CN1145391A - 瓷砖高级填缝剂的制备方法 - Google Patents

瓷砖高级填缝剂的制备方法 Download PDF

Info

Publication number
CN1145391A
CN1145391A CN 96115732 CN96115732A CN1145391A CN 1145391 A CN1145391 A CN 1145391A CN 96115732 CN96115732 CN 96115732 CN 96115732 A CN96115732 A CN 96115732A CN 1145391 A CN1145391 A CN 1145391A
Authority
CN
China
Prior art keywords
ceramic tile
spackling
tackifier
kilograms
senior
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 96115732
Other languages
English (en)
Other versions
CN1060498C (zh
Inventor
刘其成
高传刚
张�杰
刘成江
王家新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shangdong Shuangfeng Stock Co., Ltd.
Original Assignee
XIKAI BUILDING MATERIAL CO Ltd ZIBO CITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIKAI BUILDING MATERIAL CO Ltd ZIBO CITY filed Critical XIKAI BUILDING MATERIAL CO Ltd ZIBO CITY
Priority to CN 96115732 priority Critical patent/CN1060498C/zh
Publication of CN1145391A publication Critical patent/CN1145391A/zh
Application granted granted Critical
Publication of CN1060498C publication Critical patent/CN1060498C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明提供一种瓷砖高级填缝剂的制备方法，其组成为白水泥、水洗石英砂及浓缩增粘剂，填缝剂各成分的重量百分组成分别为白水泥30-40％、水洗石英砂55-67％、浓缩增粘剂3-9％。该填缝剂和现有技术相比，具有施工范围广、粘着力强、防水、耐风化、施工方便、硬化时间长，能给施工人员留有充分的使用时间等特点，可广泛用瓷砖和其建筑材料缝隙的填充，因而，具有很好的推广使用价值。

Description

瓷砖高级填缝剂的制备方法
本发明涉及一种建筑材料，具体地说是一种瓷砖高级填缝剂的制备方法。
在现代的建筑物中瓷砖已成为主要的建筑装饰材料广泛地用于建筑物的内外墙壁及地面的装饰装修，在现有技术中，瓷砖与建筑物的内外墙壁及地面的粘着施工，多是用普通建筑用水泥细砂和水调和成水泥砂浆作为填缝剂使用，这种用普通水泥和水调和成的填缝剂在施工中广泛存在的不足是粘着力低、硬化时间快，短时间用不完，填缝剂便会失效，导致装修施工完毕后不长的时间内就发生填缝剂在风吹日晒雨淋的自然环境因素的影响下风化脱落，导致雨水渗入瓷砖与墙体之间使粘着剂失去粘着力而使瓷砖脱落，这不仅对施工质量造成严重影响，而且瓷砖从高处自然脱落随时会对过往行人和车辆构成潜在的伤害。
本发明的目的是提供一种防水、耐风化的专门用于填补瓷砖之间缝隙的瓷砖高级填缝剂的制备方法。
本发明的瓷砖高级填缝剂的制备方法，所用原料主要包括白水泥、石英砂及浓缩增粘剂，该填缝剂各成份的重量百分组成分别为：白水泥30-40％、石英砂55-67％、浓缩增粘剂3-9％。
该瓷砖高级填缝剂中浓缩增粘剂各成分重量百分组成为：硫酸钙5-12％、熟石灰10-25％、氧化锌10-15％、硅酸钠40-60％、硅酸钾10-25％，将各成分混合粉碎至70-120目备用。
该瓷砖高级填缝剂的配制方法为：将白水泥、细度为40-60目的水洗石英砂与浓缩增粘剂按比例放入滚筒搅拌器中充分搅拌混合均匀，出料包装成袋即为成品。
实施例：
配方一
本发明的瓷砖高级填缝剂中所使用的浓缩增粘剂的制备：取硫酸钙11公斤、熟石灰10公斤、氧化锌14公斤、硅酸钠45公斤、硅酸钾20公斤，将各成分粉碎至70-120目混合均匀备用。
本发明的瓷砖高级填缝剂的制备方法为，按重量百分比取白水泥30公斤、细度为40-60目水洗石英砂65公斤、浓缩增粘剂3公斤。将白水泥、水洗石英砂与浓缩增粘剂按比例放入滚筒搅拌器中充分搅拌混合均匀，出料包装成袋即为成品。
配方二
本发明的瓷砖高级填缝剂中所使用的浓缩增粘剂的制备：取硫酸钙8公斤、熟石灰15公斤、氧化锌10公斤、硅酸钠42公斤、硅酸钾25公斤，将各成分粉碎至70-120目混合均匀备用。
本发明的瓷砖高级填缝剂的制备方法为，按重量百分比取白水泥40公斤、细度为40-60目水洗石英砂55公斤、浓缩增粘剂5公斤。将白水泥、水洗石英砂与浓缩增粘剂按比例放入滚筒搅拌器中充分搅拌混合均匀，出料包装成袋即为成品。
配方三
本发明的瓷砖高级填缝剂中所使用的浓缩增粘剂的制备：取硫酸钙11公斤、熟石灰13公斤、氧化锌10公斤、硅酸钠55公斤、硅酸钾11公斤，将各成分粉碎至70-120目混合均匀备用。
本发明的瓷砖高级填缝剂的制备方法为，按重量百分比取白水泥36公斤、细度为40-60目水洗石英砂60公斤、浓缩增粘剂4公斤。将白水泥、水洗石英砂与浓缩增粘剂按比例放入滚筒搅拌器中充分搅拌均匀，出料包装成袋即为成品。
本发明的最佳配方为：
本发明的瓷砖高级填缝剂中所使用的浓缩增粘剂的制备：取硫酸钙11公斤、熟石灰12公斤、氧化锌8公斤、硅酸钠60公斤、硅酸钾9公斤，将各成分粉碎至70-120目混合均匀备用。
本发明的瓷砖高级填缝剂的制备方法为，按重量百分比取白水泥35公斤、细度为40-60目水洗石英砂60公斤、浓缩增粘剂5公斤。将白水泥、水洗石英砂与浓缩增粘剂按比例放入滚筒搅拌器中充分搅拌混合均匀，出料包装成袋即为成品。
上述各配方中浓缩增粘剂的用量视使用白水泥的标号适当增减。
本发明的瓷砖高级填缝剂的制备方法生产的填缝剂在瓷砖的粘着装饰施工中的加水量与填缝剂的配比为4∶1调和成膏状，填于瓷砖与瓷砖之间即可，为了使填缝剂的颜色和瓷砖相协调，可根据瓷砖的颜色向填缝剂中加入适量的色料。
该填缝剂的技术指标与现有技术指标对比如下：
项目                  现行建筑标准    本产品指标
调整时间/分                 ≥5           10
晾置时间/分                 10            15
14天抗拉强度MPa/cm          ≥1           1.29
7天浸水后抗拉强度MPa/cm     ≥0.7         0.85
7天100℃水煮抗拉强度MPa/cm  ≥0.7         0.86
25次冻融后抗拉强度MPa/cm    ≥0.7         0.75
本发明的瓷砖高级填缝剂的制备方法生产的填缝剂和现有技术相比，具有应用范围广、粘着力强、防水耐风化、施工方便、硬化时间长、能给施工人员留有充分的使用时间等特点，可用于瓷砖、石材以及其他建筑材料缝隙的填充、因而，具有很好的推广使用价值。

Claims (3)

1.瓷砖高级填缝剂的制备方法，包括白水泥、石英砂及浓缩增粘剂，其特征在于填缝剂各成份的重量百分组成为白水泥30-40％、石英砂55-67％、浓缩增粘剂3-9％。
2.根据权利要求1所述的瓷砖高级填缝剂的制备方法，其特征在于浓缩增粘剂的化学组成为：硫酸钙5-10％、熟石灰10-25％、氧化锌10-15％、硅酸钠40-60％、硅酸钾10-25％，将各成分混合粉碎至70-120目备用。
3.根据权利要求1所述的瓷砖高级填缝剂的制备方法，其特征在于填缝剂的配制方法为：将白水泥、细度为40-60目的水洗石英砂与浓缩增粘剂按比例放入滚筒搅拌器中充分搅拌混合均匀。
CN 96115732 1996-04-08 1996-04-08 瓷砖高级填缝剂 Expired - Fee Related CN1060498C (zh)