CN101701102A - 高电击穿强度改性聚苯醚及其制作工艺 - Google Patents
高电击穿强度改性聚苯醚及其制作工艺 Download PDFInfo
- Publication number
- CN101701102A CN101701102A CN200910233102A CN200910233102A CN101701102A CN 101701102 A CN101701102 A CN 101701102A CN 200910233102 A CN200910233102 A CN 200910233102A CN 200910233102 A CN200910233102 A CN 200910233102A CN 101701102 A CN101701102 A CN 101701102A
- Authority
- CN
- China
- Prior art keywords
- percent
- polyphenyl ether
- breakdown strength
- electric breakdown
- modified polyphenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种有机高分子复合材料,更具体地说,是涉及一种高电击穿强度改性聚苯醚及其制备方法,是由以下成分按重量比组成,聚苯醚粉料:30-80%;聚苯乙烯:5-40%,陶瓷微粉:0-35%;高岭土微粉:0-35%;抗氧化剂:0.3-1.5%;增韧剂:0.1-3.0%;偶联剂:0.1-2.8%;高分子量硅油:0.1-3.0%;相容剂:1-5%;其他助剂:0.3-5.5%,本发明的一种高电击穿强度改性聚苯醚及其制作工艺,在保持聚苯醚原有优点前提下,具备较好改善的高电击穿强度改性,并且生产采购方便,原辅材料和生产设备均采用国产,生产成本和原材料成本低廉,这样较大提高了竞争力。
Description
技术领域
本发明涉及一种有机高分子复合材料,更具体地说,是涉及一种高电击穿强度改性聚苯醚及其制备方法。
背景技术
聚苯醚是一种能耐受较高温度的热塑性工程塑料,相对密度较低,吸水率很小,可以离火后自熄,在宽广的温度范围内具有良好的机械性能和电性能;玻璃化温度是热塑性塑料中最高的,高温下耐蠕变性也是所有热塑性工程塑料中最优异的;成型收缩率和热膨胀系数小,尺寸稳定,适于制造精密制品;具有优良的耐酸碱和耐化学试剂的特性;水解稳定性好,制品在高压蒸汽中反复使用其性能均无明显变化。虽然聚苯醚具有上述很多优点,但由于熔体流动性差,成型温度高,加工工艺要求苛刻,制品易产生应力开裂,因而限制了它的使用。因此,展开了对聚苯醚的复合改性研究,以期改善其缺点,有效利用其优点。聚苯醚的系列优点,使其最适用于潮湿、高温、有负载,而又需具备优良的机械性能、尺寸稳定性和电性能的场合,例如电子电气行业的较多领域。又由于其抗蠕变性好,又特别适合用于做各种紧固件和连接件。由于耐酸碱和耐水解性好,又适用于做各种阀、泵件等等。但是,在实际应用过程中,发现复合聚苯醚在有较高电击穿强度要求时还是有不足,较大影响了使用效果、应用范围,而这些正是本发明要解决的问题。
本发明的系列产品具有极大改善电击穿强度的特征,同时充分符合欧盟“废旧电子电气设备”(WEEE)和“有害物质限用指令”(RoHS)法规及其他环保规定,对环保要求严格的应用领域都能使用。
发明内容
本发明的目的在于克服现有技术的缺陷,提供一种能够通过注塑的方式大量快速生产不同尺寸的齿轮,且具有较好的自润滑耐磨性的高电击穿强度改性聚苯醚原料。
本发明提供的技术方案如下:本发明的一种高电击穿强度改性聚苯醚,是由以下成分按重量比组成,聚苯醚粉料:30-80%;聚苯乙烯:5-40%,陶瓷微粉:0-35%;高岭土微粉:0-35%;抗氧化剂:0.3-1.5%;增韧剂:0.1-3.0%;偶联剂:0.1-2.8%;高分子量硅油:0.1-3.0%;相容剂:1-5%;其他助剂:0.3-5.5%。
本发明所述的高电击穿强度改性聚苯醚生产流程是:先将陶瓷微粉与高岭土微粉与偶联剂按比例混合十分钟后再自然放置6小时,聚苯乙烯与聚苯醚粉料、高分子量硅油在混料机中混合10分钟,然后与抗氧化剂、增韧剂、偶联剂、相容剂以及其他助剂按照比例称量后在混料机中低速混合10分钟,再经积木式平行同向双螺杆挤出机在中等强度剪切的螺杆组合情况下抽真空匀速混炼挤出,水冷拉条切粒经过筛分脱水制得高电击穿强度改性聚苯醚材料。
本发明有效的克服了现有技术的缺陷,具有以下优点:
本发明的一种高电击穿强度改性聚苯醚及其制作工艺,在保持聚苯醚原有优点前提下,具备较好改善的高电击穿强度改性,并且生产采购方便,原辅材料和生产设备均采用国产,生产成本和原材料成本低廉,这样较大提高了竞争力。
具体实施方式
以下是本发明所述的高电击穿强度改性聚苯醚原料的最佳实施例,并不因此限定本发明的保护范围。
实施例一,提供一种高电击穿强度改性聚苯醚,由以下成分按重量比组成,聚苯醚粉料:35%;聚苯乙烯:20%,陶瓷微粉:15%;高岭土微粉:10%;抗氧化剂:0.5%;增韧剂:3%;硅烷偶联剂:0.5%;高分子量硅油:1.5%;相容剂:3%;其他助剂:1.5%。
先将陶瓷微粉、高岭土微粉与硅烷偶联剂按比例混合十分钟后再自然放置6小时,聚苯醚粉料、聚苯乙烯与高分子量硅油在混料机中混合10分钟,然后与抗氧化剂、增韧剂、偶联剂、相容剂以及其他助剂按照比例称量后在混料机中低速混合10分钟,混料机采用低速混合,搅拌叶应与筒壁间隙小于0.5厘米,原辅料混合效果应目视各种粒子和粉末基本均匀,没有明显团块或集聚;再经积木式平行同向双螺杆挤出机在中等强度剪切的螺杆组合情况下抽真空匀速混炼挤出,双螺杆挤出机使用40长径比,水冷拉条切粒经过筛分脱水制得高电击穿强度改性聚苯醚材料。
Claims (2)
1.一种高电击穿强度改性聚苯醚,其特征在于:是由以下成分按重量比组成,聚苯醚粉料:30-80%;聚苯乙烯:5-40%,陶瓷微粉:0-35%;高岭土微粉:0-35%;抗氧化剂:0.3-1.5%;增韧剂:0.1-3.0%;偶联剂:0.1-2.8%;高分子量硅油:0.1-3.0%;相容剂:1-5%;其他助剂:0.3-5.5%。
2.一种制备高电击穿强度改性聚苯醚的方法,其特征在于:包括如下步骤:先将陶瓷微粉与高岭土微粉与偶联剂按比例混合十分钟后再自然放置6小时,聚苯乙烯与聚苯醚粉料、高分子量硅油在混料机中混合10分钟,然后与抗氧化剂、增韧剂、偶联剂、相容剂以及其他助剂按照比例称量后在混料机中低速混合10分钟,再经积木式平行同向双螺杆挤出机在中等强度剪切的螺杆组合情况下抽真空匀速混炼挤出,水冷拉条切粒经过筛分脱水制得高电击穿强度改性聚苯醚材料。