CN115160902A - 一种用于箱涵修复的抗渗防腐修复涂料及其制备方法 - Google Patents
一种用于箱涵修复的抗渗防腐修复涂料及其制备方法 Download PDFInfo
- Publication number
- CN115160902A CN115160902A CN202210816491.1A CN202210816491A CN115160902A CN 115160902 A CN115160902 A CN 115160902A CN 202210816491 A CN202210816491 A CN 202210816491A CN 115160902 A CN115160902 A CN 115160902A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- component
- permeability
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种用于箱涵修复的抗渗防腐修复涂料及其制备方法，抗渗防腐修复涂料由A组分、B组分和C组分组成；A组分包括环氧乙烯基酯树脂、苯乙烯混合物、领苯二甲酸、丙烯酸甲酯、丙二醇、N‑羟甲基丙烯酰胺、新戊二醇、乙酸乙酯、硅烷偶联剂、聚氨酯丙烯酸酯和异氰酸三缩水甘油酯；B组分包括陶瓷微粉、有机酸、玻璃纤维粉、有机膨润土混合物、二氧化硅、颜料、硫酸钡、滑石粉和乙酸乙酯；C组分包括甲基六氢苯酐、双氰胺、三乙醇胺和过氧化物。本发明能达到很好的修复、抗渗、防腐、防水、耐酸碱、抗冻融、耐冲击等性能，同时具有良好的机械稳定性等特点，附着力出色，耐盐雾可达4000H，耐酸碱大于2000H，可适用于低温高湿的施工环境。
Description
技术领域
本发明涉及污水管道维修技术领域，具体涉及一种用于箱涵修复的抗渗防腐修复涂料及其制备方法。
背景技术
城市的污水处理的量很大，尤其是大中型城市，主要干线常常采用箱涵的方式输送污水。市政地下排污管道是维持城市正常运转的重要基础设施，在以往的建设过程中，由于忽略了一般混凝土与污水的匹配性研究。我国修建的大量混凝土排污管道和箱涵在经年累月污水的冲刷及腐蚀介质的作用下，遭到了严重的损伤。特别是当箱涵运行十年，二十年以后，出现了污水箱涵的大面积受腐蚀现象，特别在上部结构，腐蚀更厉害，结构的抗弯刚度和抗弯承载能力，有所削弱。如果不及时处理，会影响箱涵结构安全。
传统的防腐涂料主要有环氧、过氯乙烯、氯化橡胶、丙烯酸防腐油漆、无机防腐油漆、高氯化聚乙烯、氟碳、聚酯材料、聚氨酯材料、醇酸材料，后来又发展到使用水性环氧材料、乙烯基树脂材料、聚脲、陶瓷等材料。目前的防腐涂料一般在使用中都有较大的限制，需要温度＞10℃，湿度＜70％，在低温高湿环境中，成膜效果差或膜易溶解，防腐性能不足。
发明内容
本发明的目的在于克服现有技术的不足，提供一种用于箱涵修复的抗渗防腐修复涂料及其制备方法，通过该抗渗防腐修复涂料可以提高箱涵基体的抗渗、防腐、防水、耐酸碱、抗冻融、耐冲击等性能，使其具有良好的机械稳定性。
本发明的技术方案如下：
一种用于箱涵修复的抗渗防腐修复涂料，该抗渗防腐修复涂料由A组分、B组分和C组分组成；
所述A组分包括环氧乙烯基酯树脂、苯乙烯混合物、领苯二甲酸、丙烯酸甲酯、丙二醇、N-羟甲基丙烯酰胺、新戊二醇、乙酸乙酯、硅烷偶联剂、聚氨酯丙烯酸酯和异氰酸三缩水甘油酯；
所述B组分包括陶瓷微粉、有机酸、玻璃纤维粉、有机膨润土混合物、二氧化硅、颜料、硫酸钡、滑石粉和乙酸乙酯；
所述C组分包括甲基六氢苯酐、双氰胺、三乙醇胺和过氧化物。
所述A组分的百分占比为50％～65％，所述B组分的百分占比为30％～45％，所述C组分的百分占比为1％～5％。
其中，所述A组分包括5～40重量份环氧乙烯基酯树脂、8～17重量份苯乙烯混合物、5～20重量份领苯二甲酸、5～15重量份丙烯酸甲酯、0.5～5重量份丙二醇、0.5～5重量份N-羟甲基丙烯酰胺、1～5重量份新戊二醇、1～10重量份乙酸乙酯、0.5～1重量份硅烷偶联剂、0.5～5重量份聚氨酯丙烯酸酯和0.5～5重量份异氰酸三缩水甘油酯。
其中，所述B组分包括1～8重量份陶瓷微粉、1～5重量份有机酸、1～10重量份玻璃纤维粉、1～5重量份有机膨润土混合物、1～5重量份二氧化硅、5～10重量份颜料、5～10重量份硫酸钡、3～10重量份滑石粉和1～3重量份乙酸乙酯。
其中，所述C组分包括5～10重量份甲基六氢苯酐、3～10重量份双氰胺、1～8重量份三乙醇胺和1～5重量份过氧化物。
一种用于箱涵修复的抗渗防腐修复涂料的制备方法，包括以下步骤：
S1、将5～40重量份环氧乙烯基酯树脂、8～17重量份苯乙烯混合物、5～20重量份领苯二甲酸、5～15重量份丙烯酸甲酯、0.5～5重量份丙二醇、0.5～5重量份N-羟甲基丙烯酰胺、1～5重量份新戊二醇、1～10重量份乙酸乙酯、0.5～1重量份硅烷偶联剂、0.5～5重量份聚氨酯丙烯酸酯和0.5～5重量份异氰酸三缩水甘油酯在150℃下搅拌均匀；
S2、加入1～8重量份陶瓷微粉、1～5重量份有机酸、1～10重量份玻璃纤维粉、1～5重量份有机膨润土混合物、1～5重量份二氧化硅、5～10重量份颜料、5～10重量份硫酸钡、3～10重量份滑石粉和1～3重量份乙酸乙酯，搅拌均匀；
S3、涂装前加入5～10重量份甲基六氢苯酐、3～10重量份双氰胺、1～8重量份三乙醇胺和1～5重量份过氧化物，搅拌均匀。
相对于现有技术，本发明的有益效果在于：本发明在材料组合上结合了环氧、乙烯基涂料的各别优点，A组分含有三聚氰胺酯接支硅烷乙烯基/间苯杂接硅氮長链乙烯基，B组分通过将填料与长链胺基硅烷预处理，C组分形成复合型固化剂。所制成的抗渗防腐修复涂料可适用于低温高湿的施工环境(湿度大于90％，温度大于-10℃的环境)，其基材表面有明水，涂层厚度可超3毫米，且能达到很好的修复、抗渗、防腐、防水、耐酸碱、抗冻融、耐冲击等性能，同时具有良好的机械稳定性等特点，附着力出色(大于2Mpa或基体破坏)，耐盐雾可达4000H，耐酸碱大于2000H等等。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
为了说明本发明所述的技术方案，下面通过具体实施例来进行说明。
实施例一
本实施例提供一种用于箱涵修复的抗渗防腐修复涂料，该抗渗防腐修复涂料由A组分、B组分和C组分组成，A组分的百分占比为50％，B组分的百分占比为45％，C组分的百分占比为5％。
所述A组分包括5重量份环氧乙烯基酯树脂、8重量份苯乙烯混合物、5重量份领苯二甲酸、5重量份丙烯酸甲酯、0.5重量份丙二醇、0.5重量份N-羟甲基丙烯酰胺、1重量份新戊二醇、1重量份乙酸乙酯、0.5重量份硅烷偶联剂、0.5重量份聚氨酯丙烯酸酯和0.5重量份异氰酸三缩水甘油酯。
所述B组分包括8重量份陶瓷微粉、5重量份有机酸、10重量份玻璃纤维粉、5重量份有机膨润土混合物、5重量份二氧化硅、10重量份颜料、10重量份硫酸钡、10重量份滑石粉和3重量份乙酸乙酯。
所述C组分包括10重量份甲基六氢苯酐、10重量份双氰胺、8重量份三乙醇胺和5重量份过氧化物。
该抗渗防腐修复涂料的制备方法包括以下步骤：
S1、将5重量份环氧乙烯基酯树脂、8重量份苯乙烯混合物、5重量份领苯二甲酸、5重量份丙烯酸甲酯、0.5重量份丙二醇、0.5重量份N-羟甲基丙烯酰胺、1重量份新戊二醇、1重量份乙酸乙酯、0.5重量份硅烷偶联剂、0.5重量份聚氨酯丙烯酸酯和0.5重量份异氰酸三缩水甘油酯在150℃下搅拌均匀；
S2、加入8重量份陶瓷微粉、5重量份有机酸、10重量份玻璃纤维粉、5重量份有机膨润土混合物、5重量份二氧化硅、10重量份颜料、10重量份硫酸钡、10重量份滑石粉和3重量份乙酸乙酯，搅拌均匀；
S3、涂装前加入10重量份甲基六氢苯酐、10重量份双氰胺、8重量份三乙醇胺和5重量份过氧化物，搅拌均匀。
实施例二
本实施例提供一种用于箱涵修复的抗渗防腐修复涂料，该抗渗防腐修复涂料由A组分、B组分和C组分组成，A组分的百分占比为58％，B组分的百分占比为38％，C组分的百分占比为4％。
所述A组分包括25重量份环氧乙烯基酯树脂、12重量份苯乙烯混合物、12重量份领苯二甲酸、10重量份丙烯酸甲酯、3重量份丙二醇、3重量份N-羟甲基丙烯酰胺、3重量份新戊二醇、5重量份乙酸乙酯、0.7重量份硅烷偶联剂、3重量份聚氨酯丙烯酸酯和3重量份异氰酸三缩水甘油酯。
所述B组分包括5重量份陶瓷微粉、3重量份有机酸、6重量份玻璃纤维粉、3重量份有机膨润土混合物、3重量份二氧化硅、8重量份颜料、8重量份硫酸钡、7重量份滑石粉和2重量份乙酸乙酯。
所述C组分包括8重量份甲基六氢苯酐、8重量份双氰胺、6重量份三乙醇胺和4重量份过氧化物。
该抗渗防腐修复涂料的制备方法包括以下步骤：
S1、将25重量份环氧乙烯基酯树脂、12重量份苯乙烯混合物、12重量份领苯二甲酸、10重量份丙烯酸甲酯、3重量份丙二醇、3重量份N-羟甲基丙烯酰胺、3重量份新戊二醇、5重量份乙酸乙酯、0.7重量份硅烷偶联剂、3重量份聚氨酯丙烯酸酯和3重量份异氰酸三缩水甘油酯在150℃下搅拌均匀；
S2、加入5重量份陶瓷微粉、3重量份有机酸、6重量份玻璃纤维粉、3重量份有机膨润土混合物、3重量份二氧化硅、8重量份颜料、8重量份硫酸钡、7重量份滑石粉和2重量份乙酸乙酯，搅拌均匀；
S3、涂装前加入8重量份甲基六氢苯酐、8重量份双氰胺、6重量份三乙醇胺和4重量份过氧化物，搅拌均匀。
实施例三
本实施例提供一种用于箱涵修复的抗渗防腐修复涂料，该抗渗防腐修复涂料由A组分、B组分和C组分组成，A组分的百分占比为65％，B组分的百分占比为34％，C组分的百分占比为1％。
所述A组分包括40重量份环氧乙烯基酯树脂、17重量份苯乙烯混合物、20重量份领苯二甲酸、15重量份丙烯酸甲酯、5重量份丙二醇、5重量份N-羟甲基丙烯酰胺、5重量份新戊二醇、10重量份乙酸乙酯、1重量份硅烷偶联剂、5重量份聚氨酯丙烯酸酯和5重量份异氰酸三缩水甘油酯。
所述B组分包括3重量份陶瓷微粉、2重量份有机酸、3重量份玻璃纤维粉、2重量份有机膨润土混合物、2重量份二氧化硅、7重量份颜料、7重量份硫酸钡、5重量份滑石粉和1重量份乙酸乙酯。
所述C组分包括5重量份甲基六氢苯酐、3重量份双氰胺、1重量份三乙醇胺和1重量份过氧化物。
该抗渗防腐修复涂料的制备方法包括以下步骤：
S1、将40重量份环氧乙烯基酯树脂、17重量份苯乙烯混合物、20重量份领苯二甲酸、15重量份丙烯酸甲酯、5重量份丙二醇、5重量份N-羟甲基丙烯酰胺、5重量份新戊二醇、10重量份乙酸乙酯、1重量份硅烷偶联剂、5重量份聚氨酯丙烯酸酯和5重量份异氰酸三缩水甘油酯在150℃下搅拌均匀；
S2、加入3重量份陶瓷微粉、2重量份有机酸、3重量份玻璃纤维粉、2重量份有机膨润土混合物、2重量份二氧化硅、7重量份颜料、7重量份硫酸钡、5重量份滑石粉和1重量份乙酸乙酯，搅拌均匀；
S3、涂装前加入5重量份甲基六氢苯酐、3重量份双氰胺、1重量份三乙醇胺和1重量份过氧化物，搅拌均匀。
实施例一至实施例三的试验结果如下表：
综上所述，该抗渗防腐修复涂料能达到很好的修复、抗渗、防腐、防水、耐酸碱、抗冻融、耐冲击等性能，同时具有良好的机械稳定性等特点，附着力出色(大于2Mpa或基体破坏)，耐盐雾可达4000H，耐酸碱大于2000H。该抗渗防腐修复涂料可适用于低温高湿的施工环境(湿度大于90％，温度大于-10℃的环境)。
以上仅为本发明的较佳实施例而已，并不用于限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (6)
1.一种用于箱涵修复的抗渗防腐修复涂料，其特征在于：该抗渗防腐修复涂料由A组分、B组分和C组分组成；
所述A组分包括环氧乙烯基酯树脂、苯乙烯混合物、领苯二甲酸、丙烯酸甲酯、丙二醇、N-羟甲基丙烯酰胺、新戊二醇、乙酸乙酯、硅烷偶联剂、聚氨酯丙烯酸酯和异氰酸三缩水甘油酯；
所述B组分包括陶瓷微粉、有机酸、玻璃纤维粉、有机膨润土混合物、二氧化硅、颜料、硫酸钡、滑石粉和乙酸乙酯；
所述C组分包括甲基六氢苯酐、双氰胺、三乙醇胺和过氧化物。
2.根据权利要求1所述的一种用于箱涵修复的抗渗防腐修复涂料，其特征在于：所述A组分的百分占比为50％～65％，所述B组分的百分占比为30％～45％，所述C组分的百分占比为1％～5％。
3.根据权利要求2所述的一种用于箱涵修复的抗渗防腐修复涂料，其特征在于：所述A组分包括5～40重量份环氧乙烯基酯树脂、8～17重量份苯乙烯混合物、5～20重量份领苯二甲酸、5～15重量份丙烯酸甲酯、0.5～5重量份丙二醇、0.5～5重量份N-羟甲基丙烯酰胺、1～5重量份新戊二醇、1～10重量份乙酸乙酯、0.5～1重量份硅烷偶联剂、0.5～5重量份聚氨酯丙烯酸酯和0.5～5重量份异氰酸三缩水甘油酯。
4.根据权利要求2所述的一种用于箱涵修复的抗渗防腐修复涂料，其特征在于：所述B组分包括1～8重量份陶瓷微粉、1～5重量份有机酸、1～10重量份玻璃纤维粉、1～5重量份有机膨润土混合物、1～5重量份二氧化硅、5～10重量份颜料、5～10重量份硫酸钡、3～10重量份滑石粉和1～3重量份乙酸乙酯。
5.根据权利要求2所述的一种用于箱涵修复的抗渗防腐修复涂料，其特征在于：所述C组分包括5～10重量份甲基六氢苯酐、3～10重量份双氰胺、1～8重量份三乙醇胺和1～5重量份过氧化物。
6.一种根据权利要求1～5任意一项所述用于箱涵修复的抗渗防腐修复涂料的制备方法，其特征在于，包括以下步骤：
S1、将5～40重量份环氧乙烯基酯树脂、8～17重量份苯乙烯混合物、5～20重量份领苯二甲酸、5～15重量份丙烯酸甲酯、0.5～5重量份丙二醇、0.5～5重量份N-羟甲基丙烯酰胺、1～5重量份新戊二醇、1～10重量份乙酸乙酯、0.5～1重量份硅烷偶联剂、0.5～5重量份聚氨酯丙烯酸酯和0.5～5重量份异氰酸三缩水甘油酯在150℃下搅拌均匀；
S2、加入1～8重量份陶瓷微粉、1～5重量份有机酸、1～10重量份玻璃纤维粉、1～5重量份有机膨润土混合物、1～5重量份二氧化硅、5～10重量份颜料、5～10重量份硫酸钡、3～10重量份滑石粉和1～3重量份乙酸乙酯，搅拌均匀；
S3、涂装前加入5～10重量份甲基六氢苯酐、3～10重量份双氰胺、1～8重量份三乙醇胺和1～5重量份过氧化物，搅拌均匀。