CN113979633B - 一种高硬度能化学钢化用钠钙硅玻璃的制备方法 - Google Patents
一种高硬度能化学钢化用钠钙硅玻璃的制备方法 Download PDFInfo
- Publication number
- CN113979633B CN113979633B CN202111399075.8A CN202111399075A CN113979633B CN 113979633 B CN113979633 B CN 113979633B CN 202111399075 A CN202111399075 A CN 202111399075A CN 113979633 B CN113979633 B CN 113979633B
- Authority
- CN
- China
- Prior art keywords
- glass
- sodium
- calcium
- hardness
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
玻璃2 | 玻璃2 | 玻璃3 | 玻璃3 | |
冷却速度(K/S) | 60 | 150 | 60 | 150 |
维氏硬度(kgf/mm2) | 743 | 792 | 698 | 755 |
压应力(mpa) | 912 | 930 | 902 | 920 |
Claims (2)