CN114671431A - 一种人造金刚石生产用原材料的处理方法 - Google Patents
一种人造金刚石生产用原材料的处理方法 Download PDFInfo
- Publication number
- CN114671431A CN114671431A CN202210199276.1A CN202210199276A CN114671431A CN 114671431 A CN114671431 A CN 114671431A CN 202210199276 A CN202210199276 A CN 202210199276A CN 114671431 A CN114671431 A CN 114671431A
- Authority
- CN
- China
- Prior art keywords
- pyrophyllite
- dolomite
- graphite
- crushing
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种人造金刚石生产用原材料的处理方法，步骤一：选用叶蜡石和白云石进行复合，具体的：(1)将叶蜡石和白云石进行表面清洁，采用高压水枪进行冲洗，冲洗干净过进行烘干；(2)烘干结束后使用破碎机和研磨机对叶蜡石和白云石进行破碎和粉碎；(3)将叶蜡石和白云石粉末进行焙烧制成复合腔体，即叶蜡石内复合白云石衬套；步骤二：触媒选用11E系列或HT系列合成触媒，石墨选用石墨柱；将石墨柱进行除杂粉碎制成石墨粉，并将石墨粉和合成触媒交替装入步骤一中的复合腔体中，并通过压机在一定的压力和温度下保持10‑20分钟即可。本发明与现有技术相比的优点在于：合理的对原料进行选择和配比，从而有效提高制成人造金刚石的质量和产量。
Description
技术领域
本发明涉及金刚石生产原材料处理方法技术领域，具体是指一种人造金刚石生产用原材料的处理方法。
背景技术
金刚石俗称"金刚钻"，也就是我们常说的钻石，它是一种由纯碳组成的矿物，也是自然界中最坚硬的物质。自18世纪证实了金刚石是由纯碳组成的以后，人们就开始了对人造金刚石的研究，只是在20世纪50年代通过高压研究和高压实验技术的进展，才获得真正的成功和迅速的发展，人造金刚石亦被广泛应用于各种工业，工艺行业。
人造金刚石的制备原料通常需要用到制备腔体、主要制成原料为触媒和石墨，通过触媒和石墨在合成腔体内一定压力和温度的情况下变成人造金刚石。但是目前原材料的选用和处理都不够完美，需要进一步的改进，从而提高人造金刚石制备的质量和产量。
发明内容
本发明要解决的技术问题是克服以上技术缺陷，提供一种人造金刚石生产用原材料的处理方法，合理的对原料进行选择和配比，从而有效提高制成人造金刚石的质量和产量。
为解决上述技术问题，本发明提供的技术方案为：一种人造金刚石生产用原材料的处理方法，包括以下步骤：
步骤一：合成腔体材料的选择和制备
选用叶蜡石和白云石进行复合，具体的：(1)将叶蜡石和白云石进行表面清洁，采用高压水枪进行冲洗，冲洗干净过进行烘干；
(2)烘干结束后使用破碎机和研磨机对叶蜡石和白云石进行破碎和粉碎；
(3)将叶蜡石和白云石粉末进行焙烧制成复合腔体，即叶蜡石内复合白云石衬套；
步骤二：触媒、石墨材料的选择
(1)触媒选用11E系列或HT系列合成触媒，石墨选用石墨柱；
(2)将石墨柱进行除杂粉碎制成石墨粉，并将石墨粉和合成触媒交替装入步骤一中的复合腔体中，并通过压机在一定的压力和温度下保持10-20分钟即可。
优选的，所述石墨粉与合成触媒的重量比为6：4。
优选的，所述步骤一中叶蜡石和白云石的粉碎目数为10-50目。
本发明与现有技术相比的优点在于：采用叶蜡石和白云石进行复合制成的复合腔体，其密封性和保温性较好，从而保证制备金刚石时的压强和温度，采用粉末状的合成触媒和石墨粉有助于增大接触反应面积，同时11E系列或HT系列合成触媒制成的金刚石的低磁百分比、透光度和黄度都较为理想，另外石墨和触媒的配比能够使得制得的金刚石各项指标综合较优。
具体实施方式
下面对本发明做进一步的详细说明。
一种人造金刚石生产用原材料的处理方法，包括以下步骤：
步骤一：合成腔体材料的选择和制备
选用叶蜡石和白云石进行复合，具体的：(1)将叶蜡石和白云石进行表面清洁，采用高压水枪进行冲洗，冲洗干净过进行烘干；
(4)烘干结束后使用破碎机和研磨机对叶蜡石和白云石进行破碎和粉碎；
(5)将叶蜡石和白云石粉末进行焙烧制成复合腔体，即叶蜡石内复合白云石衬套；
步骤二：触媒、石墨材料的选择
(3)触媒选用11E系列或HT系列合成触媒，石墨选用石墨柱；
(4)将石墨柱进行除杂粉碎制成石墨粉，并将石墨粉和合成触媒交替装入步骤一中的复合腔体中，并通过压机在一定的压力和温度下保持10-20分钟即可。
所述石墨粉与合成触媒的重量比为6：4。
所述步骤一中叶蜡石和白云石的粉碎目数为10-50目。
本发明在具体实施时，采用叶蜡石和白云石进行复合制成的复合腔体，白云石含有优良的保温性和不发生相变特征，其密封性和保温性较好，可以提升压力利用率，从而保证制备金刚石时的压强和温度，采用粉末状的合成触媒和石墨粉有助于增大接触反应面积，同时11E系列或HT系列合成触媒制成的金刚石的低磁百分比、透光度和黄度都较为理想，另外石墨和触媒的配比能够使得制得的金刚石各项指标综合较优。
以上对本发明及其实施方式进行了描述，这种描述没有限制性，所示的也只是本发明的实施方式之一，实际的结构并不局限于此。总而言之如果本领域的普通技术人员受其启示，在不脱离本发明创造宗旨的情况下，不经创造性的设计出与该技术方案相似的结构方式及实施例，均应属于本发明的保护范围。
Claims (3)
1.一种人造金刚石生产用原材料的处理方法，其特征在于：包括以下步骤：
步骤一：合成腔体材料的选择和制备
选用叶蜡石和白云石进行复合，具体的：(1)将叶蜡石和白云石进行表面清洁，采用高压水枪进行冲洗，冲洗干净过进行烘干；
(2)烘干结束后使用破碎机和研磨机对叶蜡石和白云石进行破碎和粉碎；
(3)将叶蜡石和白云石粉末进行焙烧制成复合腔体，即叶蜡石内复合白云石衬套；
步骤二：触媒、石墨材料的选择
(1)触媒选用11E系列或HT系列合成触媒，石墨选用石墨柱；
(2)将石墨柱进行除杂粉碎制成石墨粉，并将石墨粉和合成触媒交替装入步骤一中的复合腔体中，并通过压机在一定的压力和温度下保持10-20分钟即可。
2.根据权利要求1所述的一种人造金刚石生产用原材料的处理方法，其特征在于：所述石墨粉与合成触媒的重量比为6：4。
3.根据权利要求1所述的一种人造金刚石生产用原材料的处理方法，其特征在于：所述步骤一中叶蜡石和白云石的粉碎目数为10-50目。