CN114837000A - 一种数码印花用染料及其制备方法和应用 - Google Patents
一种数码印花用染料及其制备方法和应用 Download PDFInfo
- Publication number
- CN114837000A CN114837000A CN202110140943.4A CN202110140943A CN114837000A CN 114837000 A CN114837000 A CN 114837000A CN 202110140943 A CN202110140943 A CN 202110140943A CN 114837000 A CN114837000 A CN 114837000A
- Authority
- CN
- China
- Prior art keywords
- parts
- dye
- digital printing
- colorant
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及纺织品加工技术领域，具体公开了一种数码印花用染料及其制备方法和应用，所述数码印花用染料包括以下的原料：钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷与水。本发明提供的数码印花用染料通过多种原料的配合使用，可在各种面料上直接刷所述数码印花用染料进行数码印花，免上前处理助剂及免盖面浆，工艺流程简化，印花工艺可控性和可靠性提高，更加环保，由于是直接进行数码印花，大大降低了生产成本，解决了现有数码印花工艺大多采用白墨彩墨等染料，存在生产成本高的问题，具有广阔的市场前景。
Description
技术领域
本发明涉及纺织品加工技术领域，具体是一种数码印花用染料及其制备方法和应用。
背景技术
随着科技水平的不断提高，印花行业也得到快速发展。目前的各种印花技术很多，其中，传统的手式台板印花工艺，存在印花不透气、高能耗、高污染、设备投资大、用人多、工序长等问题，而且污染处理成本高，不符合环保需求，导致面临关停压力。为此，通过数码印花技术可以避免因耗纸带来的间接耗水和水污染，有效减少了环保压力。而且，数码印花是利用数码技术进行的印花，给纺织印染带来了一个前所未有的发展机遇，印花产品具有精细、明晰、层次丰厚、自然的特性，深受消费者的喜欢。
目前，在数码印花技术中，涂料数码白墨彩墨直喷印花工艺可以制备出，色彩丰富的纺织印染产品。但是，以上的技术方案在应用中存在以下不足：涂料数码白墨彩墨直喷印花工艺的工序长，需要用前处理液、盖面浆，工序多，白墨彩墨等染料成本高，能耗大且成本相对高，使用设备成本高，单位效益低，无法大面积产业化。因此，现有数码印花工艺所采用的染料大多存在成本高的缺陷。
发明内容
本发明实施例的目的在于提供一种数码印花用染料及其制备方法和应用，以解决上述背景技术中提出的现有数码印花工艺大多采用白墨彩墨等染料，存在生产成本高的问题。
为实现上述目的，本发明提供如下技术方案：
一种数码印花用染料，其原料包括钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷、水。
作为本发明进一步的方案：所述数码印花用染料包括以下按照重量份的原料：钛白粉100-140份、流变增稠剂35-65份、二氧化硅80-120份、二乙烯三胺45-65份、着色剂15-35份、消泡剂6-14份、氯化铵35-65份、丙烯酸树酯120-150份、聚氨酯120-150份、醋酸120-160份、二甲胺15-35份、环氧氯丙烷35-65份、水80-120份。
本发明实施例的另一目的在于提供一种数码印花用染料的制备方法，所述的数码印花用染料的制备方法，包括以下步骤：按照比例称取钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷与水，然后将称取的二甲胺溶解在水中，然后加入称取的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、环氧氯丙烷进行混合均匀，即可得到所述数码印花用染料。
本发明实施例的另一目的在于提供一种采用上述的数码印花用染料的制备方法制备得到的数码印花用染料。
本发明实施例的另一目的在于提供一种所述的数码印花用染料在纺织品加工中的应用。
与现有技术相比，本发明的有益效果是：
本发明制备的数码印花用染料通过钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷、水等原料的配合使用，具有透气、无水化的优点，可在各种面料上直接刷所述数码印花用染料进行数码印花，免上前处理助剂及免盖面浆，工艺流程简化，印花工艺可控性和可靠性提高，更加环保，面料使用范围广，由于是直接进行数码印花，生产成本对比白墨彩墨直喷数码印花工艺可降低90％左右，大大降低了生产成本，解决了现有数码印花工艺大多采用白墨彩墨等染料，存在生产成本高的问题，具有广阔的市场前景。
具体实施方式
下面结合具体实施例对本发明作进一步详细地说明。以下实施例将有助于本领域的技术人员进一步理解本发明，但不以任何形式限制本发明。应当指出的是，对本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进。这些都属于本发明的保护范围。
本发明实施例提供的一种数码印花用染料，具体是一种无水化数码印花纳米透气染料，其原料包括钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷、水。
作为本发明的另一优选实施例，所述数码印花用染料包括以下按照重量份的原料：钛白粉100-140份、流变增稠剂35-65份、二氧化硅80-120份、二乙烯三胺45-65份、着色剂15-35份、消泡剂6-14份、氯化铵35-65份、丙烯酸树酯120-150份、聚氨酯120-150份、醋酸120-160份、二甲胺15-35份、环氧氯丙烷35-65份、水80-120份。
作为本发明的另一优选实施例，所述数码印花用染料包括以下按照重量份的原料：钛白粉110-130份、流变增稠剂40-60份、二氧化硅90-110份、二乙烯三胺50-60份、着色剂20-30份、消泡剂8-12份、氯化铵40-60份、丙烯酸树酯130-140份、聚氨酯130-140份、醋酸130-150份、二甲胺20-30份、环氧氯丙烷40-60份、水100-110份。
优选的，所述数码印花用染料包括以下按照重量份的原料：钛白粉120份、流变增稠剂50份、二氧化硅100份、二乙烯三胺55份、着色剂25份、消泡剂10份、氯化铵50份、丙烯酸树酯135份、聚氨酯135份、醋酸140份、二甲胺25份、环氧氯丙烷50份、水105份。
作为本发明的另一优选实施例，所述流变增稠剂选自透明粉、碱溶胀型增稠剂、聚氨酯增稠剂、羧甲基纤维素、膨润土中的任意一种。
需要说明的是，本发明中的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷、水等均为市售产品。
作为本发明的另一优选实施例，所述着色剂选自无机颜料或有机颜料，所述无机颜料可选自氧化物、铬酸盐、硫酸盐、硅酸盐、硼酸盐、钼酸盐、磷酸盐、钒酸盐、铁氰酸盐、氢氧化物、硫化物、金属等；所述有机颜料可选自偶氮颜料、酞菁颜料、蒽醌、靛族、喹吖啶酮、二恶嗪等。
作为本发明的另一优选实施例，所述着色剂选自白色素、碳黑、氧化铁黑中的任意一种。
作为本发明的另一优选实施例，优选的，所述着色剂是白色素，所述白色素一般指食用二氧化钛，具体的粒径大小根据需要进行选择，当然，也可以是采用浆料型白色素系列产品，例如A型、B型、C型、D型、E型、F型、G型和H型等白色素产品。
作为本发明的另一优选实施例，当所述着色剂是白色素时，所述数码印花用染料对应的为无水化数码印花纳米透气白色底浆，可在各种面料，例如硅油面料、丝光面料上直接刷所述无水化数码印花纳米透气白色底浆进行数码印花，免上前处理助剂及免盖面浆，更加环保，面料使用范围广，由于是直接进行数码印花，生产成本对比白墨彩墨直喷数码印花工艺可降低90％左右，大大降低了生产成本。
本发明实施例还提供一种数码印花用染料的制备方法，所述的数码印花用染料的制备方法具体包括以下步骤：
按照比例称取钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷与水，然后将称取的二甲胺溶解在水中，然后加入称取的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、环氧氯丙烷进行混合均匀，即可得到所述数码印花用染料。
作为本发明的另一优选实施例，在所述的数码印花用染料的制备方法中，还包括进行包装的步骤，包装的具体工艺可以采用现有技术，这里并不作赘述，可以根据需求进行选择。
本发明实施例还提供一种采用上述的数码印花用染料的制备方法制备得到的数码印花用染料。
本发明实施例还提供一种所述数码印花用染料在纺织品加工中的应用。
作为本发明的另一优选实施例，在所述的数码印花用染料在纺织品加工中的应用，具体可以是作为染料来进行数码印花在雪纺纱、牛津布、涤纶布、涤棉布等上面，进而可以T恤衫、广告衫、文化衫、连衣裙、运动服、时尚内衣等服装，具有广阔的市场前景。
以下通过列举具体实施例对本发明的数码印花用染料的技术效果做进一步的说明。
实施例1
一种数码印花用染料，包括以下的原料：钛白粉120千克、流变增稠剂(具体是透明粉)50千克、二氧化硅100千克、二乙烯三胺55千克、白色素25千克、消泡剂10千克、氯化铵50千克、丙烯酸树酯135千克、聚氨酯135千克、醋酸140千克、二甲胺25千克、环氧氯丙烷50千克、水105千克。
在本实施例中，所述数码印花用染料的制备方法如下：
称取上述的所有原料进行混合均匀，即可得到所述数码印花用染料。
实施例2
一种数码印花用染料，包括以下的原料：钛白粉100千克、流变增稠剂(具体是透明粉)35千克、二氧化硅80千克、二乙烯三胺45千克、着色剂15千克、消泡剂6千克、氯化铵35千克、丙烯酸树酯120千克、聚氨酯120千克、醋酸120千克、二甲胺15千克、环氧氯丙烷35千克、水80千克。其中所述着色剂是无机颜料。
在本实施例中，所述数码印花用染料的制备方法如下：
称取上述的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷与水，然后将称取的二甲胺溶解在水中，然后加入称取的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、环氧氯丙烷进行混合均匀，即可得到所述数码印花用染料。
实施例3
一种数码印花用染料，包括以下的原料：钛白粉140千克、流变增稠剂(具体是透明粉)65千克、二氧化硅120千克、二乙烯三胺65千克、着色剂35千克、消泡剂14千克、氯化铵65千克、丙烯酸树酯150千克、聚氨酯150千克、醋酸160千克、二甲胺35千克、环氧氯丙烷65千克、水120千克。其中所述着色剂是有机颜料。
在本实施例中，所述数码印花用染料的制备方法如下：
称取上述的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷与水，然后将称取的二甲胺溶解在水中，然后加入称取的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、环氧氯丙烷进行混合均匀，即可得到所述数码印花用染料。
实施例4
一种数码印花用染料，包括以下的原料：钛白粉110千克、流变增稠剂(具体是透明粉)40千克、二氧化硅90千克、二乙烯三胺50千克、着色剂20千克、消泡剂8千克、氯化铵40千克、丙烯酸树酯130千克、聚氨酯130千克、醋酸130千克、二甲胺20千克、环氧氯丙烷40千克、水100千克。其中所述着色剂是白色素。
在本实施例中，所述数码印花用染料的制备方法如下：
称取上述的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷与水，然后将称取的二甲胺溶解在水中，然后加入称取的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、环氧氯丙烷进行混合均匀，即可得到所述数码印花用染料。
实施例5
与实施例4相比，除了数码印花用染料的原料包括：钛白粉130千克、流变增稠剂(具体是透明粉)60千克、二氧化硅110千克、二乙烯三胺60千克、着色剂30千克、消泡剂12千克、氯化铵60千克、丙烯酸树酯140千克、聚氨酯140千克、醋酸150千克、二甲胺30千克、环氧氯丙烷60千克、水110千克。其他与实施例4相同。
实施例6
与实施例3相比，除了数码印花用染料的原料包括：钛白粉110-130千克、流变增稠剂(具体是透明粉)45千克、二氧化硅95千克、二乙烯三胺55千克、着色剂25千克、消泡剂8千克、氯化铵45千克、丙烯酸树酯135千克、聚氨酯130千克、醋酸135千克、二甲胺25千克、环氧氯丙烷45千克、水105千克。其他与实施例3相同。
实施例7
与实施例3相比，除了着色剂是碳黑外，其他与实施例3相同。
实施例8
与实施例3相比，除了着色剂是氧化铁黑外，其他与实施例3相同。
实施例9
与实施例3相比，除了流变增稠剂是碱溶胀型增稠剂外，其他与实施例3相同。
实施例10
与实施例3相比，除了流变增稠剂是聚氨酯增稠剂外，其他与实施例3相同。
实施例11
与实施例3相比，除了流变增稠剂是羧甲基纤维素外，其他与实施例3相同。
实施例12
与实施例3相比，除了流变增稠剂是膨润土外，其他与实施例3相同。
实施例13
与实施例3相比，除了着色剂是氧化物外，其他与实施例3相同。
实施例14
与实施例3相比，除了着色剂是硅酸盐外，其他与实施例3相同。
实施例15
与实施例3相比，除了着色剂是铁氰酸盐外，其他与实施例3相同。
实施例16
与实施例3相比，除了着色剂是酞菁颜料外，其他与实施例3相同。
需要说明的是，本发明提供的数码印花用染料以及数码印花工艺，相对于现有数码印花技术，具有以下优点：
(1)本发明的无水化数码印花纳米透气印花工艺流程简化，印花工艺可控性和可靠性提高。
(2)本发明的数码印花用染料减少工序，减少其它助剂的使用，更加环保。
(3)本发明的数码印花用染料可在各种面料使用，例如在硅油面料、丝光面料上直接刷本纳米数码白底浆进行数码印花，免上前处理助剂及免盖面浆，更加环保，面料使用范围广。
(4)初步测算，无水化数码印花纳米透气直接印花生产成本对比白彩墨直喷数码印花工艺可降低90％左右。
(5)采用新型数码设备，直接建厂投资成本大幅降低，可快速建厂生产，印花生产方式更加灵活、智能，品质高。
上面对本发明的较佳实施方式作了详细说明，但是本发明并不限于上述实施方式，在本领域的普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下作出各种变化。这里无需也无法对所有的实施方式予以穷举。而由此所引申出的显而易见的变化或变动仍处于本发明的保护范围之中。
Claims (10)
1.一种数码印花用染料，其特征在于，所述数码印花用染料的原料包括钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷、水。
2.根据权利要求1所述的数码印花用染料，其特征在于，所述数码印花用染料包括以下按照重量份的原料：钛白粉100-140份、流变增稠剂35-65份、二氧化硅80-120份、二乙烯三胺45-65份、着色剂15-35份、消泡剂6-14份、氯化铵35-65份、丙烯酸树酯120-150份、聚氨酯120-150份、醋酸120-160份、二甲胺15-35份、环氧氯丙烷35-65份、水80-120份。
3.根据权利要求1所述的数码印花用染料，其特征在于，所述数码印花用染料包括以下按照重量份的原料：钛白粉110-130份、流变增稠剂40-60份、二氧化硅90-110份、二乙烯三胺50-60份、着色剂20-30份、消泡剂8-12份、氯化铵40-60份、丙烯酸树酯130-140份、聚氨酯130-140份、醋酸130-150份、二甲胺20-30份、环氧氯丙烷40-60份、水100-110份。
4.根据权利要求1所述的数码印花用染料，其特征在于，所述数码印花用染料包括以下按照重量份的原料：钛白粉120份、流变增稠剂50份、二氧化硅100份、二乙烯三胺55份、着色剂25份、消泡剂10份、氯化铵50份、丙烯酸树酯135份、聚氨酯135份、醋酸140份、二甲胺25份、环氧氯丙烷50份、水105份。
5.根据权利要求1所述的数码印花用染料，其特征在于，所述流变增稠剂选自透明粉、碱溶胀型增稠剂、聚氨酯增稠剂、羧甲基纤维素、膨润土中的任意一种。
6.根据权利要求1所述的数码印花用染料，其特征在于，所述着色剂选自无机颜料或有机颜料。
7.根据权利要求6所述的数码印花用染料，其特征在于，所述着色剂选自白色素、碳黑、氧化铁黑中的任意一种。
8.一种如权利要求1-7任一所述的数码印花用染料的制备方法，其特征在于，包括以下步骤：按照比例称取钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、二甲胺、环氧氯丙烷与水，然后将称取的二甲胺溶解在水中，然后加入称取的钛白粉、流变增稠剂、二氧化硅、二乙烯三胺、着色剂、消泡剂、氯化铵、丙烯酸树酯、聚氨酯、醋酸、环氧氯丙烷进行混合均匀，得到所述数码印花用染料。
9.一种采用权利要求8所述的数码印花用染料的制备方法制备得到的数码印花用染料。
10.一种如权利要求1或2或3或4或5或6或7或9所述的数码印花用染料在纺织品加工中的应用。