CN105970404A - Preparation method of high-quality viscose, cotton and wool elastic fabric - Google Patents
Preparation method of high-quality viscose, cotton and wool elastic fabric Download PDFInfo
- Publication number
- CN105970404A CN105970404A CN201610480919.4A CN201610480919A CN105970404A CN 105970404 A CN105970404 A CN 105970404A CN 201610480919 A CN201610480919 A CN 201610480919A CN 105970404 A CN105970404 A CN 105970404A
- Authority
- CN
- China
- Prior art keywords
- cotton
- viscose glue
- preparation
- dyeing
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of high-quality viscose, cotton and wool elastic fabric. The method comprises steps as follows: preparation of raw materials: viscose, cotton and wool blended yarn and spandex yarn are prepared; implementation of a weaving process: double-faced ribbing type composite texture is woven by a double-faced ribber, the viscose, cotton and wool blended yarn and the spandex yarn are connected in 1F, wherein the viscose, cotton and wool blended yarn is surface yarn, the spandex yarn is ground yarn, the surface yarn is always located on the front side of the fabric, and viscose, cotton and wool blended yarn is connected in 2F; implementation of a presetting process: the prepared fabric is preset, the temperature of a setting machine is set at 180-200 DEG C, setting is performed after the fabric is immersed in clear water, and the speed is 20-25 m/min; implementation of a dyeing process: cotton and wool are dyed with a two-bath method, and the process comprises pretreatment, wool dyeing and aftertreatment as well as cotton dyeing and aftertreatment; implementation of an afterfinish process: vibrating drying is performed after dyeing is completed, a softening agent is added after drying, and final setting is performed. The preparation method has the benefits as follows: the prepared fabric touches soft and fluffy, has high elasticity, good moisture absorbing performance and excellent thermal insulation performance and is particularly suitable for preparation of close-fitting thermal underwear for the autumn and the winter.
Description
Technical field
The present invention relates to textile and prepare correlative technology field, be specifically related to a kind of high-grade viscose glue cotton wool stretch fabric
Preparation method.
Background technology
Cotton, viscose glue is cellulose fibre, and moisture absorption is ventilative, antistatic, soft the most comfortable, and wherein viscose glue be one regenerated fiber
Cellulose fiber, has the smooth feel of uniqueness.Pilus Caprae seu Ovis is a kind of natural protein fibre, and wool product has soft fluffy, moisture absorption
Property good, warmth retention property is excellent, be difficult to features such as staiing, gloss is soft, is deeply liked by consumers in general, is a kind of high in textile industry
The representative of shelves raw material.Spandex is a kind of functional fibre with high resiliency and recovery, as long as adding a small amount of spandex in fabric
Silk just can be greatly enhanced elasticity and the recovery of fabric, thus improves fit property and the wrinkle resistance of fabric, is to take kind fabric
Increase the most important fibrous raw material of bullet.The fabric made in conjunction with the feature of cotton, viscose glue and Pilus Caprae seu Ovis, not only soft fluffy, the feel of wool are by force, more
Have the advantages that moisture absorption is warming, then be equipped with suitable organizational structure and polyurethane elastic filament, increase its elasticity, be particularly suitable for system
Standby autumn and winter thermal underwear clothes next to the skin.
Summary of the invention
The invention aims to make up the deficiencies in the prior art, it is provided that a kind of high-grade viscose glue cotton wool stretch fabric
Preparation method, soft fluffy, the high resilience of viscose glue cotton wool stretch fabric that the method is made, good hygroscopicity, warming
Property is good.
In order to reach the purpose of the present invention, technical scheme is as follows:
The preparation method of a kind of high-grade viscose glue cotton wool stretch fabric, it is characterised in that comprise the following steps:
1), raw material is prepared: viscose glue cotton wool blended yarn and spandex thread
2), weaving process: (described rib knitting machine plane No. is 18G to the two-sided rib knitting machine selecting type to be 34 inches of 18G, barrel dliameter
Being 34 inches, type is that profit reaches rib knitting machine) it is woven into two-sided rib-loop type complex tissue, 1F connects viscose glue cotton wool blended yarn and spandex
Silk, wherein viscose glue cotton wool blended yarn is veil, and spandex thread is wire gauze, and veil is all the time at fabric face, and 2F connects viscose glue cotton Pilus Caprae seu Ovis
Mixed yarn,
Viscose glue cotton wool blended yarn a length of 15.0cm/25 pin in 1F, spandex thread line length is 4.5cm/25 pin, and 2F line length is
9.5cm/25 pin；
3), presetting technology: by described step 2) prepare fabric carry out pre-setting, forming machine temperature be set to 180～
200 DEG C, crossing clear water wet fixed, speed is 20～25m/min；
4), dyeing: using two bath method dye hair set cottons, process includes pre-treatment, woolen dyed and post processing, cotton dyeing
And post processing；
5), postfinishing process: baking of shaking after having dyeed, dry temperature 150 DEG C, after drying, add softening agent the final shaping, fixed
Type temperature 150 DEG C, speed 15-20m/min.
Preferably, described step 4) in dyeing include:
(1) pre-treating technology flow process: add Pilus Caprae seu Ovis degreaser under room temperature, with the ramp to 70～75 DEG C of 3 DEG C/min,
Draining after insulation 20min, then washing 2 times；
(2) woolen dyed with aftertreatment technology flow process: room temperature adds woolen dyed auxiliary agent and dyestuff, with 0.7 DEG C/min's
Ramp to 60 DEG C, is incubated 10min, then proceedes to the ramp with 0.7 DEG C/min to 95～100 DEG C, is incubated 30min,
Then draining after being cooled to 75～80 DEG C with the speed of 1 DEG C/min,
Woolen dyed complete after clean successively with detergent, clear water, glacial acetic acid, clear water；
(3) cotton dyeing and aftertreatment technology flow process: 40 DEG C add cotton dyeing auxiliary agent and dyestuff, with the speed liter of 1 DEG C/min
Warm to 60～65 DEG C, insulation 60min after addition soda, draining,
Wherein, dyeing type is day slope overflow dyeing machine, main pump rotating speed 55, carries cloth wheel speed 60, nozzle location 90,60S/
Circle, gap 4.
Preferably, the formula of Pilus Caprae seu Ovis degreaser is as follows:
Close fibre and use refining agent 1g/L
Refining agent 0.5g/L
Soda 1g/L
Matrii Sulfas Exsiccatus 5g/L.
Preferably, the formula of described woolen dyed auxiliary agent:
Matrii Sulfas Exsiccatus 5g/L
Anti-wrinkle agent 3g/L in bath
Chelating dispersing agent 3g/L
Glacial acetic acid 0.13g/L
Levelling agent 1g/L.
Preferably, the formula of described cotton dyeing auxiliary agent:
Chelating dispersing agent 3g/L
Anti-wrinkle agent 3g/L in bath
Matrii Sulfas Exsiccatus 30g/L.
Further, the effective gate width preparing finished product fabric is 175～180cm, and Gram Mass is 270～290g, wherein
Viscose glue cotton wool blended yarn ratio is 93%～97%, and spandex thread is 3%～7%.
Preferably, in viscose glue cotton wool blended yarn, the ratio of viscose glue, cotton and Pilus Caprae seu Ovis is 2:1:1.
Preferably, wherein Pilus Caprae seu Ovis is Australia's electoral wool, and its quality count is 70S, and fineness scope is at 18.1-
20.0μm；Wherein viscose glue is Austria's Lenzin viscose glue, and cotton is Xinjiang Long staple cotton.
The invention have the benefit that
Soft fluffy, the high resilience of fabric for preparing, good hygroscopicity, warmth retention property are good, are particularly suitable for preparation patch
The autumn and winter thermal underwear clothes of body.
Accompanying drawing explanation
Fig. 1 is the weave diagram of top grade viscose glue cotton wool stretch fabric of the present invention；
Fig. 2 is woolen dyed process curve figure.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described, but protection scope of the present invention is not limited solely to implement
Example.
Shown in Fig. 1 and Fig. 2, the preparation method of a kind of high-grade viscose glue cotton wool stretch fabric, it is characterised in that include
Following steps:
1) raw material, is prepared: viscose glue cotton wool blended yarn and spandex thread, wherein viscose glue cotton wool blended yarn is that 38S/1 glues
Collodion wool blended yarn, spandex thread is 30D Lycra.In viscose glue cotton wool blended yarn, the ratio of viscose glue, cotton and Pilus Caprae seu Ovis is 2:1:
1.Wherein Pilus Caprae seu Ovis is Australia's electoral wool, and its quality count is 70S, and fineness scope is in 18.1-20.0 μm；Wherein glue
Glue is Austria's Lenzin viscose glue, and cotton is Xinjiang Long staple cotton.
2), weaving process: selecting type is that the two-sided rib knitting machine of 34 inches of 18G is woven into two-sided rib-loop type complex tissue,
1F connects viscose glue cotton wool blended yarn and spandex thread, and wherein viscose glue cotton wool blended yarn is veil, and spandex thread is wire gauze, and veil is all the time
At fabric face, 2F connects viscose glue cotton wool blended yarn,
Viscose glue cotton wool blended yarn a length of 15.0cm/25 pin in 1F, spandex thread line length is 4.5cm/25 pin, and 2F line length is
9.5cm/25 pin；
3), presetting technology: in order to keep the dimensionally stable of spandex face fabric, by described step 2) prepare fabric carry out pre-
Sizing, forming machine temperature is set to 188 DEG C, crosses clear water wet fixed, and speed is 20～25m/min；
4), dyeing: using two bath method dye hair set cottons, process includes pre-treatment, woolen dyed and post processing, cotton dyeing
And post processing；
5), postfinishing process: baking of shaking after having dyeed, dry temperature 150 DEG C, after drying, add softening agent the final shaping, fixed
Type temperature 150 DEG C, speed 15-20m/min.
Described step 4) in dyeing include:
(1) pre-treating technology flow process: add Pilus Caprae seu Ovis degreaser under room temperature, with the ramp to 70 DEG C of 3 DEG C/min, insulation
Draining after 20min, then washing 2 times；
(2) woolen dyed with aftertreatment technology flow process: room temperature adds woolen dyed auxiliary agent and dyestuff, with 0.7 DEG C/min's
Ramp to 60 DEG C, is incubated 10min, then proceedes to the ramp with 0.7 DEG C/min to 98 DEG C, is incubated 30min, then with
The speed of 1 DEG C/min be cooled to 78 DEG C after draining,
Woolen dyed complete after clean successively with detergent, clear water, glacial acetic acid, clear water；
(3) cotton dyeing and aftertreatment technology flow process: 40 DEG C add cotton dyeing auxiliary agent and dyestuff, with the speed liter of 1 DEG C/min
Warm to 60 DEG C, insulation 60min after addition soda, draining,
Wherein, dyeing type is day slope overflow dyeing machine, main pump rotating speed 55, carries cloth wheel speed 60, nozzle location 90,60S/
Circle, gap 4.
Wherein the formula of Pilus Caprae seu Ovis degreaser is as follows:
Close fibre refining agent WX-240 1g/L
Refining agent COLhc 0.5g/L
Soda 1g/L
Matrii Sulfas Exsiccatus 5g/L.
The formula of the most woolen dyed auxiliary agent:
Matrii Sulfas Exsiccatus 5g/L
Anti-wrinkle agent 3g/L in bath
Chelating dispersing agent G600c 3g/L
Glacial acetic acid 0.13g/L
Levelling agent CFE 1g/L.
The wherein formula of cotton dyeing auxiliary agent:
Chelating dispersing agent G600c 3g/L
Anti-wrinkle agent 3g/L in bath
Matrii Sulfas Exsiccatus 30g/L.
The effective gate width preparing finished product fabric is 175～180cm, and Gram Mass is 270～290g, wherein viscose glue cotton sheep
Wool-rich blended yarns ratio is 96%, and spandex thread is 4%.
Last it is noted that above example only in order to the present invention is described and and unrestricted technology described in the invention
Scheme, therefore, although this specification with reference to each above-mentioned embodiment to present invention has been detailed description, but, this
Field it is to be appreciated by one skilled in the art that still the present invention can be modified or equivalent, and all without departing from this
The technical scheme of the spirit and scope of invention and improvement thereof, it all should be contained in scope of the presently claimed invention.
Claims (8)
1. the preparation method of a high-grade viscose glue cotton wool stretch fabric, it is characterised in that comprise the following steps:
1), raw material is prepared: include viscose glue cotton wool blended yarn and spandex thread；
2), weaving process: selecting type is that the two-sided rib knitting machine of 34 inches of 18G is by described viscose glue cotton wool blended yarn and spandex thread
Being woven into two-sided rib-loop type complex tissue, 1F connects viscose glue cotton wool blended yarn and spandex thread, and wherein viscose glue cotton wool blended yarn is
Veil, spandex thread is wire gauze, and both relative positions keep constant, and veil is all the time at fabric face, and 2F connects viscose glue cotton Pilus Caprae seu Ovis and mixes
Spinning,
Viscose glue cotton wool blended yarn a length of 15.0cm/25 pin in 1F, spandex thread line length is 4.5cm/25 pin, and 2F line length is
9.5cm/25 pin；
3), presetting technology: by described step 2) prepare fabric carry out pre-setting, forming machine temperature is set to 180～200
DEG C, cross clear water wet fixed, speed is 20～25m/min；
4), dyeing: use two bath methods dye hairs set cottons, process include pre-treatment, woolen dyed and post processing, cotton dyeing and after
Process；
5), postfinishing process: baking of shaking after having dyeed, dry temperature 150 DEG C, after drying, add softening agent the final shaping, sizing temperature
Spend 150 DEG C, speed 15-20m/min.
The preparation method of high-grade viscose glue cotton wool stretch fabric the most according to claim 1, it is characterised in that described step
4) dyeing in includes:
(1) pre-treating technology flow process: add Pilus Caprae seu Ovis degreaser under room temperature, with the ramp to 70～75 DEG C of 3 DEG C/min, insulation
Draining after 20min, then washing 2 times；
(2) woolen dyed with aftertreatment technology flow process: room temperature adds woolen dyed auxiliary agent and dyestuff, with the speed of 0.7 DEG C/min
It is warmed up to 60 DEG C, is incubated 10min, then proceed to the ramp with 0.7 DEG C/min to 95～100 DEG C, be incubated 30min, then
Draining after being cooled to 75～80 DEG C with the speed of 1 DEG C/min,
Woolen dyed complete after clean successively with detergent, clear water, glacial acetic acid, clear water；
(3) cotton dyeing and aftertreatment technology flow process: 40 DEG C add cotton dyeing auxiliary agent and dyestuff, arrive with the ramp of 1 DEG C/min
60～65 DEG C, insulation 60min after addition soda, draining,
Wherein, dyeing type be day slope overflow dyeing machine, main pump rotating speed 55, carry cloth wheel speed 60, nozzle location 90,60S/ circle,
Gap 4.
The preparation method of high-grade viscose glue cotton wool stretch fabric the most according to claim 2, it is characterised in that Pilus Caprae seu Ovis oil removing
The formula of agent is as follows:
Close fibre and use refining agent 1g/L
Refining agent 0.5g/L
Soda 1g/L
Matrii Sulfas Exsiccatus 5g/L.
The preparation method of high-grade viscose glue cotton wool stretch fabric the most according to claim 2, it is characterised in that described Pilus Caprae seu Ovis
The formula of dyeing assistant:
Matrii Sulfas Exsiccatus 5g/L
Anti-wrinkle agent 3g/L in bath
Chelating dispersing agent 3g/L
Glacial acetic acid 0.13g/L
Levelling agent 1g/L.
The preparation method of high-grade viscose glue cotton wool stretch fabric the most according to claim 2, it is characterised in that described cotton
The formula of color auxiliary agent:
Chelating dispersing agent 3g/L
Anti-wrinkle agent 3g/L in bath
Matrii Sulfas Exsiccatus 30g/L.
The preparation method of high-grade viscose glue cotton wool stretch fabric the most according to claim 1, it is characterised in that prepare finished product
The effective gate width of fabric is 175～180cm, and Gram Mass is 270～290g, and wherein viscose glue cotton wool blended yarn ratio is
93%～97%, spandex thread is 3%～7%.
The preparation method of high-grade viscose glue cotton wool stretch fabric the most according to claim 1, it is characterised in that cotton at viscose glue
In wool blended yarn, the ratio of viscose glue, cotton and Pilus Caprae seu Ovis is 2:1:1.
The preparation method of high-grade viscose glue cotton wool stretch fabric the most according to claim 7, it is characterised in that wherein Pilus Caprae seu Ovis
For Australia's electoral wool, its quality count is 70S, and fineness scope is in 18.1-20.0 μm；Wherein viscose glue is Austria
Lenzin viscose glue, cotton is Xinjiang Long staple cotton.