效剂不足以与阻燃剂发生协效作用,从而难以实现氧指数升高的效果。
具体地,在本发明的一些具体实施例中,阻燃剂与协效剂的重量比例在以下范围内:1:1至10:1的范围内、2:1至10:1的范围内、3:1至10:1的范围内、1:1至9:1的范围内、1:1至8:1的范围内、1:1至7:1的范围内、2:1至9:1的范围内、2:1至8:1的范围内、2:1至7:1的范围内、3:1至9:1的范围内、3:1至8:1的范围内或3:1至7:1的范围内。
在本发明的一些实施方式中,缚酸剂与抗氧剂的重量比在0.5:1至5:1的范围内,优选地,缚酸剂与抗氧剂的重量比在1:1至2:1的范围内。在本发明中,由于缚酸剂和抗氧剂具有协同作用,能够同时对阻燃剂进行热稳定,因此,缚酸剂与抗氧剂的重量比需要在0.5:1至5:1的范围内以实现共同促进阻燃剂在高温(300℃以上)处理中热稳定的效果。在具体实施例中,缚酸剂与抗氧剂的重量比可以在以下范围内:1:1.5至4.5:1、1:1.4至4:1、1:1.3至3.5:1、1:1.2至3:1、1:1.1至2.5:1或1:1至2:1。
在本发明的一些实施方式中,阻燃剂组合物中的缚酸剂和抗氧剂的总量与溴化丁二烯-苯乙烯嵌段共聚物的量的重量比率在1:20至1:3的范围内。优选地,缚酸剂和抗氧剂的总量与溴化丁二烯-苯乙烯嵌段共聚物的量的重量比率在1:12至1:5的范围内。更优选地,缚酸剂和抗氧剂的总量与溴化丁二烯-苯乙烯嵌段共聚物的量的重量比率在1:8至1:10的范围内。
在本发明中,缚酸剂与抗氧剂作为稳定阻燃剂的添加剂,当缚酸剂和抗氧剂的总量与溴化丁二烯-苯乙烯嵌段共聚物的量的重量比率小于1:20时,由于添加量过少,因此不能有效地起到稳定阻燃剂的效果,使得阻燃剂在高温加工过程中,不能有效地保持阻燃特性。
当缚酸剂和抗氧剂的总量与溴化丁二烯-苯乙烯嵌段共聚物的量的重量比率大于1:3时,缚酸剂和抗氧剂的总量过多,将对聚合物体系的力学性能产生不利影响。
具体地,在本发明的一些具体实施例中,阻燃剂组合物中的缚酸剂和抗氧剂的总量与溴化丁二烯-苯乙烯嵌段共聚物的量的重量比率在以下范围内:1:20至1:3的范围内、1:18至1:3.5的范围内、1:16至1:4的范围内、1:14至1:4.5的范围内、1:12至1:5的范围内、1:10至1:5.5的范围内、1:8至1:6的范围内、1:8至1:10的范围内、1:6至1:6.5的范围内、1:4至1:7的范围内、1:2至1:7.5的范围内或1:1至1:8的范围内。
在本发明的一些实施方式中,主抗氧剂与辅抗氧剂的重量比在1:0.5至1:5的范围内;优选地,主抗氧剂与辅抗氧剂的重量比在1:1至1:2的范围内。具体地,在本发明的一些具体实施例中,主抗氧剂与辅抗氧剂的重量比在以下范围内:1:0.75至1:4.5的范围内、1:1至1:4的范围内、1:1.25至1:3.5的范围内、1:1.5至1:3的范围内、1:1.75至1:2.5的范围内、1:1至1:2的范围内、1:1至1:3的范围内或1:1至1:5的范围内。
在本发明的一些实施方式中,本发明的聚合物组合物中聚合物基体没有特别的限制,只要是已知的热塑性材料均可以被采用。在优选实施方式中,聚合物基体包含聚苯乙烯、聚醚酰亚胺、丙烯酸、氟碳化合物、聚酰胺、聚乙烯、聚酯、聚丙烯、聚碳酸酯、聚氨酯、聚醚醚酮、聚苯硫醚和聚醚酮酮、或它们两种以上的混合物或共聚物。
在本发明的具体实施方式中,基于100重量份的聚合物组合物的总重量,聚合物基体的量在90重量份至99重量份的范围内。在优选实施方式中,基于100重量份的聚合物组合物的总重量,聚合物基体的量可以在以下范围内:90.5重量份至98.5重量份的范围内、91重量份至98重量份的范围内、91.5重量份至97.5重量份的范围内、92重量份至97重量份的范围内、92.5重量份至96.5重量份的范围内、93重量份至96重量份的范围内、93.5重量份至95.5重量份的范围内、94重量份至95重量份的范围内、97重量份至98重量份的范围内、95重量份至96重量份的范围内或91重量份至92重量份的范围内。
基于100重量份的聚合物组合物的总重量,阻燃剂的量在1重量份至10重量份的范围内。在优选实施方式中,基于100重量份的聚合物组合物的总重量,阻燃剂的量可以在以下范围内:1重量份至10重量份的范围内、2重量份至9重量份的范围内、3重量份至8重量份的范围内、4重量份至6重量份的范围内、1重量份至9重量份的范围内、1重量份至8重量份的范围内、1重量份至7重量份的范围内、1重量份至6重量份的范围内、1重量份至5重量份的范围内、2重量份至10重量份的范围内、3重量份至10重量份的范围内、4重量份至10重量份的范围内、5重量份至10重量份的范围内、2重量份至6重量份的范围内、2重量份至4重量份的范围内、3重量份至5重量份的范围内、4重量份至6重量份的范围内或5重量份至7重量份的范围内。
基于100重量份的聚合物组合物的总重量,缚酸剂的量在0.1重量份至0.5重量份的范围内。在优选实施方式中,基于100重量份的聚合物组合物的总重量,缚酸剂的量可以在以下范围内:0.1重量份至0.5重量份的范围内、0.15重量份至0.45重量份的范围内、0.2重量份至0.4重量份的范围内、0.25重量份至0.35重量份的范围内、0.1重量份至0.2重量份的范围内、0.1重量份至0.15重量份的范围内、0.15重量份至0.2重量份的范围内、0.2重量份至0.28重量份的范围内、0.3重量份至0.35重量份的范围内或0.35重量份至0.4重量份的范围内。
基于100重量份的聚合物组合物的总重量,抗氧剂的量在0.1重量份至0.5重量份的范围内。在优选实施方式中,基于100重量份的聚合物组合物的总重量,抗氧剂的量可以在以下范围内:0.1重量份至0.5重量份的范围内、0.15重量份至0.45重量份的范围内、0.2重量份至0.4重量份的范围内、0.25重量份至0.35重量份的范围内、0.1重量份至0.2重量份的范围内、0.1重量份至0.15重量份的范围内、0.15重量份至0.2重量份的范围内、0.2重量份至0.28重量份的范围内、0.3重量份至0.35重量份的范围内或0.35重量份至0.4重量份的范围内。
在抗氧剂包含主抗氧剂和辅抗氧剂的实施方式中,基于100重量份的聚合物组合物的总重量,主抗氧剂和辅抗氧剂的量可以分别在0.05重量份至0.20重量份的范围内。在优选实施方式中,基于100重量份的聚合物组合物的总重量,主抗氧剂和辅抗氧剂的量可以分别在以下范围内:0.05重量份至0.20重量份的范围内、0.06重量份至0.19重量份的范围内、0.07重量份至0.18重量份的范围内、0.08重量份至0.17重量份的范围内、0.09重量份至0.16重量份的范围内、0.1重量份至0.15重量份的范围内、0.11重量份至0.14重量份的范围内、0.12重量份至0.13重量份的范围内、0.05重量份至0.07重量份的范围内、0.08重量份至0.1重量份的范围内、0.1重量份至0.13重量份的范围内、0.15重量份至0.17重量份的范围内或0.18重量份至0.20重量份的范围内。
基于100重量份的聚合物组合物的总重量,协效剂的量在0.2重量份至5重量份,的范围内。在优选实施方式中,基于100重量份的聚合物组合物的总重量,协效剂的量可以在以下范围内:0.2重量份至5重量份的范围内、0.25重量份至4.5重量份的范围内、0.3重量份至4重量份的范围内、0.35重量份至3.5重量份的范围内、0.4重量份至3重量份的范围内、0.45重量份至2.5重量份的范围内、0.5重量份至2重量份的范围内、0.5重量份至1.5重量份的范围内、0.75重量份至1.25重量份的范围内、0.4重量份至0.7重量份的范围内、0.8重量份至1重量份的范围内、1重量份至1.2重量份的范围内、1.2重量份至1.4重量份的范围内或1.3重量份至1.6重量份的范围内。
在本发明的优选实施例中,基于100重量份的本发明的聚合物组合物的总重量,本发明的聚合物组合物包括以下物质或由以下物质组成:91.5重量份至97.5重量份的聚合物基体,2重量份至6重量份的阻燃剂,0.2重量份至0.3重量份的缚酸剂,0.2重量份至0.3重量份的抗氧剂,以及0.5重量份至1.5重量份的协效剂。
在抗氧剂包含主抗氧剂和辅抗氧剂的实施方式中,基于100重量份的本发明的聚合物组合物的总重量,本发明的聚合物组合物包括以下物质或由以下物质组成:90重量份至99重量份的聚合物基体,1重量份至10重量份的阻燃剂,0.1重量份至0.5重量份的缚酸剂,0.05重量份至0.20重量份的主抗氧剂,0.05重量份至0.20重量份的辅抗氧剂,以及0.2重量份至5重量份的协效剂。
在优选实施例中,基于100重量份的本发明的聚合物组合物的总重量,本发明的聚合物组合物包括以下物质或由以下物质组成:91.5重量份至97.5重量份的聚合物基体,2重量份至6重量份的阻燃剂,0.2重量份至0.3重量份的缚酸剂,0.1重量份至0.15重量份的主抗氧剂,0.1重量份至0.15重量份的辅抗氧剂,以及0.5重量份至1.5重量份的协效剂。
在本申请的另一些实施方式中,本发明的聚合物组合物进一步包含0.02重量份至0.1重量份的发泡剂。在本发明的具体实施方式中,基于100重量份的聚合物组合物的总重量,发泡剂的量可以在以下范围内:0.02重量份至0.1重量份的范围内、0.03重量份至0.09重量份的范围内、0.04重量份至0.08重量份的范围内或0.05重量份至0.07重量份的范围内。
在本申请的另一些实施方式中,本发明的聚合物组合物进一步包含的0.001重量份至0.03重量份成核剂。在本发明的具体实施方式中,基于100重量份的聚合物组合物的总重量,成核剂的量可以在以下范围内:0.001重量份至0.03重量份的范围内、0.003重量份至0.025重量份的范围内、0.005重量份至0.02重量份的范围内、0.008重量份至0.015重量份的范围内或0.01重量份至0.02重量份的范围内。
在本发明的另一个典型的实施方式中,提供了一种聚合物母料组合物,其包含第一母料和第二母料。在第一母料中,基于100重量份的第一母料的总重量包含5重量份至20重量份的协效剂,和80重量份至95重量份的聚合物基体;并且在第二母料中,基于100重量份的第二母料的总重量包含40重量份至60重量份的阻燃剂,2重量份至5重量份的缚酸剂,2重量份至3.75重量份的抗氧剂,和30重量份至60重量份的聚合物基体,第一母料与第二母料的重量比在1:2至1:4的范围内。在使用上述聚合物母料组合物的情况下,能够有效提高聚合物的极限氧指数并且使得聚合物成品的阻燃性能和机械性能得到有效的平衡。在本实施方式中使用的协效剂、聚合物基体、阻燃剂、缚酸剂以及抗氧剂均可以选自前文描述的这些材料,此处将不进行重复描述。在一个具体实施方式中,第一母料与第二母料为共混物。在另一个实施方式中,第一母料与第二母料为彼此独立的且未共混在一起。
在本发明的一些实施方式中,本发明的聚合物组合物中,阻燃剂与协效剂的重量比例在1:1至10:1的范围内。在优选实施方式中,阻燃剂与协效剂的重量比例在3:1至7:1的范围内。当阻燃剂与协效剂的重量比例小于1:1时,由于阻燃剂含量过少,从而不能有效地实现阻燃效果。当阻燃剂与协效剂的重量比例大于10:1,阻燃剂含量过多,使得协效剂不足以与阻燃剂发生协效作用,从而难以实现氧指数升高的效果。
具体地,在本发明的一些具体实施例中,阻燃剂与协效剂的重量比例在以下范围内:1:1至10:1的范围内、2:1至10:1的范围内、3:1至10:1的范围内、1:1至9:1的范围内、1:1至8:1的范围内、1:1至7:1的范围内、2:1至9:1的范围内、2:1至8:1的范围内、2:1至7:1的范围内、3:1至9:1的范围内、3:1至8:1的范围内或3:1至7:1的范围内。
在本发明的一些实施方式中,缚酸剂与抗氧剂的重量比在0.5:1至5:1的范围内,优选地,缚酸剂与抗氧剂的重量比在1:1至2:1的范围内。在本发明中,由于缚酸剂和抗氧剂具有协同作用,能够同时对阻燃剂进行热稳定,因此,缚酸剂与抗氧剂的重量比需要在0.5:1至5:1的范围内,以实现共同促进阻燃剂在高温(300℃以上)处理中热稳定的效果。在具体实施例中,缚酸剂与抗氧剂的重量比可以在以下范围内:1:1.5至4.5:1、1:1.4至4:1、1:1.3至3.5:1、1:1.2至3:1、1:1.1至2.5:1或1:1至2:1。
在本发明的一些实施方式中,抗氧剂包括主抗氧剂和辅抗氧剂。主抗氧剂与辅抗氧剂的重量比在1:0.5至1:5的范围内;优选地,主抗氧剂与辅抗氧剂的重量比在1:1至1:2的范围内。具体地,在本发明的一些具体实施例中,主抗氧剂与辅抗氧剂的重量比在以下范围内:1:0.75至1:4.5的范围内、1:1至1:4的范围内、1:1.25至1:3.5的范围内、1:1.5至1:3的范围内、1:1.75至1:2.5的范围内、1:1至1:2的范围内、1:1至1:3的范围内或1:1至1:5的范围内。
在本发明的一些实施方式中,本发明的聚合物组合物中聚合物基体没有特别的限制,只要是已知的热塑性材料均可以被采用。在优选实施方式中,聚合物基体包含聚苯乙烯、聚醚酰亚胺、丙烯酸、氟碳化合物、聚酰胺、聚乙烯、聚酯、聚丙烯、聚碳酸酯、聚氨酯、聚醚醚酮、聚苯硫醚和聚醚酮酮、或它们两种以上的混合物或共聚物。
在本发明的另一个典型的实施方式中,提供了一种包含本发明的聚合物组合物的板材。由于包含前文描述的本发明的聚合物组合物,因此包含其的板材将具有期望的阻燃性、高极限氧指数以及优异的阻燃性和机械性的平衡。
在本发明的另一个典型的实施方式中,提供了一种由本发明的聚合物组合物或本发明的聚合物母料组合物制备的板材。通过使用本发明的聚合物组合物或本发明的聚合物母料组合物,所制备的板材包含的有效量的阻燃剂、缚酸剂、抗氧剂和协效剂。因此,通过使用本发明的聚合物组合物或本发明的聚合物母料组合物制备的板材具有优异的阻燃性和机械性能。
实施例
以下结合具体实施例对本申请作进一步详细描述,这些实施例不能理解为限制本申请所要求保护的范围。
在以下表1中列出了在以下各实施例中所使用的各组分以及这些组分的简要描述及来源。
表1各实施例中所使用的各组分以及这些组分的简要描述及来源
聚合物发泡材料的制备
采用两阶段挤出法,使用汉塑公司的85200型挤出机组合(其包括一个双螺杆挤出机和一个单螺杆挤出机),按照下表2中所示的含量分别将各个组分通过不同的喂料器加入到双螺杆挤出机中。在挤出机组合的第一段(双螺杆挤出机)中,其中双螺杆挤出机的螺纹直径为85mm,并且其加热段温度为190℃至220℃。在通过双螺杆挤出机后,将获得的混合物导入挤出机组合的第二段(单螺杆挤出机),其中单螺杆挤出机的螺纹直径为200mm,将13.5kg发泡剂(二氧化碳和酒精)(商购自上海比阳)一起导入单螺杆挤出机中,并且在70℃-120℃的温度下穿过单口干挤出机,通过模具和成型设备得到发泡板材。
以下实施例1-18以及比较例1-2中的数据单位均为kg/h,挤出机组合的总产量为300kg/h。
表2实施例1-18和比较例1-2的聚合物发泡材料的组成及其含量
注:化合物1:为苯乙烯-溴化丁二烯二元嵌段共聚物,具有10重量份至30重量份的苯乙烯嵌段,10,000至13,000克/摩尔的重均分子量,50重量份至60重量份的1,2-丁二烯嵌段以及40重量份至50重量份的1,4-丁二烯嵌段;
化合物2:为苯乙烯-溴化丁二烯-苯乙烯三元嵌段共聚物,具有25重量份至40重量份的苯乙烯嵌段,14,000至16,000克/摩尔的重均分子量,50重量份至90重量份的1,2-丁二烯嵌段以及10重量份至50重量份的1,4-丁二烯嵌段。
上述化合物1和化合物2均商购自德国朗盛集团。
发泡材料的性能测试
通过以下表3的测试条件分别测试通过实施例1-18及比较例1-2制备的发泡材料:
表3对各实施例进行的测试项目及其测试标准
测试项目 | 测试条件 |
极限氧指数 | 根据ASTM D 2863-97测试标准 |
水平燃烧测试 | 根据ISO 9772:2001测试标准 |
燃烧性能等级 | 根据GB 8624-2012测试标准 |
材料密度 | 通过密度测定仪测试材料密度 |
导热率 | 根据GB/T 10295-2008测试标准 |
压缩强度 | 根据GB/T 8813-2008测试标准 |
通过以下表4示出了测试结果。
表4对各实施例进行测试的测试结果
通过以上实验结果可以看出,本发明的聚合物可以实现有效的LOI的增加,纯PS(比较例1)的LOI为19.7%,本发明的实施例1-18均实现了LOI的有效增长。在仅使用阻燃剂而不是用协效剂的比较例2中,LOI的增长率较低,因此不能达到预期的阻燃效果。通过水平燃烧测试的结果可以看出,本发明的聚合物组合物均能够达到HF1的水平燃烧等级。
此外,通过以上的材料密度、导热率和压缩强度的测试实验结果表明,在使用本发明的聚合物组合物制备发泡板材的情况下,可以使得聚合物发泡材料的阻燃性能和机械性能得到有效的平衡,在提高成品阻燃性的情况下,仍然能够保持成品具有良好的导热率和压缩性能。通过密度测定仪测试的材料密度结果表明,实施例1-18的发泡材料的密度、导热率与压缩强度均与比较例1(纯PS发泡材料)的结果接近。由本发明的聚合物组合物制备的发泡材料在机械性能方面与纯PS发泡材料近似,从而表明本申请的聚合物组合物能够在有效提高阻燃效果的同时实现了与机械性能的平衡。
其他具体实施例
具体实施例1.一种聚合物组合物,包含:
聚合物基体,90重量份至99重量份;
阻燃剂,1重量份至10重量份;
缚酸剂,0.1重量份至0.5重量份;
抗氧剂,0.1重量份至0.5重量份;以及
协效剂,0.2重量份至5重量份,
上述重量份均基于100重量份的聚合物组合物的总重量。
具体实施例2.根据具体实施例1的聚合物组合物,缚酸剂包括氧化锡类缚酸剂、水滑石类缚酸剂或它们的组合。
具体实施例3.根据具体实施例1的聚合物组合物,所述缚酸剂包含单丁基氧化锡、二丁基氧化锡、三丁基氧化锡、二戊基氧化锡、二辛基氧化锡、Al2O3·6MgO·CO2·12H2O、Mg4.5Al2(OH)13·CO3·3.5H2O、4MgO·Al2O3·CO2·9H2O、4MgO·Al2O3·CO2·6H2O、ZnO·3MgO·Al2O3·CO2·8H2O、ZnO·3MgO·Al2O3·CO2·5H2O、Mg4.5Al2(OH)13·CO3、Mg4.5Al2(OH)13·CO3·3H2O、Mg4.5Al2(OH)13·O0.2·(CO3)0.8以及它们的任意组合。
具体实施例4.根据具体实施例1或2的聚合物组合物,抗氧剂包括主抗氧剂和辅抗氧剂,并且其中主抗氧剂包含受阻酚类抗氧剂、胺类抗氧剂、硫醚类抗氧剂、三嗪类抗氧剂或它们的组合,辅抗氧剂包含亚磷酸酯类抗氧剂、三嗪类抗氧剂或它们的组合。
具体实施例5.根据具体实施例4的阻燃剂组合物,主抗氧剂包含四[β-(3.5-二叔丁基,4-羟基苯基)丙酸]季戊四酯醇、四(3,5-二叔丁基-4-羟基)苯丙酸季戊四醇酯、2,6-二叔丁基对甲苯酚、4-羟甲基-2,6-二叔丁基苯酚、2,6-二叔丁基-α-二甲氨基苯酚、N-环己基-N’-苯基对苯二胺、N,N’-二苯基对苯二胺、硫代二丙酸二月桂酸酯、2,4-二(十二烷基硫甲基)-6-甲基苯酚、6-(4-羟基-3,5-二叔丁基苯胺基)-2,4-双(辛基硫基)-1,3,5-三嗪、2-正辛基硫代-4,6-双(4’-羟基-3,5-二叔丁基苯氧基)-1,3,5-三嗪或它们的任意组合。
具体实施例6.根据具体实施例4的阻燃剂组合物,辅抗氧剂包含亚磷酸三(2,4-二叔丁基苯基)酯、二(2,4-二-丁基苯)季戊四醇二磷酸酯、亚磷酸双酚A酯、亚磷酸三丁酯、6-(4-羟基-3,5-二叔丁基苯胺基)-2,4-双(辛基硫基)-1,3,5-三嗪、2-正辛基硫代-4,6-双(4’-羟基-3,5-二叔丁基苯氧基)-1,3,5-三嗪或它们的任意组合。
具体实施例7.根据具体实施例1或2的聚合物组合物,协效剂包含锌化合物、膨胀石墨、联枯或它们的任意组合。
具体实施例8.根据具体实施例7的聚合物组合物,协效剂包含膨胀石墨、锡酸锌、硼酸锌、氧化锌、或联枯它们的任意组合。
具体实施例9.根据具体实施例1或2的聚合物组合物,阻燃剂为溴化丁二烯-苯乙烯嵌段共聚物,并且其中溴化丁二烯-苯乙烯嵌段共聚物包含溴化1,2-丁二烯嵌段、溴化1,4-丁二烯嵌段、或它们的组合;基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中溴化丁二烯嵌段,溴化1,2-丁二烯嵌段的量在50重量份至90重量份的范围内,并且溴化1,4-丁二烯嵌段的量在10重量份至50重量份的范围内。
具体实施例10.根据具体实施例9的聚合物组合物,基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物,溴化丁二烯-苯乙烯嵌段共聚物包含10重量份至40重量份的苯乙烯嵌段以及60重量份至90重量份的溴化丁二烯嵌段;并且溴化丁二烯-苯乙烯嵌段共聚物具有使用双酚A均聚碳酸酯标准品通过凝胶渗透色谱测量的100,000到160,000克/摩尔的重均分子量。
具体实施例11.根据具体实施例1或2的聚合物组合物,阻燃剂与协效剂的比例在1:1至10:1的范围内。
具体实施例12.根据具体实施例11的聚合物组合物,阻燃剂与协效剂的比例在3:1至7:1的范围内。
具体实施例13.根据具体实施例1或2的聚合物组合物,缚酸剂与抗氧剂的质量比在0.5:1至5:1的范围内。
具体实施例14.根据具体实施例4的聚合物组合物,主抗氧剂与辅抗氧剂的重量比在1:0.5至1:5的范围内。
具体实施例15.根据具体实施例1或2的聚合物组合物,聚合物基体包含聚苯乙烯、聚醚酰亚胺、丙烯酸、氟碳化合物、聚酰胺、聚乙烯、聚酯、聚丙烯、聚碳酸酯、聚氨酯、聚醚醚酮、聚苯硫醚、聚醚酮酮、或它们的任意组合。
具体实施例16.根据具体实施例1或2的聚合物组合物,包括:
聚合物基体,91.5重量份至97.5重量份;
阻燃剂,2重量份至6重量份;
缚酸剂,0.2重量份至0.3重量份;
抗氧剂,0.2重量份至0.3重量份;以及
协效剂,0.5重量份至1.5重量份,
上述重量份均基于100重量份的聚合物组合物的总重量。
具体实施例17.根据具体实施例4的聚合物组合物,包括:
聚合物基体,90重量份至99重量份;
阻燃剂,1重量份至10重量份;
缚酸剂,0.1重量份至0.5重量份;
主抗氧剂,0.05重量份至0.20重量份;
辅抗氧剂,0.05重量份至0.20重量份;以及
协效剂,0.2重量份至5重量份,
上述重量份均基于100重量份的聚合物组合物的总重量。
具体实施例18.根据具体实施例16的聚合物组合物,包括:
聚合物基体,91.5重量份至97.5重量份;
阻燃剂,2重量份至6重量份;
缚酸剂,0.2重量份至0.3重量份;
主抗氧剂,0.1重量份至0.15重量份;
辅抗氧剂,0.1重量份至0.15重量份;以及
协效剂,0.5重量份至1.5重量份,
上述重量份均基于100重量份的聚合物组合物的总重量。
具体实施例19.根据具体实施例1或2的聚合物组合物,聚合物组合物进一步包含:
发泡剂,1重量份至5重量份。
具体实施例20.根据具体实施例1或2的聚合物组合物,聚合物组合物进一步包含:
成核剂,0.1重量份至1重量份。
具体实施例21.一种聚合物母料组合物,包含
第一母料,基于100重量份的第一母料的总重量包含5重量份至20重量份的协效剂,和80重量份至95重量份的聚合物基体;
第二母料,基于100重量份的第二母料的总重量包含40重量份至60重量份的阻燃剂,2重量份至5重量份的缚酸剂,2重量份至3.75重量份的抗氧剂,和30重量份至60重量份的聚合物基体,
第一母料与第二母料的重量比在1:2至1:4的范围内。
具体实施例22.根据具体实施例21的聚合物母料组合物,缚酸剂包括氧化锡类缚酸剂、水滑石类缚酸剂或它们的组合。
具体实施例23.根据具体实施例21的聚合物母料组合物,抗氧剂包括主抗氧剂和辅抗氧剂,并且其中主抗氧剂包含受阻酚类抗氧剂、胺类抗氧剂、硫醚类抗氧剂、三嗪类抗氧剂或它们的组合,辅抗氧剂包含亚磷酸酯类抗氧剂、三嗪类抗氧剂或它们的组合。
具体实施例24.根据具体实施例21的聚合物母料组合物,协效剂包含锌化合物、膨胀石墨、联枯或它们的任意组合。
具体实施例25.根据具体实施例21的聚合物母料组合物,阻燃剂为溴化丁二烯-苯乙烯嵌段共聚物,并且其中溴化丁二烯-苯乙烯嵌段共聚物包含溴化1,2-丁二烯嵌段、溴化1,4-丁二烯嵌段、或它们的组合;基于100重量份的溴化丁二烯-苯乙烯嵌段共聚物中溴化丁二烯嵌段,溴化1,2-丁二烯嵌段的量在50重量份至90重量份的范围内,并且溴化1,4-丁二烯嵌段的量在10重量份至50重量份的范围内。
具体实施例26.根据具体实施例21的聚合物母料组合物,阻燃剂与协效剂的比例在1:1至10:1的范围内。
具体实施例27.根据具体实施例21的聚合物母料组合物,阻燃剂与协效剂的比例在3:1至7:1的范围内。
具体实施例28.根据具体实施例21的聚合物母料组合物,缚酸剂与抗氧剂的质量比在0.5:1至5:1的范围内。
具体实施例29.根据具体实施例23的聚合物母料组合物,主抗氧剂与辅抗氧剂的重量比在1:0.5至1:5的范围内。
具体实施例30.根据具体实施例21的聚合物母料组合物,聚合物基体包含聚苯乙烯、聚醚酰亚胺、丙烯酸、氟碳化合物、聚酰胺、聚乙烯、聚酯、聚丙烯、聚碳酸酯、聚氨酯、聚醚醚酮、聚苯硫醚、聚醚酮酮、或它们的任意组合。
具体实施例31.一种包含具体实施例1至20中任一项的聚合物组合物的板材。
具体实施例32.一种由具体实施例1至20中任一项的聚合物组合物或具体实施例21至30中任一项的聚合物母料组合物制备的板材。
以上所述仅为本发明的优选实施例而已,并不用于限制本发明,对于本领域的技术人员来说,本发明可以有各种更改和变化。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (10)
1.一种聚合物组合物,其特征在于,包含:
聚合物基体,90重量份至99重量份;
阻燃剂,1重量份至10重量份;
缚酸剂,0.1重量份至0.5重量份;
抗氧剂,0.1重量份至0.5重量份;以及
协效剂,0.2重量份至5重量份,
上述重量份均基于100重量份的所述聚合物组合物的总重量。
2.根据权利要求1所述的聚合物组合物,其特征在于,所述缚酸剂包括氧化锡类缚酸剂、水滑石类缚酸剂或它们的组合。
3.根据权利要求1或2所述的聚合物组合物,其特征在于,所述抗氧剂包括主抗氧剂和辅抗氧剂,并且其中所述主抗氧剂包含受阻酚类抗氧剂、胺类抗氧剂、硫醚类抗氧剂、三嗪类抗氧剂、或它们两种以上的任意组合,所述辅抗氧剂包含亚磷酸酯类抗氧剂、三嗪类抗氧剂、或它们的组合。
4.根据权利要求1或2所述的聚合物组合物,其特征在于,所述协效剂包含锌化合物、膨胀石墨、联枯、或它们两种以上的任意组合。
5.根据权利要求1或2所述的聚合物组合物,其特征在于,所述阻燃剂为溴化丁二烯-苯乙烯嵌段共聚物,并且其中所述溴化丁二烯-苯乙烯嵌段共聚物包含溴化1,2-丁二烯嵌段、溴化1,4-丁二烯嵌段、或它们的组合;基于100重量份的所述溴化丁二烯-苯乙烯嵌段共聚物中的溴化丁二烯嵌段,所述溴化1,2-丁二烯嵌段的量在50重量份至90重量份的范围内,并且所述溴化1,4-丁二烯嵌段的量在10重量份至50重量份的范围内。
6.根据权利要求1或2所述的聚合物组合物,其特征在于,所述阻燃剂与所述协效剂的重量比例在1:1至10:1的范围内。
7.根据权利要求1或2所述的聚合物组合物,其特征在于,所述缚酸剂与所述抗氧剂的重量比在0.5:1至5:1的范围内。
8.一种聚合物母料组合物,其特征在于,包含:
第一母料,基于100重量份的第一母料的总重量包含5重量份至20重量份的协效剂,和80重量份至95重量份的聚合物基体;
第二母料,基于100重量份的第二母料的总重量包含40重量份至60重量份的阻燃剂,2重量份至5重量份的缚酸剂,2重量份至3.75重量份的抗氧剂,和30重量份至60重量份的所述聚合物基体,
所述第一母料与所述第二母料的重量比在1:2至1:4的范围内。
9.一种包含权利要求1至7中任一项所述的聚合物组合物的板材。
10.一种由权利要求1至7中任一项所述的聚合物组合物或权利要求8所述的聚合物母料组合物制备的板材。