CN114854288A - 金属家居用品喷涂双组份手感弹性涂料及其制备方法 - Google Patents
金属家居用品喷涂双组份手感弹性涂料及其制备方法 Download PDFInfo
- Publication number
- CN114854288A CN114854288A CN202210573423.7A CN202210573423A CN114854288A CN 114854288 A CN114854288 A CN 114854288A CN 202210573423 A CN202210573423 A CN 202210573423A CN 114854288 A CN114854288 A CN 114854288A
- Authority
- CN
- China
- Prior art keywords
- agent
- metal
- preparation
- component
- double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了金属家居用品喷涂双组份手感弹性涂料及其制备方法，包括如下步骤：1)面漆的制备：按照橡胶漆:固化剂:稀释剂＝10:(1.1‑1.2):(4‑6)的重量比例，混合、高速分散均匀，用80‑120目的滤网过滤后，备用；2)底漆的制备：按照金属有色漆:固化剂:稀释剂＝1:0.5:(1‑1.2)的重量比例，进行混合、搅拌均匀，用80‑120目的滤网过滤后，备用。本发明所述的金属家居用品喷涂双组份手感弹性涂料，很好装饰保护功能，色彩多样绚丽，有极强视角冲击。
Description
【技术领域】
本发明涉及涂料技术领域，具体涉及金属家居用品喷涂双组份手感弹性涂料及其制备方法。
【背景技术】
弹性涂料是以合成树脂乳液为基料，与颜料、填料及助剂配制而成，施涂一定厚度(干膜厚度大于等于150μm)后，具有弥补因基材伸缩(运动)产生细小裂纹的有弹性的功能性涂料。弹性涂料不仅具有普通涂料的保护和装饰作用，而且具有防水和遮盖裂缝功能。国际比较流行的是质感涂料它属于弹性涂料的一种，具有以下几种特点：表现力丰富，立体感强，柔韧性、可塑性极强附着力强，易擦洗，耐酸碱，不褪色、不起皮、不开裂，维修重涂容易等。
弹性涂料的分类及品种：
1、溶剂型弹性涂料：溶剂型弹性涂料是以高分子合成树脂为主要成膜物质，有机溶剂为稀释剂，加入一定量的颜料、填料及助剂，经混合、搅拌溶解、研磨而配制成的一种挥发性涂料。弹性涂料涂刷在外墙面以后，随着涂料中所含溶剂的挥发，成膜物质与其他不挥发组分共同形成均匀连续的薄膜，即涂层。由于涂膜较紧密，通常具有较好的硬度、光泽、耐水性、耐酸碱性和良好的耐候性、耐污染性等特点。但由于施工时有大量易耐的有机溶剂挥发，容易污染环境。漆膜透气性差，又有疏水性，如在潮湿基层上施工，易产生起皮、脱落等现象。
2、乳液型弹性涂料：乳液型弹性涂料，主要是以高分子合成树脂乳液为主要成膜物质的外墙涂料称为乳液型外墙涂料。按乳液制造方法不同可以分为两类：一是由单体通过乳液聚合工艺直接合成的乳液；二是由高分子合成树脂通过乳化方法制成的乳液。按涂料的质感又可分为乳胶漆(薄型乳液涂料)、厚质涂料及彩色砂壁状涂料等。
3、无机高分子弹性涂料：无机高分子建筑弹性涂料是来发展起来的一大类新型建筑涂料。建筑上广泛应用的有碱金属硅酸盐和硅溶胶两类。有机高分子建筑涂料一般都有耐老化性能较差、耐热性差、表面硬度小等缺点。无机分子涂料恰好在这些方面性能较好，耐老化性、耐高温、耐腐蚀、耐久性等性能好，涂膜硬度大、耐磨性好，若选材合理，耐水性能也好，而且原材料来源广泛，价格便宜，因而来受到国内外普遍重视，发展较快。
随着社会的发展，人们生活水平日益提高，对于涂料的要求不仅仅局限于装饰作用，还必须具备一些特殊功能及作用，同时也更注重健康、环保。目前已有弹性涂料的研究，例如中国专利申请号CN201310587467.6公开了一种聚氨酯防水防腐涂料及其制备方法，该聚氨酯防水防腐涂料，分为X组分和Y组分，重量混合比为2:1，X组分按重量比由以下组分组成：40-50份活泼氢聚合物、20-25份甲苯二异氰酸酯、4-6份地沟油、4-6份荧光粉、0.9-1.4份X组分防沉剂、0.4-0.45份X组分催化剂、4-8份乙酸乙酯、1.5-2份氟化钙、0-0.15份酸性调节剂；Y组分按重量比由以下组分组成：7-9份多元醇、10-13份苯乙烯、10-13份丁二烯、25-28份丙烯腈，15-17份聚酯树脂、10-12份填料、3-4.5份白颜料、0.2-0.7份Y组分催化剂、0.4-1份Y组分助剂。又例如中国专利申请号CN201510959153.3公开了一种单组份聚氨酯防水涂料及其制备方法，制备该单组份聚氨酯防水涂料的原料配方包括：脂肪族异氰酸酯、非疏水型聚醚多元醇、催化剂、含羟基反应型疏水剂，该发明的单组份聚氨酯防水涂料的制备原料配方中的含羟基反应型疏水剂具有疏水性以及与原料配方中的其它组分有更好的相容性，从而提高了含羟基反应型疏水剂与脂肪族异氰酸酯生成的预聚体与单组份聚氨酯防水涂料中的其它组分的相容性，避免了疏水剂的析出。再例如中国专利申请号CN201610627186.2公开了一种水性双组分聚氨酯弹性涂料及其制备方法，此油漆采用两种水性改性聚氨酯树脂双拼搅拌混合后加入水性异氰酸酯类固化剂固化成膜，并且解决了填料在水性涂料体系中难分散的问题，该产品喷涂后具有特殊柔软的触感及高弹性表面手感，耐冲击性、耐刮擦和耐化学品性强，和溶剂型的弹性漆相比具有优异的耐候性，长时间使用不会出现漆膜发粘回软等不良现象。
总的来说，现有的涂料环保性能欠佳，不适合金属家居用品喷涂。
【发明内容】
针对现有的双组份弹性涂料性能的不足，本发明的目的是提供金属家居用品喷涂双组份手感弹性涂料及其制备方法，得到的金属家居用品喷涂双组份手感弹性涂料，很好装饰保护功能，色彩多样绚丽，有极强视角冲击
本发明的目的通过以下技术方案实现：
上述金属家居用品喷涂双组份手感弹性涂料的制备方法，包括如下步骤：
1)面漆的制备：按照橡胶漆:固化剂:稀释剂＝10:(1.1-1.2):(4-6)的重量比例，混合、高速分散均匀，用80-120目的滤网过滤后，备用；
所述的橡胶漆，由以下重量比例的原料制成：聚酯树脂50％、醋酸丁酯(CAS：123-86-4)40％、流平剂1.5％、消光剂6.5％、促进剂0.3％、弹性助剂1.7％；
2)底漆的制备：按照金属有色漆:固化剂:稀释剂＝1:0.5:(1-1.2)的重量比例，进行混合、搅拌均匀，用80-120目的滤网过滤后，备用；
所述的金属有色漆，由以下重量比例的原料制成：羟基丙烯酸树脂(CAS：9003-01-4)65％、醋酸丁酯(CAS：123-86-6)10％、丙二醇甲醚醋酸酯(CAS：108-65-6)10％、流平剂0.2％、消泡剂0.2％、分散剂0.6％、颜料14％。
本发明中：
步骤1)所述的高速分散均匀，是采用5000转40-50分钟均匀到细度25微米。
所述的固化剂，由以下重量比例的原料制成：醋酸丁酯(CAS：123-86-4)10％和三聚体预聚物(HDI，CAS：28182-81-2)90％；
所述的稀释剂，由以下重量比例的原料制成：醋酸丁酯(CAS：123-86-4)30％和丙二醇甲醚醋酸酯(PMA，CAS：108-65-6)70％；
所述的流平剂，选自聚醚改性聚二甲基硅氧烷，CAS：128192-17-6；所述的消光剂，选自二氧化硅，CAS：2189-520；所述的促进剂，选自有机铋复盐，CAS：77-58-7；所述的弹性助剂，选自丙烯酸改性甲基硅氧烷，CAS：68554-71-2；
所述的消泡剂，选自破泡聚硅氧烷，CAS：9006-65-9；
所述的分散剂，选自高分子量嵌段共聚物，CAS：58128-2；
所述的颜料，选自钛白粉，CAS：13463-67-7。
本发明还涉及上述金属家居用品喷涂双组份手感弹性涂料的制备方法得到的金属家居用品喷涂双组份手感弹性涂料，具有如下技术指标：
外观与性状：无色或淡黄色透明液体；相对密度：0.97；燃烧热：3204.4KJ/mol；闪点：27℃；溶解性：不溶于水，用配套稀释剂稀释性能好；主要用途：主要用于木器装饰和保护。
上述金属家居用品喷涂双组份手感弹性涂料的施工方法，包括如下步骤：
1)前期处理：工件除油去污，磷化；
2)金属底材的涂装：将底漆进行喷涂，让涂上底漆的工件自然干燥4-5小时，或者30-40℃烘烤2-3小时；
3)金属家居用品喷涂双组份手感弹性涂料的涂装：涂装前把所需要的工具用稀释剂清洗干净，喷房或者施工环境的湿度在60-70℃之间；
将金属家居用品喷涂双组份手感弹性涂料，底漆厚度150μm、面漆厚度75μm，使工件表面均匀覆盖金属家居用品喷涂双组份手感弹性涂料，让成品自然干燥或烘干。
本发明中：
步骤1)所述的前期处理，是保证工件表面平整，7天内无锈蚀及锈点，保证双组份金属底漆对底材的附着力、封闭性、从而延迟成品在日常使用过程中出现锈斑、锈迹。
步骤2)所述的金属底材的涂装，使用双组份金属底漆，保证了漆膜对金属底材的封闭性、致密性、抗腐蚀抗老化和耐酸碱性，根据现场喷涂的情况调节链速、转速和出油量，使工件表面的油漆均匀覆盖底材。
步骤3)所述的喷房或者施工环境的湿度，保证湿度在60-70℃之间，低于30％或高于80％的湿度禁止施工喷涂，除非采取加热抽湿的强制措施；所述的让成品自然干燥或烘干，是让成品自然干燥养护7-8小时(夏天3-5小时)或者低温(30-40℃)烘烤2-3小时，即可下挂。
步骤2)所述的双组份金属底漆和步骤3)所述的双组份手感弹性涂料，活化期在4-5小时，配漆的原则采取少量多次法，避免固化浪费。
步骤2)所述的双组份金属底漆和步骤3)所述的双组份手感弹性涂料，极其敏感，最忌水、醇类、氨类物质的接触及混入，否则漆膜会出现不干、返粘、耐刮性差等问题。
步骤2)和步骤3)的喷涂过程中，保证喷房干净无颗粒跌落，晾干线要进行密封无尘埃，同时也要通风透气，有条件的话可以对空气进行过滤，产品的漆膜满足欧盟Reach法规认证，符合美国加州CP65及国标GB18581-2009的标准。
和现有技术相比，本发明具有如下优点：
本发明所述的金属家居用品喷涂双组份手感弹性涂料的制备方法得到的金属家居用品喷涂双组份手感弹性涂料，很好装饰保护功能，色彩多样绚丽，有极强视角冲击，有温暖如春的触软感。
【具体实施方式】
以下结合实施例对本发明的具体实施方式做进一步说明。
实施例：
金属家居用品喷涂双组份手感弹性涂料的制备方法，包括如下步骤：
1)面漆的制备：按照橡胶漆:固化剂:稀释剂＝10:(1.1-1.2):(4-6)的重量比例，混合、高速分散均匀(采用5000转40-50分钟均匀到细度25微米)，用80-120目的滤网过滤后，备用；
所述的橡胶漆，由以下重量比例的原料制成：聚酯树脂50％、醋酸丁酯(CAS：123-86-4)40％、流平剂1.5％、消光剂6.5％、促进剂0.3％、弹性助剂1.7％；
2)底漆的制备：按照金属有色漆:固化剂:稀释剂＝1:0.5:(1-1.2)的重量比例，进行混合、搅拌均匀，用80-120目的滤网过滤后，备用；
所述的金属有色漆，由以下重量比例的原料制成：羟基丙烯酸树脂(CAS：9003-01-4)65％、醋酸丁酯(CAS：123-86-6)10％、丙二醇甲醚醋酸酯(CAS：108-65-6)10％、流平剂0.2％、消泡剂0.2％、分散剂0.6％、颜料14％。
所述的流平剂，选自聚醚改性聚二甲基硅氧烷；所述的消光剂，选自二氧化硅；所述的促进剂，选自有机铋复盐；所述的弹性助剂，选自丙烯酸改性甲基硅氧烷；
所述的固化剂，由以下重量比例的原料制成：醋酸丁酯10％和三聚体预聚物90％；
所述的稀释剂，由以下重量比例的原料制成：醋酸丁酯30％和丙二醇甲醚醋酸酯70％；
所述的消泡剂，选自破泡聚硅氧烷；所述的分散剂，选自高分子量嵌段共聚物；所述的颜料，选自钛白粉。
上述金属家居用品喷涂双组份手感弹性涂料的施工方法，包括如下步骤：
1)前期处理：工件除油去污，磷化；
2)金属底材的涂装：将底漆进行喷涂，让涂上底漆的工件自然干燥4-5小时，或者30-40℃烘烤2-3小时；
3)金属家居用品喷涂双组份手感弹性涂料的涂装：涂装前把所需要的工具用稀释剂清洗干净，喷房或者施工环境的湿度在60-70℃之间；
将金属家居用品喷涂双组份手感弹性涂料，底漆厚度150μm、面漆厚度75μm，使工件表面均匀覆盖金属家居用品喷涂双组份手感弹性涂料，让成品自然干燥或烘干。
对比例：
现有金属家居用品喷涂是金属氨基烤漆、粉末涂料；需要190℃高温烘烤，不能常温干燥，耗能大，排放大，且色彩单一，不能满足多元化个性化需求。
实验例：
实施例得到涂料喷涂后，得到金属家居用品成品的性能测试符合以下要求：
上述说明是针对本发明较佳可行实施例的详细说明，但实施例并非用以限定本发明的专利申请范围，凡本发明所提示的技术精神下所完成的同等变化或修饰变更，均应属于本发明所涵盖专利范围。
Claims (7)
1.金属家居用品喷涂双组份手感弹性涂料的制备方法，其特征在于：包括如下步骤：
1)面漆的制备：按照橡胶漆:固化剂:稀释剂＝10:(1.1-1.2):(4-6)的重量比例，混合、高速分散均匀，用80-120目的滤网过滤后，备用；
所述的橡胶漆，由以下重量比例的原料制成：聚酯树脂50％、醋酸丁酯40％、流平剂1.5％、消光剂6.5％、促进剂0.3％、弹性助剂1.7％；
2)底漆的制备：按照金属有色漆:固化剂:稀释剂＝1:0.5:(1-1.2)的重量比例，进行混合、搅拌均匀，用80-120目的滤网过滤后，备用；
所述的金属有色漆，由以下重量比例的原料制成：羟基丙烯酸树脂65％、醋酸丁酯10％、丙二醇甲醚醋酸酯10％、流平剂0.2％、消泡剂0.2％、分散剂0.6％、颜料14％。
2.根据权利要求1所述的金属家居用品喷涂双组份手感弹性涂料的制备方法，其特征在于：步骤1)所述的高速分散均匀，是采用5000转40-50分钟均匀到细度25微米。
3.根据权利要求1所述的金属家居用品喷涂双组份手感弹性涂料的制备方法，其特征在于：所述的固化剂，由以下重量比例的原料制成：醋酸丁酯10％和三聚体预聚物90％。
4.根据权利要求1所述的金属家居用品喷涂双组份手感弹性涂料的制备方法，其特征在于：所述的稀释剂，由以下重量比例的原料制成：醋酸丁酯30％和丙二醇甲醚醋酸酯70％。
5.根据权利要求1所述的金属家居用品喷涂双组份手感弹性涂料的制备方法，其特征在于：所述的流平剂，选自聚醚改性聚二甲基硅氧烷；所述的消光剂，选自二氧化硅；所述的促进剂，选自有机铋复盐；所述的弹性助剂，选自丙烯酸改性甲基硅氧烷。
6.根据权利要求1所述的金属家居用品喷涂双组份手感弹性涂料的制备方法，其特征在于：所述的消泡剂，选自破泡聚硅氧烷；所述的分散剂，选自高分子量嵌段共聚物；所述的颜料，选自钛白粉。
7.金属家居用品喷涂双组份手感弹性涂料，其特征在于：采用权利要求1-6任一项所述的金属家居用品喷涂双组份手感弹性涂料的制备方法得到。