CN115538189A - 一种高耐磨pvc人造革后处理方法及pvc人造革 - Google Patents

一种高耐磨pvc人造革后处理方法及pvc人造革 Download PDF

Info

Publication number
CN115538189A
CN115538189A CN202211335701.1A CN202211335701A CN115538189A CN 115538189 A CN115538189 A CN 115538189A CN 202211335701 A CN202211335701 A CN 202211335701A CN 115538189 A CN115538189 A CN 115538189A
Authority
CN
China
Prior art keywords
artificial leather
pvc artificial
parts
pvc
post
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202211335701.1A
Other languages
English (en)
Inventor
戴锦煌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jinduoli Plastic Co ltd Huiyang District Huizhou City
Original Assignee
Jinduoli Plastic Co ltd Huiyang District Huizhou City
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jinduoli Plastic Co ltd Huiyang District Huizhou City filed Critical Jinduoli Plastic Co ltd Huiyang District Huizhou City
Priority to CN202211335701.1A priority Critical patent/CN115538189A/zh
Publication of CN115538189A publication Critical patent/CN115538189A/zh
Pending legal-status Critical Current

Abstract

本发明涉及PVC处理技术领域，尤其是一种高耐磨PVC人造革后处理方法，包括如下步骤：S1、表面清洁，选取需处理的PVC人造革，利用蘸有清洁剂的清洁布对其表面进行清洁，清洁完成后室温放置待其表面干燥；S2、面层处理，取拿上述处理后的PVC人造革，在其表面涂覆一抗菌层，涂覆完成后进行烘干，所述抗菌层包括0.5％‑1.5％的无机抗菌剂和98％‑99％的耐水改性PVA乳液组成；本发明中通过设置在PVC人造革上再依次设置抗菌层、耐磨层及防护层以增强PVC人造革的各项性能，能够极大的提升PVC人造革在实际使用过程中的耐用能力，在本发明中由于设置有杀菌层，其使用起来更加安全，有效的表面细菌的滋生，保证了用户的使用环境。

Description

一种高耐磨PVC人造革后处理方法及PVC人造革
技术领域
本发明涉及PVC处理技术领域，尤其涉及一种高耐磨PVC人造革后处理方法及PVC人造革。
背景技术
pvc革是在织物上涂覆PVC树脂、增塑剂、稳定剂等助剂制成的糊.或者再覆合一层PVC膜，然后经一定的工艺过程加工制成的。制品强度高，加工容易，成本低廉。可做各种箱包、座套、衬里、杂物等。但耐油性、耐高温性差，低温柔软性和手感较差，人造革可以分为许多种类，随着科技的不断发展，人们对于人造革的制造工艺要求也越来越高。
PVC人造革在加工完成后一般需要对其进行后处理，以便增强其各项性能，但是现有的后处理方式较为单一，因此实现的效果不佳，实用性不强，值得继续提出改进。
发明内容
本发明的目的是为了解决现有技术中存在上述缺点，而提出的一种高耐磨PVC人造革后处理方法及PVC人造革。
为了实现上述目的，本发明采用了如下技术方案：
设计一种高耐磨PVC人造革后处理方法，包括如下步骤：
S1、表面清洁，选取需处理的PVC人造革，利用蘸有清洁剂的清洁布对其表面进行清洁，清洁完成后室温放置待其表面干燥；
S2、面层处理，取拿上述处理后的PVC人造革，在其表面涂覆一抗菌层，涂覆完成后进行烘干，所述抗菌层包括0.5％-1.5％的无机抗菌剂和98％-99％的耐水改性PVA乳液组成；
S3、耐磨层制备，对面层处理后的PVC人造革涂覆一层耐磨层，所述耐磨层由PVC树脂80份、增塑剂8-30份、稳定剂2-12份、抗氧剂2-10份、纳米材料2-10份组成。
优选的，所述S1步骤中室温放置的时间为30min。
优选的，所述S2步骤中无机抗菌剂为银基、锌基、钛基抗菌剂中的一种或多种。
优选的，所述S2中抗菌层包括1％的无机抗菌剂和98.5％的耐水改性PVA乳液组成。
优选的，所述S3中耐磨层由PVC树脂80份、增塑剂19份、稳定剂7份、抗氧剂6份、纳米材料6份组成。
优选的，还包括防滑层，所述防滑层由带颗粒乳胶喷涂于耐磨层上形成。
本发明还提出了一种PVC人造革，所述PVC人造革通过上述的后处理方法进行后处理得到。
本发明提出的一种高耐磨PVC人造革后处理方法及PVC人造革，有益效果在于：本发明中通过设置在PVC人造革上再依次设置抗菌层、耐磨层及防护层以增强PVC人造革的各项性能，能够极大的提升PVC人造革在实际使用过程中的耐用能力，其次，在本发明中由于设置有杀菌层，其使用起来更加安全，有效的表面细菌的滋生，保证了用户的使用环境，整体加工流程简单，容易操作且安全环保。
具体实施方式
下面将结合本发明实施例中，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。
实施例一
一种高耐磨PVC人造革后处理方法，包括如下步骤：
S1、表面清洁，选取需处理的PVC人造革，利用蘸有清洁剂的清洁布对其表面进行清洁，清洁完成后室温放置待其表面干燥，其中，本实施例中室温放置的时间为30min；
S2、面层处理，取拿上述处理后的PVC人造革，在其表面涂覆一抗菌层，涂覆完成后进行烘干，抗菌层包括0.5％的无机抗菌剂和98％的耐水改性PVA乳液组成，本实施例中无机抗菌剂为银基、锌基、钛基抗菌剂中的一种或多种，本领域技术人员能够根据实际的使用需求进行选用；
S3、耐磨层制备，对面层处理后的PVC人造革涂覆一层耐磨层，耐磨层由PVC树脂80份、增塑剂8份、稳定剂2份、抗氧剂2-10份、纳米材料2份组成。
进一步来说，在本发明中还包括防滑层，防滑层由带颗粒乳胶喷涂于耐磨层上形成，通过设置的防滑层不仅能够进一步增强PVC人造革表面的耐磨性，且能够增强PVC人造革的表面的防滑性能。
本发明中还提出了一种PVC人造革，其是由上述的后处理方法进行后处理得到。
实施例二
本实施例与实施例一的区别在于，本实施例中S2步骤中抗菌层包括1％的无机抗菌剂和98.5％的耐水改性PVA乳液组成；
S3步骤中耐磨层由PVC树脂80份、增塑剂19份、稳定剂7份、抗氧剂6份、纳米材料6份组成。
实施例三
在本实施中S2步骤中抗菌层包括1.5％的无机抗菌剂和99％的耐水改性PVA乳液组成；而S3步骤中耐磨层由PVC树脂80份、增塑剂30份、稳定剂12份、抗氧剂10份、纳米材料10份组成。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (7)

1.一种高耐磨PVC人造革后处理方法，其特征在于，包括如下步骤：
S1、表面清洁，选取需处理的PVC人造革，利用蘸有清洁剂的清洁布对其表面进行清洁，清洁完成后室温放置待其表面干燥；
S2、面层处理，取拿上述处理后的PVC人造革，在其表面涂覆一抗菌层，涂覆完成后进行烘干，所述抗菌层包括0.5％-1.5％的无机抗菌剂和98％-99％的耐水改性PVA乳液组成；
S3、耐磨层制备，对面层处理后的PVC人造革涂覆一层耐磨层，所述耐磨层由PVC树脂80份、增塑剂8-30份、稳定剂2-12份、抗氧剂2-10份、纳米材料2-10份组成。
2.根据权利要求1所述的一种高耐磨PVC人造革后处理方法，其特征在于：所述S1步骤中室温放置的时间为30min。
3.根据权利要求1所述的一种高耐磨PVC人造革后处理方法，其特征在于：所述S2步骤中无机抗菌剂为银基、锌基、钛基抗菌剂中的一种或多种。
4.根据权利要求1所述的一种高耐磨PVC人造革后处理方法，其特征在于：所述S2中抗菌层包括1％的无机抗菌剂和98.5％的耐水改性PVA乳液组成。
5.根据权利要求1所述的一种高耐磨PVC人造革后处理方法，其特征在于：所述S3中耐磨层由PVC树脂80份、增塑剂19份、稳定剂7份、抗氧剂6份、纳米材料6份组成。
6.根据权利要求1所述的一种高耐磨PVC人造革后处理方法，其特征在于：还包括防滑层，所述防滑层由带颗粒乳胶喷涂于耐磨层上形成。
7.根据权利要求1所述的一种PVC人造革，其特征在于：所述PVC人造革通过权利要求1-6任一项所述的后处理方法进行后处理得到。
CN202211335701.1A 2022-10-28 2022-10-28 一种高耐磨pvc人造革后处理方法及pvc人造革 Pending CN115538189A (zh)