CN1144237A - 导线用阻燃硅橡胶及其制造工艺 - Google Patents

导线用阻燃硅橡胶及其制造工艺 Download PDF

Info

Publication number
CN1144237A
CN1144237A CN 96104281 CN96104281A CN1144237A CN 1144237 A CN1144237 A CN 1144237A CN 96104281 CN96104281 CN 96104281 CN 96104281 A CN96104281 A CN 96104281A CN 1144237 A CN1144237 A CN 1144237A
Authority
CN
China
Prior art keywords
sizing material
silicone rubber
wire
silicon oil
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 96104281
Other languages
English (en)
Inventor
苏华
张贞瑞
熊巍峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIAOYUAN JINGXI CHEMICAL INDUSTRY Co SHANGRAO CITY
Original Assignee
LIAOYUAN JINGXI CHEMICAL INDUSTRY Co SHANGRAO CITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIAOYUAN JINGXI CHEMICAL INDUSTRY Co SHANGRAO CITY filed Critical LIAOYUAN JINGXI CHEMICAL INDUSTRY Co SHANGRAO CITY
Priority to CN 96104281 priority Critical patent/CN1144237A/zh
Publication of CN1144237A publication Critical patent/CN1144237A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种制造导线用的阻燃硅橡胶及其制造工艺，它以甲基乙烯基硅橡胶为母体材料，苯胼三唑和氯铂酸为阻燃剂，白炭黑为补强剂，羟基硅油为助剂，再经过混炼、开炼等工艺后即制得成品。本发明具有阻燃效果好、绝缘程度高、耐电压、抗老化、机械强度高的优点。用本发明制成的导线可广泛用于各种电子、电器产品，并用在各种公共场所、宾馆、住宅等地方，可减少大量的火灾事故的发生，为社会带来巨大的经济效益和社会效益。

Description

导线用阻燃硅橡胶及其制造工艺
本发明涉及绝缘材料，尤其是涉及一种导线用阻燃硅橡胶及其制造工艺。
由于越来越多的现代化电子、电器产品进入宾馆、商场、住宅及其它重要部门，功率越来越大，原有的线路老化严重，负荷已不能满足要求，象氯乙烯和橡胶等材料制成的导线绝缘层，因工作温度太低、强度差、易老化，已无法满足日益发展的要求，经常引起火灾，造成惨重的物质和人员损失。授权公告号为CN2122766Y的专利“高电压复合绝缘电缆线”的绝缘层由改性硅橡胶制成，其外层还有一层防护层，绝缘程度高、抗老化、耐热耐寒，但其缺点是不具有阻燃性能，在电线绝缘层起火后不仅不能隔绝氧气起阻燃作用，反而会燃烧起助燃作用。
本发明的目的在于提供一种用于制造导线的阻燃效果好、绝缘程度高、耐电压、抗老化的阻燃硅橡胶及其制造工艺。
本发明的目的是这样实现的：本发明的五种成份的配方(按重量百分比计)为：
甲基乙烯基硅橡胶：45～60％
苯胼三唑：10～15％  氯铂酸：5～8％
羟基硅油：1～2％    白炭黑：20～30％
本发明的制造工艺为：
1、将甲基乙烯基硅橡胶和白炭黑投入密炼机内，再加入羟基硅油，加热进行混炼，加热温度为90～130℃，时间为2～5个小时。
2、加入苯胼三唑和氯铂酸，加热并抽真空，再进行混炼，加热温度为100～300℃，时间为0.5～3个小时，真空度为300～700mmHg。
3、混炼完毕后，将胶料从密炼机内放出进行冷却静置，冷却后的胶料温度降至20～50℃。
4、把冷却后的胶料再送入双辊机上开炼，并加入羟基硅油调整，经薄通后使胶料具有表面光泽，再调节细辊间距至0.2～0.3mm，让胶料全部通过该间隙并刮下，重复三次。
5、将上述胶料重复步骤4开炼三遍即得成品。
本发明以甲基乙烯基硅橡胶为母体材料，苯胼三唑和氯铂酸为阻燃剂，白炭黑为补强剂，羟基硅油为助剂，经过混炼、开炼等工艺后制得的成品，在被加热时阻燃剂会在母体材料表面形成保护层，隔绝同氧气的接触，达到阻燃的目的。经测试，本发明的主要技术指标为：
硬度(邵氏)       60       永久压缩变形％     ≤10
扯断强度(MPa)    ≥9      体积电阻(Ω/cm)    1×1015
撕裂强度(KN/m)   ≥350    阻燃性             94UL标准Vo级
因此本发明具有阻燃效果好、绝缘程度高、耐电压、抗老化、机械强度高的优点，它还具有工艺简单、投资少、回收期短、无环保污染、三废排放的优点，用本发明制成的导线可广泛用于各种电子、电器产品，并用在各种公共场所、宾馆、商场、住宅及其它重要部门，可减少大量的火灾事故的发生，保护国家的财产和人民的生命安全，减少经济损失，为社会带来巨大的经济效益和社会效益。
下面结合实施例对本发明作进一步详细说明。
实施例1：
1、将600kg甲基乙烯基硅橡胶和240kg白炭黑投入密炼机内，再加入5kg羟基硅油，加热进行混炼，加热温度为130℃，加热时间为5个小时。
2、再加入苯胼三唑100kg和氯铂酸50kg，加热并抽真空，再进行混炼，加热温度为300℃，时间为3个小时，真空度为700mmHg。
3、混炼完毕后，将胶料从密炼机内放出冷却静置至50℃。
4、把胶料再送入双辊机上开炼，并加入5kg羟基硅油调整，经薄通后使胶料具有表面光泽，再调节细辊间距至0.3mm，让胶料全部通过该间隙并刮下，重复三次。
5、将上述胶料重复步骤4开炼三遍即得成品。
实施例2：
1、将450kg甲基乙烯基硅橡胶和300kg白炭黑投入密炼机内，再加入10kg羟基硅油，加热进行混炼，加热温度为90℃，时间为2个小时。
2、再加入150kg苯胼三唑和80kg氯铂酸，加热并抽真空，再进行混炼，加热温度为100℃，时间为30分钟，真空度为300mmHg。
3、混炼完毕后，将胶料从密炼机内放出冷却静置至20℃。
4、把胶料再送入双辊机上开炼，并加入10kg羟基硅油调整，经薄通后使胶料具有表面光泽，再调节细辊间距至0.2mm，让胶料全部通过该间隙并刮下，重复三次。
5、将上述胶料重复步骤4开炼三遍即得成品。
实施例3：
1、将570kg甲基乙烯基硅橡胶和200kg白炭黑投入密炼机内，再加入13kg羟基硅油，加热进行混炼，加热温度为110℃，时间为4个小时。
2、再加入140kg苯胼三唑和70kg氯铂酸，加热并抽真空，再进行混炼，加热温度为180℃，时间为2个小时，真空度为500mmHg。
3、混炼完毕后，将胶料从密炼机内放出冷却静置至30℃。
4、再把胶料送入双辊机上开炼，并加入7kg羟基硅油调整，经薄通后使胶料具有表面光泽，再调节细辊间距至0.25mm，让胶料全部通过该间隙并刮下，重复三次。
5、将上述胶料重复步骤4开炼三遍即得成品。

Claims (2)

1、一种导线用阻燃硅橡胶，其特征在于：五种成份的配方(按重量百分比计)为：
甲基乙烯基硅橡胶：45～60％
苯胼三唑：10～15％  氯铂酸：5～8％
羟基硅油：1～2％    白炭黑：20～30％
2、一种制造如权利要求1所述的导线用阻燃硅橡胶的工艺，其特征在于：
(1)将甲基乙烯基硅橡胶和白炭黑投入密炼机内，再加入羟基硅油，加热进行混炼，加热温度为90～130℃，时间为2～5个小时。
(2)加入苯胼三唑和氯铂酸，加热并抽真空，再进行混炼，加热温度为100～300℃，时间为0.5～3个小时，真空度为300～700mmHg。
(3)混炼完毕后，将胶料从密炼机内放出进行冷却静置，冷却后的胶料温度降至20～50℃。
(4)把冷却后的胶料再送入双辊机上开炼，并加入羟基硅油调整，经薄通后使胶料具有表面光泽，再调节细辊间距至0.2～0.3mm，让胶料全部通过该间隙并刮下，重复三次。
(5)将上述胶料重复步骤4开炼三遍即得成品。
CN 96104281 1996-04-12 1996-04-12 导线用阻燃硅橡胶及其制造工艺 Pending CN1144237A (zh)