CN115287035A - 一种高粘接力预制型跑道胶黏剂 - Google Patents

一种高粘接力预制型跑道胶黏剂 Download PDF

Info

Publication number
CN115287035A
CN115287035A CN202211018027.4A CN202211018027A CN115287035A CN 115287035 A CN115287035 A CN 115287035A CN 202211018027 A CN202211018027 A CN 202211018027A CN 115287035 A CN115287035 A CN 115287035A
Authority
CN
China
Prior art keywords
parts
adhesion
prefabricated runway
runway adhesive
prefabricated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202211018027.4A
Other languages
English (en)
Inventor
全洪晖
吴会歌
全家琦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Tengwei Technology Co ltd
Original Assignee
Guangdong Tengwei Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangdong Tengwei Technology Co ltd filed Critical Guangdong Tengwei Technology Co ltd
Priority to CN202211018027.4A priority Critical patent/CN115287035A/zh
Publication of CN115287035A publication Critical patent/CN115287035A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高粘接力预制型跑道胶黏剂，该高粘接力预制型跑道胶黏剂包括如下质量份的各组分：异氰酸酯基硅烷5份至10份、二聚酸二异氰酸酯3份至6份、聚醚多元醇15份至30份、弹性丙烯酸树脂5份至10份、羟乙基纤维素1份至2份、聚已二酸已二醇酯5份至10份、脂类溶剂20份至30份，余量为水。在其中一个实施例中，所述聚醚多元醇包括如下质量份的各组分：聚氧化丙烯二醇20份至30份、聚氧化丙烯三醇20份至30份、聚四氢呋喃二醇20份至30份、环氧丙烷聚醚三元醇20份至30份。上述高粘接力预制型跑道胶黏剂，粘接力高、耐候性好、稳定性高、柔韧性好，可以将跑道牢固地粘黏到地面上，在长时间的使用工程中也不会出现脱胶起皮的现象。

Description

一种高粘接力预制型跑道胶黏剂
技术领域
本发明涉及涂料领域，特别是涉及一种高粘接力预制型跑道胶黏剂。
背景技术
塑胶跑道又称全天候田径运动跑道。塑胶跑道具有一定的弹性和色彩，具有一定的抗紫外线能力和耐老化力是国际上公认的最佳全天候室外运动场地坪材料。塑胶跑道施工在沥青或水泥基础上，基础做法与道路施工大致相同。基础表面平整度要求较高，以保证塑胶面层厚度一致，弹性均匀。
目前市场上的塑胶跑道分为现浇型和预制型两种。预制型塑胶由于它具有传统预制型塑胶跑道应有的各项使用功能，同时不含橡胶颗粒，无脱粒产生，非常适合频繁使用，安装方便维护简便，维修成本低等特点受到市场的青睐。
传统的预制型塑胶跑道由于聚氨酯胶水与地面的粘合，粘接力不足，在长时间使用的过程中容易脱胶。
发明内容
基于此，有必要提供一种高粘接力预制型跑道胶黏剂。
一种高粘接力预制型跑道胶黏剂，该高粘接力预制型跑道胶黏剂包括如下质量份的各组分：异氰酸酯基硅烷5份至10份、二聚酸二异氰酸酯3份至6份、聚醚多元醇15份至30份、弹性丙烯酸树脂5份至10份、羟乙基纤维素1份至2份、聚已二酸已二醇酯5份至10份、脂类溶剂20份至30份，余量为水。
在其中一个实施例中，所述脂类溶剂包括如下质量份的各组分：乙酸乙酯30份至40份、乙酸丁酯30份至40份、丙酮30份至40份。
在其中一个实施例中，所述聚醚多元醇包括如下质量份的各组分：聚氧化丙烯二醇20份至30份、聚氧化丙烯三醇20份至30份、聚四氢呋喃二醇20份至30份、环氧丙烷聚醚三元醇20份至30份。
在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括抗氧化剂0.01份至0.05份。
在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括分散剂0.3份至0.5份。
在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括紫外线吸收剂0.01份至0.05份。
在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括增稠剂0.1份至0.3份。
在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括防冻剂0.1份至0.5份。
在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括稳定剂0.1份至0.5份。
在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括消泡剂0.1份至0.2份。
上述高粘接力预制型跑道胶黏剂，粘接力高、耐候性好、稳定性高、柔韧性好，可以将跑道牢固地粘黏到地面上，在长时间的使用工程中也不会出现脱胶起皮的现象。
附图说明
图1为一个实施例中高粘接力预制型跑道胶黏剂的组分图。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
一种高粘接力预制型跑道胶黏剂，该高粘接力预制型跑道胶黏剂包括如下质量份的各组分：异氰酸酯基硅烷5份至10份、二聚酸二异氰酸酯3份至6份、聚醚多元醇15份至30份、弹性丙烯酸树脂5份至10份、羟乙基纤维素1份至2份、聚已二酸已二醇酯5份至10份、脂类溶剂20份至30份，余量为水。
上述高粘接力预制型跑道胶黏剂，粘接力高、耐候性好、稳定性高、柔韧性好，可以将跑道牢固地粘黏到地面上，在长时间的使用工程中也不会出现脱胶起皮的现象。
为了溶解高粘接力预制型跑道胶黏剂中的脂类，使得高粘接力预制型跑道胶黏剂中各组分充分混合均匀，在其中一个实施例中，所述脂类溶剂包括如下质量份的各组分：乙酸乙酯30份至40份、乙酸丁酯30份至40份、丙酮30份至40份。乙酸乙酯、乙酸丁酯以及丙酮是良好的脂类溶剂，可以将高粘接力预制型跑道胶黏剂中的脂类成分有效地溶解，从而使得高粘接力预制型跑道胶黏剂中各组分可以充分混合均匀。
为了进一步地提高所述高粘接力预制型跑道胶黏剂的站粘性，在其中一个实施例中，所述聚醚多元醇包括如下质量份的各组分：聚氧化丙烯二醇20份至30份、聚氧化丙烯三醇20份至30份、聚四氢呋喃二醇20份至30份、环氧丙烷聚醚三元醇20份至30份。聚氧化丙烯二醇、聚氧化丙烯三醇、聚四氢呋喃二醇以及环氧丙烷聚醚三元醇可以与异氰酸酯基硅烷以及二聚酸二异氰酸酯进行有效且充分地聚合反应，产生的聚合物提高了所述高粘接力预制型跑道胶黏剂的站粘性。进一步地，所述高粘接力预制型跑道胶黏剂还包括催化剂0.01份至0.05份，具体的催化剂为异辛酸锌，以促进聚合反应的高效进行。
为了增加高粘接力预制型跑道胶黏剂的抗氧化性能，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括抗氧化剂0.01份至0.05份。具体的，抗氧化剂为2-叔丁基-4-甲基苯酚。2-叔丁基-4-甲基苯酚为受阻酚类抗氧剂，可以有效地提高上述高粘接力预制型跑道胶黏剂的抗氧化性能。
为了提高高粘接力预制型跑道胶黏剂各组分混合地均匀性，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括分散剂0.3份至0. 5份。具体的，分散剂为丙烯酸酯共聚物，丙烯酸酯共聚物可以使得高粘接力预制型跑道胶黏剂各组分充分地分散开来，从而提高了高粘接力预制型跑道胶黏剂各组分混合地均匀性，以增加高粘接力预制型跑道胶黏剂的稳定性。
为了增加高粘接力预制型跑道胶黏剂的抗紫外线性能，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括紫外线吸收剂0.01份至0.05份。具体的，紫外线吸收剂包括如下质量份的各组分：2-羟基-4-N-辛氧基二苯甲酮40份至60份和2-羟基-4-甲氧基-二苯甲酮40份至60份。紫外线吸收剂提高了高粘接力预制型跑道胶黏剂的抗紫外线性能，从而增加高粘接力预制型跑道胶黏剂的耐候性。
为了增加高粘接力预制型跑道胶黏剂的粘性，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括增稠剂0.1份至0. 3份。具体的，增稠剂包括如下质量份的各组分：丙二醇藻蛋白酸酯30份至40份和甲基纤维素30份至40份、聚丙烯酸钠30份至40份。增稠剂增加了高粘接力预制型跑道胶黏剂的粘性，提高了高粘接力预制型跑道胶黏剂与地面的结合力。
为了增加高粘接力预制型跑道胶黏剂的抗低温性能，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括防冻剂0.1份至0.5份。防冻剂包括如下质量份的各组分：亚硝酸钠30份至40份、氯化钙30份至40份以及亚硝酸钙30份至40份。防冻剂增加了高粘接力预制型跑道胶黏剂的抗低温性能。
为了增加高粘接力预制型跑道胶黏剂的稳定性，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括稳定剂0.1份至0.5份。具体的，稳定剂为磷酸二异辛酯。磷酸二异辛酯可以有效地增加高粘接力预制型跑道胶黏剂的稳定性。
为了避免高粘接力预制型跑道胶黏剂在生产和使用过程中产生大量气泡，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括消泡剂0.1份至0.2份。具体的，消泡剂为有机硅消泡剂。有机硅消泡剂可以有效地避免高粘接力预制型跑道胶黏剂在生产和使用过程中产生大量气泡。
为了增加高粘接力预制型跑道胶黏剂的防沉性，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括防沉剂0.1份至0.2份。具体的，防沉剂为气相二氧化硅。气相二氧化硅可以有效地增加高粘接力预制型跑道胶黏剂的防沉性，提高所述高粘接力预制型跑道胶黏剂的粘附性和附着力。
为了增加高粘接力预制型跑道胶黏剂的耐磨性能，在其中一个实施例中，所述高粘接力预制型跑道胶黏剂还包括白炭黑0.1份至0.2份。具体的，白炭黑可以有效地增加高粘接力预制型跑道胶黏剂的粘度和耐磨性能。
对高粘接力预制型跑道胶黏剂下20摄氏度至60摄氏度的温度下，凝结70天后，进行试验结果如下表所示：
Figure 913932DEST_PATH_IMAGE001
根据上述测试结果可知，高粘接力预制型跑道胶黏剂的性能优异，可以满足跑道的高稳定性粘接需求。
以上实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。

Claims (10)

1.一种高粘接力预制型跑道胶黏剂，其特征在于，包括如下质量份的各组分：异氰酸酯基硅烷5份至10份、二聚酸二异氰酸酯3份至6份、聚醚多元醇15份至30份、弹性丙烯酸树脂5份至10份、羟乙基纤维素1份至2份、聚已二酸已二醇酯5份至10份、脂类溶剂20份至30份，余量为水。
2.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述脂类溶剂包括如下质量份的各组分：乙酸乙酯30份至40份、乙酸丁酯30份至40份、丙酮30份至40份。
3.根据权利要求2所述的高粘接力预制型跑道胶黏剂，其特征在于，所述聚醚多元醇包括如下质量份的各组分：聚氧化丙烯二醇20份至30份、聚氧化丙烯三醇20份至30份、聚四氢呋喃二醇20份至30份、环氧丙烷聚醚三元醇20份至30份。
4.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述高粘接力预制型跑道胶黏剂还包括抗氧化剂0.01份至0.05份。
5.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述高粘接力预制型跑道胶黏剂还包括分散剂0.3份至0. 5份。
6.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述高粘接力预制型跑道胶黏剂还包括紫外线吸收剂0.01份至0.05份。
7.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述高粘接力预制型跑道胶黏剂还包括增稠剂0.1份至0. 3份。
8.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述高粘接力预制型跑道胶黏剂还包括防冻剂0.1份至0.5份。
9.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述高粘接力预制型跑道胶黏剂还包括稳定剂0.1份至0.5份。
10.根据权利要求1所述的高粘接力预制型跑道胶黏剂，其特征在于，所述高粘接力预制型跑道胶黏剂还包括消泡剂0.1份至0.2份。
CN202211018027.4A 2022-08-24 2022-08-24 一种高粘接力预制型跑道胶黏剂 Pending CN115287035A (zh)