CN114752328A - 基于环保型的环氧美缝剂 - Google Patents
基于环保型的环氧美缝剂 Download PDFInfo
- Publication number
- CN114752328A CN114752328A CN202210284944.0A CN202210284944A CN114752328A CN 114752328 A CN114752328 A CN 114752328A CN 202210284944 A CN202210284944 A CN 202210284944A CN 114752328 A CN114752328 A CN 114752328A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- agent
- bottle
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供基于环保型的环氧美缝剂,它包括A组分和B组分;所述A组分包括下述质量份的原料:环氧树脂94份、稀释剂6份、消泡剂0.02份、触变剂6份;所述B组分包括下述质量份的原料:改性脂环胺固化剂16份、脂肪胺18份、稀释剂38份、消泡剂0.02份、触变剂6份、分散剂2份;所述A组分与B组分点质量比为1:1‑1.18。采用本方案后,有效实现智能自动化生产,其工艺设置合理,使用效果好,生产速度快。
Description
技术领域
本发明涉及胶水技术领域,尤其是指基于环保型的环氧美缝剂。
背景技术
美缝剂是勾缝剂的升级产品,美缝剂的装饰性实用性明显优于彩色填缝剂,解决了瓷砖缝隙不美观和脏黑问题等。美缝剂可以在瓷砖粘接后直接填加到瓷砖缝隙中。适合2mm以上的缝隙填充,施工比普通型方便,是填缝剂的升级换代产品。美缝剂施工后具有光泽,颜色丰富自然细腻,如金色、银色、珠光色等,而白色、黑色色度明显高于白水泥、彩色填缝剂,给墙面带来更好的整体效果,因此装饰性大大强于白水泥、彩色填缝剂。并且其凝固后,表面光滑如瓷,可以和瓷砖一起擦洗,具有抗渗透防水的特性,可以做到真正的瓷砖缝隙永不变黑,传统的美缝剂在灌装后,胶瓶由成胶输送带承托向后输送,通过机械手抓取进行装箱,这种方式下机械手一次只能抓取一个胶瓶,其动作频率高,易损坏。
发明内容
本发明的目的在于克服现有技术的不足,提供一种基于环保型的工艺设置合理、使用效果好、生产速度快的环氧美缝剂。
为实现上述目的,本发明所提供的技术方案为:基于环保型的环氧美缝剂,它包括A组分和B组分;
所述A组分包括下述质量份的原料:环氧树脂92-96份、稀释剂4-8份、消泡剂0.01-0.03份、触变剂3-9份;
所述B组分包括下述质量份的原料:改性脂环胺固化剂12-20份、脂肪胺13-23份、稀释剂30-45份、消泡剂0.01-0.03份、触变剂5-8份、分散剂1-3份;
所述A组分与B组分点质量比为1:1-1.18。
所述改性脂环胺的制备方法包括:
控制真空度为-0.1MPa,将4,4’-二氨基二苯醚、双马来酰亚胺按照摩尔比为1:1.5加入反应釜,反应温度为125℃,反应时间为4h,保温1h,得到改性脂环胺。
所述环氧树脂为双酚A型环氧树脂、双酚F型环氧树脂或其组合。
所述稀释剂为苯甲醇、甲苯、二甲苯、正丁醇中的至少一种。
所述脂环胺固化剂为3,3-二甲基-4,4-二氨基二环己基甲烷、4,4'-二氨基二环己基甲烷、1,6-二氨基己烷、二氨基二苯甲烷、4,4’-二氨基二苯醚中的至少一种。
所述脂肪胺固化剂为聚醚胺、乙二胺、二乙烯三胺、三乙烯四胺、双马来酰亚胺、多胺中的至少一种。
所述触变剂为亲水型气相二氧化硅、疏水型气相二氧化硅中的至少一种。
所述环氧美缝剂的制备方法包括有以下步骤:
1)、A组分的制备:按质量份称取原料,先将环氧树脂和稀释剂充分混合2小时,然后加入其余原料混合均匀,即得A组分:
2)、B组分的制备:按质量份称取原料,先将改性脂环胺固化剂、脂肪胺、稀释剂充分混合,然后加入其它原料混合均匀,即得B组分;
3)、将A组分、B组分分别倒入相应的灌装机,通过灌装头将A组分、B组分分别灌入胶瓶相应的胶筒内;
4)、通过熔口机对灌装后的胶筒进行封口,封口后进入包装系统;
5)、包装系统内的成胶输送带带动胶筒行至成胶挡板处;
6)、通过成胶推送气缸将胶瓶推送至托瓶组件上;
7)、通过转轮板带动托瓶组件将胶瓶层叠至托瓶滑板上进行层叠;
8)、通过机械手将层叠好的胶瓶抓取放入包装箱,即成。
本发明在采用上述方案后,采用环氧树脂、稀释剂等制成A组份流体基质,然后再采用改性脂肪胺、脂环胺固化剂、触变剂等制成B组份环保基质,通过流体基质和环保基质反应形成环保型的美缝剂,采用改性脂肪胺和环氧树脂配合,其环保性好,使用后耐潮湿性好,使用寿命长,同时在灌装后设计自动包装系统,使胶水在灌装后可以实现快速入箱包装,有效实现智能自动化生产,其工艺设置合理,使用效果好,生产速度快。
附图说明
图1为本发明的整体结构示意图。
图2为本发明的胶瓶推送板安装示意图。
图3为本发明的托瓶组件结构示意图。
图4为本发明的托瓶板铰接示意图。
具体实施方式
下面结合所有附图对本发明作进一步说明,本发明的较佳实施例为:参见附图1至附图4,本实施例所述的基于环保型的环氧美缝剂包括A组分和B组分;
所述A组分包括下述质量份的原料:环氧树脂92-96份、稀释剂4-8份、消泡剂0.01-0.03份、触变剂3-9份;
所述B组分包括下述质量份的原料:改性脂环胺固化剂12-20份、脂肪胺13-23份、稀释剂30-45份、消泡剂0.01-0.03份、触变剂5-8份、分散剂1-3份;
所述A组分与B组分点质量比为1:1-1.18。
所述改性脂环胺的制备方法包括:
控制真空度为-0.1MPa,将4,4’-二氨基二苯醚、双马来酰亚胺按照摩尔比为1:1.5加入反应釜,反应温度为125℃,反应时间为4h,保温1h,得到改性脂环胺。
所述环氧树脂为双酚A型环氧树脂、双酚F型环氧树脂或其组合。
所述稀释剂为苯甲醇、甲苯、二甲苯、正丁醇中的至少一种。
所述脂环胺固化剂为3,3-二甲基-4,4-二氨基二环己基甲烷、4,4'-二氨基二环己基甲烷、1,6-二氨基己烷、二氨基二苯甲烷、4,4’-二氨基二苯醚中的至少一种。
所述脂肪胺固化剂为聚醚胺、乙二胺、二乙烯三胺、三乙烯四胺、双马来酰亚胺、多胺中的至少一种。
所述触变剂为亲水型气相二氧化硅、疏水型气相二氧化硅中的至少一种。
所述环氧美缝剂的制备方法包括有以下步骤:
1)、A组分的制备:按质量份称取原料,先将环氧树脂和稀释剂充分混合2小时,然后加入其余原料混合均匀,即得A组分:
2)、B组分的制备:按质量份称取原料,先将改性脂环胺固化剂、脂肪胺、稀释剂充分混合,然后加入其它原料混合均匀,即得B组分;
3)、将A组分、B组分分别倒入相应的灌装机,通过灌装头将A组分、B组分分别灌入胶瓶相应的胶筒内;
4)、通过熔口机对灌装后的胶筒进行封口,封口后进入包装系统;
5)、包装系统内的成胶输送带带动胶筒行至成胶挡板处;
6)、通过成胶推送气缸将胶瓶推送至托瓶组件上;
7)、通过转轮板带动托瓶组件将胶瓶层叠至托瓶滑板上进行层叠;
8)、通过机械手将层叠好的胶瓶抓取放入包装箱,即成。
包装系统包括有安装在动力架501上的两块转轮板502,两块转轮板502中心之间通过同步轴连接,两块转轮板502相对一侧设有数量大于4组的托瓶组件,托瓶组件以同步轴为中心呈环形均匀分布在两块转轮板502之间,托瓶组件处的转轮板502上设有贯穿的推瓶槽507,推瓶槽507外侧设有成胶输送带508,转轮板502输出方向的动力架501上固定有两条托瓶轨道503,两条托瓶轨道503其中一端伸至两块转轮板502下部之间,托瓶轨道503上活动安装有托瓶滑板504,托瓶轨道503其中一端安装有推板气缸505,推板气缸505的活塞杆与托瓶滑板504底部连接,托瓶滑板504顶部竖直插装有数量大于2的限位隔板506,相邻限位隔板506之间预留有胶瓶层叠区。
托瓶组件包括有托瓶铰杆509、托瓶板510,其中,托瓶铰杆509为两条,托瓶铰杆509呈n形,其n形顶部通过铰杆销与相应的转轮板502铰接,托瓶铰杆509的两条侧壁自然垂吊,两条托瓶铰杆的垂吊端相对折弯形成托板铰块,托瓶滑板504的宽度小于两个托板铰块之间的距离,托板铰块顶部活动铰接有托瓶板510,托瓶板510其中一端的端部两侧与托板铰块顶部铰接,托瓶板510另一端悬空,两块托瓶板510的悬空端之间形成托瓶区。
成胶输送带508输出端其中一侧位于推瓶槽507外侧,成胶输送带508输出端另一侧设有成胶推送气缸511,成胶推送气缸511的活塞杆上安装有胶瓶推送板512,胶瓶推送板512正对推瓶槽507,成胶输送带508输出端端部竖直固定有成胶挡板513。
在采用上述方案后,封口后的胶瓶由成胶输送带承托向后输送,当行至成胶输送带输出端时被成胶挡板阻挡,动力架上安装有转轮板电机,转轮板电机按常规方式带动同步轴转动,同步轴同步带动两块转轮板转动,当转轮板的推瓶槽行至成胶输送带处时(其中一个推瓶槽位于转轮板最下方位置),成胶推送气缸的活塞杆伸出,带动胶瓶推送板将成胶输送带输出端的胶瓶(与成胶挡板接触的胶瓶),推向推瓶槽,使胶瓶穿过推瓶槽和托瓶铰杆的n形槽后行至托瓶板上,托瓶板在托板铰块的限位作用下不会向下旋转,原始状态呈水平状态,两块托瓶板的悬空端之间形成托瓶区;胶瓶由两块托瓶板共同承托,转轮板继续转动,当带有胶瓶的托瓶组件行至转轮板的输出方向时(胶瓶层叠区上方),胶瓶进入胶瓶层叠区,转轮板继续运行带动托瓶组件下行(胶瓶层叠区下方),胶瓶在限位隔板的作用下两侧被限位,托瓶板继续下行时,托瓶板底部会与托瓶滑板(或与下层的胶瓶)接触,托瓶板的悬空端会向上旋转,托瓶板的悬空端向上会顶起胶瓶(使胶瓶呈水平状态),防止胶瓶侧倾,当托瓶板的悬空端向下经过限位隔板后,托瓶板上的胶瓶即由托瓶滑板(或下层的胶瓶)承托,完成胶瓶层叠,当其中一个胶瓶层叠区的胶瓶层叠满之后,推板气缸带动托瓶滑板行走一个工位,继续进行层叠,层叠满的胶瓶层叠区通过外部机械手一次性抓出进行装箱,
以上所述之实施例只为本发明之较佳实施例,并非以此限制本发明的实施范围,故凡依本发明之形状、原理所作的变化,均应涵盖在本发明的保护范围内。
Claims (8)
1.基于环保型的环氧美缝剂,其特征在于:它包括A组分和B组分;
所述A组分包括下述质量份的原料:环氧树脂92-96份、稀释剂4-8份、消泡剂0.01-0.03份、触变剂3-9份;
所述B组分包括下述质量份的原料:改性脂环胺固化剂12-20份、脂肪胺13-23份、稀释剂30-45份、消泡剂0.01-0.03份、触变剂5-8份、分散剂1-3份;
所述A组分与B组分点质量比为1:1-1.18。
2.根据权利要求书1所述基于环保型的环氧美缝剂,其特征在于:所述改性脂环胺的制备方法包括:
控制真空度为-0.1MPa,将4,4’-二氨基二苯醚、双马来酰亚胺按照摩尔比为1:1.5加入反应釜,反应温度为125℃,反应时间为4h,保温1h,得到改性脂环胺。
3.根据权利要求书1所述基于环保型的环氧美缝剂,其特征在于:所述环氧树脂为双酚A型环氧树脂、双酚F型环氧树脂或其组合。
4.根据权利要求书1所述基于环保型的环氧美缝剂,其特征在于:所述稀释剂为苯甲醇、甲苯、二甲苯、正丁醇中的至少一种。
5.根据权利要求书1所述基于环保型的环氧美缝剂,其特征在于:所述脂环胺固化剂为3,3-二甲基-4,4-二氨基二环己基甲烷、4,4'-二氨基二环己基甲烷、1,6-二氨基己烷、二氨基二苯甲烷、4,4’-二氨基二苯醚中的至少一种。
6.根据权利要求书1所述基于环保型的环氧美缝剂,其特征在于:所述脂肪胺固化剂为聚醚胺、乙二胺、二乙烯三胺、三乙烯四胺、双马来酰亚胺、多胺中的至少一种。
7.根据权利要求书1所述基于环保型的环氧美缝剂,其特征在于:所述触变剂为亲水型气相二氧化硅、疏水型气相二氧化硅中的至少一种。
8.根据权利要求书1所述基于环保型的环氧美缝剂,其特征在于:其特征在于,所述环氧美缝剂的制备方法包括有以下步骤:
1)、A组分的制备:按质量份称取原料,先将环氧树脂和稀释剂充分混合2小时,然后加入其余原料混合均匀,即得A组分:
2)、B组分的制备:按质量份称取原料,先将改性脂环胺固化剂、脂肪胺、稀释剂充分混合,然后加入其它原料混合均匀,即得B组分;
3)、将A组分、B组分分别倒入相应的灌装机,通过灌装头将A组分、B组分分别灌入胶瓶相应的胶筒内;
4)、通过熔口机对灌装后的胶筒进行封口,封口后进入包装系统;
5)、包装系统内的成胶输送带带动胶筒行至成胶挡板处;
6)、通过成胶推送气缸将胶瓶推送至托瓶组件上;
7)、通过转轮板带动托瓶组件将胶瓶层叠至托瓶滑板上进行层叠;
8)、通过机械手将层叠好的胶瓶抓取放入包装箱,即成。