CN114164539B - Environment-friendly washable fabric for suction and discharge antibacterial machine and production process - Google Patents
Environment-friendly washable fabric for suction and discharge antibacterial machine and production process Download PDFInfo
- Publication number
- CN114164539B CN114164539B CN202111414477.0A CN202111414477A CN114164539B CN 114164539 B CN114164539 B CN 114164539B CN 202111414477 A CN202111414477 A CN 202111414477A CN 114164539 B CN114164539 B CN 114164539B
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- iterative
- environment
- yarn
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an environment-friendly washable fabric of a suction and discharge antibacterial machine, wherein warp yarns are blended yarns of mercerized wool and D-type antibacterial iterative terylene, and weft yarns are elastic core-spun yarns; the sheath yarn of the elastic core-spun yarn is blended yarn of mercerized wool and D-type antibacterial iterative terylene. The environment-friendly suction and discharge antibacterial machine washable fabric adopts mercerized wool and antibacterial iterative terylene blended yarns as warp yarns, uses covering yarns formed by wrapping spandex with the blended yarns as weft yarns, and has excellent skin-friendly soft touch, elasticity, moisture absorption and sweat releasing performance, antibacterial property and machine washable performance. The invention discloses a production process of washable fabric of an environment-friendly suction and discharge antibacterial machine.
Description
Technical Field
The invention belongs to the technical field of fabric production, and particularly relates to an environment-friendly washable fabric for a suction and discharge antibacterial machine and a production process.
Background
Along with the change of life concept of people, the shirt fabric worn next to the skin not only meets the wearing comfort and the simple and easy management, but also has the functional requirements of moisture absorption, sweat releasing, antibacterial property and the like. The iterative terylene has good hydrophilicity and good moisture regain, but in the actual production, the boiling water shrinkage ratio of the iterative terylene is large, about 10 percent, so that the dyeing liquid can not penetrate through wool tops during dyeing to cause the problems of colored patterns and non-colored patterns; the shrinkage further influences the elasticity of the mercerized wool iterative polyester blended yarn and the spandex core-spun yarn, and further influences the width stability of the fabric; the iterative terylene after-finishing temperature has poor shaping effect on spandex elastic varieties; the setting temperature of the conventional spandex varieties also influences the hand feeling and color of the iterative terylene; in order to make shirt fabric soft in hand feeling, a softener is commonly used in after-finishing, but the color of iterative terylene is greatly changed after contacting the softener.
Disclosure of Invention
The invention aims to overcome the defects in the prior art and provide the washable fabric of the environment-friendly suction and discharge antibacterial machine, which takes mercerized wool, D-type silver ion antibacterial iterative terylene and spandex as main fiber raw materials, has excellent moisture absorption and sweat releasing performance and antibacterial performance, is soft in hand feeling and good in rebound resilience, and can be washed by the machine.
In order to achieve the technical effects, the technical scheme of the invention is as follows: an environment-friendly washable fabric of a suction and discharge antibacterial machine is characterized in that warp yarns are blended yarns of mercerized wool and D-type antibacterial iterative terylene, and weft yarns are elastic core-spun yarns; the sheath yarn of the elastic core-spun yarn is blended yarn of mercerized wool and D-type antibacterial iterative terylene.
The preferred technical scheme is that the main raw material fiber components comprise the following components in parts by mass: 48-52 parts of mercerized wool, 44-48 parts of D-type antibacterial iterative terylene and 2-6 parts of spandex.
The second purpose of the invention is to provide a production process of the washable fabric for the environment-friendly suction and discharge antibacterial machine, which is the washable fabric for the environment-friendly suction and discharge antibacterial machine and comprises the following steps: the method comprises the following steps of dyeing, spinning, yarn weaving and after-finishing raw material fibers respectively, wherein before the D-type antibacterial iterative terylene dyeing, the method also comprises the pre-shrinking treatment and the complex combing of a D-type antibacterial iterative terylene ball, and the top pre-shrinking treatment process comprises the following steps: steaming at 110-122 deg.c for 50-60 min. The compound combing treatment can enable the D-type antibacterial iterative polyester wool tops to be fluffy and remove the phenomenon of disordered tops.
The preferable technical scheme is that the dye solution of the D-type antibacterial iterative terylene comprises low-temperature disperse dye, acetic acid and water, and the mass concentration of the acetic acid in the dye solution is 3.7-4.6%. The dye solution is simple in composition, the pH value of the dye solution is adjusted by using acetic acid, and the preferable low-temperature disperse dye has excellent dye uptake to the D-type antibacterial iterative terylene.
The preferable technical scheme is that the D-type antibacterial iterative terylene dyeing process comprises the following steps: dyeing at 40-45 ℃, heating to 58-62 ℃ in the first section, keeping the temperature for 3-8 min, heating to 110-114 ℃ in the second section, and keeping the temperature for 55-70 min; the rate of the second-stage heating is 0.95-1.2 ℃/min. More preferably, the rate of the second-stage heating is 1 to 1.1 ℃/min. Furthermore, the D-type antibacterial iterative terylene is dyed on the hollow sphere in a winding way, and dye liquor can permeate from the inner direction and the outer direction, so that the dyeing is uniform.
The preferable technical scheme is that the D-type antibacterial iterative terylene dyeing process further comprises the following steps: and (2) carrying out acid reduction cleaning on the dyed D-type antibacterial iterative terylene, wherein the main components of the cleaning solution for acid reduction cleaning are organic acid and an acid reduction cleaning agent, the mass percentage of the organic acid in the cleaning solution is 0.85-1.1%, and the cleaning temperature is 60-68 ℃.
The preferred technical scheme is that the speed ratio of the core yarn and the sheath yarn in the elastic core-spun yarn is 1:2. The elasticity of the yarns is weakened by adjusting the speed ratio, so that the fabric width stability is improved while the elastic recovery of the fabric is met, and the after-finishing setting temperature is favorably reduced.
The preferable technical proposal is that the warp yarn is 116 plus or minus 2S/2 blended yarn, and the weft yarn is 106 plus or minus 2S/2 elastic core-spun yarn; the width of the machine for weaving the yarn is 208 plus or minus 2cm, the warp density is 300 plus or minus 5 threads/10 cm, and the weft density is 300 plus or minus 5 threads/10 cm. The width of the upper machine is increased, the warp density and weft density of the upper machine are reduced, the shrinkage rate of the residual boiling water of the antibacterial iterative fibers and the elasticity of spandex yarns are adapted, the internal stress of the fibers, the yarns and the gray fabric can be eliminated, the fibers, the yarns and the gray fabric can be fully and naturally shrunk, and the lower setting temperature for after finishing can be adopted.
The preferable technical scheme is that the after-finishing comprises singeing, open width wool washing, wool drying, intermediate detection, finishing, brushing, shearing, heat setting and steaming in a tank, wherein the heat setting process parameters are as follows: the temperature is 175-185 ℃, the open width is 156 +/-2 cm, and the overfeeding is 10-12%. The fabric has the advantages of stable size after heat setting at 200 ℃ but rough hand feeling and yellow color, and after the heat setting temperature treatment is preferably adopted, the fabric has soft and natural hand feeling, good elasticity and stable size.
The preferable technical scheme is that the after-finishing tank also comprises the steps of dry collision and fabric preshrinking in sequence after steaming. The dry collision can make the fabric more fluffy, loose and thick, the preshrinking makes the fabric smooth and soft, and the dry collision and preshrinking improve the hand feeling and simultaneously improve the moisture absorption.
The invention has the advantages and beneficial effects that:
the environment-friendly absorption and discharge antibacterial machine washable fabric adopts mercerized wool and antibacterial iterative terylene blended yarns as warp yarns, and core spun yarns formed by wrapping spandex with the blended yarns as weft yarns, and has excellent skin-friendly soft touch, elasticity, moisture absorption and sweat releasing performance, antibacterial property and machine washable performance;
the production process of the washable fabric of the environment-friendly suction and discharge antibacterial machine comprises the steps of firstly carrying out antibacterial iterative polyester preshrinking treatment, and compared with the existing polyester preshrinking, the preshrinking temperature is low, but the treatment time is obviously prolonged, the fiber shrinkage of the inner layer and the outer layer of a hair ball is more consistent, the phenomenon of color splash generated during dyeing is effectively reduced, the shrinkage of boiling water is reduced from 10% before preshrinking treatment to about 2% after treatment, and the production requirements of subsequent spinning and after finishing are met.
Detailed Description
The following further describes embodiments of the present invention with reference to examples. The following examples are only for illustrating the technical solutions of the present invention more clearly, and the protection scope of the present invention is not limited thereby.
Example 1
The production process of the washable fabric of the environment-friendly suction and discharge antibacterial machine comprises the following steps:
s1, preparing 16.5-micron mercerized wool, 1.7DD type antibacterial iterative polyester fiber strips and spandex as fiber raw materials of washable fabric of an environment-friendly suction and discharge antibacterial machine;
s2, pre-shrinking the antibacterial iterative polyester fiber strip, steaming for 1 hour at the temperature of 120 +/-2 ℃, combing the wool strip subjected to shrinkage rate reduction again, and pouring the package of the antibacterial iterative polyester fiber strip of the solid ball into the package of the antibacterial iterative polyester fiber strip of the hollow ball;
s3, dyeing the mercerized wool and the antibacterial iterative polyester fiber strips respectively:
1. the mercerized wool dyeing process comprises the following steps:
pretreatment: running the sodium bicarbonate solution at 40 deg.C for 30min, emptying, and running clear water for 3 times at 35 deg.C for 5 min;
dyeing: adding an auxiliary agent at the dyeing starting temperature of 35 ℃ for running for 5min, then adding a dye for running for 20min, and then starting to heat to 45 ℃, wherein the heating rate is 0.5 ℃/min; after the temperature is increased to 70 ℃ after the temperature is increased by 10min at 45 ℃, the temperature increasing rate is 1 ℃/min; running for 5min at 70 deg.C, heating to 90 deg.C, and heating at a rate of 1 deg.C/min; keeping the temperature at 90 ℃ for 70min, and then emptying;
alkali post-treatment: running 3 g/L sodium carbonate at 80 deg.C for 20min, and flushing with hot water to clear the water in the foot;
and (3) neutralization treatment: running 1% detergent and 0.5% formic acid at 40 deg.C for 20min, and taking out;
2. the antibacterial iterative polyester fiber dyeing process comprises the following steps: adopting low-temperature disperse dye, wherein the dye solution comprises 0.2 percent of disperse yellow SE-3RL, 0.033 percent of disperse red jade S-5BL, 1.55 percent of disperse blue 2BLN and 0.42 percent of dyeing auxiliary agent acetic acid;
dyeing: adding auxiliary agent at 45 ℃ for dyeing, operating the dye for 5min, then starting to heat to 60 ℃, keeping the temperature for 5min, heating at the rate of 1 ℃/min, then starting to heat to 110 ℃ at 60 ℃, and heating at the rate of 1 ℃/min. Keeping the temperature at 110 ℃ for 60min and then emptying.
And (3) post-treatment: adding 1.8% acidic reducing agent BOR (Shanghai Yongxin Burlington REDUCTEX BOR liquid reduction cleaning agent) and 1% acetic acid, operating at 65 deg.C for 15min, emptying, and taking out.
And (3) carrying out dewatering, repeated washing and drying on the dyed mercerized wool and the antibacterial iterative polyester fiber, mixing strips according to the ratio of 52.
Yarn specification: the warp adopts 116S/2; the weft yarns adopt 106S/2 elastic core-spun yarns, the core yarns are spandex of 30D, the sheath yarns are untwisted single yarns spun by the two colored wool tops, and the core yarns and the sheath yarns are fed according to the speed ratio of 1:2.
The spinning process starts from sliver mixing, a first needle, a second needle, a third needle, a thick first yarn, a rough yarn and a fine yarn are used, the number of the combined yarn is 6, 8, 3, 2, 4 and 1, the draft multiples are 8, 7.6, 7.3, 7.0, 10.1, 11.13 and 26.2, and the tension of each path is moderate;
the spinning speed is 8000-8600r/min, and the two-for-one twisting speed is 8800r/min; warp yarn is winded and yarn is steamed at 80 ℃ for 10min, folded yarn is steamed at 88 ℃ of 15min +90 ℃ for 15min, weft yarn elastic core-spun yarn is steamed at 90 ℃ of 30min +95 ℃ for 35 min;
weaving: the width of the upper machine is increased to 208cm, and the warp density and weft density of the upper machine are 300 x 300 (root/10 cm);
the after-treatment comprises the following steps:
singeing: the flow rate is 12 mbar, the speed is 100 m/min, the flame is moderate by one-way reversing;
open-width washing: adding 150 g/l of lotion, at a speed of 300 m/min for 20min, and flushing for 20min;
drying the woolen cloth: temperature 80 ℃, open width 154 cm, overfeed 8%;
checking, trimming, brushing and shearing;
heat setting: the temperature is 180 ℃, the speed is 20m/min, the scutching is 156 percent, and the overfeeding is 12 percent;
steaming in a pot: steam pressure p =1kgf/cm 2 The temperature is 105 +/-2 ℃, the steam circulation time is 6min, and the cooling time is 1min;
softening: mechanically softening an Italy imported ZONCO device, and physically impacting and softening for 20min at normal temperature at the speed of 600 m/min;
pre-shrinking the fabric: 3kg of steam at a speed of 20m/min and 2 sections of steam boxes.
Example 2, comparative examples 0 to 2
The samples of the examples 1 to 2 and the comparative examples 0 to 2 are the same batch of antibacterial iterative terylene, the iterative terylene wool tops are preshrunk treated according to the process parameters of the following table, the boiling water shrinkage rate of the inner and outer layer fibers of the preshrunk hair bulb is detected, and the preshrunk effect is examined by comparing the dyeing result:
example 1 and comparative examples 3 to 5
Based on the same mercerized wool antibacterial iterative polyester fiber blended yarn as in example 1, the fabric is woven and treated according to the spinning speed ratio, warp and weft density, upper machine width, setting temperature and steaming specification in comparative examples 3 to 5 shown in the following table, and the obtained finished product of the washable fabric of the environment-friendly suction and discharge antibacterial machine is subjected to steaming detection on size stability (GB/T26382-2011 combed wool fabric), and the style of the finished product is evaluated:
example 1 and comparative examples 6 to 9
The same after-finishing steps (singeing, open width washing, drying, intermediate detection, finishing, brushing, shearing, heat setting and pot steaming) as those of example 1 are adopted for the washable fabric of the environment-friendly suction and discharge antibacterial machine, the dry collision and fabric pre-shrinking treatment is carried out on the steamed fabric of example 1, and the softening agent treatment and hot alkali softening agent removal treatment are selected for the steamed fabric of comparative examples 6 to 9 according to the following table to evaluate the style and hygroscopicity of finished products:
the dry collision and fabric preshrinking treatment is adopted, the treatment of softening agent and hot alkali softening agent removal is reduced, the waste water generated in the production process is reduced, the fabric is not discolored, and the fabric has soft hand feeling and good moisture absorption.
Example 1 test results of the washable fabric for the environmental protection suction and discharge antibacterial machine are as follows:
1. dimensional stability: relaxed dimensional change rate (machine washable class): length-1%, width-1%; the length of the total size change rate (machine washable) is-1 percent, and the width is-1 percent;
2. moisture absorption: the water absorption rate is 128%, the drip diffusion time is 5s, the wicking height is 141mm, and the requirements specified in GB/T21655.1-2008 standard are met;
3. quick drying: the evaporation rate is 0.56g/h; moisture permeability 15200 g/(m) 2 24 h) meets the requirements specified in the GB/T21655.1-2008 standard;
4. color fastness: the water color fastness, the acid sweat stain resistance color fastness, the alkali sweat stain resistance color fastness, the ironing resistance color fastness, the friction color fastness, the washing resistance color fastness and the milk dry cleaning color fastness are all 4-5 grades;
5. bacteriostatic properties (before washing): staphylococcus aureus > 99%, escherichia coli 88%.
The foregoing is only a preferred embodiment of the present invention, and it should be noted that, for those skilled in the art, various modifications and decorations can be made without departing from the technical principle of the present invention, and these modifications and decorations should also be regarded as the protection scope of the present invention.
Claims (9)
1. A production process of washable fabric of an environment-friendly suction and discharge antibacterial machine is characterized in that warp yarns of the washable fabric of the environment-friendly suction and discharge antibacterial machine are blended yarns of mercerized wool and D-type antibacterial iterative terylene, and weft yarns are elastic core-spun yarns; the sheath yarn of the elastic core-spun yarn is blended yarn of mercerized wool and D-type antibacterial iterative terylene;
the method comprises the following steps: the method is characterized by also comprising the preshrinking treatment and the complex combing of the D-type antibacterial iterative terylene ball before the D-type antibacterial iterative terylene dyeing, wherein the top preshrinking treatment process comprises the following steps: steaming at 110-122 deg.c for 50-60 min.
2. The production process of the washable fabric for the environment-friendly suction and discharge antibacterial machine as claimed in claim 1, wherein the main raw material fiber components of the washable fabric for the environment-friendly suction and discharge antibacterial machine comprise, in parts by mass: 48-52 parts of mercerized wool, 44-48 parts of D-type antibacterial iterative terylene and 2-6 parts of spandex.
3. The production process of the washable fabric for the environment-friendly suction and discharge antibacterial machine as claimed in claim 1, wherein the components of the dye solution of the D-type antibacterial iterative terylene are low-temperature disperse dye, acetic acid and water, and the mass concentration of the acetic acid in the dye solution is 3.7-4.6%.
4. The production process of the washable fabric of the environment-friendly suction and discharge antibacterial machine as claimed in claim 3, wherein the D-type antibacterial iterative polyester dyeing process comprises the following steps: dyeing at 40-45 ℃, heating to 58-62 ℃ in the first section, keeping the temperature for 3-8 min, heating to 110-114 ℃ in the second section, and keeping the temperature for 55-70 min; the rate of the second-stage heating is 0.95-1.2 ℃/min.
5. The production process of the washable fabric for the environment-friendly suction and discharge antibacterial machine as claimed in claim 4, wherein the D-type antibacterial iterative polyester dyeing process further comprises: and (2) carrying out acid reduction cleaning on the dyed D-type antibacterial iterative terylene, wherein the main components of the cleaning solution for acid reduction cleaning are organic acid and an acid reduction cleaning agent, the mass percentage of the organic acid in the cleaning solution is 0.85-1.1%, and the cleaning temperature is 60-68 ℃.
6. The process for producing the washable fabric for environmental protection suction and discharge antibacterial machines according to claim 1, wherein the speed ratio of the core yarn to the sheath yarn in the elastic core-spun yarn is 1:2.
7. The production process of the washable fabric for environmental protection suction and discharge antibacterial machines as recited in claim 1, wherein the warp yarn is 116 ± 2S/2 blended yarn, and the weft yarn is 106 ± 2S/2 elastic core-spun yarn; the width of the machine for weaving the yarn is 208 plus or minus 2cm, the warp density is 300 plus or minus 5 threads/10 cm, and the weft density is 300 plus or minus 5 threads/10 cm.
8. The production process of the washable fabric for the environment-friendly suction and discharge antibacterial machine according to claim 3 or 7, characterized in that the after-finishing comprises singeing, open-width washing, drying, middle detection, finishing, brushing, shearing, heat setting and steaming in a tank, wherein the heat setting process parameters are as follows: the temperature is 175-185 ℃, the open width is 156 +/-2 cm, and the overfeed is 10-12%.
9. The process for producing environment-friendly suction and discharge antibacterial machine washable fabric according to claim 7, characterized in that the after-finishing tank further comprises the steps of dry collision and fabric preshrinking in sequence after steaming.