CN114685875A - 一种pe拉伸缠绕膜增白工艺 - Google Patents

一种pe拉伸缠绕膜增白工艺 Download PDF

Info

Publication number
CN114685875A
CN114685875A CN202011581868.7A CN202011581868A CN114685875A CN 114685875 A CN114685875 A CN 114685875A CN 202011581868 A CN202011581868 A CN 202011581868A CN 114685875 A CN114685875 A CN 114685875A
Authority
CN
China
Prior art keywords
layer
parts
tackifier
mixing
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202011581868.7A
Other languages
English (en)
Inventor
马虎
王霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Hengxin Sanyou Electromechanical Co ltd
Original Assignee
Suzhou Hengxin Sanyou Electromechanical Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Hengxin Sanyou Electromechanical Co ltd filed Critical Suzhou Hengxin Sanyou Electromechanical Co ltd
Priority to CN202011581868.7A priority Critical patent/CN114685875A/zh
Publication of CN114685875A publication Critical patent/CN114685875A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种PE拉伸缠绕膜增白工艺，具体涉及高分子材料领域，包括单层挤出工艺：按照重量份，由双峰线性低密度聚乙烯30～40份、PE 45～65份、甲基纤维素3～5份、增白剂0.2～3份、增粘剂1～7份混合而成，所述增粘剂为聚异丁烯或超低密度聚乙烯中的其中一种。本发明通过添加增白剂，能够使单层挤出工艺、双层挤出工艺和三层单层挤出工艺生产的PE拉伸缠绕膜透明度高，光亮度好，同时增加了甲基纤维素，能够使PE拉伸缠绕膜具有优良的拉伸强度。

Description

一种PE拉伸缠绕膜增白工艺
技术领域
本发明涉及高分子材料技术领域，更具体地说，本发明涉及一种 PE拉伸缠绕膜增白工艺。
背景技术
PE拉伸膜(又称缠绕膜)具有较高的拉伸强度、抗撕裂强度，并具 有良好的自粘性，因此能使物体裹成一个整体，防止运输时散落倒塌。 该膜具有优良的透明性。包裹物体美观大方，并能使物体防水、防尘、 防损坏。该膜广泛用于货物托盘包装，如电子、建材、化工、金属制 品、汽车配件、电线电缆、日用品、食品、造纸等行业的捆裹包装。 规格：机用膜宽500mm,手工膜宽300mm,350mm,450mm,500mm,厚 15um-50um.可在线分切各种规格。粘性分单面粘、双面粘，产品分手 工缠绕膜和机用缠绕膜两大系列。
但是在实际使用时，现有的PE拉伸膜在一些方面还存在着一些缺 点，需要进一步的改进，现有的PE拉伸缠绕膜存在光泽度不足，透明 度不够的状况，并且PE拉伸缠绕膜的拉伸强度也不足。
发明内容
为了克服现有技术的上述缺陷，本发明的实施例提供一种PE拉 伸缠绕膜增白工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种PE拉伸缠绕 膜增白工艺，包括单层挤出工艺：
按照重量份，由双峰线性低密度聚乙烯30～40份、PE 45～65 份、甲基纤维素3～5份、增白剂0.2～3份、增粘剂1～7份混合而 成。
进一步的，包括双层挤出工艺：所述双层分别为A层/B层，按 照重量百分比，由10％的A层和90％的B层组成，其中，所述A层由 双峰线性低密度聚乙烯25～30份、增粘剂1～4份和甲基纤维素2～ 4份混合而成，所述B层由PE 55～65份、增白剂0.2～3份和增粘 剂0～7份混合而成。
进一步的，包括双层挤出工艺：所述双层分别为A层/B层，按 照重量百分比，由20％的A层和80％的B层组成，其中，所述A层由 双峰线性低密度聚乙烯30～35份、增粘剂1～5份和甲基纤维素2～ 5份混合而成，所述B层由PE 50～60份、增白剂0.2～3份和增粘 剂0～7份混合而成。
进一步的，包括双层挤出工艺：所述双层分别为A层/B层，按 照重量百分比，由30％的A层和70％的B层组成，其中，所述A层由 双峰线性低密度聚乙烯35～40份、增粘剂1～5份和甲基纤维素2～ 5份混合而成，所述B层由PE 45～55份、增白剂0.2～3份和增粘 剂0～7份混合而成。
进一步的，包括三层挤出工艺：所述三层分别为A层/B层/C层， 按照重量百分比，由10％的A层、80％的B层和10％的C层组成，所述 A层由A层由双峰线性低密度聚乙烯5～7份、增粘剂1～3份和甲基 纤维素1～2份混合而成，所述B层由双峰线性低密度聚乙烯40～45 份、PE 50～60份、增白剂0.2～3份和增粘剂0～7份混合而成，所 述C层由PE 7～9份、增粘剂1～4份和甲基纤维素2～3份混合而成。
进一步的，包括三层挤出工艺：所述三层分别为A层/B层/C层， 按照重量百分比，由20％的A层、60％的B层和20％的C层组成，所述 A层由A层由双峰线性低密度聚乙烯10～15份、增粘剂1～3份和甲 基纤维素2～5份混合而成，所述B层由双峰线性低密度聚乙烯25～ 35份、PE 30～40份、增白剂0.2～3份和增粘剂1～7份混合而成， 所述C层由PE 12～18份、增粘剂2～3份和甲基纤维素2～4份混合 而成。
进一步的，包括三层分别为A层/B层/C层，按照重量百分比， 由30％的A层、40％的B层和30％的C层组成，所述A层由A层由双峰 线性低密度聚乙烯15～20份、增粘剂1～4份和甲基纤维素2～5份 混合而成，所述B层由双峰线性低密度聚乙烯20～30份、PE 20～25 份、增白剂0.2～3份和增粘剂1～5份混合而成，所述C层由PE 18～ 20份、增粘剂2～3份和甲基纤维素2～4份混合而成。
进一步的，所述增粘剂为聚异丁烯或超低密度聚乙烯中的其中一 种。
本发明的技术效果和优点：
本发明通过添加增白剂，能够使单层挤出工艺、双层挤出工艺和 三层单层挤出工艺生产的PE拉伸缠绕膜透明度高，光亮度好，同时 增加了甲基纤维素，能够使PE拉伸缠绕膜具有优良的拉伸强度。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完 整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部 的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性 劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明提供了一种PE拉伸缠绕膜增白工艺，包括单层挤出工艺：
按照重量份，由双峰线性低密度聚乙烯30～40份、PE 45～65 份、甲基纤维素3～5份、增白剂0.2～3份、增粘剂1～7份混合而 成，增粘剂为聚异丁烯或超低密度聚乙烯中的其中一种。
实施例2
一种PE拉伸缠绕膜增白工艺，包括双层挤出工艺：所述双层分 别为A层/B层，按照重量百分比，由10％的A层和90％的B层组成， 其中，所述A层由双峰线性低密度聚乙烯25～30份、增粘剂1～4份 和甲基纤维素2～4份混合而成，所述B层由PE 55～65份、增白剂 0.2～3份和增粘剂0～7份混合而成，增粘剂为聚异丁烯或超低密度 聚乙烯中的其中一种。
实施例3
一种PE拉伸缠绕膜增白工艺，包括双层挤出工艺：所述双层分 别为A层/B层，按照重量百分比，由20％的A层和80％的B层组成， 其中，所述A层由双峰线性低密度聚乙烯30～35份、增粘剂1～5份 和甲基纤维素2～5份混合而成，所述B层由PE 50～60份、增白剂 0.2～3份和增粘剂0～7份混合而成，增粘剂为聚异丁烯或超低密度 聚乙烯中的其中一种。
实施例4
一种PE拉伸缠绕膜增白工艺，包括双层挤出工艺：所述双层分 别为A层/B层，按照重量百分比，由30％的A层和70％的B层组成， 其中，所述A层由双峰线性低密度聚乙烯35～40份、增粘剂1～5份 和甲基纤维素2～5份混合而成，所述B层由PE 45～55份、增白剂 0.2～3份和增粘剂0～7份混合而成，增粘剂为聚异丁烯或超低密度 聚乙烯中的其中一种。
实施例5
一种PE拉伸缠绕膜增白工艺，包括三层挤出工艺：所述三层分 别为A层/B层/C层，按照重量百分比，由10％的A层、80％的B层和 10％的C层组成，所述A层由A层由双峰线性低密度聚乙烯5～7份、 增粘剂1～3份和甲基纤维素1～2份混合而成，所述B层由双峰线性 低密度聚乙烯40～45份、PE 50～60份、增白剂0.2～3份和增粘剂 0～7份混合而成，所述C层由PE 7～9份、增粘剂1～4份和甲基纤 维素2～3份混合而成，增粘剂为聚异丁烯或超低密度聚乙烯中的其 中一种。
实施例6
一种PE拉伸缠绕膜增白工艺，包括三层挤出工艺：所述三层分 别为A层/B层/C层，按照重量百分比，由20％的A层、60％的B层和 20％的C层组成，所述A层由A层由双峰线性低密度聚乙烯10～15份、 增粘剂1～3份和甲基纤维素2～5份混合而成，所述B层由双峰线性低密度聚乙烯25～35份、PE 30～40份、增白剂0.2～3份和增粘剂 1～7份混合而成，所述C层由PE 12～18份、增粘剂2～3份和甲基 纤维素2～4份混合而成，增粘剂为聚异丁烯或超低密度聚乙烯中的 其中一种。
实施例7
一种PE拉伸缠绕膜增白工艺，包括三层分别为A层/B层/C层， 按照重量百分比，由30％的A层、40％的B层和30％的C层组成，所述 A层由A层由双峰线性低密度聚乙烯15～20份、增粘剂1～4份和甲 基纤维素2～5份混合而成，所述B层由双峰线性低密度聚乙烯20～30份、PE 20～25份、增白剂0.2～3份和增粘剂1～5份混合而成， 所述C层由PE 18～20份、增粘剂2～3份和甲基纤维素2～4份混合 而成，增粘剂为聚异丁烯或超低密度聚乙烯中的其中一种。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明， 凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等， 均应包含在本发明的保护范围之内。

Claims (8)

1.一种PE拉伸缠绕膜增白工艺，其特征在于，包括单层挤出工艺：
按照重量份，由双峰线性低密度聚乙烯30～40份、PE 45～65份、甲基纤维素3～5份、增白剂0.2～3份、增粘剂1～7份混合而成。
2.根据权利要求1所述的一种PE拉伸缠绕膜增白工艺，其特征在于，包括双层挤出工艺：所述双层分别为A层/B层，按照重量百分比，由10％的A层和90％的B层组成，其中，所述A层由双峰线性低密度聚乙烯25～30份、增粘剂1～4份和甲基纤维素2～4份混合而成，所述B层由PE 55～65份、增白剂0.2～3份和增粘剂0～7份混合而成。
3.根据权利要求2所述的一种PE拉伸缠绕膜增白工艺，其特征在于，包括双层挤出工艺：所述双层分别为A层/B层，按照重量百分比，由20％的A层和80％的B层组成，其中，所述A层由双峰线性低密度聚乙烯30～35份、增粘剂1～5份和甲基纤维素2～5份混合而成，所述B层由PE 50～60份、增白剂0.2～3份和增粘剂0～7份混合而成。
4.根据权利要求3所述的一种PE拉伸缠绕膜增白工艺，其特征在于，包括双层挤出工艺：所述双层分别为A层/B层，按照重量百分比，由30％的A层和70％的B层组成，其中，所述A层由双峰线性低密度聚乙烯35～40份、增粘剂1～5份和甲基纤维素2～5份混合而成，所述B层由PE 45～55份、增白剂0.2～3份和增粘剂0～7份混合而成。
5.根据权利要求4所述的一种PE拉伸缠绕膜增白工艺，其特征在于，包括三层挤出工艺：所述三层分别为A层/B层/C层，按照重量百分比，由10％的A层、80％的B层和10％的C层组成，所述A层由A层由双峰线性低密度聚乙烯5～7份、增粘剂1～3份和甲基纤维素1～2份混合而成，所述B层由双峰线性低密度聚乙烯40～45份、PE50～60份、增白剂0.2～3份和增粘剂0～7份混合而成，所述C层由PE 7～9份、增粘剂1～4份和甲基纤维素2～3份混合而成。
6.根据权利要求5所述的一种PE拉伸缠绕膜增白工艺，其特征在于，包括三层挤出工艺：所述三层分别为A层/B层/C层，按照重量百分比，由20％的A层、60％的B层和20％的C层组成，所述A层由A层由双峰线性低密度聚乙烯10～15份、增粘剂1～3份和甲基纤维素2～5份混合而成，所述B层由双峰线性低密度聚乙烯25～35份、PE 30～40份、增白剂0.2～3份和增粘剂1～7份混合而成，所述C层由PE 12～18份、增粘剂2～3份和甲基纤维素2～4份混合而成。
7.根据权利要求6所述的一种PE拉伸缠绕膜增白工艺，其特征在于，包括三层分别为A层/B层/C层，按照重量百分比，由30％的A层、40％的B层和30％的C层组成，所述A层由A层由双峰线性低密度聚乙烯15～20份、增粘剂1～4份和甲基纤维素2～5份混合而成，所述B层由双峰线性低密度聚乙烯20～30份、PE 20～25份、增白剂0.2～3份和增粘剂1～5份混合而成，所述C层由PE 18～20份、增粘剂2～3份和甲基纤维素2～4份混合而成。
8.根据权利要求7所述的一种PE拉伸缠绕膜增白工艺，其特征在于：所述增粘剂为聚异丁烯或超低密度聚乙烯中的其中一种。
CN202011581868.7A 2020-12-28 2020-12-28 一种pe拉伸缠绕膜增白工艺 Pending CN114685875A (zh)