CN114085646A - 一种非固化自愈性自粘防水涂料、防水卷材及其制备方法 - Google Patents
一种非固化自愈性自粘防水涂料、防水卷材及其制备方法 Download PDFInfo
- Publication number
- CN114085646A CN114085646A CN202111506895.2A CN202111506895A CN114085646A CN 114085646 A CN114085646 A CN 114085646A CN 202111506895 A CN202111506895 A CN 202111506895A CN 114085646 A CN114085646 A CN 114085646A
- Authority
- CN
- China
- Prior art keywords
- parts
- styrene
- waterproof
- waterproof coating
- self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种非固化自愈性自粘防水涂料、防水卷材及其制备方法，涉及防水涂料及防水卷材技术领域。所述防水涂料包括以下重量份的各组分：沥青：40～50份，橡胶油：8～10份，苯乙烯‑异戊二烯‑苯乙烯共聚物：2～3份，丁苯橡胶：2～3份，增粘树脂：4～6份，马来酸酐：2～4份，聚酰胺：2～4份，乙撑双硬脂酰胺：2～4份，防老剂：1～2份和填料：20～24份。本发明所提供的防水涂料和防水卷材具有良好的自愈自粘性能，并且具有优异的抗拉强度、耐热性能和低温柔性。
Description
技术领域
本发明涉及防水涂料及防水卷材技术领域，尤其是涉及一种非固化自愈性自粘防水涂料、防水卷材及其制备方法。
背景技术
建筑外墙用瓷砖和防水涂料是比较常见的外墙装饰方式。通常防水涂料以水乳型防水涂料为主，涂料经固化后具有良好的延伸性和抗渗透性能，起到防止雨水渗漏的功能。将防水涂料浸渍在胎体上，制作成的防水材料产品，以卷材形式提供，称为防水卷材。防水卷材通常具有良好的耐水性和一定的机械强度，是重要的建筑工程防水材料之一。
非固化橡胶沥青类涂料是建筑物进行防水、防渗透而经常采用的一类涂料。非固化橡胶沥青防水涂料是以橡胶、沥青、软化油为主要组份，加入温控剂与填料混合制成的具有粘性的膏状体。
近来，非固化橡胶沥青类涂料受到越来越多的关注，现有技术中也采用多种改性剂等助剂来提高该类防水涂料的综合性能。然而，目前该类型的防水涂料还存在一些缺陷，例如柔软性很差(尤其是低温柔性较差)以及耐热性能一般。因此，有必要继续研发综合性能更优异的非固化防水涂料。
鉴于此，特提出本发明。
发明内容
本发明的目的在于提供一种非固化自愈性自粘防水涂料、防水卷材及其制备方法。本发明所提供的防水涂料和防水卷材具有良好的自愈自粘性能，并且具有优异的抗拉强度、耐热性能和低温柔性。
本发明提供的技术方案如下：
在一个方面，本发明提供一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青：40～50份，橡胶油：8～10份，苯乙烯-异戊二烯-苯乙烯共聚物：2～3份，丁苯橡胶：2～3份，增粘树脂：4～6份，马来酸酐：2～4份，聚酰胺：2～4份，乙撑双硬脂酰胺：2～4份，防老剂：1～2份和填料：20～24份。
在一个实施方案中，本发明的非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青：43～48份，橡胶油：8.5～9.5份，苯乙烯-异戊二烯-苯乙烯共聚物：2.5～2.8份，丁苯橡胶：2.3～2.9份，增粘树脂：4.5～5.5份，马来酸酐：2.2～3.5份，聚酰胺：2.5～3.8份，乙撑双硬脂酰胺：2.6～3.6份，防老剂：1.5～1.8份和填料：22～23份。
本发明使用马来酸酐接枝沥青与聚酰胺可增强涂料与不同基层的自粘效果；使用马来酸酐接枝沥青与乙撑双硬脂酰胺，降低体系粘度，提高其自愈性，提高其耐热性。
在一个实施方案中，所述橡胶油包括石蜡基橡胶油、环烷基橡胶油和芳香基橡胶油中的一种或多种。
在一个实施方案中，所述沥青使用常规商购的沥青种类，优选包括70#沥青、90#沥青中的任一种。
在一个实施方案中，所述苯乙烯-异戊二烯-苯乙烯共聚物包括苯乙烯-异戊二烯-苯乙烯共聚物1105(SIS 1105)、苯乙烯-异戊二烯-苯乙烯共聚物1126(SIS 1126)和苯乙烯-异戊二烯-苯乙烯共聚物1106(SIS 1106)中的一种或多种。
在一个实施方案中，所述丁苯橡胶为含胶量50％以上的丁苯橡胶。
在一个实施方案中，所述增粘树脂包括C5石油树脂(碳五树脂)、古马隆石油树脂和萜烯树脂中的任一种。
在一个实施方案中，所述马来酸酐包括顺丁烯二酸酐。
在一个实施方案中，所述聚酰胺包括中性聚酰胺；所述乙撑双硬脂酰胺包括N,N’-乙撑双硬脂酰胺。
在一个实施方案中，所述填料包括滑石粉、轻钙中的任一种；所述防老剂包括紫外线吸收剂和/或抗热氧老化防老剂；所述紫外线吸收剂选自UV-P、UV-O、UV-351中的任一种；所述抗热氧老化防老剂选自防老剂D、防老剂IPPD中的任一种。
在另一个方面，本发明提供了所述防水涂料的制备方法，所述方法包括以下步骤：将沥青与橡胶油加入反应釜中，加热至175～185℃，加入苯乙烯-异戊二烯-苯乙烯、丁苯橡胶，溶胀1～2h，然后加入增粘树脂，溶胀0.3～0.6h，然后加入聚酰胺与马来酸酐反应0.8～1.2h，加入乙撑双硬脂酰胺反应0.3～0.6h，研磨后加入防老剂和填料。
在另一个方面，本发明提供了一种防水卷材，所述防水卷材含有前述的防水涂料。
在一个实施方案中，将前述的防水涂料刮涂至高密度聚乙烯胎体，两面覆隔离材料制得防水卷材；优选地，所述隔离材料为硅油隔离膜。
在一个具体的实施方案中，所述高密度聚乙烯胎体的表面覆有玻璃纤维，两面覆以丁基橡胶沥青为自粘胶层的高分子防水卷材。
在一个实施方案中，所述胎体的上下表面膜可根据不同的应用部位采用不同的隔离材料制成柔性防水卷材。
有益效果：
本发明提供的防水涂料和防水卷材不仅防水效果好、自粘合效果好；而且耐热和耐老化性能优异、低温性能突出；
本发明提供的防水涂料和防水卷材对破损或损伤具有自我愈合能力、抗拉强度高，对基层收缩变形和开裂的适应能力强；
本发明提供的防水涂料和防水卷材安全环保：基层粘结不脱落、不窜水、施工过程不污染环境。
具体实施方式
下面将结合实施例对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青(70#)：45份，橡胶油(石蜡基橡胶油)：9份，苯乙烯-异戊二烯-苯乙烯共聚物(SIS 1105)：2.5份，丁苯橡胶：2.5份，增粘树脂(C5石油树脂)：5份，马来酸酐(顺丁烯二酸酐)：3份，聚酰胺(中性聚酰胺)：3份，乙撑双硬脂酰胺(N,N’-乙撑双硬脂酰胺)：3份，防老剂(紫外线吸收剂UV-P)：1.5份和填料(滑石粉)：22份。
上述非固化自愈性自粘防水涂料经以下制备工艺制得：
将沥青与橡胶油加入反应釜中，加热至180℃，加入SIS、SBR，溶胀1.5h，然后加入增粘树脂，溶胀0.5h，然后加入聚酰胺与马来酸酐反应1h，加入乙撑双硬脂酰胺反应0.5h，研磨后加入防老剂和填料，均匀搅拌。
实施例2
一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青(70#)：40份，橡胶油(石蜡基橡胶油)：8份，苯乙烯-异戊二烯-苯乙烯共聚物(SIS 1105)：2份，丁苯橡胶：2份，增粘树脂(C5石油树脂)：4份，马来酸酐(顺丁烯二酸酐)：2份，聚酰胺(中性聚酰胺)：2份，乙撑双硬脂酰胺(N,N’-乙撑双硬脂酰胺)：2份，防老剂(紫外线吸收剂UV-P)：1份和填料(滑石粉)：20份。
制备方法同实施例1。
实施例3
一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青(70#)：50份，橡胶油(石蜡基橡胶油)：10份，苯乙烯-异戊二烯-苯乙烯共聚物(SIS 1105)：3份，丁苯橡胶：3份，增粘树脂(C5石油树脂)：6份，马来酸酐(顺丁烯二酸酐)：4份，聚酰胺(中性聚酰胺)：4份，乙撑双硬脂酰胺(N,N’-乙撑双硬脂酰胺)：4份，防老剂(紫外线吸收剂UV-P)：2份和填料(滑石粉)：24份。
制备方法同实施例1。
实施例4
一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青(70#)：50份，橡胶油(环烷基橡胶油)：10份，苯乙烯-异戊二烯-苯乙烯共聚物(SIS 1106)：3份，丁苯橡胶：3份，增粘树脂(C5石油树脂)：6份，马来酸酐(顺丁烯二酸酐)：4份，聚酰胺(中性聚酰胺)：4份，乙撑双硬脂酰胺(N,N’-乙撑双硬脂酰胺)：4份，防老剂(紫外线吸收剂UV-P)：2份和填料(滑石粉)：24份。
制备方法同实施例1。
实施例5
一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青(70#)：50份，橡胶油(环烷基橡胶油)：10份，苯乙烯-异戊二烯-苯乙烯共聚物(SIS 1106)：3份，丁苯橡胶：3份，增粘树脂(古马隆石油树脂)：6份，马来酸酐(顺丁烯二酸酐)：4份，聚酰胺(中性聚酰胺)：4份，乙撑双硬脂酰胺(N,N’-乙撑双硬脂酰胺)：4份，防老剂(紫外线吸收剂UV-P)：2份和填料(轻钙)：24份。
制备方法同实施例1。
实施例6
一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青(70#)：50份，橡胶油(环烷基橡胶油)：10份，苯乙烯-异戊二烯-苯乙烯共聚物(SIS 1106)：3份，丁苯橡胶：3份，增粘树脂(萜烯树脂)：6份，马来酸酐(顺丁烯二酸酐)：4份，聚酰胺(中性聚酰胺)：4份，乙撑双硬脂酰胺(N,N’-乙撑双硬脂酰胺)：4份，防老剂(防老剂D)：2份和填料(轻钙)：24份。
制备方法同实施例1。
实施例7
一种非固化自愈性自粘防水涂料，包括以下重量份的各组分：沥青(70#)：45份，橡胶油(石蜡基橡胶油)：9份，苯乙烯-异戊二烯-苯乙烯共聚物(SIS 1105)：2.5份，丁苯橡胶：2.5份，增粘树脂(C5石油树脂)：5份，马来酸酐(顺丁烯二酸酐)：3份，聚酰胺(中性聚酰胺)：3份，乙撑双硬脂酰胺(N,N’-乙撑双硬脂酰胺)：3份，防老剂(紫外线吸收剂UV-P)：1.5份和填料(滑石粉)：22份。
上述非固化自愈性自粘防水涂料经以下制备工艺制得：
将沥青与橡胶油加入反应釜中，加热至176℃，加入SIS、SBR，溶胀2h，然后加入增粘树脂，溶胀0.3h，然后加入聚酰胺与马来酸酐反应1.2h，加入乙撑双硬脂酰胺反应0.4h，研磨后加入防老剂和填料。
对比例1
与实施例1的组分和制备方法基本相同，不同之处在于，用苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)替换实施例1中的苯乙烯-异戊二烯-苯乙烯共聚物(SIS)。
对比例2
与实施例1的组分和制备方法基本相同，不同之处在于，不添加马来酸酐。
对比例3
与实施例1的组分和制备方法基本相同，不同之处在于，马来酸酐的添加量过低，为0.5份。
对比例4
与实施例1的组分和制备方法基本相同，不同之处在于，马来酸酐的添加量过高，为10份。
对比例5
与实施例1的组分和制备方法基本相同，不同之处在于，聚酰胺的添加量过低，为0.5份。
对比例6
与实施例1的组分和制备方法基本相同，不同之处在于，聚酰胺的添加量过高，为9份。
效果性能测试：
将实施例1-7的防水涂料刮涂至高密度聚乙烯胎体，两面覆隔离材料硅油隔离膜制得非固化自愈性自粘防水卷材。
将对比例1-6的防水涂料刮涂至高密度聚乙烯胎体，两面覆隔离材料硅油隔离膜制得非固化自愈性自粘防水卷材。
对制得的防水卷材进行检测，检测依据是：GB/T 35467-2017《湿铺防水卷材》；GB23441--2009《自粘聚合物改性沥青防水卷材》；GB/T 328.9-2007《建筑防水卷材试验方法第9部分:高分子防水卷材拉伸性能》；GB/T328.14-2007《建筑防水卷材试验方法第14部分：沥青防水卷材低温柔性》；GB/T 35468-20I7《种植屋面用耐根穿刺防水卷材》。
检测环境为：22℃～24℃；相对湿度为50％～55％。
耐热性：80℃，2h；无流淌、滑动、滴落；
低温柔性：-25℃，无裂纹；
不透水性：0.4MPa，120min无渗水；
热老化(80℃，168h)：拉力保持率，伸长率保持率；
断裂伸长率：标准条件、碱、盐、热以及紫外线处理下的平均断裂伸长率。
在表1中示出了实施例1-7与对比例1-6防水涂料的各项性能参数。
表1.防水涂料制得非固化自愈性自粘防水卷材的性能检测
综上实验测定结果，本发明实施例的防水卷材各项性能参数如下：耐热性80℃，2h；无流淌、滑动、滴落，本发明卷材最高耐热90℃；低温柔性：-31℃，无裂纹；粘结强度：卷材与基层剥离强度≥2.8N/mm；抗拉强度高：拉力≥600N/50mm，延伸率≥400％。
此外，本发明防水卷材耐老化性能好：可正常使用寿命35年以上；安全环保：基层粘结不脱落、不窜水、施工过程不污染环境；对基层收缩变形和开裂的适应能力强。自愈性能优异：破损部位自动愈合。
最后应说明的是：以上各实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述各实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分或者全部技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的范围。
Claims (10)
1.一种非固化自愈性自粘防水涂料，其特征在于，包括以下重量份的各组分：沥青：40～50份，橡胶油：8～10份，苯乙烯-异戊二烯-苯乙烯共聚物：2～3份，丁苯橡胶：2～3份，增粘树脂：4～6份，马来酸酐：2～4份，聚酰胺：2～4份，乙撑双硬脂酰胺：2～4份，防老剂：1～2份和填料：20～24份。
2.根据权利要求1所述的防水涂料，其特征在于，所述橡胶油包括石蜡基橡胶油、环烷基橡胶油和芳香基橡胶油中的一种或多种。
3.根据权利要求1所述的防水涂料，其特征在于，所述苯乙烯-异戊二烯-苯乙烯共聚物包括苯乙烯-异戊二烯-苯乙烯共聚物1105、苯乙烯-异戊二烯-苯乙烯共聚物1126和苯乙烯-异戊二烯-苯乙烯共聚物1106中的一种或多种。
4.根据权利要求1所述的防水涂料，其特征在于，所述增粘树脂包括C5石油树脂、古马隆石油树脂和萜烯树脂中的一种或多种。
5.根据权利要求1所述的防水涂料，其特征在于，所述马来酸酐包括顺丁烯二酸酐。
6.根据权利要求1所述的防水涂料，其特征在于，所述聚酰胺包括中性聚酰胺；所述乙撑双硬脂酰胺包括N,N’-乙撑双硬脂酰胺。
7.根据权利要求1所述的防水涂料，其特征在于，所述填料包括滑石粉、轻钙中的任一种；所述防老剂包括紫外线吸收剂和/或抗热氧老化防老剂；优选地，所述紫外线吸收剂选自UV-P、UV-O、UV-351中的任一种；所述抗热氧老化防老剂选自防老剂D、防老剂IPPD中的任一种。
8.权利要求1～7中任一项所述防水涂料的制备方法，其特征在于，所述方法包括以下步骤：将沥青与橡胶油加热至175～185℃，加入苯乙烯-异戊二烯-苯乙烯共聚物、丁苯橡胶，溶胀1～2h，然后加入增粘树脂，溶胀0.3～0.6h，然后加入聚酰胺与马来酸酐反应0.8～1.2h，加入乙撑双硬脂酰胺反应0.3～0.6h，研磨后加入防老剂和填料。
9.一种防水卷材，其特征在于，所述防水卷材含有根据权利要求1～7中任一项所述的防水涂料。
10.根据权利要求9所述的防水卷材，其特征在于，将权利要求1～7中任一项所述的防水涂料刮涂至高密度聚乙烯胎体，两面覆隔离材料制得所述防水卷材；优选地，所述隔离材料为硅油隔离膜。