CN113754950A - 不露纤的玻纤增强聚丙烯及其制作工艺 - Google Patents
不露纤的玻纤增强聚丙烯及其制作工艺 Download PDFInfo
- Publication number
- CN113754950A CN113754950A CN202010492885.7A CN202010492885A CN113754950A CN 113754950 A CN113754950 A CN 113754950A CN 202010492885 A CN202010492885 A CN 202010492885A CN 113754950 A CN113754950 A CN 113754950A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- reinforced polypropylene
- fiber reinforced
- polypropylene
- exposure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种有机高分子复合材料，更具体地说是涉及一种不露纤的玻纤增强聚丙烯及其制作工艺，是由以下成分按重量比组成，聚丙烯：49.5‑95％，无碱玻纤：5‑50％；热稳定剂：0.1‑3.0％，玻纤处理剂：0.1‑3.0％，偶联剂：0.2‑8％，光稳定剂：0.1‑2.0％，紫外线吸收剂：0.1‑2.0％，其他助剂：1.3‑5.5％，本发明的一种不露纤的玻纤增强聚丙烯低温时不变脆、并且在耐磨、不易老化、不易发生融体破裂，长期与热金属接触也不容易分解，收缩范围及收缩值小，不容易发生缩孔，凹痕，变形，同时尺寸稳定，生产出来的产品表面光洁度高。
Description
技术领域
本发明涉及一种有机高分子复合材料，更具体地说，是涉及一种不露纤的玻纤增强聚丙烯及其制作工艺。本发明还涉及制作这种聚丙烯原料的方法。
背景技术
聚丙烯(PP)作为热塑塑料聚合物在塑料领域内有十分广泛的应用，目前应用最多的几种工程塑料之一，聚丙烯极好的流动性能和宽范围的流速，以及其它独特的聚合物特性相结合，使它具有优异的加工性能，同时又价格低廉，无毒、无味，密度度小，可在100度左右使用.具有良好的电性能和高频绝缘性不受湿度影响，适于制作一般机械零件，耐腐蚀零件和绝缘零件。常见的酸、碱有机溶剂对它几乎不起作用，可用于食具。被利用来生产许多种不同类型的具有内在的强韧机械性能的产品。良好的加工性能与极好的抗应力断裂性能产生了优良的模塑成型的密封罩。一般而言，低流速配方材料用于生产厚壁产品和那些要求韧性的产品。高流速的材料用于生产薄壁部件和要求快速加工的产品。
但低温时变脆、不耐磨、易老化、易发生融体破裂，长期与热金属接触易分解，收缩范围及收缩值大，易发生缩孔、凹痕、变形，同时尺寸不稳定等缺点，从而限制了聚丙烯的应用。因此，展开了对聚丙烯进行复合改性的研究。而提高聚丙烯材料综合的物理力学性能所使用的最有效最普及的方法，就是采用玻璃纤维复合增强。但玻璃纤维复合增强的方法在大幅提高聚丙烯物理力学性能的同时，又有个明显缺点，就是由于玻纤和聚丙烯两相界面不易良好结合，导致容易在产品表面产生玻纤外露现象，也就是通常业内人士所说的露纤/浮纤，这样就明显降低了产品表面光洁度，使产品表面粗糙和发花，从而限制了这种原材料在对表面光洁度或美观程度要求较高的产品上的应用。本技术发明就是为了有效克服这种现象而产生的。
发明内容
本发明的目的在于有效的克服了现有聚丙烯原料的缺陷，提供一种外观与未改良同类差不多但性能可比改良后的同类材料不露纤的玻纤增强聚丙烯原料。
本发明提供的技术方案如下：不露纤的玻纤增强聚丙烯是由以下成分按重量比组成，聚丙烯：49.5-95％，无碱玻纤：5-50％；热稳定剂：0.1-3.0％，玻纤处理剂：0.1-3.0％，偶联剂：0.2-8％，光稳定剂：0.1-2.0％，紫外线吸收剂：0.1-2.0％，其他助剂：1.3-5.5％。
本发明所述的不露纤的玻纤增强绿色环保尼龙6材料的制备方法，包括如下步骤：先将聚丙烯、无碱玻纤、热稳定剂、玻纤处理剂、偶联剂、光稳定剂、紫外线吸收剂、其他助剂按照比例称量后在混料机中低速混合10分钟，后再经双螺杆挤出机在适宜强度剪切的螺杆组合情况下由侧面加入无卤无碱玻纤进行混炼挤出，水冷拉条切粒再经过筛分脱水制得一种不露纤的玻纤增强聚丙烯材料。
本发明有效的克服了现有聚丙烯的缺陷，具有以下优点：
本发明的一种不露纤的玻纤增强聚丙烯低温时不变脆、并且在耐磨、不易老化、不易发生融体破裂，长期与热金属接触也不容易分解，收缩范围及收缩值小，不容易发生缩孔，凹痕，变形，同时尺寸稳定，生产出来的产品表面光洁度高。
具体实施方式
以下是本发明所述的不露纤的玻纤增强聚丙烯原料的实施例，并不因此限定本发明的保护范围。
实施例一，提供一种不露纤的玻纤增强绿色环保聚丙烯原料，由以下成分按重量比组成，聚丙烯：65％，无碱玻纤：30％；热稳定剂：0.5％，玻纤处理剂：1.0％，偶联剂：1.0％，光稳定剂：0.5％，紫外线吸收剂：0.5％，其他助剂：1.5％；
先将聚丙烯、热稳定剂、玻纤处理剂、偶联剂、光稳定剂、紫外线吸收剂、其他助剂按照比例称量后在混料机中低速混合10分钟，混料机采用低速混合，不锈钢材质，搅拌叶应与筒壁间隙小于0.5厘米，原辅料混合效果应目视各种粒子和粉末基本均匀，没有明显团块或集聚，然后再使用；双螺杆挤出机使用36长径比，如果是浅槽型螺纹就使用中等强度剪切，如果是深槽型螺纹就使用偏强剪切；无卤无碱玻纤由侧面按比例加入；保持真空状态和220度条件混炼挤出；采用水冷拉条切粒方式，经过筛分脱水即制得不露纤的玻纤增强聚丙烯材料。
Claims (2)
1.一种不露纤的玻纤增强聚丙烯及其制作工艺，其特征在于：是由以下成分按重量比组成，聚丙烯：49.5-95％，无碱玻纤：5-50％；热稳定剂：0.1-3.0％，玻纤处理剂：0.1-3.0％，偶联剂：0.2-8％，光稳定剂：0.1-2.0％，紫外线吸收剂：0.1-2.0％，其他助剂：1.3-5.5％。
2.一种不露纤的玻纤增强聚丙烯及其制作工艺，其特征在于：包括如下步骤：先将聚丙烯、无碱玻纤、热稳定剂、玻纤处理剂、偶联剂、光稳定剂、紫外线吸收剂、其他助剂按照比例称量后在混料机中低速混合10分钟，后再经双螺杆挤出机在适宜强度剪切的螺杆组合情况下由侧面加入无卤无碱玻纤进行混炼挤出，水冷拉条切粒再经过筛分脱水制得一种不露纤的玻纤增强聚丙烯材料。