CN104694066A - 一种epdm颗粒专用粘合剂的制法和epdm颗粒球场的施工工艺 - Google Patents
一种epdm颗粒专用粘合剂的制法和epdm颗粒球场的施工工艺 Download PDFInfo
- Publication number
- CN104694066A CN104694066A CN201510081818.5A CN201510081818A CN104694066A CN 104694066 A CN104694066 A CN 104694066A CN 201510081818 A CN201510081818 A CN 201510081818A CN 104694066 A CN104694066 A CN 104694066A
- Authority
- CN
- China
- Prior art keywords
- epdm
- epdm particle
- polyether glycol
- adhesive specially
- making
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种EPDM颗粒专用粘合剂的制法及其施工工艺,属于体育设施材料领域,制法包括如下步骤:将30-50份聚醚多元醇,加温到100-120℃,真空度-0.095Mpa以下,脱水脱气0.5-1.5小时,水分含量≤0.05%以下;降温到40-60℃,加入15-30份二异氰酸酯、10-20份石蜡,升温至75-85℃,搅拌1.5-2.5小时;加入10-20份丙烯酸树脂、0.5-1份抗老化剂,温度在75-85℃,继续搅拌1-2小时;停止搅拌,真空度-0.095Mpa以下,脱水脱气0.5-1小时,即得此料。与传统常温粘合剂相比,实现在常温常压条件下球场的铺设,有着更高的性价比、更好的性能指标。
Description
技术领域
本发明涉及一种EPDM颗粒专用粘合剂的制法和EPDM颗粒球场的施工工艺,属于体育设施材料领域。
背景技术
EPDM球场由高强度、高弹性、强抗紫外线的EPDM颗粒拌合一定比例的粘合剂,在混凝土或沥青基础上直接摊铺、压实而成。具有长时间的使用寿命,弹性程度及动力学设计特征。是PU球场的替代产品,具有施工方便,对基础适应能力强,不易起皮、起泡等优点。
传统常温胶黏剂耐候性不佳,易黄变,易褪色。EPDM颗粒专用粘合剂属于浇注型聚氨酯弹性体的一种,广泛用于铺设各类体育运动球场场地,是目前国际上公认的运动场地的铺装材料。
聚氨酯胶粘剂是指在分子链中含有氨基甲酸酯基团(-NHCOO-)或异氰酸酯基(-NCO)的胶粘剂。聚氨酯胶粘剂按使用方式可分为单组份聚氨酯胶黏剂和双组份聚氨酯胶黏剂。聚氨酯胶黏剂本身具有较强的活性,因此对各种材料具有良好的粘接性能,对金属、大理石、陶瓷、玻璃、水泥制品、木材及大多数的塑料制品均有良好的粘接性和密封性。这也使得其广泛应用于各个领域。
发明内容
本发明目的之一是提供一种EPDM颗粒专用粘合剂的制法,用来代替传统常温粘合剂,实现在常温常压条件下球场的铺设,有着更高的性价比、更好的性能指标。
本发明另一个目的是提供一种EPDM颗粒球场的施工工艺。
本发明采用的具体技术方案是:
一种EPDM颗粒专用粘合剂的制法,包括如下步骤:
(1)加入30-50份聚醚多元醇,其水分含量≤0.05%;
(2)降温到40-60,℃加入15-30份二异氰酸酯、10-20份石蜡,升温至75-85℃,搅拌反应1.5-2.5小时;
(3)加入10-20份丙烯酸树脂、0.5-1份抗老化剂,温度在75-85,℃继续反应搅拌均匀1-2小时;
(4)停止搅拌,真空度-0.095Mpa以下,脱水脱气0.5-1小时,即得此料。
其中,所述的聚醚多元醇需要加温到100-120,℃真空度在-0.095Mpa以下,脱水脱气0.5-1.5小时,使其水分含量≤0.05%。
所述的聚醚多元醇优选分子量为3000、官能度为三的聚醚多元醇和分子量为3000、官能度为二的聚醚多元醇以任意比例混合。
其中,所述的丙烯酸树脂固含量为79%-81%。
所述的抗老化剂是抗氧剂和紫外线吸收剂按重量比1:1的混合物,所述的抗氧剂是季戊四醇酯,所述的紫外线吸收剂是二苯甲酮。
所述的二异氰酸酯为芳香族二异氰酸酯。
一种6mm纯EPDM颗粒球场的施工工艺,包括如下步骤:
(1)在基底上滚涂防水底漆;
(2)用EPDM颗粒专用粘合剂:EPDM颗粒重量比为1:5~6,搅拌均匀一次摊铺6mm。
一种6mm复合EPDM颗粒球场的施工工艺,包括如下步骤:
(1)在基底上滚涂防水底漆;
(2)用单组份粘合剂:黑色颗粒重量比为1:8,搅拌均匀摊铺4mm底层;
(3)用EPDM颗粒专用粘合剂:EPDM颗粒重量比为1:5~6,搅拌均匀一次摊铺2mm。
上述施工工艺中,除EPDM颗粒专用粘合剂外,其他原料均为现有技术的商品,在市场上很容易获得。
与现有技术相比,本发明的有益效果是:
(1)本发明中丙烯酸树脂的分子结构对光的吸收主峰处于太阳光范围之外,具有优异的耐黄变性和户外抗老化性,价格与聚醚多元醇相当,丙烯酸树脂在本发明中的使用,在成本一致的前提下提高了整个体系的耐黄变性和耐候性,尤其适用于多彩的EPDM颗粒。
(2)本发明中聚醚多元醇以官能度二和官能度三的分子量3000的聚醚多元醇按一定比例的混合使用,可以得到更好的拉伸强度和更高的断裂延伸率,更优异的保色率和高耐候性,更高的性价比和可实用性。
(3)本发明的产品生产工艺简单与常规粘合剂的生产工艺相同,所用原料均为市售商品,原料易得,操作简单,便于施工。
(4)本发明加入抗氧剂和紫外吸收剂,有良好的防止光和热引起的色变作用,继而塑胶不易褪色,不易老化,耐候性得以加强,延长了使用寿命。
(5)本发明应用于聚氨酯塑胶球场施工体系中,可实现EPDM颗粒球场的多彩化,场地拥有更高的耐候性和更好的保色率,更加有效保护运动者的运动健康和提升运动的愉悦感。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例1-4:配方(单位:Kg)
其中,聚醚多元醇是分子量为3000、官能度为三的聚醚多元醇和分子量为3000、官能度为二的聚醚多元醇以任意比例的混合物。
二苯基甲烷二异氰酸酯为环保型的二异氰酸酯。为万华化学集团股份有限公司所产的(商品牌号是:MDI-50)或德国巴斯夫集团所产的商品(牌号是:Mr),为市售商品。
其中,所选用的抗氧剂1010即为季戊四醇酯;二苯甲酮是紫外线吸收剂;所述的丙烯酸树脂固含量为79%-81%。
实施例5:最优实施例
一种EPDM颗粒专用粘合剂的制法,包括如下步骤:
(1)加入45份聚醚多元醇,控制其水分含量≤0.05%;
(2)降温到40-60℃,加入25份二异氰酸酯、15份石蜡,升温到75-85,℃搅拌反应1.5-2.5小时;
(3)加入14份树脂、1份抗老化剂,搅拌均匀,继续搅拌反应1-2小时;
(4)停止搅拌,真空度在-0.095Mpa以下脱水脱气0.5-1小时,即得此料。
Claims (8)
1.一种EPDM颗粒专用粘合剂的制法,其特征是,包括如下步骤:
(1)加入30-50份聚醚多元醇,其水分含量≤0.05%;
(2)降温到40-60℃,加入15-30份二异氰酸酯、10-20份石蜡,升温至75-85℃,搅拌反应1.5-2.5小时;
(3)加入10-20份丙烯酸树脂、0.5-1份抗老化剂,温度在75-85℃,继续反应搅拌均匀1-2小时;
(4)停止搅拌,真空度-0.095Mpa以下,脱水脱气0.5-1小时,即得EPDM颗粒专用粘合剂。
2.根据权利要求1所述的EPDM颗粒专用粘合剂的制法,其特征是,包括聚醚多元醇脱水步骤,先将所述的聚醚多元醇加热到100-120℃,真空度在-0.095Mpa以下,脱水脱气0.5-1.5小时。
3.根据权利要求1所述的EPDM颗粒专用粘合剂的制法,其特征是,所述的聚醚多元醇由分子量为3000、官能度为三的聚醚多元醇和分子量为3000、官能度为二的聚醚多元醇以任意比例混合。
4.根据权利要求1所述的EPDM颗粒专用粘合剂的制法,其特征是,所述的丙烯酸树脂固含量为79%-81%。
5.根据权利要求1所述的EPDM颗粒专用粘合剂的制法,其特征是,所述的抗老化剂是抗氧剂和紫外线吸收剂按重量比1:1的混合物,所述的抗氧剂是季戊四醇酯,所述的紫外线吸收剂是二苯甲酮。
6.根据权利要求1所述的EPDM颗粒专用粘合剂的制法,其特征是,所述的二异氰酸酯为芳香族二异氰酸酯。
7.一种6mm纯EPDM颗粒球场的施工工艺,其特征在于,包括如下步骤:
(1)在基底上滚涂防水底漆;
(2)用权利要求1的EPDM颗粒专用粘合剂:EPDM颗粒重量比为1:5~6,搅拌均匀一次摊铺6mm。
8.一种6mm复合EPDM颗粒球场的施工工艺,其特征在于,包括如下步骤:
(1)在基底上滚涂防水底漆;
(2)用单组份粘合剂:黑色颗粒重量比为1:8,搅拌均匀摊铺4mm底层;
(3)用权利要求1的EPDM颗粒专用粘合剂:EPDM颗粒重量比为1:5~6,搅拌均匀一次摊铺2mm。