CN114989545A - 一种健身器材垫脚改性pvc材料 - Google Patents
一种健身器材垫脚改性pvc材料 Download PDFInfo
- Publication number
- CN114989545A CN114989545A CN202210795409.1A CN202210795409A CN114989545A CN 114989545 A CN114989545 A CN 114989545A CN 202210795409 A CN202210795409 A CN 202210795409A CN 114989545 A CN114989545 A CN 114989545A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc material
- modified pvc
- powder
- foot pad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种健身器材垫脚改性PVC材料，所述健身器材垫脚改性PVC材料由以下重量份数组分构成：PVC树脂材料，100‑125份；增塑剂，3‑6份；润滑剂，5‑10份；热稳定剂，0.3‑1.5份；抗氧剂，3.6‑5份；硬脂酸钙，2.5‑4.6份；羰基铁粉，2‑5份；增白剂，1.5‑2.3份；石蜡粉，0.5‑7份；黄麻纤维，1‑6份；流平剂，2.3‑5份；耐磨剂，10‑15份；氯化聚乙烯粉，0.5‑3份；抗冲击改性剂，5‑20份；包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，3‑10份。采用本申请中的健身器材垫脚改性PVC材料，不仅可以利用特质的耐磨剂、抗冲击改性剂等组分来提高耐磨性能、抗压性能，而且可以保证一定的弹性，尤其适用于健身器材的垫脚的特殊要求，解决了耐磨度差、稳定性不足、抗压差的问题。
Description
技术领域
本发明涉及PVC材料领域，尤其涉及一种健身器材垫脚改性PVC材料。
背景技术
目前，随着人们生活水平的提高，人们对于健身的需求也越来越高，健身器材常以训练功能多少来分为单功能和综合型多功能两大类。单功能器械，常用的有划船器、健美车、健步机、跑步机、美腰机等。它们的主要功能是：它们的主要功能是：增加臂力：哑铃握力器多功能仰卧起坐板。划船器：主要用来增强手臂力量、背阔肌和动作协调能力。AMT体适能运动机：与其他的健身方式不同，用户可以在不同的运动模式和完全零冲击体验下，类似于登楼梯、步行、慢跑和长跑间自由转换。您可以通过这种即时转换模式功能，调整您的训练模式来达到针对特定肌肉群训练的目标。
但是，现有的健身器材垫脚存在以下缺陷：
由于健身器材的特重情况，作为健身器材的脚垫，不仅要有一定的摩擦力，而且还要求一定的稳定性和耐磨度，市面上的健身器材的脚垫存在耐磨度差、稳定性不足、抗压差的问题。
发明内容
为了克服现有技术的不足，本发明的目的之一在于提供一种健身器材垫脚改性PVC材料，其能解决耐磨度差、稳定性不足、抗压差的问题。
本发明的目的之一采用如下技术方案实现：
一种健身器材垫脚改性PVC材料，所述健身器材垫脚改性PVC材料由以下重量份数组分构成：
PVC树脂材料，100-125份；
增塑剂，3-6份；
润滑剂，5-10份；
热稳定剂，0.3-1.5份；
抗氧剂，3.6-5份；
硬脂酸钙，2.5-4.6份；
羰基铁粉，2-5份；
增白剂，1.5-2.3份；
石蜡粉，0.5-7份；
黄麻纤维，1-6份；
流平剂，2.3-5份；
耐磨剂，10-15份；
氯化聚乙烯粉，0.5-3份；
抗冲击改性剂，5-20份；
包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，3-10份。
进一步地，所述耐压稳定剂的组分为：聚丙烯酰胺1-3份，铝矿石粉20-50份，木纤维20-30份，瓜儿胶1-1.5份，二乙烯基苯2-3份，羧甲基纤维素钠0.5-2份。
进一步地，所述抗冲击改性剂的组分为：碳酸钙90-120份，月桂酸2-5份，无菌水1-15份，羧基丁腈胶乳2-6份。
进一步地，所述增塑剂为丙烯酸聚合物。
进一步地，所述增白剂的组分为：荧光增白剂0.5-2份，三羧基三乙胺10-15份，无菌水2-15份，二氢萜品醇3-5份，桂基醚硫酸钠15-20份，酵母3-5份。
进一步地，所述抗氧剂的组分为：聚烯烃粉料90-100份，乙二醇0.5-2份，乙酰丙酮合0.1-3份。
进一步地，所述流平剂的组分为：聚醚改性聚硅氧烷2-8份，丙烯酸丁酯3-12份，聚醚改性聚硅氧烷3-10份，炭黑2-15份。
进一步地，所述耐磨剂的组分为：硅烷偶联剂50份，硼酸锌1-5份，滑石粉10-15份，白炭黑20份。
进一步地，所述热稳定剂采用(C12H12N2S)(C6H8O4)Zn。
进一步地，所述硬脂酸钙为硬脂酸、氢氧化钙悬浊液和氧化锌在稀氨水催化下于水介质中加热反应而得到的硬脂酸钙湿料。
相比现有技术，本发明的有益效果在于：
所述健身器材垫脚改性PVC材料由以下重量份数组分构成：PVC树脂材料，100-125份；增塑剂，3-6份；润滑剂，5-10份；热稳定剂，0.3-1.5份；抗氧剂，3.6-5份；硬脂酸钙，2.5-4.6份；羰基铁粉，2-5份；增白剂，1.5-2.3份；石蜡粉，0.5-7份；黄麻纤维，1-6份；流平剂，2.3-5份；耐磨剂，10-15份；氯化聚乙烯粉，0.5-3份；抗冲击改性剂，5-20份；包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，3-10份。采用本申请中的健身器材垫脚改性PVC材料，不仅可以利用特质的耐磨剂、抗冲击改性剂等组分来提高耐磨性能、抗压性能，而且可以保证一定的弹性，尤其适用于健身器材的垫脚的特殊要求，解决了耐磨度差、稳定性不足、抗压差的问题。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，而可依照说明书的内容予以实施，并且为了让本发明的上述和其他目的、特征和优点能够更明显易懂，以下特举较佳实施例，并配合附图，详细说明如下。
附图说明
图1为3个实施例的性能测试图。
具体实施方式
下面，结合附图以及具体实施方式，对本发明做进一步描述，需要说明的是，在不相冲突的前提下，以下描述的各实施例之间或各技术特征之间可以任意组合形成新的实施例。
需要说明的是，当组件被称为“固定于”另一个组件，它可以直接在另一个组件上或者也可以存在居中的组件。当一个组件被认为是“连接”另一个组件，它可以是直接连接到另一个组件或者可能同时存在居中组件。当一个组件被认为是“设置于”另一个组件，它可以是直接设置在另一个组件上或者可能同时存在居中组件。本文所使用的术语“垂直的”、“水平的”、“左”、“右”以及类似的表述只是为了说明的目的。
除非另有定义，本文所使用的所有的技术和科学术语与属于本发明的技术领域的技术人员通常理解的含义相同。本文中在本发明的说明书中所使用的术语只是为了描述具体的实施例的目的，不是旨在于限制本发明。本文所使用的术语“及/或”包括一个或多个相关的所列项目的任意的和所有的组合。
一种健身器材垫脚改性PVC材料，所述健身器材垫脚改性PVC材料由以下重量份数组分构成：PVC树脂材料，100-125份；增塑剂，3-6份；润滑剂，5-10份；热稳定剂，0.3-1.5份；抗氧剂，3.6-5份；硬脂酸钙，2.5-4.6份；羰基铁粉，2-5份；增白剂，1.5-2.3份；石蜡粉，0.5-7份；黄麻纤维，1-6份；流平剂，2.3-5份；耐磨剂，10-15份；氯化聚乙烯粉，0.5-3份；抗冲击改性剂，5-20份；包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，3-10份。采用本申请中的健身器材垫脚改性PVC材料，不仅可以利用特质的耐磨剂、抗冲击改性剂等组分来提高耐磨性能、抗压性能，而且可以保证一定的弹性，尤其适用于健身器材的垫脚的特殊要求，解决了耐磨度差、稳定性不足、抗压差的问题。
实施例1：PVC树脂材料，100-份；增塑剂，4份；润滑剂，5份；热稳定剂，1份；抗氧剂，4份；硬脂酸钙，4份；羰基铁粉，3份；增白剂，2份；石蜡粉，0.9份；黄麻纤维，2份；流平剂，3份；耐磨剂，11份；氯化聚乙烯粉，2份；抗冲击改性剂，6份；包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，5份。
实施例2：PVC树脂材料，120份；增塑剂，4.2份；润滑剂，5.3份；热稳定剂，1.1份；抗氧剂，4份；硬脂酸钙，4份；羰基铁粉，3份；增白剂，2份；石蜡粉，0.9份；黄麻纤维，2份；流平剂，3份；耐磨剂，11份；氯化聚乙烯粉，2份；抗冲击改性剂，6.2份；包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，5.5份。
实施例3：PVC树脂材料，90份；增塑剂，4份；润滑剂，5份；热稳定剂，1份；抗氧剂，4份；硬脂酸钙，4份；羰基铁粉，3份；增白剂，2份；石蜡粉，0.9份；黄麻纤维，2份；流平剂，3份；耐磨剂，11份；氯化聚乙烯粉，2份；抗冲击改性剂，7份；包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，6份。
请具体参阅图1，为性能测试图。
优选的，所述耐压稳定剂的组分为：聚丙烯酰胺1-3份，铝矿石粉20-50份，木纤维20-30份，瓜儿胶1-1.5份，二乙烯基苯2-3份，羧甲基纤维素钠0.5-2份。所述抗冲击改性剂的组分为：碳酸钙90-120份，月桂酸2-5份，无菌水1-15份，羧基丁腈胶乳2-6份。所述增塑剂为丙烯酸聚合物。
优选的，所述增白剂的组分为：荧光增白剂0.5-2份，三羧基三乙胺10-15份，无菌水2-15份，二氢萜品醇3-5份，桂基醚硫酸钠15-20份，酵母3-5份。所述抗氧剂的组分为：聚烯烃粉料90-100份，乙二醇0.5-2份，乙酰丙酮合0.1-3份。
优选的，所述流平剂的组分为：聚醚改性聚硅氧烷2-8份，丙烯酸丁酯3-12份，聚醚改性聚硅氧烷3-10份，炭黑2-15份。所述耐磨剂的组分为：硅烷偶联剂50份，硼酸锌1-5份，滑石粉10-15份，白炭黑20份。所述热稳定剂采用(C12H12N2S)(C6H8O4)Zn。所述硬脂酸钙为硬脂酸、氢氧化钙悬浊液和氧化锌在稀氨水催化下于水介质中加热反应而得到的硬脂酸钙湿料。
需要特别说明的是：在一优选的实施例中，还包括聚氯乙烯树脂1-10份、环氧大豆油8-10份，氯醋8-12份，热塑性丁苯橡胶5-20份。此实施例中可以进一步提高弹性性能。
在另一优选的实施例中，还包括纳米蒙脱土1-20份、环氧大豆油8-10份，季戊四醇4、3-5份，热塑性丁苯橡胶5-20份。此实施例中可以提高整体性能。
在另一优选的实施例中，还包括纳米蒙脱土1-20份、聚氯乙烯树脂1-10份、环氧大豆油8-10份，氯醋8-12份，热塑性丁苯橡胶5-20份，季戊四醇4、3-5份，热塑性丁苯橡胶5-20份。
上述实施方式仅为本发明的优选实施方式，不能以此来限定本发明保护的范围，本领域的技术人员在本发明的基础上所做的任何非实质性的变化及替换均属于本发明所要求保护的范围。
Claims (10)
1.一种健身器材垫脚改性PVC材料，其特征在于，所述健身器材垫脚改性PVC材料由以下重量份数组分构成：
PVC树脂材料，100-125份；
增塑剂，3-6份；
润滑剂，5-10份；
热稳定剂，0.3-1.5份；
抗氧剂，3.6-5份；
硬脂酸钙，2.5-4.6份；
羰基铁粉，2-5份；
增白剂，1.5-2.3份；
石蜡粉，0.5-7份；
黄麻纤维，1-6份；
流平剂，2.3-5份；
耐磨剂，10-15份；
氯化聚乙烯粉，0.5-3份；
抗冲击改性剂，5-20份；
包含聚丙烯酰胺、铝矿石粉的耐压稳定剂，3-10份。
2.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述耐压稳定剂的组分为：聚丙烯酰胺1-3份，铝矿石粉20-50份，木纤维20-30份，瓜儿胶1-1.5份，二乙烯基苯2-3份，羧甲基纤维素钠0.5-2份。
3.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述抗冲击改性剂的组分为：碳酸钙90-120份，月桂酸2-5份，无菌水1-15份，羧基丁腈胶乳2-6份。
4.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述增塑剂为丙烯酸聚合物。
5.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述增白剂的组分为：荧光增白剂0.5-2份，三羧基三乙胺10-15份，无菌水2-15份，二氢萜品醇3-5份，桂基醚硫酸钠15-20份，酵母3-5份。
6.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述抗氧剂的组分为：聚烯烃粉料90-100份，乙二醇0.5-2份，乙酰丙酮合0.1-3份。
7.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述流平剂的组分为：聚醚改性聚硅氧烷2-8份，丙烯酸丁酯3-12份，聚醚改性聚硅氧烷3-10份，炭黑2-15份。
8.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述耐磨剂的组分为：硅烷偶联剂50份，硼酸锌1-5份，滑石粉10-15份，白炭黑20份。
9.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述热稳定剂采用(C12H12N2S)(C6H8O4)Zn。
10.如权利要求1所述的健身器材垫脚改性PVC材料，其特征在于：所述硬脂酸钙为硬脂酸、氢氧化钙悬浊液和氧化锌在稀氨水催化下于水介质中加热反应而得到的硬脂酸钙湿料。