CN114769322A - 一种双金属复合无缝钢管的热轧轧制规程优化方法 - Google Patents

一种双金属复合无缝钢管的热轧轧制规程优化方法 Download PDF

Info

Publication number
CN114769322A
CN114769322A CN202210699476.3A CN202210699476A CN114769322A CN 114769322 A CN114769322 A CN 114769322A CN 202210699476 A CN202210699476 A CN 202210699476A CN 114769322 A CN114769322 A CN 114769322A
Authority
CN
China
Prior art keywords
tube
diameter
finished
pipe
seamless steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202210699476.3A
Other languages
English (en)
Other versions
CN114769322B (zh
Inventor
胡建华
王小花
陈建勋
苟毓俊
何宗霖
丁小凤
双远华
李靖
杨晟
郝亚栋
马佳旺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taiyuan University of Science and Technology
Original Assignee
Taiyuan University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiyuan University of Science and Technology filed Critical Taiyuan University of Science and Technology
Priority to CN202210699476.3A priority Critical patent/CN114769322B/zh
Publication of CN114769322A publication Critical patent/CN114769322A/zh
Application granted granted Critical
Publication of CN114769322B publication Critical patent/CN114769322B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于无缝钢管热轧领域，具体涉及一种双金属复合无缝钢管的热轧轧制规程优化方法，包括根据成品复合无缝钢管中覆层与基层的尺寸参数并结合覆层及基层各自在成品复合无缝钢管中的体积占比，获取覆层、基层在各自热膨胀系数下热成品复合无缝钢管在热状态下对应的尺寸参数，选择张减减径率获得轧后荒管尺寸以及芯棒直径，选择总减壁率，得出毛管尺寸参数，选择扩径率，确定出管坯半径，随后基于热成品复合无缝钢管的总体积与管坯总体积相等的条件以及根据覆层、基层各自在复合无缝钢管总体积中的占比，最终获得管坯尺寸参数。通过本发明公开的轧制规程优化方法，能够合理分配各轧机变形量，使得穿孔机、轧管机和减径机负担平衡。

Description

一种双金属复合无缝钢管的热轧轧制规程优化方法
技术领域
本发明涉及无缝钢管热轧领域，具体涉及一种双金属复合无缝钢管的热轧轧制规程优化方法，尤其涉及一种通过穿孔、热连轧、张力减径新型工艺生产的双金属复合无缝钢管，并采用按逆轧制道次方向计算出其无缝钢管管坯尺寸的轧制规程优化方法。
背景技术
不锈钢/碳钢复合材料具有碳钢的耐腐蚀性以及不锈钢优异的强度和韧性的优点，因此，不锈钢/碳钢复合材料在石油化工、海洋工程和建筑领域具有广阔的应用前景。在无缝管行业，对于强腐蚀、高磨损、高工作压力环境下使用的流体管道，通常采用高品质的不锈钢或高合金含量的无缝钢管，这类管材由于大量添加合金元素，其价格是普通无缝钢管的几倍或几十倍。在这种背景下复合无缝钢管应运而生，复合无缝钢管已经在腐蚀性较强的石油、石化行业、核工业以及医药、食品加工等领域获得广泛认同，可通过内层复合耐磨金属，从而满足电厂粉煤、矿山矿粉和尾矿浆输送等高磨损工作环境的要求。
热轧钢管生产的轧制表是指计算轧管工艺过程中主要参数的表格，它是轧管工艺过程的基础。编制轧制表是以成品管的钢种、规格为依据，从车间现有的设备、工具和坯料规格出发, 合理分配各道次的变形量，计算出相应的毛管尺寸、坯料尺寸、工具的主要尺寸和轧机的主要调整参数等。轧制表是进行钢管生产和操作的技术指导规范，它在很大程度上决定整个机组的生产能力、钢管质量、工具寿命、能源及其他经济指标。编制后还应验算主要设备强度，测定验算各轧机上的节奏时间。如个别机组的节奏时间过长，或设备强度、能力不足，则应重新分配变形量，消除薄弱环节。由于轧制规程和轧件原始条件、设备条件、工艺条件和目标要求等因素有关，还和轧制过程中物理力学性能变化等因素直接相关，各种因素之间还存在相互作用和相互影响，可见轧制规程的制定的复杂性，所以，轧制生产早期主要是使用经验法和能耗曲线法等来制定轧制规程，这些传统的轧制规程制定方法由于简单有效，所以直到目前还大量使用在轧制生产中。但这种方法很依赖于人工经验，容易造成耗材多，对设备的运行状态和轧制状态缺乏充分的考虑。
因此，在如何保证外径、壁厚为目标的前提下，研究以负荷均衡分配为目标，实现对轧制规程进行优化设定。不仅能适用于新产品的开发，而且可以提高尺寸精度和内外表面质量，轧制设备寿命等。这有助于改变目前钢管企业在新产品开发中的瓶颈问题，提高企业的创新能力和核心竞争力。
发明内容
鉴于此，本发明的目的在于，提供一种双金属复合无缝钢管的热轧轧制规程优化方法，旨在克服传统的轧制规程过于依赖人工经验，无法均衡分配负荷的缺陷。
为了达到上述发明目的，采取如下的技术方案：
一种双金属复合无缝钢管的热轧轧制规程优化方法，包括以下步骤：
根据成品复合无缝钢管中覆层与基层的尺寸参数并结合覆层及基层各自在成品复合无缝钢管中的体积占比，获取覆层、基层在各自热膨胀系数下热成品复合无缝钢管在热状态下对应的尺寸参数；其中，所述覆层为不锈钢层，所述基层为碳钢层，且所述成品复合无缝钢管中覆层与基层的尺寸参数包括成品复合无缝钢管的外径与内径、不锈钢层的壁厚及长度、碳钢层的壁厚及长度；
根据所述热成品复合无缝钢管在热状态下的尺寸参数，在张力减径过程中，设定减壁率为0%，并同时选择张减减径率，由此获得轧后荒管尺寸参数；其中，所述轧后荒管尺寸参数包括轧后荒管内、外径、轧后荒管壁厚及轧后荒管长度；
基于获得的轧后荒管尺寸参数，结合并设定芯棒与荒管内径之间的间隙，确定出芯棒的直径；
基于确定的芯棒直径同时选择芯棒穿孔过程中的总减壁率，得出穿孔毛管的尺寸参数；其中，所述穿孔毛管的尺寸参数包括穿孔毛管的外径、穿孔毛管的壁厚及穿孔毛管的长度；
根据得出的穿孔毛管的尺寸参数，结合设定的扩径率，由此确定出管坯的半径，随后基于热成品复合无缝钢管的总体积与管坯总体积相等的条件以及根据覆层、基层各自在复合无缝钢管总体积中的占比，最终获得管坯的尺寸参数；其中，所述管坯的尺寸参数包括管坯的半径及直径、管坯的壁厚以及管坯的长度；
将管坯直径与毛管外径作差，判断差值结果是否在管坯直径或毛管外径的±(5~10) %范围内，若满足则直接得出管坯尺寸；若不在指定范围内，则返回重新选定扩径率，重新确定管坯尺寸。
进一步的，所述覆层、基层在各自热膨胀系数下热成品复合无缝钢管在热状态下对应的尺寸参数及公式如下：
Figure 141995DEST_PATH_IMAGE001
公式（1）
Figure 59135DEST_PATH_IMAGE002
公式（2）
Figure 838872DEST_PATH_IMAGE003
公式（3）
Figure 234082DEST_PATH_IMAGE004
公式（4）
Figure 986137DEST_PATH_IMAGE005
公式（5）
Figure 808599DEST_PATH_IMAGE006
公式（6）
Figure 75633DEST_PATH_IMAGE007
公式（7）
其中，
Figure 274533DEST_PATH_IMAGE008
—热成品管外径；
Figure 943412DEST_PATH_IMAGE009
—成品管内径；
Figure 123726DEST_PATH_IMAGE010
—热成品管中不锈钢壁厚；
Figure 878055DEST_PATH_IMAGE011
—成品管中不锈钢壁厚；
Figure 615067DEST_PATH_IMAGE012
—热成品管中碳钢壁厚；
Figure 138452DEST_PATH_IMAGE013
—成品管中碳钢壁厚；
Figure 505980DEST_PATH_IMAGE014
—热成品管内径；
Figure 747605DEST_PATH_IMAGE015
—热成品管壁厚；
Figure 22729DEST_PATH_IMAGE016
—热成品管长度；
Figure 666200DEST_PATH_IMAGE017
—热成品管中不锈钢长度；
Figure 1366DEST_PATH_IMAGE018
—热成品管中碳钢长度；
Figure 908449DEST_PATH_IMAGE019
—成品管长度；
Figure 987264DEST_PATH_IMAGE020
—不锈钢的热膨胀系数；
Figure 485241DEST_PATH_IMAGE021
—碳钢的热膨胀系数；
Figure 256888DEST_PATH_IMAGE022
—终轧的温度；
Figure 207527DEST_PATH_IMAGE023
—覆层的总体积；
Figure 27715DEST_PATH_IMAGE024
—基层的总体积；
Figure 380199DEST_PATH_IMAGE025
—成品管的总体积。
更进一步的，所述不锈钢的热膨胀系数
Figure 322747DEST_PATH_IMAGE020
=18.97
Figure 760682DEST_PATH_IMAGE026
，碳钢的热膨胀系数
Figure 368250DEST_PATH_IMAGE021
=14.9
Figure 840819DEST_PATH_IMAGE026
，终轧的温度
Figure 954269DEST_PATH_IMAGE027
为700-900℃。
优选地，在张力减径过程中，选择张减减径率，并依据以下的公式，获得轧后荒管的外径；
Figure 879499DEST_PATH_IMAGE028
公式（8）
其中，
Figure 103807DEST_PATH_IMAGE029
—张减减径率，选择24%~60%，
Figure 102987DEST_PATH_IMAGE030
—轧后荒管外径，
Figure 387338DEST_PATH_IMAGE031
—减径后外径。
优选地，设定芯棒与荒管内径之间的间隙为1-3mm。
较佳地，选择芯棒穿孔过程中的总减壁率，并依据以下的公式，得出穿孔毛管的壁厚；
Figure 799865DEST_PATH_IMAGE032
公式（9）
其中，
Figure 827864DEST_PATH_IMAGE033
—总减壁率，选择30%~70%，
Figure 196397DEST_PATH_IMAGE034
—穿孔毛管壁厚，
Figure 386070DEST_PATH_IMAGE035
—轧后荒管壁厚。
更佳地，设定的扩径率为110%~115%。
优选地，将管坯直径与毛管外径作差，判断差值结果是否在管坯直径或毛管外径的±(5~10) %范围内，依据如下的公式：
Figure 285893DEST_PATH_IMAGE036
公式（10）。
本发明的有益效果：
本发明公开了一种通过穿孔、热连轧、张力减径新型工艺生产的双金属复合无缝钢管，采用按逆轧制道次方向最终获取其无缝钢管管坯尺寸的轧制规程制定方法。通过本发明公开的轧制规程的优化方法，容易获取得到双金属复合无缝钢管的覆层以及基层各自的壁厚进而合理地分配各轧机的变形量，使得穿孔机、轧管机和减径机负担平衡。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动性的前提下，还可以根据这些附图获得其他的附图。
图1为本发明一种双金属复合无缝钢管的热轧轧制规程优化方法的流程图；
图2为不同温度下金属材料的线膨胀系数一览表。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
目前制造复合无缝钢管主要的工艺方法有机械复合法和冶金复合法，机械复合法包括热轧复合方法、热挤压复合法、铸造复合方法、爆炸焊接复合方法、组合式双金属复合无缝钢管生产方法、激光包覆法等。
本发明针对碳钢20钢与不锈钢316L的复合材料，采用穿孔、热连轧、张力减径的方式来获得双金属复合无缝钢管，并对生产的复合无缝钢管制定它的轧制规程方法。
需要说明的是：编制轧制表之前，首先应该了解生产和设备情况，例如轧机的结构形式、强度和刚度、工具形状和尺寸、管坯尺寸规格、孔型系列以及所轧材料的加工性能等。编制后通过实践不断修正和完成，轧制表的编制一般应遵守下述原则：
(1)合理地分配各轧机的变形量，使得穿孔机、轧管机和减径机负担平衡；
(2)尽量用最少管坯尺寸种类和工具完成轧制计划；
(3)合理选择各轧机的变形参数，保证产品质量和生产力。斜轧穿孔机的延伸系数在1.3~5.7范围内，压缩带处的压缩率为10%~17%，顶头前压缩率在4%~9%之间，合金钢取小值；连续轧管机的延伸系数一般为4~10，斜轧轧管机的延伸系数一般不超过3，顶管机的延伸系数可达15，在一般定径机上，每架直径压缩率不大于3. 5%，斜轧定径机的直径压缩量取1 ~ 2mm；
(4)合理地选择管坯尺寸，管坯尺寸应根据毛管外径来选择，圆管坯直径应接近于毛管外径，一般管坯直径与毛管外径之差在±(5 ~10) %范围内；
(5)了解制管材料的特性以及工艺过程和变形制度对管材力学性能、物理性能和工艺性能的影响，以便获得高性能的产品。
另外，编制轧制表的方法大致有两种：一种是按逆轧制道次方向进行编制，即由定径向前推算到坯料尺寸，此法主要适用于新设计车间的典型产品；另一种是从轧管机出发向两头工序推算，此法主要适用于已投产车间的新产品设计，因为投产车间总有一定规格数量的坯料、工具和轧管机孔型系统等，所以设计新产品应首先考虑已有工具和坯料规格，以及轧管机孔型系统是否能满足要求，以尽量减少工具和坯料储备。
不管哪种计算方法，思考方法与计算内容是相同的。本发明采用第一种方法按逆轧制道次方向推理得出其无缝钢管管坯的尺寸。具体包括如下的步骤：
根据成品复合无缝钢管中覆层与基层的尺寸参数并结合覆层及基层各自在成品复合无缝钢管中的体积占比，获取覆层、基层在各自热膨胀系数下热成品复合无缝钢管在热状态下对应的尺寸参数；其中，所述覆层为不锈钢层，所述基层为碳钢层，且所述成品复合无缝钢管中覆层与基层的尺寸参数包括成品复合无缝钢的外径与内径、不锈钢层的壁厚及长度、碳钢层的壁厚及长度；
根据所述热成品复合无缝钢管在热状态下的尺寸参数，在张力减径过程中，设定减壁率为0%，并同时选择张减减径率，由此获得轧后荒管尺寸参数；其中，所述轧后荒管尺寸参数包括轧后荒管内、外径、轧后荒管壁厚及轧后荒管长度；
基于获得的轧后荒管尺寸参数，结合并设定芯棒与荒管内径之间的间隙，确定出芯棒的直径；
基于确定的芯棒直径同时选择芯棒穿孔过程中的总减壁率，得出穿孔毛管的尺寸参数；其中，所述穿孔毛管的尺寸参数包括穿孔毛管的外径、穿孔毛管的壁厚及穿孔毛管的长度；
根据得出的穿孔毛管的尺寸参数，结合设定的扩径率，由此确定出管坯的半径，随后基于热成品复合无缝钢管的总体积与管坯总体积相等的条件以及根据覆层、基层各自在复合无缝钢管总体积中的占比，最终获得管坯的尺寸参数；其中，所述管坯的尺寸参数包括管坯的半径及直径、管坯的壁厚以及管坯的长度；
将管坯直径与毛管外径作差，判断差值结果是否在管坯直径或毛管外径的±(5~10) %范围内，若满足则直接得出管坯尺寸；若不在指定范围内，则返回重新选定扩径率，重新确定管坯尺寸。
下面将结合具体的实施数据及图1的流程对本发明的一种双金属复合无缝钢管的热轧轧制规程优化方法进行详细的说明。
已知给定成品管直径
Figure 852004DEST_PATH_IMAGE037
为159mm，不锈钢壁厚
Figure 153672DEST_PATH_IMAGE038
为3mm，碳钢壁厚
Figure 451929DEST_PATH_IMAGE039
=9mm，成品管内径
Figure 839048DEST_PATH_IMAGE040
=135mm，成品管长度
Figure 208850DEST_PATH_IMAGE041
为10m，给出按逆轧制道次方向计算轧制规程的具体制定方法，详细计算过程如下：
Figure 99445DEST_PATH_IMAGE042
热成品管的尺寸计算
Figure 896500DEST_PATH_IMAGE001
公式（1）
根据图2所示内容，选取温度在700℃时，不锈钢的热膨胀系数和碳钢的热膨胀系数，并将选取的数据带入公式（1），得到以下数据：
Figure 692287DEST_PATH_IMAGE043
Figure 865779DEST_PATH_IMAGE044
Figure 876460DEST_PATH_IMAGE044
公式（2）
Figure 844416DEST_PATH_IMAGE045
Figure 878231DEST_PATH_IMAGE046
公式（3）
Figure 589835DEST_PATH_IMAGE047
Figure 455023DEST_PATH_IMAGE048
公式（4）
Figure 593881DEST_PATH_IMAGE049
Figure 367189DEST_PATH_IMAGE050
公式（5）
Figure 616905DEST_PATH_IMAGE051
Figure 602178DEST_PATH_IMAGE052
公式（6）
Figure 911937DEST_PATH_IMAGE053
Figure 982661DEST_PATH_IMAGE054
公式（7）
Figure 973751DEST_PATH_IMAGE055
其中，
Figure 813531DEST_PATH_IMAGE008
—热成品管外径；
Figure 294191DEST_PATH_IMAGE009
—成品管内径；
Figure 586632DEST_PATH_IMAGE010
—热成品管中不锈钢壁厚；
Figure 630680DEST_PATH_IMAGE011
—成品管中不锈钢壁厚；
Figure 324967DEST_PATH_IMAGE012
—热成品管中碳钢壁厚；
Figure 976528DEST_PATH_IMAGE013
—成品管中碳钢壁厚；
Figure 21844DEST_PATH_IMAGE014
—热成品管内径；
Figure 354737DEST_PATH_IMAGE015
—热成品管壁厚；
Figure 903530DEST_PATH_IMAGE016
—热成品管长度；
Figure 991571DEST_PATH_IMAGE017
—热成品管中不锈钢长度；
Figure 445555DEST_PATH_IMAGE018
—热成品管中碳钢长度；
Figure 644455DEST_PATH_IMAGE019
—成品管长度；
Figure 47755DEST_PATH_IMAGE020
—不锈钢的热膨胀系数；
Figure 306698DEST_PATH_IMAGE021
—碳钢的热膨胀系数；
Figure 61027DEST_PATH_IMAGE022
—终轧的温度；
Figure 735722DEST_PATH_IMAGE023
—覆层的总体积；
Figure 259108DEST_PATH_IMAGE024
—基层的总体积；
Figure 688952DEST_PATH_IMAGE025
—成品管的总体积。
Figure 664998DEST_PATH_IMAGE056
减径机钢管尺寸计算
Figure 392652DEST_PATH_IMAGE057
Figure 36123DEST_PATH_IMAGE058
Figure 371289DEST_PATH_IMAGE059
Figure 100210DEST_PATH_IMAGE060
公式（8）
设定
Figure 116708DEST_PATH_IMAGE061
，得出
Figure 614685DEST_PATH_IMAGE062
Figure 120753DEST_PATH_IMAGE062
其中，
Figure 336971DEST_PATH_IMAGE063
—减径后外径；
Figure 219476DEST_PATH_IMAGE064
—减径后不锈钢壁厚；
Figure 761841DEST_PATH_IMAGE065
—减径后碳钢壁厚；
Figure 829023DEST_PATH_IMAGE066
—张减减径率，
Figure 266957DEST_PATH_IMAGE067
—轧后荒管外径。
Figure 687574DEST_PATH_IMAGE068
连轧管机钢管尺寸计算
Figure 160144DEST_PATH_IMAGE062
此张减过程中减壁率为0%
Figure 945697DEST_PATH_IMAGE069
Figure 870928DEST_PATH_IMAGE070
Figure 95236DEST_PATH_IMAGE071
Figure 422312DEST_PATH_IMAGE072
（通过体积不变计算）
Figure 706663DEST_PATH_IMAGE073
其中，
Figure 306140DEST_PATH_IMAGE067
—轧后荒管外径；
Figure 68560DEST_PATH_IMAGE074
—轧后荒管中不锈钢壁厚；
Figure 250143DEST_PATH_IMAGE075
—轧后荒管中碳钢壁厚；
Figure 705395DEST_PATH_IMAGE076
—轧后荒管壁厚；
Figure 542901DEST_PATH_IMAGE077
—轧后荒管内径；
Figure 109011DEST_PATH_IMAGE078
—轧后荒管长度（通过体积不变计算）；
Figure 145100DEST_PATH_IMAGE079
—芯棒直径；
Figure 771254DEST_PATH_IMAGE080
—芯棒和荒管内径之间的间隙，取2.35mm
Figure 345323DEST_PATH_IMAGE081
穿孔机钢管尺寸计算
Figure 449546DEST_PATH_IMAGE082
，设定
Figure 605720DEST_PATH_IMAGE083
公式（9）
Figure 402775DEST_PATH_IMAGE084
Figure 11611DEST_PATH_IMAGE085
Figure 122787DEST_PATH_IMAGE086
Figure 133468DEST_PATH_IMAGE087
（通过体积不变计算）
其中，
Figure 101424DEST_PATH_IMAGE088
—总减壁率；
Figure 197556DEST_PATH_IMAGE089
—穿孔毛管壁厚；
Figure 833461DEST_PATH_IMAGE090
—穿孔毛管外径；
Figure 964228DEST_PATH_IMAGE091
—穿孔毛管长度(通过体积不变原理计算)，而且可根据穿孔毛管壁厚与轧后荒管壁厚确定出总压下量。
Figure 103085DEST_PATH_IMAGE092
管坯尺寸计算
Figure 686513DEST_PATH_IMAGE093
Figure 873912DEST_PATH_IMAGE094
Figure 859186DEST_PATH_IMAGE095
Figure 168944DEST_PATH_IMAGE096
即：
Figure 239669DEST_PATH_IMAGE097
得出
Figure 480026DEST_PATH_IMAGE098
根据覆层、基层各自在复合无缝钢管总体积中的占比，即
Figure 319806DEST_PATH_IMAGE099
Figure 800466DEST_PATH_IMAGE100
同时：
Figure 92907DEST_PATH_IMAGE101
Figure 950005DEST_PATH_IMAGE102
Figure 581974DEST_PATH_IMAGE103
Figure 233535DEST_PATH_IMAGE104
其中，
Figure 278852DEST_PATH_IMAGE105
—穿孔毛管半径；
Figure 674061DEST_PATH_IMAGE106
—管坯半径；
Figure 409805DEST_PATH_IMAGE107
—热成品管的总体积；
Figure 497846DEST_PATH_IMAGE108
—管坯的总体积；
Figure 764880DEST_PATH_IMAGE109
—管坯长度；
Figure 698201DEST_PATH_IMAGE110
—覆层的总体积；
Figure 367079DEST_PATH_IMAGE111
—基层的总体积；
Figure 563706DEST_PATH_IMAGE112
—管坯中不锈钢壁厚；
Figure 52456DEST_PATH_IMAGE113
—管坯中碳钢壁厚。
将管坯直径与毛管外径作差，判断差值结果是否在管坯直径或毛管外径的±(5~10) %范围内，若满足则直接得出管坯尺寸；若不在指定范围内，则返回重新选定扩径率，重新确定管坯尺寸。
Figure 55047DEST_PATH_IMAGE036
公式（10）
其中，
Figure 578432DEST_PATH_IMAGE114
—管坯直径；
Figure 742697DEST_PATH_IMAGE090
—穿孔毛管外径；
其中，
Figure 171273DEST_PATH_IMAGE115
；
Figure 711976DEST_PATH_IMAGE116
；
Figure 89868DEST_PATH_IMAGE117
；
Figure 690613DEST_PATH_IMAGE118
；
Figure 153956DEST_PATH_IMAGE119
。
通过上述逆轧制道次方向公开的轧制规程的优化方法，容易获取得到双金属复合无缝钢管的覆层以及基层各自的壁厚进而合理地分配各轧机的变形量，使得穿孔机、轧管机和减径机负担平衡。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，包括以下步骤：
根据成品复合无缝钢管中覆层与基层的尺寸参数并结合覆层及基层各自在成品复合无缝钢管中的体积占比，获取覆层、基层在各自热膨胀系数下热成品复合无缝钢管在热状态下对应的尺寸参数；其中，所述覆层为不锈钢层，所述基层为碳钢层，且所述成品复合无缝钢管中覆层与基层的尺寸参数包括成品复合无缝钢管的外径与内径、不锈钢层的壁厚及长度、碳钢层的壁厚及长度；
根据所述热成品复合无缝钢管在热状态下的尺寸参数，在张力减径过程中，设定减壁率为0%，并同时选择张减减径率，由此获得轧后荒管尺寸参数；其中，所述轧后荒管尺寸参数包括轧后荒管内、外径、轧后荒管壁厚及轧后荒管长度；
基于获得的轧后荒管尺寸参数，结合并设定芯棒与荒管内径之间的间隙，确定出芯棒的直径；
基于确定的芯棒直径同时选择芯棒穿孔过程中的总减壁率，得出穿孔毛管的尺寸参数；其中，所述穿孔毛管的尺寸参数包括穿孔毛管的外径、穿孔毛管的壁厚及穿孔毛管的长度；
根据得出的穿孔毛管的尺寸参数，结合设定的扩径率，由此确定出管坯的半径，随后基于热成品复合无缝钢管的总体积与管坯总体积相等的条件以及根据覆层、基层各自在复合无缝钢管总体积中的占比，最终获得管坯的尺寸参数；其中，所述管坯的尺寸参数包括管坯的半径及直径、管坯的壁厚以及管坯的长度；
将管坯直径与毛管外径作差，判断差值结果是否在管坯直径或毛管外径的±(5~10) %范围内，若满足则直接得出管坯尺寸；若不在指定范围内，则返回重新选定扩径率，重新确定管坯尺寸。
2.根据权利要求1所述的一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，所述覆层、基层在各自热膨胀系数下热成品复合无缝钢管在热状态下对应的尺寸参数及公式如下：
Figure DEST_PATH_IMAGE002
公式（1）
Figure DEST_PATH_IMAGE004
公式（2）
Figure DEST_PATH_IMAGE006
公式（3）
Figure DEST_PATH_IMAGE008
公式（4）
Figure DEST_PATH_IMAGE010
公式（5）
Figure DEST_PATH_IMAGE012
公式（6）
Figure DEST_PATH_IMAGE014
公式（7）
其中，
Figure DEST_PATH_IMAGE016
—热成品管外径；
Figure DEST_PATH_IMAGE018
—成品管内径；
Figure DEST_PATH_IMAGE020
—热成品管中不锈钢壁厚；
Figure DEST_PATH_IMAGE022
—成品管中不锈钢壁厚；
Figure DEST_PATH_IMAGE024
—热成品管中碳钢壁厚；
Figure DEST_PATH_IMAGE026
—成品管中碳钢壁厚；
Figure DEST_PATH_IMAGE028
—热成品管内径；
Figure DEST_PATH_IMAGE030
—热成品管壁厚；
Figure DEST_PATH_IMAGE032
—热成品管长度；
Figure DEST_PATH_IMAGE034
—热成品管中不锈钢长度；
Figure DEST_PATH_IMAGE036
—热成品管中碳钢长度；
Figure DEST_PATH_IMAGE038
—成品管长度；
Figure DEST_PATH_IMAGE040
—不锈钢的热膨胀系数；
Figure DEST_PATH_IMAGE042
—碳钢的热膨胀系数；
Figure DEST_PATH_IMAGE044
—终轧的温度；
Figure DEST_PATH_IMAGE046
—覆层的总体积；
Figure DEST_PATH_IMAGE048
—基层的总体积；
Figure DEST_PATH_IMAGE050
—成品管的总体积。
3.根据权利要求2所述的一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，所述不锈钢的热膨胀系数
Figure 769116DEST_PATH_IMAGE040
=18.97
Figure DEST_PATH_IMAGE052
，碳钢的热膨胀系数
Figure 420677DEST_PATH_IMAGE042
=14.9
Figure 934835DEST_PATH_IMAGE052
，终轧的温度
Figure DEST_PATH_IMAGE054
为700-900℃。
4.根据权利要求3所述的一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，在张力减径过程中，选择张减减径率，并依据以下的公式，获得轧后荒管的外径；
Figure DEST_PATH_IMAGE056
公式（8）
其中，
Figure DEST_PATH_IMAGE058
—张减减径率，选择24%~60%，
Figure DEST_PATH_IMAGE060
—轧后荒管外径，
Figure DEST_PATH_IMAGE062
—减径后外径。
5.根据权利要求4所述的一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，设定芯棒与荒管内径之间的间隙为1-3mm。
6.根据权利要求5所述的一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，选择芯棒穿孔过程中的总减壁率，并依据以下的公式，得出穿孔毛管的壁厚；
Figure DEST_PATH_IMAGE064
公式（9）
其中，
Figure DEST_PATH_IMAGE066
—总减壁率，选择30%~70%，
Figure DEST_PATH_IMAGE068
—穿孔毛管壁厚，
Figure DEST_PATH_IMAGE070
—轧后荒管壁厚。
7.根据权利要求6所述的一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，设定的扩径率为110%~115%。
8.根据权利要求7所述的一种双金属复合无缝钢管的热轧轧制规程优化方法，其特征在于，将管坯直径与毛管外径作差，判断差值结果是否在管坯直径或毛管外径的±(5~10)%范围内，依据如下的公式：
Figure DEST_PATH_IMAGE072
公式（10）。
CN202210699476.3A 2022-06-20 2022-06-20 一种双金属复合无缝钢管的热轧轧制规程优化方法 Active CN114769322B (zh)