CN115045106A - 面料用的防紫外线的三防整理剂及配置方法和使用方法 - Google Patents
面料用的防紫外线的三防整理剂及配置方法和使用方法 Download PDFInfo
- Publication number
- CN115045106A CN115045106A CN202210502067.XA CN202210502067A CN115045106A CN 115045106 A CN115045106 A CN 115045106A CN 202210502067 A CN202210502067 A CN 202210502067A CN 115045106 A CN115045106 A CN 115045106A
- Authority
- CN
- China
- Prior art keywords
- parts
- finishing agent
- ultraviolet
- fabric
- proof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了面料用的防紫外线的三防整理剂及配置方法和使用方法，三防整理剂包括按照重量份数计的如下组分：固态混合物5‑11份、液态溶液55‑82份与试剂溶液10.81‑16.15份；固态混合物包括按照重量份数计的如下组分：二氧化钛3‑5份与2‑羟基‑4‑甲氧基二苯甲酮2‑3份；液态溶液包括按照重量份数计的如下组分：聚酯多元醇25‑35份，聚醚酯多元醇8‑15份，多异氰酸酯单体4‑12份，环氧树脂3‑5份与溶剂40‑55份；试剂溶液包括按照重量份数计的如下组分：芳香族超支化聚酯0.2‑0.8份，扩链剂0.5‑1份，催化剂0.01‑0.05份与溶剂10‑15份。通过固态混合物和液态溶液与试剂溶液混合制得的三防整理剂，其解决了现有三防整理剂存在防护紫外线能力较差的技术问题，得到了一种防辐射效果好的三防整理剂。
Description
技术领域
本发明涉及服装用染料技术领域，尤其涉及一种面料用的防紫外线的三防整理剂及配置方法和使用方法。
背景技术
紫外线是电磁波谱中频率为750THz～30PHz，对应真空中波长为400nm～10nm辐射的总称，不能引起人们的视觉。它是频率比蓝紫光高的不可见光，其会导致晒黑、晒红、微血管扩张、皮肤炎等问题，长时间照射还会灼伤皮肤。
因此需要适当减少紫外线照射，而目前在面料上采用的防紫外线的方式通常有两种：
第一种是在三防整理剂中添加的2-羟基-4-甲氧基二苯甲酮，使得面料获得防紫外线的性能。
另一种则是反光布的方式，具体是在面料上涂上一层二氧化钛或钛白粉，对紫外线进行反射。
综上第一种方式中，获得的防护紫外线的能力较差，而第二种方式的防护能力好，但是面料过于厚重，通常应于帐篷，窗帘等，无法适用于人体穿着。
发明内容
针对现有技术中所存在的不足，本发明提供了一种面料用的防紫外线的三防整理剂及配置方法和使用方法，其解决了现有三防整理剂存在防护紫外线能力较差的技术问题。
根据本发明的实施例记载的一种面料用的防紫外线的三防整理剂，包括按照重量份数计的如下组分：固态混合物5-11份、液态溶液55-82份与试剂溶液10.81-16.15份；
所述固态混合物包括按照重量份数计的如下组分：二氧化钛3-5份与2-羟基-4-甲氧基二苯甲酮2-3份；
所述液态溶液包括按照重量份数计的如下组分：聚酯多元醇25-35份，聚醚酯多元醇8-15份，多异氰酸酯单体4-12份，环氧树脂3-5份与溶剂40-55份；
所述试剂溶液包括按照重量份数计的如下组分：芳香族超支化聚酯0.2-0.8份，扩链剂0.5-1份，催化剂0.01-0.05份与溶剂10-15份。
本发明的技术原理为：采用二氧化钛与2-羟基-4-甲氧基二苯甲酮混合成的固态混合物，使得防紫外线的能力进一步提高，因为二氧化钛能有效的反射紫外线，而2-羟基-4-甲氧基二苯甲酮作为良好的紫外线吸收剂，两者相互配合互进一步提高了三防整理剂的防紫外线能力。
相比于现有技术，本发明具有如下有益效果：通过固态混合物和液态溶液与试剂溶液混合制得的三防整理剂，其解决了现有三防整理剂存在防护紫外线能力较差的技术问题，得到了一种防辐射效果好的三防整理剂。
进一步的，所述整理剂中还包括重量份数计为2-3份的阻燃剂。
进一步的，所述阻燃剂为苯基磷酸二酯。
进一步的，所述整理剂中还包括抗菌剂，所述抗菌剂为纳米银，采用重量份数计为1-2份的所述纳米银代替部分二氧化钛，使得所述二氧化钛的重量份数计为1-4份。
进一步的，所述溶剂为去离子水。
根据本发明的实施例记载的一种面料用的防紫外线的三防整理剂的配置方法，包括：
S1、固态混合：将二氧化钛与2-羟基-4-甲氧基二苯甲酮按比例混合，得到固态混合物；
S2、液态混合：将聚酯多元醇、聚醚酯多元醇、多异氰酸酯单体、环氧树脂、芳香族超支化聚酯与溶剂进行混合，得到混合溶液；
S3、试剂混合；将扩链剂、催化剂与溶剂进行混合，得到试剂溶液。
相比于现有技术，本发明将固态混合物、液态溶液与试剂溶液分开混合，避免在使用前固态混合物沉淀，液态溶液与试剂溶液发生反应。
进一步的，所述S1步骤中还加入了苯基磷酸二酯。
进一步的，所述S1步骤中还加入了纳米银。
根据本发明的实施例记载的一种面料用的防紫外线的三防整理剂的使用方法，包括：
a、混合：将5-11份的固态混合物、55-82份的液态溶液与10.81-16.15份的试剂溶液混合，得到整理剂；
b、面料浸轧：取适量的所述a步骤中混合的得到的整理剂，对需要加工的面料进行浸轧处理。
c、烘干：将所述b步骤中处理后的面料进行烘干，所述烘干温度为130-150℃，烘干时间为1-1.5min。
相比于现有技术，本发明在使用前才将固态混合物、液态溶液与试剂溶液进行最终的混合，使得使用时的固态混合物能均匀分布在液态溶液中。
进一步的，所述b步骤中的温度需要保持在≤35℃，轧液率为60-80％。
具体实施方式
下面结合实施例对本发明中的技术方案进一步说明。
本发明记载的面料用的防紫外线的三防整理剂，包括按照重量份数计的如下组分：固态混合物5-11份、液态溶液80-122份与试剂溶液10.71-16.85份。
具体的固态混合物包括按照重量份数计的如下组分：二氧化钛3-5份、2-羟基-4-甲氧基二苯甲酮2-3份与阻燃剂2-3份，其中阻燃剂为苯基磷酸二酯。
液态溶液包括按照重量份数计的如下组分：聚酯多元醇25-35份，聚醚酯多元醇8-15份，多异氰酸酯单体4-12份，环氧树脂3-5份与溶剂40-55份，溶剂为去离子水。
试剂溶液包括按照重量份数计的如下组分：芳香族超支化聚酯0.2-0.8份，扩链剂0.5-1份，催化剂0.01-0.05份与溶剂10-15份，其中溶剂为去离子水，扩链剂为N-甲基二乙醇胺，催化剂为三亚乙基二胺，
具体的整理剂中还包括抗菌剂，抗菌剂为纳米银，采用重量份数计为1-2份的纳米银代替部分二氧化钛，使得二氧化钛的重量份数计为1-4份，因为纳米银具有优良的抗菌性能的同时还具有优良的反射紫外线的能力，通过纳米银材质，代替部分的二氧化钛，使得整理剂具有抗菌性能的同时还减少了二氧化钛的用量，降低了成本，具体如采用1纳米银与4份二氧化钛或2纳米银与1份二氧化钛等。
本发明记载的面料用的防紫外线的三防整理剂的配置方法，包括：
S1、固态混合：将二氧化钛、纳米银、2-羟基-4-甲氧基二苯甲酮与苯基磷酸二酯按比例混合，得到固态混合物。
S2、液态混合：将聚酯多元醇、聚醚酯多元醇、多异氰酸酯单体、环氧树脂与溶剂进行混合，得到混合溶液。
S3、试剂混合；将扩链剂、催化剂、芳香族超支化聚酯与溶剂进行混合，得到试剂溶液。
固态混合物、混合溶液与试剂溶液分别储存使得他们相互之间不接触，防止固态混合物沉底，防止扩链剂、催化剂与芳香族超支化聚酯与聚酯多元醇、聚醚酯多元醇、多异氰酸酯单体与环氧树脂发生反应。
本发明记载的面料用的防紫外线的三防整理剂的使用方法，包括：
a、混合：将5-11份的固态混合物、55-82份的液态溶液与10.81-16.15份的试剂溶液混合，得到整理剂。
b、面料浸轧：取适量的所述a步骤中混合的得到的整理剂，对需要加工的面料进行浸轧处理，具体的温度需要保持在≤35℃，轧液率为60-80％。
c、烘干：将所述b步骤中处理后的面料进行烘干，所述烘干温度为130-150℃，烘干时间为1-1.5min。
实施例1
采用二氧化钛3份、2-羟基-4-甲氧基二苯甲酮2份与苯基磷酸二酯2份混合得到固态混合物。
采用聚酯多元醇25份，聚醚酯多元醇8份，多异氰酸酯单体4份，环氧树脂3份与离子水40份混合得到液态溶液。
采用芳香族超支化聚酯0.2份，扩链剂0.5份，催化剂0.01份与离子水10份混合得到试剂溶液。
然后取固态混合物7份、液态溶液80份与试剂溶液10.71份混合得到三防整理剂，然后进行面料浸轧与烘干得到成品面料。
实施例2
采用二氧化钛5份、2-羟基-4-甲氧基二苯甲酮3份与苯基磷酸二酯3份混合得到固态混合物。
采用聚酯多元醇35份，聚醚酯多元醇15份，多异氰酸酯单体12份，环氧树脂5份与离子水55份混合得到液态溶液。
采用芳香族超支化聚酯0.8份，扩链剂1份，催化剂0.05份与离子水15份混合得到试剂溶液。
然后取固态混合物11份、液态溶液122份与试剂溶液16.85份混合得到三防整理剂，然后进行面料浸轧与烘干得到成品面料。
实施例3
采用二氧化钛2份、2-羟基-4-甲氧基二苯甲酮2份、苯基磷酸二酯2份与纳米银1份混合得到固态混合物。
采用聚酯多元醇25份，聚醚酯多元醇8份，多异氰酸酯单体4份，环氧树脂3份与离子水40份混合得到液态溶液。
采用芳香族超支化聚酯0.2份，扩链剂0.5份，催化剂0.01份与离子水10份混合得到试剂溶液。
然后取固态混合物7份、液态溶液80份与试剂溶液10.71份混合得到三防整理剂，然后进行面料浸轧与烘干得到成品面料。
实施例4
采用二氧化钛3份、2-羟基-4-甲氧基二苯甲酮3份、苯基磷酸二酯3份与纳米银2份混合得到固态混合物。
采用聚酯多元醇35份，聚醚酯多元醇15份，多异氰酸酯单体12份，环氧树脂5份与离子水55份混合得到液态溶液。
采用芳香族超支化聚酯0.8份，扩链剂1份，催化剂0.05份与离子水15份混合得到试剂溶液。
然后取固态混合物11份、液态溶液122份与试剂溶液16.85份混合得到三防整理剂，然后进行面料浸轧与烘干得到成品面料。
对比例1
采用2-羟基-4-甲氧基二苯甲酮5份与苯基磷酸二酯2份混合形成固态混合物，然后采用与实施例1与实施例3相同的液态溶液与试剂溶液制得三防整理剂，并经过面料浸轧与烘干得到成品面料。
同时按照GB-T 18830-2002的方法进行抗紫外线的性能测试，测试结果如下表所示：
相对与只采用2-羟基-4-甲氧基二苯甲酮这种紫外线吸收剂，混入二氧化钛用于反射紫外线，使得紫外线防护系数进一步提高，且波长在315～400nm的日光紫外线辐射的投射率能维持在≤0.2％。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (10)
1.一种面料用的防紫外线的三防整理剂，其特征在于：包括按照重量份数计的如下组分：固态混合物5-11份、液态溶液80-122份与试剂溶液10.71-16.85份；
所述固态混合物包括按照重量份数计的如下组分：二氧化钛3-5份与2-羟基-4-甲氧基二苯甲酮2-3份；
所述液态溶液包括按照重量份数计的如下组分：聚酯多元醇25-35份，聚醚酯多元醇8-15份，多异氰酸酯单体4-12份，环氧树脂3-5份与溶剂40-55份；
所述试剂溶液包括按照重量份数计的如下组分：芳香族超支化聚酯0.2-0.8份，扩链剂0.5-1份，催化剂0.01-0.05份与溶剂10-15份。
2.如权利要求1所述的一种面料用的防紫外线的三防整理剂，其特征在于：所述整理剂中还包括重量份数计为2-3份的阻燃剂。
3.如权利要求2所述的一种面料用的防紫外线的三防整理剂，其特征在于：所述阻燃剂为苯基磷酸二酯。
4.如权利要求1所述的一种面料用的防紫外线的三防整理剂，其特征在于：所述整理剂中还包括抗菌剂，所述抗菌剂为纳米银，采用重量份数计为1-2份的所述纳米银代替部分二氧化钛，使得所述二氧化钛的重量份数计为1-4份。
5.如权利要求1所述的一种面料用的防紫外线的三防整理剂，其特征在于：所述溶剂为去离子水。
6.一种面料用的防紫外线的三防整理剂的配置方法，其特征在于：包括：
S1、固态混合：将二氧化钛与2-羟基-4-甲氧基二苯甲酮按比例混合，得到固态混合物；
S2、液态混合：将聚酯多元醇、聚醚酯多元醇、多异氰酸酯单体、环氧树脂与溶剂进行混合，得到混合溶液；
S3、试剂混合；将扩链剂、催化剂、芳香族超支化聚酯与溶剂进行混合，得到试剂溶液。
7.如权利要求6所述的一种面料用的防紫外线的三防整理剂的配置方法，其特征在于：所述S1步骤中还加入了苯基磷酸二酯。
8.如权利要求6或7所述的一种面料用的防紫外线的三防整理剂的配置方法，其特征在于：所述S1步骤中还加入了纳米银。
9.一种面料用的防紫外线的三防整理剂的使用方法，其特征在于：包括：
a、混合：将5-11份的固态混合物、55-82份的液态溶液与10.81-16.15份的试剂溶液混合，得到整理剂；
b、面料浸轧：取适量的所述a步骤中混合的得到的整理剂，对需要加工的面料进行浸轧处理；
c、烘干：将所述b步骤中处理后的面料进行烘干，所述烘干温度为130-150℃，烘干时间为1-1.5min。
10.如权利要求9所述的一种面料用的防紫外线的三防整理剂的使用方法，其特征在于：所述b步骤中的温度需要保持在≤35℃，轧液率为60-80％。