CN115651384B - 一种pc/abs合金及其制备方法和应用 - Google Patents
一种pc/abs合金及其制备方法和应用 Download PDFInfo
- Publication number
- CN115651384B CN115651384B CN202211319196.1A CN202211319196A CN115651384B CN 115651384 B CN115651384 B CN 115651384B CN 202211319196 A CN202211319196 A CN 202211319196A CN 115651384 B CN115651384 B CN 115651384B
- Authority
- CN
- China
- Prior art keywords
- agent
- burn
- parts
- ultraviolet
- abs alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种PC/ABS合金，按重量份计，包括以下组分：PC树脂60‑95份；ABS树脂5‑20份；阻燃剂5‑20份；抗紫外线剂0.3‑1.5份；防烧穿剂，抗紫外线剂重量份的30‑60%；所述的防烧穿剂选自长链线性饱和羧酸盐、焦磷酸二氢二钠、三聚磷酸钠、六偏磷酸钠、磷酸二氢钠、磷酸二氢铵、磷酸二辛脂、亚磷酸三苯酯、磷酸二异辛酯中的至少一种；所述的抗紫外线剂选自苯并三唑类抗紫外线剂、受阻胺类抗紫外线剂、三嗪类抗紫外线剂中的至少一种。本发明通过选用特定含量的防烧穿剂与特定抗紫外线剂的复配，通过抗UV剂和防烧穿剂复配能够改变体系分解历程，更容易促进成炭，此外在分解过程中还能起到增加分解产生气体量，起到热量隔绝的效果，使熔体更不容易烧穿。
Description
技术领域
本发明涉及高分子材料技术领域，特别是涉及一种PC/ABS合金及其制备方法和应用。
背景技术
聚碳酸酯(简称PC树脂)是一类主链上兼具柔性碳酸酯基团、刚性苯环基团的高度线性热塑性聚合物材料，这样的分子链结构赋予了PC材料良好的刚性、耐热性以及优异的耐缺口冲击性能。PC与ABS共混可以综合两者的优良性能，PC/ABS合金一方面它的耐热性，冲击强度和拉伸强度优于ABS，另一方面它的成本和熔体粘度比PC低，加工性能比PC好，其制品内应力和冲击强度对制品厚度的敏感性都大大降低。可用于成型大面积或薄壁长流程制品。广泛应用于机械零件、电器部件、帽盔及生产汽车车身等要求兼有优良抗冲击性和刚性的制品。如汽车内外部件、家电(电视、电话机等)、电脑及周边设备、办公自动化设备外壳、通讯器材等多个领域。但是，无卤阻燃PC/ABS合金由于熔体强度较低，容易烧穿，因此很难通过5VA阻燃测试。为了解决材料容易烧穿的问题，常见的改善方法是增加矿粉填充、增加玻纤来提高熔体强度，或者过度提高阻燃剂含量来实现快速阻燃从而防止烧穿。但是上述方法第一会增加成本，大量的填料或阻燃剂的加入也会降低其它性能。
但是，提升阻燃性是无法提升防烧穿性，这是由于阻燃性能可以通过抗滴落剂来提升，其作用机理是通过抗滴落剂带动熔体回缩使得厚度提升来实现。耐烧穿性能不能通过抗滴落剂来实现，且抗滴落剂的回缩对于烧穿还会有副作用，加速穿控速度。
发明内容
本发明的目的在于，克服上述技术缺陷，提供一种不容易烧穿的PC/ABS合金，及其制备方法和应用。
本发明是通过以下技术方案实现的：
一种PC/ABS合金，按重量份计，包括以下组分：
PC树脂 60-95份；
ABS树脂 5-20份；
阻燃剂 5-20份；
抗紫外线剂 0.3-1.5份；
防烧穿剂 抗紫外线剂重量份的30-60%；
所述的防烧穿剂选自长链线性饱和羧酸盐、焦磷酸二氢二钠、三聚磷酸钠、六偏磷酸钠、磷酸二氢钠、磷酸二氢铵、磷酸二辛脂、亚磷酸三苯酯、磷酸二异辛酯中的至少一种；
所述的抗紫外线剂选自苯并三唑类抗紫外线剂、受阻胺类抗紫外线剂、三嗪类抗紫外线剂中的至少一种。
现有技术常用的抗紫外线剂还有二苯甲酮抗紫外线剂、癸二酸酯抗紫外线剂，但是这两种抗紫外线剂无法协效本发明的防烧穿剂达到放烧穿的技术效果。
优选的，抗紫外线剂含量为0.6-0.9份。
优选的，所述的抗紫外线剂选自三嗪类抗紫外线剂。
优选的，所述的防烧穿剂选自长链线性饱和羧酸盐、焦磷酸二氢二钠、三聚磷酸钠、六偏磷酸钠、磷酸二氢钠、磷酸二氢铵中的至少一种；
进一步优选的，所述的防烧穿剂选自长链线性饱和羧酸盐；
所述的长链线性饱和羧酸盐为碳链长度为C28-C32的线性饱和羧酸盐，所述的碳链长度为C28-C32的线性饱和羧酸盐选自碳链长C28-C32的钠盐、碳链长C28-C32的钙盐、碳链长C28-C32的镁盐、碳链长C28-C32的锌盐中的至少一种。可选的，所述的PC树脂选自双酚A型聚碳酸酯，熔融指数在3-22g/10min之间，测试条件为300℃，1.2kg；所述的ABS树脂的熔融指数在7-42g/10min之间，测试条件为220℃，10kg，测试标准：ISO 1133。
所述的阻燃剂选自磷系阻燃剂，选自磷酸三苯酯、双酚A-双（二苯基磷酸酯）、间苯二酚双（二苯基磷酸酯）、苯氧基聚磷腈中的至少一种。
可以根据实际需要，选择性添加0-2份助剂；所述的助剂选自抗氧剂、润滑剂中的至少一种。
抗氧剂可以是：1,3,5-三甲基-2,4,6-三(3,5-二-叔丁基-4-羟基苄基)苯；2,5-二-叔丁基-4-羟基苄基二甲胺；二乙基-3,5-二-叔丁基-4-羟基苄基磷酸酯；硬脂基-3,5-二-叔丁基-4-羟基苄基磷酸酯；3,5-二-叔丁基-4-羟基苯基-3,5-二硬脂基-硫代三唑基胺；2,6-二-叔丁基-4-羟基甲基苯酚；2,4-二-(正辛硫基)-6-(4-羟基-3,5-二-叔丁基甘油烯丙基醚基)-1,3,5-三嗪；N,N’-六亚甲基二(3,5-二-叔丁基-4-羟基-氢化肉桂酰胺)；N,N’-双-(3-(3,5-二-叔丁基-4-羟基苯基)丙酰基)己二胺；十八烷基-3-(3,5-二-叔丁基-4-羟基苯基)丙酸酯；季戊四醇基-四[3-(3,5-二-叔丁基-4-羟基苯基)丙酸酯]；三甘醇-二[3-(3,5-二甲基-4-羟基苯基)丙酸酯]；二缩三乙二醇双[β-(3-叔丁基-4-羟基-5-甲基苯基)丙酸酯]；2,2’-硫代二乙基-二[3-(3,5-二-叔丁基-4-羟基苯基)丙酸酯，等。
润滑剂可以是：硬脂酸盐类润滑剂、脂肪酸类润滑剂、硬脂酸酯类润滑剂中的至少一种；所述的硬脂酸盐类润滑剂选自硬脂酸钙、硬脂酸镁、硬脂酸锌中的至少一种；所述的脂肪酸类润滑剂选自脂肪酸、脂肪酸衍生物、脂肪酸酯中的至少一种；所述的硬脂酸酯类润滑剂选自季戊四醇硬脂酸酯中的至少一种。
本发明的PC/ABS合金的制备方法，包括以下步骤：将ABS树脂、PC树脂、抗紫外线剂、防烧穿剂、阻燃剂混合均匀，通过双螺杆挤出机挤出造粒，得到PC/ABS合金。
本发明的PC/ABS合金的应用，用于制备电器电控盒、逆变器、电器开关。
本发明具有如下有益效果：
本发明通过选用特定含量的防烧穿剂与抗紫外线剂的复配，通过抗UV剂和防烧穿剂复配能够改变体系分解历程，更容易促进成炭，此外在分解过程中还能起到增加分解产生气体量，起到热量隔绝的效果，使本发明的PC/ABS合金无需过度增加阻燃剂也能够实现不容易烧穿（UL94-5VA样条/2.5mm大于等于6次点燃火焰次数，UL94-5VA样板/2.5mm大于等于5次点燃火焰次数）。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明，但不以任何形式限制本发明。应当指出的是，对本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进。这些都属于本发明的保护范围。
本发明所用实验原料来源如下：
PC-1：PC WY-106BR，双酚A型聚碳酸酯，熔融指数6g/10min（300℃、1.2kg），利华益维远化学股份有限公司；
PC-2：LXZY1920-01，双酚A型聚碳酸酯，熔融指数22g/10min（300℃、1.2kg），鲁西化工集团股份有限公司；
ABS-1：奇美，ABS PA-757，熔融指数18g/10min（220℃、10kg）；
ABS-2：LG，ABS HP181，熔融指数40g/10min（220℃、10kg）
抗紫外线剂A：三嗪类抗紫外线剂，牌号 RIASORB UV-1164；
抗紫外线剂B：苯并三唑类抗紫外线剂，牌号 RIASORB UV-P；
抗紫外线剂C：苯并三唑类抗紫外线剂，牌号 RIASORB UV-234；
抗紫外线剂D：受阻胺类抗紫外线剂，牌号 RIASORB UV-123；
抗紫外线剂E：二苯甲酮抗紫外线剂，牌号 RIASORB UV-531；
抗紫外线剂F：癸二酸酯抗紫外线剂，牌号紫外线吸收剂UV-292。
双酚A-双（二苯基磷酸酯）：WSFR-BDP-N2，浙江万盛科技有限公司
焦磷酸二氢二钠：DHPP，Taihei Chemical Industrial Co , Ltd
三聚磷酸钠：三聚磷酸钠，吴江市旭龙化工有限公司；
六偏磷酸钠：六偏磷酸钠，佛山市佳琦化工有限公司；
磷酸二氢钠：磷酸二氢钠，上海阿拉丁生化科技股份有限公司；
磷酸二辛脂：磷酸二辛脂，默克生命化学有限公司；
亚磷酸三苯酯：亚磷酸三苯酯，默克生命化学有限公司；
碳链长C28-C32钠盐：NAV101，科莱恩化学；
碳链长C28-C32钙盐：CAV102，科莱恩化学；；
碳链长C28-C32镁盐：褐煤酸镁，上海阿拉丁生化科技股份有限公司；
碳链长C28-C32锌盐：褐煤酸锌，上海阿拉丁生化科技股份有限公司；
硬脂酸锌：ZINC STEARATE(BS-2818)，中山华明泰科技股份有限公司；
硬脂酸钙：CALCIUM STEARATE(BS-3818)，中山华明泰科技股份有限公司；
硬脂酸镁：硬脂酸镁，法基化学有限公司；
实施例和对比例PC/ABS合金的制备方法：将ABS树脂、PC树脂、抗紫外线剂、防烧穿剂、阻燃剂混合均匀，通过双螺杆挤出机挤出造粒，螺杆的温度设置为200-260℃，转速为350转/min，得到PC/ABS合金。
各项测试方法：
（1）5VA样条测试：按照UL94-2018 5V燃烧要求对标准样条测试进行，记录样条失效时施加火焰次数。
（2）5VA样板测试：按照UL94-2018 5V燃烧要求对标准样板测试进行，记录样条失效时施加火焰次数。
表1：实施例1-7 PC/ABS合金各组分（重量份）及测试结果
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | 实施例7 | |
| PC-1 | 60 | 70 | 70 | 70 | 70 | 70 | 95 |
| ABS-1 | 20 | 10 | 10 | 10 | 10 | 10 | 5 |
| 双酚A-双（二苯基磷酸酯） | 5 | 12 | 12 | 12 | 12 | 12 | 20 |
| 抗紫外线剂A | 0.3 | 0.4 | 0.6 | 0.8 | 0.9 | 1.1 | 1.5 |
| 焦磷酸二氢二钠 | 0.18 | 0.2 | 0.3 | 0.4 | 0.45 | 0.55 | 0.45 |
| UL94-5VA样条/2.5mm | 6 | 6 | 7 | 7 | 7 | 6 | 6 |
| UL94-5VA样板/2.5mm | 5 | 5 | 6 | 6 | 6 | 6 | 6 |
由实施例2-6可知，优选的抗紫外线剂添加量下耐烧穿性更好。
表2：实施例8-14PC/ABS合金各组分（重量份）及测试结果
| 实施例8 | 实施例9 | 实施例10 | 实施例11 | 实施例12 | 实施例13 | 实施例14 | |
| PC-1 | 70 | 70 | 70 | 70 | 70 | 70 | 70 |
| ABS-1 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
| 双酚A-双（二苯基磷酸酯） | 12 | 12 | 12 | 12 | 12 | 12 | 12 |
| 抗紫外线剂A | 0.8 | 0.8 | 0.8 | 0.8 | |||
| 抗紫外线剂B | 0.8 | ||||||
| 抗紫外线剂C | 0.8 | ||||||
| 抗紫外线剂D | 0.8 | ||||||
| 焦磷酸二氢二钠 | 0.4 | 0.4 | 0.4 | ||||
| 碳链长C28-C32钠盐 | 0.4 | ||||||
| 碳链长C28-C32钙盐 | 0.4 | ||||||
| 碳链长C28-C32镁盐 | 0.4 | ||||||
| 碳链长C28-C32锌盐 | 0.4 | ||||||
| UL94-5VA样条/2.5mm | 6 | 6 | 6 | 7 | 7 | 7 | 7 |
| UL94-5VA样板/2.5mm | 5 | 5 | 5 | 7 | 7 | 6 | 7 |
由实施例4/8-10可知，所述的抗紫外线剂优选三嗪类抗紫外线剂。
表2：实施例15-20PC/ABS合金各组分（重量份）及测试结果
| 实施例15 | 实施例16 | 实施例17 | 实施例18 | 实施例19 | 实施例20 | |
| PC-1 | 70 | 70 | 70 | 70 | 70 | |
| PC-2 | 70 | |||||
| ABS-1 | 10 | 10 | 10 | 10 | 10 | |
| ABS-2 | 10 | |||||
| 双酚A-双（二苯基磷酸酯） | 12 | 12 | 12 | 12 | 12 | 12 |
| 抗紫外线剂A | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 | 0.8 |
| 三聚磷酸钠 | 0.4 | 0.4 | ||||
| 六偏磷酸钠 | 0.4 | |||||
| 磷酸二氢钠 | 0.4 | |||||
| 磷酸二辛脂 | 0.4 | |||||
| 亚磷酸三苯酯 | 0.4 | |||||
| UL94-5VA样条/2.5mm | 7 | 7 | 7 | 6 | 6 | 7 |
| UL94-5VA样板/2.5mm | 6 | 6 | 6 | 5 | 5 | 6 |
由实施例4/11-19可知，防烧穿剂优选长链线性饱和羧酸盐。
表3：对比例1-8 PC/ABS合金各组分（重量份）及测试结果
| 对比例1 | 对比例2 | 对比例3 | 对比例4 | 对比例5 | 对比例6 | 对比例7 | 对比例8 | |
| PC-1 | 70 | 70 | 70 | 70 | 70 | 70 | 70 | 70 |
| ABS-1 | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
| 双酚A-双（二苯基磷酸酯） | 12 | 12 | 12 | 12 | 12 | 12 | 12 | |
| 抗紫外线剂A | 0.8 | 0.8 | 0.8 | 0.1 | 1.8 | |||
| 抗紫外线剂E | 0.8 | |||||||
| 抗紫外线剂F | 0.8 | |||||||
| 焦磷酸二氢二钠 | 0.4 | 0.4 | 0.16 | 0.56 | 0.4 | 0.4 | 0.4 | 0.4 |
| UL94-5VA样条/2.5mm | 6 | 5 | 4 | 4 | 4 | 3 | 4 | 4 |
| UL94-5VA样板/2.5mm | 4 | 4 | 3 | 5 | 4 | 3 | 3 | 4 |
由对比例1/2可知，其它种类的抗紫外线剂无法实现协同防烧穿剂改变体系分解历程、促进成炭、热量隔绝的效果，因此防烧穿性能差。
由对比例3/4可知，防烧穿剂含量过高或过低会导致防烧穿性不足。
由对比例5/6可知，抗紫外线剂/阻燃剂的存在是实现防烧穿的必要技术特征之一。
由对比例7/8可知，抗紫外线剂含量过高或过低也会导致防烧穿性不足。
表4：对比例9-11 PC/ABS合金各组分（重量份）及测试结果
| 对比例9 | 对比例10 | 对比例11 | |
| PC-1 | 70 | 70 | 70 |
| ABS-1 | 10 | 10 | 10 |
| 双酚A-双（二苯基磷酸酯） | 12 | 12 | 12 |
| 抗紫外线剂A | 0.8 | 0.8 | 0.8 |
| 硬脂酸锌 | 0.4 | ||
| 硬脂酸钙 | 0.4 | ||
| 硬脂酸镁 | 0.4 | ||
| UL94-5VA样条/2.5mm | 5 | 5 | 5 |
| UL94-5VA样板/2.5mm | 4 | 5 | 4 |
由对比例9-11可知，本领域常用的含金属离子润滑剂无法实现本发明的技术效果。
Claims (10)
1.一种PC/ABS合金，其特征在于，按重量份计，包括以下组分：
PC树脂 60-95份；
ABS树脂 5-20份；
阻燃剂 5-20份；
抗紫外线剂 0.3-1.5份；
防烧穿剂 抗紫外线剂重量份的30-60%；
所述的防烧穿剂选自长链线性饱和羧酸盐、焦磷酸二氢二钠、三聚磷酸钠、六偏磷酸钠、磷酸二氢钠、磷酸二氢铵、磷酸二辛脂、亚磷酸三苯酯、磷酸二异辛酯中的至少一种，所述的长链线性饱和羧酸盐为碳链长度为C28-C32的线性饱和羧酸盐，所述的碳链长度为C28-C32的线性饱和羧酸盐选自碳链长C28-C32的钠盐、碳链长C28-C32的钙盐、碳链长C28-C32的镁盐、碳链长C28-C32的锌盐中的至少一种；
所述的抗紫外线剂选自苯并三唑类抗紫外线剂、受阻胺类抗紫外线剂、三嗪类抗紫外线剂中的至少一种。
2.根据权利要求1所述的PC/ABS合金，其特征在于，抗紫外线剂含量为0.6-0.9份。
3.根据权利要求1所述的PC/ABS合金，其特征在于，所述的抗紫外线剂选自三嗪类抗紫外线剂。
4.根据权利要求1所述的PC/ABS合金，其特征在于，所述的防烧穿剂选自长链线性饱和羧酸盐、焦磷酸二氢二钠、三聚磷酸钠、六偏磷酸钠、磷酸二氢钠、磷酸二氢铵中的至少一种。
5.根据权利要求1所述的PC/ABS合金，其特征在于，所述的防烧穿剂选自长链线性饱和羧酸盐。
6.根据权利要求1所述的PC/ABS合金，其特征在于，所述的PC树脂选自双酚A型聚碳酸酯，熔融指数在3-22g/10min之间，测试条件为300℃，1.2kg；所述的ABS树脂的熔融指数在7-42g/10min之间，测试条件为220℃，10kg。
7.根据权利要求1所述的PC/ABS合金，其特征在于，所述的阻燃剂选自磷系阻燃剂；所述的磷系阻燃剂选自磷酸三苯酯、双酚A-双（二苯基磷酸酯）、间苯二酚双（二苯基磷酸酯）、苯氧基聚磷腈中的至少一种。
8.根据权利要求1所述的PC/ABS合金，其特征在于，按重量份计，还包括0-2份助剂；所述的助剂选自抗氧剂、润滑剂中的至少一种。
9.根据权利要求1-8任一项所述的PC/ABS合金的制备方法，其特征在于，包括以下步骤：将ABS树脂、PC树脂、抗紫外线剂、防烧穿剂、阻燃剂混合均匀，通过双螺杆挤出机挤出造粒，得到PC/ABS合金。
10.根据权利要求1-8任一项所述的PC/ABS合金的应用，其特征在于，用于制备电器电控盒、逆变器、电器开关。