CN114105597A - 一种轻质抹灰石膏材料 - Google Patents
一种轻质抹灰石膏材料 Download PDFInfo
- Publication number
- CN114105597A CN114105597A CN202111531549.XA CN202111531549A CN114105597A CN 114105597 A CN114105597 A CN 114105597A CN 202111531549 A CN202111531549 A CN 202111531549A CN 114105597 A CN114105597 A CN 114105597A
- Authority
- CN
- China
- Prior art keywords
- parts
- gypsum
- plastering gypsum
- containing material
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种轻质抹灰石膏材料，按重量份数计原料包括：石膏600–800份、轻骨料50–90份、重钙粉200–300份、减水剂1.0–2.0份、缓凝剂1.0–1.5份、纤维素醚0.5–1.0份、胶粉5–10份、淀粉醚0.2–0.4份、引气剂0.15–0.25份、触变润滑剂0.5–1.0份、水400–500份。本发明的轻质抹灰石膏材料绿色环保，粘结力强、不易脱落、收缩性小，施工方便、和易性好，具有良好的保水性和工作性，强度增长快，可节约工期。
Description
技术领域
本发明属于抹灰石膏领域，具体涉及一种轻质抹灰石膏材料。
背景技术
近年来，加气混凝土砌块、混凝土空心砌块及各种预制条板等新型墙体材料得到了大量使用，而此类墙材的抹灰大多仍沿用现场搅拌水泥砂浆和混合砂浆的做法，造成粉刷层与墙体粘结强度低，进而出现开裂、起壳甚至剥落等诸多质量问题，严重影响了建筑表观质量和使用功能。随着石膏产品的迅速发展，轻质粉刷石膏制品以其施工性能优异、粘结性好等特点，适用于工业与民用建筑的室内墙面及顶棚抹灰，有效解决了抹灰工程中空鼓、开裂、脱落等质量通病，成为水泥砂浆和混合砂浆的理想替代产品，发达国家近年80％以上的内墙采用抹灰石膏，同时基本解决工业副产石膏综合利用的难题。随着水泥、黄砂和人工价格上升，抹灰石膏具备越来越明显的综合优势，抹灰石膏替代水泥砂浆克服了传统工艺难以解决的弊端，既节约施工成本，又控制后期维修等费用，提升了施工质量，满足了各项设计及施工规范要求，已成为建筑内墙粉刷的必然选择，如何寻求一种综合性能好的抹灰石膏材料是目前急需解决的问题。
发明内容
本发明的目的在于提供一种轻质抹灰石膏材料，密度小且具有良好的粘结性能，同时可以实现隔音和保温效果。
本发明的上述目的通过以下技术方案实现：
本发明提供一种轻质抹灰石膏材料，按重量份数计，其原料包括：石膏600–800份、轻骨料50–90份、重钙粉200–300份、减水剂1.0–2.0份、缓凝剂1.0–1.5份、纤维素醚0.5–1.0份、胶粉5–10份、淀粉醚0.2–0.4份、引气剂0.15–0.25份、触变润滑剂0.5–1.0份、水400–500份。
优选地，所述石膏选自半水石膏和/或II型无水硫酸钙。
优选地，所述轻骨料为粒径70–90目的玻化微珠，其密度较小，能降低轻质抹灰石膏材料的密度，且具有隔音和保温效果。
优选地，所述触变润滑剂的主要成分为季戊四醇醇酸树脂，提纯稀释分装而成，在石膏砂浆中可以形成柔韧的凝胶体，具有保水、增稠、触变、改善手感、提高湿浆体和硬化体均匀性的作用，增加材料的触变性能。
本发明中由高性能聚羧酸减水剂、缓凝剂、纤维素醚、胶粉、淀粉醚份、引气剂、触变润滑剂按质量比为1.0–2.0：1.0–1.5：0.5–1.0：5–10：0.2–0.4：0.15–0.25：0.5–1.0组成的外加剂，在满足强度和施工性能的基础上，可以保证材料不出现早期的塑性开裂，所述淀粉醚可增加抹灰石膏的抗垂挂性能，所述胶粉可增加材料的粘结性能。
与现有技术相比，本发明的有益效果在于：
(1)本发明的轻质抹灰石膏材料添加淀粉醚，在满足基本性能的基础上，可以增加抹灰石膏的抗垂挂性能，保证抹灰石膏施工厚度较大时不坠落。
(2)本发明通过添加胶粉，在满足强度和施工性能的基础上，可以增加材料的粘结性能。
(3)本发明的轻质抹灰石膏材料通过添加触变润滑剂可改善抹灰石膏的抹面性能。
(4)本发明的轻质抹灰石膏材料绿色环保，粘结力强、不易脱落、收缩性小，施工方便、和易性好，具有良好的保水性和工作性，强度增长快，可节约工期。
附图说明
图1为实施例中轻质抹灰石膏材料的抗压强度检测现场图片。
图2为实施例中轻质抹灰石膏材料和混凝土基材的粘结强度检测现场图片。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
以下实施例采用的轻质抹灰石膏材料，按重量份数计原料包括：石膏600–800份、玻化微珠50–90份、重钙粉200–300份、减水剂1.0–2.0份、缓凝剂1.0–1.5份、纤维素醚0.5–1.0份、胶粉5–10份、淀粉醚0.2–0.4份、引气剂0.15–0.25份、触变润滑剂0.5–1.0份和水400–500份，其中玻化微珠的粒径为70–90目，石膏选自半水石膏和/或II型无水硫酸钙。
以下通过具体实施例进一步解释说明。
实施例1
按如下重量份数的原料混合制备轻质抹灰石膏材料，具体为：半水石膏600份、玻化微珠90份、重钙粉300份、减水剂1.1份、缓凝剂1.1份、纤维素醚0.6份、胶粉10份、淀粉醚0.3份、引气剂0.20份、触变润滑剂0.8份和水450份。
实施例2
按如下重量份数的原料混合制备轻质抹灰石膏材料，具体为：II型无水硫酸钙700份、玻化微珠80份、重钙粉210份、减水剂1.25份、缓凝剂1.25份、纤维素醚0.7份、胶粉10份、淀粉醚0.4份、引气剂0.20份、触变润滑剂0.8份和水450份。
实施例3
按如下重量份数的原料混合制备轻质抹灰石膏材料，具体为：半水石膏800份、玻化微珠80份、重钙粉110份、减水剂1.5份、缓凝剂1.5份、纤维素醚1.0份、胶粉10份、淀粉醚0.4份、引气剂0.20份、触变润滑剂0.8份和水450份。
实施例4
按如下重量份数的原料混合制备轻质抹灰石膏材料，具体为：半水石膏和II型无水硫酸钙的混合物680份、玻化微珠70份、重钙粉240份、减水剂1.2份、缓凝剂1.3份、纤维素醚0.7份、胶粉10份、淀粉醚0.3份、引气剂0.15份、触变润滑剂0.8份和水450份。
实施例5
按如下重量份数的原料混合制备轻质抹灰石膏材料，具体为：II型无水硫酸钙680份、玻化微珠70份、重钙粉240份、减水剂1.2份、缓凝剂1.3份、纤维素醚0.7份、胶粉10份、淀粉醚0.5份、引气剂0.15份、触变润滑剂0.8份和水450份。
实施例1–5制备的轻质抹灰石膏材料性能测试结果如表1所示。
表1
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
| 保水率(％) | 61 | 63 | 68 | 67 | 68 |
| 抗折强度(MPa) | 1.0 | 1.2 | 1.3 | 1.2 | 1.2 |
| 抗压强度(MPa) | 2.6 | 2.7 | 2.9 | 2.8 | 2.8 |
| 粘结强度(MPa) | 0.33 | 0.35 | 0.38 | 0.35 | 0.35 |
| 体积密度(kg/m<sup>3</sup>) | 990 | 980 | 960 | 980 | 980 |
综上可知，本发明的轻质抹灰石膏材料是一种绿色环保、粘结力强、不易脱落、收缩性小，施工方便、和易性好的建筑内墙材料，替代水泥砂浆具有良好的保水性和工作性，强度增长快，可节约工期。
上述对实施例的描述是为了便于该技术领域的普通技术人员能理解和使用本发明。熟悉本领域技术人员显然可以容易的对这些实施例做出各种修改，并把在此说明的一般原理应用到其他实施例中，而不必经过创造性的劳动。因此，本发明不限于上述实施例。本领域技术人员根据本发明的原理，不脱离本发明的范畴所做出的改进和修改都应该在本发明的保护范围之内。
Claims (4)
1.一种轻质抹灰石膏材料，其特征在于，按重量份数计，其原料包括：石膏600–800份、轻骨料50–90份、重钙粉200–300份、减水剂1.0–2.0份、缓凝剂1.0–1.5份、纤维素醚0.5–1.0份、胶粉5–10份、淀粉醚0.2–0.4份、引气剂0.15–0.25份、触变润滑剂0.5–1.0份、水400–500份。
2.根据权利要求1所述的轻质抹灰石膏材料，其特征在于，所述石膏选自半水石膏和/或II型无水硫酸钙。
3.根据权利要求1所述的轻质抹灰石膏材料，其特征在于，所述轻骨料为粒径70–90目的玻化微珠。
4.根据权利要求1所述的轻质抹灰石膏材料，其特征在于，所述触变润滑剂的主成分为季戊四醇醇酸树脂。