CN115304364A - 一种热疗仪用手柄按摩头材料及其制备方法 - Google Patents
一种热疗仪用手柄按摩头材料及其制备方法 Download PDFInfo
- Publication number
- CN115304364A CN115304364A CN202210678650.6A CN202210678650A CN115304364A CN 115304364 A CN115304364 A CN 115304364A CN 202210678650 A CN202210678650 A CN 202210678650A CN 115304364 A CN115304364 A CN 115304364A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- mixed ore
- ore powder
- copolyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种热疗仪用手柄按摩头材料及其制备方法，热疗仪用手柄按摩头材料的原料包括混合矿石粉末，混合矿石粉末以下重量份的组分：红石粉末10‑12重量份、蛇纹石粉末10‑12重量份、金刚药石粉末20‑23重量份、碧玺粉末20‑23重量份、海蓝宝石粉末7‑10重量份、水晶粉末7‑10重量份、饭麦石18‑20重量份。本申请的热疗仪用手柄按摩头材料用于热疗，本申请的热疗仪用手柄按摩头材料可释放出的远红外线对身体有保健作用。
Description
技术领域
本申请涉及热疗领域，尤其涉及一种热疗仪用手柄按摩头材料及其制备方法。
背景技术
运用温热能量来治疗疾病,已被记录在几千年以来的历史。希腊民族更是用所谓的”发烧疗法”来助于疾病的复原效率。韩国人早在600年前就会利用岩石板、砂石加热后,让人体躺在石板上,透过岩石板的热能渗透人体。热疗又称为热灸疗法,血管遇热即扩张,遇泠则收缩；血见热则行,遇泠则凝。运用温热功效进行保健与调理,是人类最原始的方法。古代中医将这种温热功效加以应用,发展成为中医的热灸疗法。几千年来,这种中医的古老医术,在民间流传延续至今。
回溯人类文明,曾经为了许多目的而使用各种水晶矿石。古代亚特兰提斯(Atlantis)的先进民族使用水晶去传导与利用宇宙能量。他们也运用水晶结晶的原理建造金字塔,金字塔的完美几何形体,乃复制着水晶的物理原理,将宇宙能量的较高频率传导至这个星球上。
圣经出埃及记中记载:将十二种宝石以特定的方式排成四行,组合在一起后做成胸牌,让亚伦戴在胸前,将赋予亚伦神奇的力量。
发明内容
本申请提供一种热疗仪用手柄按摩头材料及其制备方法，能够用于热疗。
本申请提供了一种热疗仪用手柄按摩头材料，热疗仪用手柄按摩头材料的原料包括混合矿石粉末，混合矿石粉末以下重量份的组分：红石粉末10-12重量份、蛇纹石粉末10-12重量份、金刚药石粉末20-23重量份、碧玺粉末20-23 重量份、海蓝宝石粉末7-10重量份、水晶粉末7-10重量份、饭麦石18-20重量份。
进一步地，混合矿石粉末为经过煅烧的粉末。
进一步地，混合矿石粉末为纳米级粉末。
进一步地，原料还包括三苯甲烷共聚酯(tritan)，三苯甲烷共聚酯(tritan) 与混合矿石粉末和水按照质量比为1:1混合得到的浆料的质量比为100:5。
本申请还提供了一种上述热疗仪用手柄按摩头材料的制备方法，包括以下步骤：将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石制成混合矿石粉末。采用X射线荧光分析确认所述混合矿石粉末的组成成分，并除去混合矿石粉末中的有害成分。将已除去有害成分的混合矿石粉末和三苯甲烷共聚酯(tritan)熔融、固化，得到热疗仪用手柄按摩头材料。
进一步地，将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石制成混合矿石粉末，包括：将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石扎成直径为10-20cm的碎石，再研磨成粒径为0.15mm的粉体，接着加工至纳米级，得到混合矿石粉末。
进一步地，在研磨成粒径为0.15mm的粉体之后，先将粉体煅烧，煅烧的条件为：以3℃/min的速度升温至1250℃后保持30-40min，再将经过煅烧的粉体加工至纳米级。
进一步地，将已除去有害成分的混合矿石粉末和三苯甲烷共聚酯(tritan) 熔融、固化，得到热疗仪用手柄按摩头材料，包括：将已除去有害成分的混合矿石粉末和水混合，得到浆料。将浆料和三苯甲烷共聚酯(tritan)混合、熔喷，然后装入模型固化，得到热疗仪用手柄按摩头材料。
进一步地，将已除去有害成分的混合矿石粉末和水混合，得到浆料，包括：将已除去有害成分的混合矿石粉末和水按照质量比为1:1混合均匀，接着过筛，得到浆料。
进一步地，在将浆料和三苯甲烷共聚酯(tritan)混合的过程中，浆料与三苯甲烷共聚酯(tritan)的质量比为5:100。
与现有技术相比，本申请具有如下有益效果：
本申请的热疗仪用手柄按摩头材料用于热疗，本申请的热疗仪用手柄按摩头材料可释放出的远红外线对身体有保健作用。
具体实施方式
下面将对本申请实施例中的技术方法进行清晰、完整地描述。显然，所描述的实施例仅仅是本申请一部分实施例，而不是全部的实施例。基于本申请中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本申请保护的范围。
本申请提供了一种热疗仪用手柄按摩头材料，热疗仪用手柄按摩头材料的原料包括混合矿石粉末，混合矿石粉末以下重量份的组分：红石粉末10-12重量份(如10重量份、11重量份、12重量份)、蛇纹石粉末10-12重量份(如 10重量份、11重量份、12重量份)、金刚药石粉末20-23重量份(如20重量份、21重量份、23重量份)、碧玺粉末20-23重量份(如20重量份、21重量份、23重量份)、海蓝宝石粉末7-10重量份(如7重量份、9重量份、10重量份)、水晶粉末7-10重量份(如7重量份、9重量份、10重量份)、饭麦石 18-20重量份(如18重量份、19重量份、20重量份)。
其中，红石具体为印度红石，含SiO2、Al2O3、K2O、Na2O等，远红外线波长0.95。
蛇纹石含SiO2、MgO、Fe2O3、CaO等，远红外线波长0.98。
金刚药石具体为朝鲜金刚药石，其含健康的Fe、Zn、Mn、Cu、Co等微量元素，可促进血液循环与有机体的成长。含Cu、Zn、Mo、I等元素，可加强抵抗力与免疫力。
碧玺具体为巴西碧玺(电气石)，是含多种元素的自然矿物，主要成份是 SiO2、TiO2、CaO、K2O、LiO、Al2O3、B2O3、MgO、Na2O、Fe2O3、FeO、MnO、 P2O5。它的表面流动着与人体生物电基本吻合的0.06ma微电流，可以平衡人体的生物电，让病理电位恢复正常。它被誉为天然的太阳能电池，可吸收储存太阳的光能，形成能量场，为人体细胞提供氧气和能量。它是一种结构特殊的结晶体，自身能产生负离子和远红外线。
海蓝宝石的分子式为Be3Al2[Si6O18]，含微量的二价铁离子(Fe2+)，化学成分为三氧化二铝(Al2O3)，含微量元素钛(Ti4+)。它具有滋补作用，能强化身体，净化身体的器官。
水晶的矿物名称为石英，其化学成分为二氧化硅(SiO2)。它有很强的净化作用。将混浊的宝石放置于水晶柱洞中一天，隔日便能蜕变成清澈的宝石。
混合矿石粉末为经过煅烧的粉末。
混合矿石粉末为纳米级粉末。
原料还包括三苯甲烷共聚酯(tritan)，三苯甲烷共聚酯(tritan)与混合矿石粉末和水按照质量比为1:1混合得到的浆料的质量比为100:5。
本申请还提供了一种上述热疗仪用手柄按摩头材料的制备方法，包括以下步骤：
步骤一、将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石制成混合矿石粉末。
上述步骤中，将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石通过碎石机扎成直径为10-20cm的碎石，再研磨成粒径为0.15mm的粉体，接着加工至纳米级，得到混合矿石粉末。
进一步地，在研磨成粒径为0.15mm的粉体之后，先将粉体煅烧，煅烧的条件为：以3℃/min的速度升温至1250℃后保持30-40min，再将经过煅烧的粉体加工至纳米级。
步骤二、采用X射线荧光分析确认所述混合矿石粉末的组成成分，并除去混合矿石粉末中的有害成分。
上述步骤中，用XRF(X射线荧光分析)确认混合矿石粉末的化学元素所占比例，与初步判定是否含有有害重金属。将有害成分萃取出来不用，并且提炼浓缩好的元素出来。
步骤三、将已除去有害成分的混合矿石粉末和三苯甲烷共聚酯(tritan)熔融、固化，得到热疗仪用手柄按摩头材料。
上述步骤包括：将已除去有害成分的混合矿石粉末和水混合，得到浆料。其中，将已除去有害成分的混合矿石粉末和水按照质量比为1:1球磨混合均匀，接着筛网过筛，得到浆料。将浆料和三苯甲烷共聚酯(tritan)搅拌混合、高温熔喷，然后装入模型固化，接着修饰，得到热疗仪用手柄按摩头材料。其中，在将浆料和三苯甲烷共聚酯(tritan)混合的过程中，浆料与三苯甲烷共聚酯 (tritan)的质量比为5:100。
本申请的热疗仪用手柄按摩头材料用于热疗，本申请的热疗仪用手柄按摩头材料可释放出的远红外线对身体有保健作用。
下面结合实施例对本申请的技术方案和有益效果进行详细说明。
实施例1
按照每重量份500g，红石10重量份、蛇纹石10重量份、金刚药石20重量份、碧玺20重量份、海蓝宝石10重量份、水晶10重量份、饭麦石20重量份通过碎石机扎成直径为10-20cm的碎石，再研磨成粒径为0.15mm的粉体，然后将粉体煅烧，煅烧的条件为：以3℃/min的速度升温至1250℃后保持 30-40min，接着将经过煅烧的粉体加工至纳米级，得到混合矿石粉末。
用XRF确认混合矿石粉末的化学元素所占比例，与初步判定是否含有有害重金属。将有害成分萃取出来不用，并且提炼浓缩好的元素出来。
将已除去有害成分的混合矿石粉末和水按照质量比为1:1球磨混合均匀，接着筛网过筛，得到浆料。然后将浆料和三苯甲烷共聚酯(tritan)搅拌混合，浆料与三苯甲烷共聚酯(tritan)的质量比为5:100，接着高温熔喷，再接着装入模型固化，最后修饰，得到热疗仪用手柄按摩头材料。
实施例2
按照每重量份500g，红石12重量份、蛇纹石12重量份、金刚药石23重量份、碧玺23重量份、海蓝宝石7重量份、水晶7重量份、饭麦石18重量份通过碎石机扎成直径为10-20cm的碎石，再研磨成粒径为0.15mm的粉体，然后将粉体煅烧，煅烧的条件为：以3℃/min的速度升温至1250℃后保持 30-40min，接着将经过煅烧的粉体加工至纳米级，得到混合矿石粉末。
用XRF确认混合矿石粉末的化学元素所占比例，与初步判定是否含有有害重金属。将有害成分萃取出来不用，并且提炼浓缩好的元素出来。
将已除去有害成分的混合矿石粉末和水按照质量比为1:1球磨混合均匀，接着筛网过筛，得到浆料。然后将浆料和三苯甲烷共聚酯(tritan)搅拌混合，浆料与三苯甲烷共聚酯(tritan)的质量比为5:100，接着高温熔喷，再接着装入模型固化，最后修饰，得到热疗仪用手柄按摩头材料。
实施例3
按照每重量份500g，红石11重量份、蛇纹石11重量份、金刚药石21重量份、碧玺22重量份、海蓝宝石9重量份、水晶8重量份、饭麦石19重量份通过碎石机扎成直径为10-20cm的碎石，再研磨成粒径为0.15mm的粉体，然后将粉体煅烧，煅烧的条件为：以3℃/min的速度升温至1250℃后保持 30-40min，接着将经过煅烧的粉体加工至纳米级，得到混合矿石粉末。
用XRF确认混合矿石粉末的化学元素所占比例，与初步判定是否含有有害重金属。将有害成分萃取出来不用，并且提炼浓缩好的元素出来。
将已除去有害成分的混合矿石粉末和水按照质量比为1:1球磨混合均匀，接着筛网过筛，得到浆料。然后将浆料和三苯甲烷共聚酯(tritan)搅拌混合，浆料与三苯甲烷共聚酯(tritan)的质量比为5:100，接着高温熔喷，再接着装入模型固化，最后修饰，得到热疗仪用手柄按摩头材料。
试验例
本申请对热疗仪用手柄按摩头材料进行了试验：
试验方法为：测试环境条件为Temp：18℃、RH％：80％，量测波长为8μ m-14μm，测量样品加热温度为60.0℃，量测仪器为Bomem MR104，规范为 ASTM E1933-99a，试验结果表明，热疗仪用手柄按摩头材料的远红外线平均放射率为0.97。
此外，依据指令为：欧盟RoHS指令2011/65/EU及其修订指令(EU) 2015/853，试验结果表明，热疗仪用手柄按摩头材料的检测结果满足欧盟RoHS 指令2011/65/EU及其修订指令(EU)2015/853要求的限值。
以上显示和描述了本申请的基本原理、主要特征和本申请的优点。本行业的技术人员应该了解，本申请不受上述实施例的限制，上述实施例和说明书中描述的只是说明本申请的原理，在不脱离本申请精神和范围的前提下，本申请还会有各种变化和改进，本申请要求保护范围由所附的权利要求书、说明书及其等效物界定。
最后所应当说明的是，以上实施例仅用以说明本申请的技术方案而非对本申请保护范围的限制，尽管参照较佳实施例对本申请作了详细说明，本领域的普通技术人员应当理解，可以对本申请的技术方案进行修改或者等同替换，而不脱离本申请技术方案的实质和范围。
Claims (10)
1.一种热疗仪用手柄按摩头材料，其特征在于，所述热疗仪用手柄按摩头材料的原料包括混合矿石粉末，所述混合矿石粉末以下重量份的组分：
红石粉末10-12重量份；
蛇纹石粉末10-12重量份；
金刚药石粉末20-23重量份；
碧玺粉末20-23重量份；
海蓝宝石粉末7-10重量份；
水晶粉末7-10重量份；
饭麦石18-20重量份。
2.如权利要求1所述的热疗仪用手柄按摩头材料，其特征在于，
所述混合矿石粉末为经过煅烧的粉末。
3.如权利要求1所述的热疗仪用手柄按摩头材料，其特征在于，
所述混合矿石粉末为纳米级粉末。
4.如权利要求1所述的热疗仪用手柄按摩头材料，其特征在于，
所述原料还包括三苯甲烷共聚酯，所述三苯甲烷共聚酯与所述混合矿石粉末和水按照质量比为1:1混合得到的浆料的质量比为100:5。
5.一种权利要求1-4任一所述的热疗仪用手柄按摩头材料的制备方法，其特征在于，包括以下步骤：
将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石制成混合矿石粉末；
采用X射线荧光分析确认所述混合矿石粉末的组成成分，并除去所述混合矿石粉末中的有害成分；
将已除去所述有害成分的所述混合矿石粉末和三苯甲烷共聚酯熔融、固化，得到热疗仪用手柄按摩头材料。
6.如权利要求5所述的制备方法，其特征在于，
将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石制成混合矿石粉末，包括：
将红石、蛇纹石、金刚药石、碧玺、海蓝宝石、水晶和饭麦石扎成直径为10-20cm的碎石，再研磨成粒径为0.15mm的粉体，接着加工至纳米级，得到所述混合矿石粉末。
7.如权利要求6所述的制备方法，其特征在于，
在研磨成粒径为0.15mm的粉体之后，先将所述粉体煅烧，煅烧的条件为：以3℃/min的速度升温至1250℃后保持30-40min，再将经过煅烧的所述粉体加工至纳米级。
8.如权利要求5所述的制备方法，其特征在于，
将已除去所述有害成分的所述混合矿石粉末和三苯甲烷共聚酯熔融、固化，得到热疗仪用手柄按摩头材料，包括：
将已除去所述有害成分的所述混合矿石粉末和水混合，得到浆料；
将所述浆料和三苯甲烷共聚酯混合、熔喷，然后装入模型固化，得到热疗仪用手柄按摩头材料。
9.如权利要求8所述的制备方法，其特征在于，
将已除去所述有害成分的所述混合矿石粉末和水混合，得到浆料，包括：
将已除去所述有害成分的所述混合矿石粉末和水按照质量比为1:1混合均匀，接着过筛，得到所述浆料。
10.如权利要求9所述的制备方法，其特征在于，
在将所述浆料和三苯甲烷共聚酯混合的过程中，所述浆料与所述三苯甲烷共聚酯的质量比为5:100。