CN116332552A - 一种低碳易和混凝土外加剂、其制备方法及用途 - Google Patents
一种低碳易和混凝土外加剂、其制备方法及用途 Download PDFInfo
- Publication number
- CN116332552A CN116332552A CN202310425666.0A CN202310425666A CN116332552A CN 116332552 A CN116332552 A CN 116332552A CN 202310425666 A CN202310425666 A CN 202310425666A CN 116332552 A CN116332552 A CN 116332552A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- concrete
- low
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种低碳易和混凝土外加剂、其制备方法及用途，低碳易和混凝土外加剂包括重量配比如下的各组分：甲氧基聚氧乙烯醚30‑60份；改性烷撑烯基聚氧乙烯醚270‑330份；碘代硫代乙酰胆碱3‑7份；硫酸亚铁溶液0.2‑1.7份；过硫酸铵1.0‑3.0份；水200‑250份；顺丁烯二酸酐30‑40份；丙烯酸羟乙酯15‑25份；水20‑30份；维生素C0.1‑0.35份；吊白粉0.20‑0.4份；巯基乙醇0.5‑1.5份；水60‑90份。该混凝土外加剂采用无碳排放和低碳排放的原料配方调配，在常温下低耗能生产。在保证混凝土强度的同时，减少混凝土施工中振捣设备的使用，并确保长距离运输不损失减水保坍性能。
Description
技术领域
本发明涉及混凝土添加剂技术，尤其涉及一种低碳易和混凝土外加剂、其制备方法及用途。
背景技术
在混凝土施工过程中，传统的混凝土添加剂主要用于减水和保坍。传统的混凝土添加剂，主要是萘系高效减水剂、木质素减水剂、氨基磺酸盐减水剂和聚羧酸减水剂等，传统产品功能单一、仅具备减水或仅具备保坍性能，掺量较高、流动性保持时间短、性能差，有毒物质含量高等缺点。如CN109336447公开的一种稳定型保坍剂及其制备和使用方法，公开了一种稳定型保坍剂由下述原料组分制成：不饱和聚醚组合物；丙烯酸类单体；阻聚剂；催化剂；氧化剂；还原剂；分子量调节剂；pH调节剂和水，其中所述不饱和聚醚组合物包括第一不饱和聚醚和第二不饱和聚醚，且其中所述第一不饱和聚醚的数均分子量小于所述第二不饱和聚醚的数均分子量；所述分子量调节剂包括巯基丙酸和/或硫代甘醇；所述阻聚剂包括对苯二酚；所述催化剂包括对甲苯磺酸；所述氧化剂包括双氧水；所述还原剂包括TP1351，七水硫酸亚铁中的一种或几种；所述pH调节剂包括碱金属氢氧化物或者碱土金属氢氧化物。
传统混凝土外加剂在制备过程中发生高温化学反应，氧化过程中存在一定二氧化碳排放，对环保不利。而且近年来，随着环保意识增强，混凝土中的必要的天然砂石也逐渐被人工砂石取代，人工砂石相对于天然砂石而言，没有经历过长时间的风吹日晒的磨砺，人工砂石菱角相对更加尖锐，不像天然砂石那样圆滑，所以人工砂石参入混凝土后，导致混凝土流动性下降，导致混凝土施工需要增加振捣或缩小施工面，且掺有人工砂石的混凝土往往不适合长距离运输，或导致混凝土长距离运输后流动性减弱，不易拌合。故混凝土添加剂技术更新势在必行。
发明内容
本发明的目的在于，针对传统的混凝土添加剂在制备过程中存在一定二氧化碳排放，混凝土采用人工砂石原材料后拌合性降低的特点，提出一种低碳易和混凝土外加剂，该混凝土外加剂采用无碳排放和低碳排放的原料配方调配，在常温下低耗能生产。具有掺量小，综合性能高，在保证混凝土强度的同时，减少混凝土施工中振捣设备的使用并确保长距离运输不损失减水保坍性能，是新型的低碳混凝土外加剂技术。
为实现上述目的，本发明采用的技术方案是：采用无碳排放和低碳排放的原料，使混凝土中的原材料之间增加分子流动性，产生润滑效果，使带有棱角的原材料具有更加流动的工作性能，是一种低碳易和混凝土外加剂，包括重量配比如下的各组分：
(1)底料：
(2)A液：
顺丁烯二酸酐 30-40份；
丙烯酸羟乙酯 15-25份；
水 20-30份；
(3)B液：
进一步地，所述低碳易和混凝土外加剂，优选包括重量配比如下的各组分：
(1)底料：
(2)A液：
顺丁烯二酸酐 33-37份；
丙烯酸羟乙酯 18-22份；
水 22-28份；
(3)B液：
进一步地，所述低碳易和混凝土外加剂，更优选的包括重量配比如下的各组分：
(1)底料：
(2)A液：
顺丁烯二酸酐 35份；
丙烯酸羟乙酯 20份；
水 25份；
(3)B液：
进一步地，所述硫酸亚铁溶液浓度为0.5-1.5％wt，优选为0.7-1.3％wt。更优选为1％wt。
进一步地，所述过硫酸铵浓度为20-30％wt，优选为25-28％wt，更优选为27.5％wt。
进一步地，所述低碳易和混凝土外加剂还包括(4)保水剂，所述保水剂包括：
黄原胶粉末 1-2份；
水 30-50份。
进一步地，优选的所述保水剂包括：
黄原胶粉末 1.2-1.8份；
水 35-45份。
进一步地，更优选的所述保水剂包括：
黄原胶粉末 1.5份；
水 40份。
进一步地，所述黄原胶粉末为食用级黄原胶粉末。
本发明的另一个目的还公开了一种低碳易和混凝土外加剂的制备方法，包括以下步骤：
步骤1按照重量配比制备A液、B液和保水剂，配制时要充分搅拌，使各种组分充分混匀，备用；
步骤2将甲氧基聚氧乙烯醚(MCPEG)、烷撑烯基聚氧乙烯醚(NPEG)和水加入反应釜，不搅拌；
步骤3按顺序添加硫酸亚铁溶液，搅拌同时加入过硫酸铵；3-10min后滴加A液和B液，A液滴加40-80min，B液滴加50-90min；
步骤4.反应温度不超过40°，保温老化50-80min；补碘代硫代乙酰胆碱、补水；
步骤5.添加保水剂。
进一步地，所述低碳易和混凝土外加剂的制备方法中A液和B液的滴加起始温度均为常温。
进一步地，所述低碳易和混凝土外加剂的制备温度控制在40℃以内。
进一步地，所述硫酸亚铁溶液现用现调。
进一步地，所述混凝土运输距离超过10公里或施工时间超过90分钟，保水剂施用量应为1.1～1.2倍。
本发明的另一个目的还公开了一种低碳易和混凝土外加剂在混凝土领域的用途。
进一步地，所述低碳易和混凝外加剂在混凝土搅拌过程中加入，该外加剂加在混凝土拌和站减水剂容器中，按混凝土配比输入拌和站设备，全自动添加。
进一步地，所述低碳易和混凝土外加剂的施用量与常规混凝土配比中减水剂配比一致。
本发明低碳易和混凝土外加剂、其制备方法及用途，与现有技术相比较具有以下优点：
1)本发明低碳易和混凝土外加剂以多碳基聚羧酸为主材，采用自研混凝土外加剂反应釜，制备过程前半段干拌，大幅降低二氧化碳排放。
2)本发明低碳易和混凝土外加剂是在散热性好、釜内光滑的混凝土外加剂反应釜中加工制作，制作过程简洁高效，无任何污染排放或残留。
3)本发明低碳易和混凝土外加剂的使用，使混凝土施工时的操作性更高，使混凝土在施工过程中流动性更好，减少振捣棒的耗能和混凝土施工用具二次清洗的耗能，更加低碳环保。
4)使用本发明低碳易和混凝土外加剂的混凝土减水保坍效果优异，混凝土流动性好，施工操作性能佳，强度提升较快。
综上，本发明低碳易和混凝土外加剂是一种低能耗、低排放、易操作和易运输的混凝土外加剂。
具体实施方式
以下结合实施例对本发明进一步说明：
实施例1
本实施例公开了一种低碳易和混凝土外加剂，制备过程如下
步骤1按照顺丁烯二酸酐35g，丙烯酸羟乙酯20g和水25g制备A液；
按照维生素C 0.25g，吊白粉0.3g，巯基乙醇1.0g和水80g制备B液；
按照黄原胶1.5g，水40g制备保水剂；
上述溶液配制时要充分搅拌，使各种组分充分混匀，备用；
步骤2将甲氧基聚氧乙烯醚(MCPEG)45g、烷撑烯基聚氧乙烯醚(NPEG)300g和水230g加入反应釜，不搅拌。
步骤3按顺序在釜底添加浓度1％硫酸亚铁溶液1g，搅拌同时加入浓度28％的过硫酸铵2g，5min后滴加A液和B液，A液滴加50min，B液滴加60min；
步骤4.反应温度不超过40°，保温老化60min；补碘代硫代乙酰胆碱5g、补水。
步骤5.添加保水剂，得到低碳易和混凝土外加剂。
对照案例混凝土配比为C35泵送混凝土配比，配比要求该外加剂为含固量6％的外加剂400g。本外加剂含固量为52.7％，取本外加剂45.5g，加水354.5g拌入混凝土中。
实施例2
本实施例公开了一种低碳易和混凝土外加剂，制备过程如下
步骤1按照顺丁烯二酸酐34g，丙烯酸羟乙酯19g，水26g制备A液；
按照维生素C 0.2g，吊白粉0.25g，巯基乙醇0.8g水70g制备B液；
按照黄原胶1.4g，水40g制备保水剂；
配制时要充分搅拌，使各种组分充分混匀，备用；
步骤2将甲氧基聚氧乙烯醚(MCPEG)50g、烷撑烯基聚氧乙烯醚(NPEG)295g和水235g加入反应釜，不搅拌。
步骤3按顺序在釜底添加浓度0.8％硫酸亚铁溶液1g，搅拌同时加入浓度27％的过硫酸铵2g，持续搅拌5min后滴加A液和B液，A液滴加50min，B液滴加60min；
步骤4.反应温度不超过40°，保温老化60min；补碘代硫代乙酰胆碱5g、补水。
步骤5.添加保水剂，得到低碳易和混凝土外加剂。
对照案例混凝土配比为C35泵送混凝土配比，配比要求该外加剂为含固量6％的外加剂400g。本外加剂含固量为52.6％，取本外加剂45.4g，加水354.6g拌入混凝土中。
对照例1
普通减水剂为外购巴斯夫配方普通减水剂，经试验，同样混凝土标号配比中固含需求为7％的早强型减水剂440g，按同样混凝土标号配比后，进行对比测验。
对照例2
保坍减水剂为外购巴斯夫配方保坍减水剂，经试验，同样混凝土标号配比中固含需求为7％的早强型减水剂440g，按同样混凝土标号配比后，进行对比测验。
将通过实施例1和实施例2制得的低碳易和混凝土外加剂与对照例1普通减水剂和对照例2保坍减水剂产品进行对比，将其添加至同样标号混凝土中检测混凝土相关性能，检测数据如表1所示。
表1性能比较
由表1可见实施例1和实施例2制备的低碳易和外加剂具有优异的初始净浆流动度、初始扩展度1h净浆流动度2h净浆流动度减水率和抗压强度。
最后应说明的是：以上各实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述各实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的范围。
Claims (10)
1.一种低碳易和混凝土外加剂，其特征在于，包括重量配比如下的各组分：
(1)底料：
(2)A液：
顺丁烯二酸酐 30-40份；
丙烯酸羟乙酯 15-25份；
水 20-30份；
(3)B液：
2.根据权利要求1所述低碳易和混凝土外加剂，其特征在于，所述硫酸亚铁溶液浓度为0.5-1.5％wt。
3.根据权利要求1所述低碳易和混凝土外加剂，其特征在于，所述过硫酸铵浓度为20-30％wt。
4.根据权利要求1所述低碳易和混凝土外加剂，其特征在于，还包括保水剂，所述保水剂包括：
黄原胶粉末 1-2份；
水 30-50份。
5.一种权利要求1-4任意一项所述低碳易和混凝土外加剂的制备方法，其特征在于，包括以下步骤：
步骤1按照重量配比制备A液、B液和保水剂，充分搅拌；
步骤2将甲氧基聚氧乙烯醚、烷撑烯基聚氧乙烯醚和水加入反应釜，不搅拌；
步骤3按顺序在釜底添加硫酸亚铁溶液，搅拌同时加入过硫酸铵；3-10min后滴加A液和B液，A液滴加40-80min，B液滴加50-90min；
步骤4.反应温度不超过40°，保温老化50-80min；补碘代硫代乙酰胆碱、补水；
步骤5.添加保水剂。
6.根据权利要求5所述低碳易和混凝土外加剂的制备方法，其特征在于，所述A液和B液的滴加起始温度均为常温。
7.根据权利要求5所述低碳易和混凝土外加剂的制备方法，其特征在于，所述低碳易和混凝土外加剂的制备温度控制在40℃以内。
8.根据权利要求5所述低碳易和混凝土外加剂的制备方法，其特征在于，所述硫酸亚铁溶液现用现调。
9.根据权利要求5所述低碳易和混凝土外加剂的制备方法，其特征在于，所述混凝土运输距离超过10公里或施工时间超过90分钟，保水剂施用量应为理论用量的1.1～1.2倍。
10.一种权利要求1-4任意一项所述低碳易和混凝土外加剂在混凝土领域的用途。