CN107574534A - A kind of antibiotic health care plumetis that can discharge anion and its production technology - Google Patents
A kind of antibiotic health care plumetis that can discharge anion and its production technology Download PDFInfo
- Publication number
- CN107574534A CN107574534A CN201710869406.7A CN201710869406A CN107574534A CN 107574534 A CN107574534 A CN 107574534A CN 201710869406 A CN201710869406 A CN 201710869406A CN 107574534 A CN107574534 A CN 107574534A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- carbon fibre
- plumetis
- dyeing
- health care
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibiotic health care plumetis that can discharge anion and its production technology, the plumetis to be made by following raw material proportioning:Dyeing of Australian wool 50%, polyester fiber 35%, mulberry silk 5%, bamboo-carbon fibre 10%;The production technology of the plumetis, comprises the following steps:(1)Dyeing process;(2)Spinning process;(3)Weaving process;(4)Finishing process.The present invention has given full play to the premium properties of bamboo-carbon fibre and mulberry silk, wool spinning fabric kind is enriched, improves the class and added value of fabric, appearance of fabrics is fine and smooth, feel is smooth, gloss is naturally soft, color is pure, and sucting wet air permeability is good, and face lines is clear, workmanship is exquisite, the healthcare function of bamboo-carbon fibre is fully demonstrated, added value of product is high, achieves good market effect.
Description
Technical field
The invention belongs to technical field of textile fabric, more particularly to a kind of antibiotic health care plumetis that can discharge anion
And its production technology.
Background technology
With the continuous improvement of people's quality of life, health, environmental consciousness constantly strengthen, to clothes comfortableization, health care,
Superior, fashion-orientation has requirements at the higher level.At present, in the market is emitting far-infrared, anion, conditioning, bacteriostasis antibiosis etc.
The method that functional textile mainly uses addition auxiliary agent during final finishing.The advantages of this method is that technique is simple, is processed into
This is low, but there is also it is very big the defects of:Continuation is poor, in general, the textile processed by afterfinish method, in washing 5-
After 10 times, functional performance can fade away.
The content of the invention
The invention aims to provide a kind of antibiotic health care plumetis that can discharge anion, the product not only has
There is the function such as conditioning, release anion, releasing far infrared, bacteriostasis antibiosis, green, promotion human metabolism,
Also the characteristics of having fully demonstrated wool/mulberry silk softness is smooth, gloss is soft.
In order to realize the purpose of the present invention, the technical scheme of use is:
A kind of antibiotic health care plumetis that can discharge anion, is made by following raw material proportioning:Dyeing of Australian wool 50%, gather
Ester fiber 35%, mulberry silk 5%, bamboo-carbon fibre 10%.
Further, the fineness of the dyeing of Australian wool is 17.5 μm, length 85mm, and the fineness of polyester fiber is
1.5D, length 90mm, the fineness of mulberry silk is 1.5D, and length 95mm, the fineness of bamboo-carbon fibre is 2D, length 85mm.
A kind of production technology for the antibiotic health care plumetis that can discharge anion as described above, comprises the following steps:
(1)Dyeing process
Wool fiber:Using the mentality of designing of 90 DEG C of low temperature dyeings, receive plain reactive dye for wool from environment-friendly type import orchid and carry out
Dyeing, and 0.5% N2 low-temp dyeing accelerants are added, woolen dyed temperature drops to 90 DEG C from 98 DEG C, reduces the damage of wool fiber,
The row yielding of spinning and the strength of yarn are improved, has saved the energy;
Bamboo-carbon fibre:Dyed using Cationic Red X-GRL Huang X-8GL, bamboo-carbon fibre ingoing silver is dyed using 120 DEG C, is
Ensure bamboo-carbon fibre level-dyeing property, acetic acid 0.4g/L, glauber salt 2g/L are first added in dye vat, with delay dyestuff on contaminated
Journey, and 1 degree/min of heating rate is strictly controlled, the pH value of dye vat is maintained between 4-4.5, when dyeing temperature is warming up to 85 DEG C
10min is incubated, is cooled after being then warming up to 120 DEG C of insulation 45min again with 1 degree/min heating rate, and injected clear water, add
The 2g/L of loose colour cleaning agent 8920, is warming up to 90 DEG C of cleaning 20min, and such dyeing causes every color fastness to reach optimal
State;
(2)Spinning process
According to the regain of bamboo-carbon fibre and the size of oil content, 6h~8h is sprayed to bamboo-carbon fibre in 1% ratio before mixed comb
Water, make to be in moisture releasing state in each operation of fiber afterwards, combing using the light feed quantities of 9g/2m choose greatly gauge 30mm from
And the quantity of card nailing neps in fiber is reduced, it is easy to road spinning efficiency after improving, silver mixing adds 40mL Shi Difenxun and crude oil auxiliary agent, goes out
The grams m of bar weight 19,7-8 times of drafting multiple;Rove uses the meter per second of speed 120, increasing tension, make strip yarn outlet with it is thick
Stretched as far as possible between spool, ensure that thick Yarn Evenness is uniform, spun yarn uses compact spinning, 7000 revs/min of speed, winder 750
Rev/min, tension pulley 100cN, 23 DEG C of temperature, humidity 75%;
(3)Weaving process
The 8% water-soluble cold slurry agent of HG-106C is added during warping beaming, makes Yarn filoplume docile, surface is brighter and cleaner, warping
280 revs/min of speed, 80 ms/min of beaming, small tension receiving coil 280N is used on loom, ensures that weaving is smoothed out.
Further, in addition to finishing process:Open washing boils → dried fixed → middle to examine → → bis- to boil → absorb water of singing → wash at a high speed
→ middle inspection → preshrunk → KD tanks steaming → finished product is repaiied in → drying → middle inspection → ripe,
Wash at a high speed:300m/min*50 ' hairs can net 4kg, platen pressure 0.5mbar;It is double to boil technique:Temperature 85 DEG C × 40 ', 1,4
Pressure roller pressurizes, HAC:0.35G/L, pH value 6.5-7.0, employ hydrophilic softening agent JT-3031 and carry out soft treatment, to keep
The hygroscopicity of fabric, it is fixed to dry:Overfeeding in 180 DEG C of * 35m/min, lower gate width 153-154cm;KD tanks steam:Processing time 120S,
Processing pressure 0.6mpar.
Further, the loom uses Italian import Azithromycin rapier loom, 315 degree of opening time, back rest 1-2, knits
Machine tension force 250-280N.
The bamboo-carbon fibre that the present invention uses have it is soft and smooth it is soft it is warm, moisture absorption is ventilative, bacteriostasis antibiosis, it is emitting far-infrared, bear from
Son transmitting concentration height, the absorption affinity that content of mineral substances is high, superpower, it is green the features such as, bamboo charcoal fiber textile is to far infrared
Emissivity is up to 0.87, and energy heat accumulation thermal, temperature rise speed is faster than common bafta, reaches the effect of dehumidifying is with drying, and have and change
Kind microcirculation, the effect such as enhance metabolism.In academia, anion is referred to as " air vitamin " or " long-lived element ", to people
Body has activating cell, purifies the health-care effects such as blood, dispelling fatigue, stable automatic nervous system, improvement allergic constitution, and 82%
Anion can be absorbed by skin, therefore with bamboo-carbon fibre textile is made and is undoubtedly and play anion healthy effect and antibacterial
The fabulous approach of antibacterial.
Mulberry silk is secretion silk liquid concretionary continuous filament yarn when matured silkworm cocoons, and is natural animal protein fiber,
Amino acid and protein during mulberry silk is rich in 18, good permeability, hygroscopicity is splendid, has good nutritive value to human body, has
The good reputation of " fiber queen ".Fiber smooth pliable, rich in gloss, there is sensation cool in summer and warm in winter.
The device have the advantages that:
1st, the present invention has given full play to the premium properties of bamboo-carbon fibre and mulberry silk, enriches wool spinning fabric kind, improves face
The class and added value of material, appearance of fabrics is fine and smooth, and feel is smooth, gloss is naturally soft, and color is pure, and sucting wet air permeability is good,
Face lines is clear, and workmanship is exquisite, has fully demonstrated the healthcare function of bamboo-carbon fibre, added value of product is high, achieves good city
Field-effect.
2nd, the wool that the present invention uses has the characteristics that very thin, frivolous, soft, cunning is glutinous, warming, and bamboo-carbon fibre has temperature adjustment
The features such as damping, release anion, releasing far infrared, bacteriostasis antibiosis, mulberry silk gloss is naturally soft, has fabric good
Moisture absorption is ventilative, the function of bacteriostasis antibiosis, antiultraviolet.
Embodiment
With reference to embodiment, the invention will be further described, but protection scope of the present invention is not limited solely to implement
Example.
The present invention is as follows from the parameter of raw material:
A kind of production technology for the antibiotic health care plumetis that can discharge anion as described above, comprises the following steps:
(1)Dyeing process
Wool fiber:High temperature for a long time boil and not only consume the substantial amounts of energy by boiling, but also can make wool yellowing, and influence fiber can
The bright-coloured Du ﹑ of Fang ﹑ Shou Gan ﹑ Guang Ze ﹑ destroy the natural quality of wool, so using the mentality of designing of low temperature dyeing, from environmental protection
Type import orchid receives plain reactive dye for wool and dyed, and adds a certain amount of 0.5% N2 low-temp dyeing accelerants, woolen dyed temperature
90 DEG C are dropped to from 98 DEG C, reduces the damage of wool fiber, the row yielding of spinning and the strength of yarn is improved, has saved energy
Source.
Bamboo-carbon fibre:Because bamboo-carbon fibre has fine pore structure, there is stronger absorption property to dyestuff, using sun
Daughter ion dyestuff(Cationic Red X-GRL Huang X-8GL)Dyed, bamboo-carbon fibre ingoing silver is dyed using 120 DEG C, to ensure
The level-dyeing property of bamboo-carbon fibre, first adds acetic acid in dye vat(0.4g/L), glauber salt(2g/L), with delay dyestuff on contaminated
Journey, and strictly control heating rate(1 degree/min), the pH value of dye vat is maintained between 4-4.5, when dyeing temperature is higher than 82 degree DEG C
When, due to the defrosting of bamboo-carbon fibre macromolecular chain segment, motion aggravation, dye molecule is easy to internally to spread from fiber surface,
Absorption is in fiber, dyeing rate increase, therefore takes the dyeing course of temperature-gradient method, is warming up to 85 DEG C of insulation 10min, then
Cool after being warming up to 120 DEG C of insulation 45min again with 1 degree/min heating rate, and injected clear water, add detergent(Loose colour is clear
The 2g/L of lotion 8920), be warming up to 90 DEG C of cleaning 20min, such dyeing causes every color fastness to reach optimum state.
(2)Spinning process
It is high according to bamboo-carbon fibre regain, there is the characteristic of very strong moisture adsorption and releasing ability, therefore pre-processed before manufacture.With reference to bamboo
The regain of Carbon fibe and the size of oil content, 6h~8h makes fiber to bamboo-carbon fibre in 1% ratio spray water before mixed comb
Moisture releasing state is in each operation afterwards;Combing is chosen greatly gauge 30mm using the light feed quantities of 9g/2m, so as to reduce fiber
The quantity of middle card nailing neps, is easy to road spinning efficiency after improving, and silver mixing adds 40mL Shi Difenxun and crude oil auxiliary agent, shaping weight 19
Grams m, 7-8 times of drafting multiple.To solve the problems, such as rove broken end, to twine roller serious, and process of roving is adjusted:When
Speed is reduced, using 120 meter per seconds;Second, increasing tension, makes strip be stretched between yarn outlet and flyer bobbin as far as possible, ensure thick
Yarn Evenness is uniform.Spun yarn uses compact spinning, 7000 revs/min of speed, 750 revs/min of winder, tension pulley 100cN, humiture
Control, 23 DEG C of temperature, humidity 75%.Due to control of the Advance of Compact Spinning Technology to spinning triangular zone, ring spinning is substantially eliminated
Filoplume caused by trigonum, therefore yarn is bright and clean, bar is dry uniform, and strength is good.
(3)Weaving process
Because considering yarn strength, while number is again higher, therefore, it is cold that 8% water-soluble HG-106C is added during warping beaming
Agent is starched, makes Yarn filoplume docile, surface is brighter and cleaner, and wearability improves, and reduces broken end.280 revs/min of warping speed, 80 meters of beaming/
Point.Small tension receiving coil 280N is used on loom, ensures that weaving is smoothed out.It is preferred that Italian import Azithromycin rapier loom, is used
Rational technological parameter, 315 degree, back rest 1-2, weaving-machine tension 250-280N of opening time, the emphasis pair warp and weft problem of hanging is controlled
System, ensure that fabric quality.
(4)Finishing process
Technological process:Open washing boil → dry fixed → middle to examine → 1 → height of singing wash it is → bis- to boil → absorb water → dry → middle inspection → ripe repaiies →
Middle inspection → preshrunk → KD tanks steaming → finished product,
Final finishing is keeps the gloss of the function of bamboo-carbon fibre and mulberry silk, using the process route singed after first wet water, each road
Using environment-friend auxiliaries, braying uses slight 40 DEG C × 40min of braying, allows fabric more to shrink and merge in braying;It is high
Speed is washed:The net 4kg of 300m/min*50 ' hairs energy, platen pressure 0.5mbar wind speed 65.It is double to boil technique:Temperature 85 DEG C/40 ', 1,4 adds
Pressure, 200ml HAC, pH value 6.5-7, fabric is allowed preferably to shrink and reply in the case where tension force acts on pressure.To reach fabric hand
Feel soft and smooth, moisture absorption is breathed freely, and is employed hydrophilic softening agent and has been carried out soft treatment, to keep the hygroscopicity of fabric, and strengthen feel,
It is water-fastness to make fabric that there is good crease-resistant recovery.Thermal finalization:Surpass in 180 DEG C of * 35m/min, lower gate width 153-154cm
Hello.Roll soft:Smooth, soft agent JT-302,30G/L, 20m/min, middle overfeeding.KD tanks steam:127# 3# techniques.
It is raw material that the bamboo-carbon fibre of the present invention, which takes mao bamboon, and the calcining that delay is obstructed using 1200 DEG C of pure oxygen high temperature and nitrogen is new
Technique and new technology so that the micropore that bamboo charcoal innately has more refine with honeycomb, then with it is poly- with honeycomb microporous structure
It is ester modified section melt spinning and be made.The maximum unusual part of the fiber is exactly each bamboo-carbon fibre all in inside and outside
The honeycomb microporous structure run through.This unique fibre structure design, can make having given play to for function 100% possessed by bamboo charcoal
Come.It is of course also possible to the bamboo-carbon fibre manufactured from other modes, does not reach effect of the invention simply.
The fabric that the present invention produces has good dimensional stability, and wearability is good, according to standard GB/T/T
26382-2011 is detected, and testing result is as follows:
A. colour fastness to rubbing:>=4-5 levels;
B. bacteriostasis rate >=95%;
C. color fastness to washing:>=4-5 levels;
D. pilling:>=4-5 levels;
E. crease recovery angle:320;
F.PH value=6.3.
Finally it should be noted that:Above example only not limits technology described in the invention to illustrate the present invention
Scheme;Therefore, although this specification with reference to above-mentioned each embodiment to present invention has been detailed description, this
Field it is to be appreciated by one skilled in the art that still can be modified to the present invention or equivalent substitution;And all do not depart from this
The technical scheme of the spirit and scope of invention and its improvement, it all should cover in scope of the presently claimed invention.
Claims (5)
1. a kind of antibiotic health care plumetis that can discharge anion, it is characterised in that be made by following raw material proportioning:The big profit of Australia
Sub-sheep hair 50%, polyester fiber 35%, mulberry silk 5%, bamboo-carbon fibre 10%.
A kind of 2. antibiotic health care plumetis that can discharge anion according to claim 1, it is characterised in that the Australia
The fineness of big Leah wool is 17.5 μm, length 85mm, and the fineness of polyester fiber is 1.5D, length 90mm, mulberry silk
Fineness is 1.5D, and length 95mm, the fineness of bamboo-carbon fibre is 2D, length 85mm.
3. a kind of production technology of antibiotic health care plumetis that can discharge anion according to claim 1 or 2, it is special
Sign is, comprises the following steps:
(1) dyeing process
Wool fiber:Using the mentality of designing of 90 DEG C of low temperature dyeings, receive plain reactive dye for wool from environment-friendly type import orchid and carry out
Dyeing, and 0.5%N2 low-temp dyeing accelerants are added, woolen dyed temperature drops to 90 DEG C from 98 DEG C, reduces the damage of wool fiber,
The row yielding of spinning and the strength of yarn are improved, has saved the energy;
Bamboo-carbon fibre:Dyed using Cationic Red X-GRL Huang X-8GL, bamboo-carbon fibre ingoing silver is dyed using 120 DEG C, is
Ensure bamboo-carbon fibre level-dyeing property, acetic acid 0.4g/L, glauber salt 2g/L are first added in dye vat, with delay dyestuff on contaminated
Journey, and 1 degree/min of heating rate is strictly controlled, the pH value of dye vat is maintained between 4-4.5, when dyeing temperature is warming up to 85 DEG C
10min is incubated, is cooled after being then warming up to 120 DEG C of insulation 45min again with 1 degree/min heating rate, and injected clear water, add
The 2g/L of loose colour cleaning agent 8920, is warming up to 90 DEG C of cleaning 20min, and such dyeing causes every color fastness to reach optimal
State;
(2) spinning process
According to the regain of bamboo-carbon fibre and the size of oil content, 6h~8h is sprayed to bamboo-carbon fibre in 1% ratio before mixed comb
Watering, make to be in moisture releasing state in each operation of fiber afterwards, combing using the light feed quantities of 9g/2m choose greatly gauge 30mm from
And the quantity of card nailing neps in fiber is reduced, it is easy to road spinning efficiency after improving, silver mixing adds 40mL Shi Difenxun and crude oil auxiliary agent, goes out
The grams m of bar weight 19,7-8 times of drafting multiple;Rove uses the meter per second of speed 120, increasing tension, make strip yarn outlet with it is thick
Being stretched as far as possible between spool, ensure that thick Yarn Evenness is uniform, spun yarn uses compact spinning, 7000 revs/min of speed, 750 turns of winder/
Point, tension pulley 100cN, 23 DEG C of temperature, humidity 75%;
(3) weaving process
The 8% water-soluble cold slurry agent of HG-106C is added during warping beaming, makes Yarn filoplume docile, surface is brighter and cleaner, warping
280 revs/min of speed, 80 ms/min of beaming, small tension receiving coil 280N is used on loom, ensures that weaving is smoothed out.
4. a kind of production technology of antibiotic health care plumetis that can discharge anion according to claim 3, its feature
It is, in addition to finishing process:Open washing boil → dry it is fixed it is → middle to examine → singe → wash at a high speed it is → bis- to boil → absorb water → dry → in
→ middle inspection → preshrunk → KD tanks steaming → finished product is repaiied in inspection → ripe,
Wash at a high speed:300m/min*50 ' hairs can net 4kg, platen pressure 0.5mbar;It is double to boil technique:Temperature 85 DEG C × 40 ', 1,4 is pressed
Roller pressurizes, HAC:0.35G/L, pH value 6.5-7.0, employ hydrophilic softening agent JT-3031 and carry out soft treatment, to keep fabric
Hygroscopicity, it is fixed to dry:Overfeeding in 180 DEG C of * 35m/min, lower gate width 153-154cm;KD tanks steam:Processing time 120S, processing
Pressure 0.6mpar.
5. a kind of production technology of antibiotic health care plumetis that can discharge anion according to claim 3, its feature
It is, the loom uses Italian import Azithromycin rapier loom, 315 degree, back rest 1-2, weaving-machine tension 250- of opening time
280N。