CN113730275A - 一种抗衰老精华液及其制备方法 - Google Patents
一种抗衰老精华液及其制备方法 Download PDFInfo
- Publication number
- CN113730275A CN113730275A CN202111191775.8A CN202111191775A CN113730275A CN 113730275 A CN113730275 A CN 113730275A CN 202111191775 A CN202111191775 A CN 202111191775A CN 113730275 A CN113730275 A CN 113730275A
- Authority
- CN
- China
- Prior art keywords
- modified vermiculite
- phytosphingosine
- resveratrol
- vermiculite
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种抗衰老精华液及其制备方法，属于日常生活用品技术领域，该种抗衰老精华液，包括以下质量百分数原料：10‑15％硬脂酸、3‑6％十六醇、0.5‑3％胶原蛋白、0.6‑3.1％九肽‑1、0.4‑2.9％生育酚乙酸酯、0.5‑3％聚山梨醇酯‑80、0.5‑3％乙基己基甘油、0.8‑1.4％聚乙二醇、0.6‑1.2％葡聚糖、0.13‑0.63％丁二醇、0.4‑1％氢氧化钾、0.08‑0.14％乙酰壳糖胺、0.5‑0.8％白藜芦醇植物鞘氨醇‑改性蛭石。本发明技术方案中，通过月桂醇油醇和环己醇对蛭石进行联合改性，改性后的蛭石具有更大层间距，由于植物鞘氨醇中含有长烷基链和羟基，所以植物鞘氨醇能够牢固的接枝到改性蛭石的层间距内，长烷基链能够实现对改性蛭石层间距的良好填充，植物鞘氨醇又与白藜芦醇具有很好的生物相容性，所以实现改性蛭石比较大的负载量。
Description
技术领域
本发明涉及日常生活用品技术领域，具体涉及一种抗衰老精华液及其制备方法。
背景技术
皮肤老化是一种持续渐进性的生理过程，直接影响皮肤的外观与功能。皱纹则是皮肤老化表现的一种标志，被称之为“人生的年轮”。随着人们生活质量的提高，防衰老去除皱纹、重返青春成了广大消费者关注的话题。随着生化科技的发展，人们正逐渐揭开皱纹的生理机制，使用生理活性物质改善皮肤因松弛而出现皱纹的可能性越来越大，以化妆品厂家为中心，近年来让脸上青春永驻的尖端研究各位引人注目。
现有技术中，抗衰老精华液中往往会添加白藜芦醇等营养物质，通过将这些物质进行简单的混合来发挥功效，这样会存在白藜芦醇在精华液中的水溶性差，导致精华液中无法富集更多的白藜芦醇，使得抗衰老精华液的效果下降。
发明内容
(一)解决的技术问题
本发明的目的是提供一种抗衰老精华液及其制备方法，解决了传统的抗衰老精华液中精华液无法富集更多的白藜芦醇的问题。
(二)技术方案
为解决上述技术问题，本发明提出如下技术方案：
一种抗衰老精华液，包括以下质量百分数原料：10-16％硬脂酸、3-5.5％十六醇、0.5-3％胶原蛋白、0.6-3.1％九肽-1、0.4-2.9％生育酚乙酸酯、0.5-3％聚山梨醇酯-80、0.5-3％乙基己基甘油、0.8-1.4％聚乙二醇、0.6-1.2％葡聚糖、0.13-0.63％丁二醇、0.4-1％氢氧化钾、0.08-0.14％乙酰壳糖胺、0.5-0.8％白藜芦醇植物鞘氨醇-改性蛭石；
优选的，所述白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，在微波辐射下反应0.5-2h，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.3-0.8％改性蛭石悬浊液和浓度为2-4％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S2中得到的浓度为0.3-0.8％改性蛭石悬浊液在微波辐射下反应5-15min，然后滴加浓度为2-4％改性蛭石悬浊液，在微波辐射下反应60-80min，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
优选的，所述白藜芦醇与乙醇溶液的质量比为1：20-30。
优选的，所述蛭石、月桂醇油醇和环己醇的质量比为1：0.5-1.5：0.5-1.5，微波辐射的条件为微波功率800w，温度30℃。
优选的，所述微波辐射的条件为微波功率800w，温度30℃。
一种抗衰老精华液的制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应；
(4)反应结束后，冷却至室温，即得成品。
优选的，一种抗衰老精华液的制备方法，步骤(1)中，混合温度20-35℃，混合时间为10-20min。
优选的，一种抗衰老精华液的制备方法，步骤(2)中，混合温度30-40℃，混合时间为20-30min。
优选的，一种抗衰老精华液的制备方法，步骤(3)中，水浴加热的温度为40-50℃，水浴加热的时间为30-40min。
优选的，一种抗衰老精华液的制备方法，步骤(3)中，搅拌的速率为600r/min。
本发明的有益效果是：
(1)本发明技术方案中，通过月桂醇油醇和环己醇对蛭石进行联合改性，改性后的蛭石具有更大层间距，由于植物鞘氨醇中含有长烷基链和羟基，所以植物鞘氨醇能够牢固的接枝到改性蛭石的层间距内，长烷基链能够实现对改性蛭石层间距的良好填充，植物鞘氨醇又与白藜芦醇具有很好的生物相容性，所以实现改性蛭石比较大的负载量，改性蛭石又能实现在抗衰老精华液中的均匀的分布，所以既提高了白藜芦醇的负载量，又解决了白藜芦醇在面部分布不均的问题。
(2)本发明技术方案中，工艺简单，微波辐射法具有简便、快速、高效、绿色等优点，近年来被广泛的应用于有机合成的加速反应和无机纳米材料的合成，原料来源丰富，广泛适用于实际应用，生成的白藜芦醇植物鞘氨醇-改性蛭石稳定性优异。
具体实施方式
下面结合具体实施方式对本发明做进一步说明，以下实施例旨在说明本发明而不是对本发明的进一步限定。以下实施例中所用的技术手段为本领域技术人员所熟知的常规手段，所有原料均为通用材料。
实施例1
一种抗衰老精华液，包括以下质量百分数原料：10％硬脂酸、3％十六醇、0.5％胶原蛋白、0.6％九肽-1、0.4％生育酚乙酸酯、0.5％聚山梨醇酯-80、0.5％乙基己基甘油、0.8％聚乙二醇、0.6％葡聚糖、0.13％丁二醇、0.4％氢氧化钾、0.08％乙酰壳糖胺、0.5％白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液，白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S2中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，白藜芦醇与乙醇溶液的质量比为1：20，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
实施例2
一种抗衰老精华液，包括以下质量百分数原料：11％硬脂酸、3.5％十六醇、1％胶原蛋白、1.1％九肽-1、0.9％生育酚乙酸酯、1％聚山梨醇酯-80、1％乙基己基甘油、0.9％聚乙二醇、0.7％葡聚糖、0.23％丁二醇、0.5％氢氧化钾、0.09％乙酰壳糖胺、0.55％白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液，白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S3中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，白藜芦醇与乙醇溶液的质量比为1：30，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
实施例3
一种抗衰老精华液，包括以下质量百分数原料：12％硬脂酸、4％十六醇、0.7％胶原蛋白、1.6％九肽-1、1.4％生育酚乙酸酯、1.5％聚山梨醇酯-80、1.5％乙基己基甘油、1％聚乙二醇、0.7％葡聚糖、0.33％丁二醇、0.6％氢氧化钾、0.1％乙酰壳糖胺、0.6％白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液，白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S3中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，白藜芦醇与乙醇溶液的质量比为1：40，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
实施例4
一种抗衰老精华液，包括以下质量百分数原料：13％硬脂酸、4.5％十六醇、0.2％胶原蛋白、2.1％九肽-1、1.9％生育酚乙酸酯、2％聚山梨醇酯-80、2％乙基己基甘油、1.2％聚乙二醇、1％葡聚糖、0.43％丁二醇、0.8％氢氧化钾、1.2％乙酰壳糖胺、0.7％白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液，白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S3中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，白藜芦醇与乙醇溶液的质量比为1：40，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
实施例5
一种抗衰老精华液，包括以下质量百分数原料：14％硬脂酸、5％十六醇、2.5％胶原蛋白、2.6％九肽-1、2.4％生育酚乙酸酯、2.5％聚山梨醇酯-80、2.5％乙基己基甘油、1.1％聚乙二醇、1.1％葡聚糖、0.53％丁二醇、0.9％氢氧化钾、0.13％乙酰壳糖胺、0.75％白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液，白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S3中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，白藜芦醇与乙醇溶液的质量比为1：40，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
实施例6
一种抗衰老精华液，包括以下质量百分数原料：15％硬脂酸、5.5％十六醇、3％胶原蛋白、3.1％九肽-1、2.9％生育酚乙酸酯、3％聚山梨醇酯-80、3％乙基己基甘油、1.4％聚乙二醇、1.2％葡聚糖、0.63％丁二醇、1％氢氧化钾、0.14％乙酰壳糖胺、0.8％白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液，白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S3中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，白藜芦醇与乙醇溶液的质量比为1：40，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
对比例1
一种抗衰老精华液，包括以下质量百分数原料：15％硬脂酸、6％十六醇、3％胶原蛋白、3.1％九肽-1、2.9％生育酚乙酸酯、3％聚山梨醇酯-80、3％乙基己基甘油、1.4％聚乙二醇、1.2％葡聚糖、0.63％丁二醇、1％氢氧化钾、0.14％乙酰壳糖胺、0.8％植物鞘氨醇-改性蛭石。
一种抗衰老精华液，植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S2中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，即得成品。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和植物鞘氨醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
对比例2
一种抗衰老精华液，包括以下质量百分数原料：15％硬脂酸、6％十六醇、3％胶原蛋白、3.1％九肽-1、2.9％生育酚乙酸酯、3％聚山梨醇酯-80、3％乙基己基甘油、1.4％聚乙二醇、1.2％葡聚糖、0.63％丁二醇、1％氢氧化钾、0.14％乙酰壳糖胺、0.8％白藜芦醇-改性蛭石。
一种抗衰老精华液，白藜芦醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，蛭石、月桂醇油醇和环己醇的质量比为1：1：1，在微波辐射下反应1h，微波辐射的条件为微波功率800w，温度30℃，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S3、将白藜芦醇与步骤S2中得到的浓度为0.5％改性蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％改性蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，即得成品。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、3％聚山梨醇酯-80、3％乙基己基甘油、乙酰壳糖胺和白藜芦醇-改性蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
对比例3
一种抗衰老精华液，包括以下质量百分数原料：15％硬脂酸、6％十六醇、3％胶原蛋白、3.1％九肽-1、2.9％生育酚乙酸酯、3％聚山梨醇酯-80、3％乙基己基甘油、1.4％聚乙二醇、1.2％葡聚糖、0.63％丁二醇、1％氢氧化钾、0.14％乙酰壳糖胺、0.8％白藜芦醇植物鞘氨醇-蛭石。
一种抗衰老精华液，白藜芦醇植物鞘氨醇-蛭石的制备过程包括以下步骤：
S1、将蛭石加超纯水分别配置成浓度为0.5％改性蛭石悬浊液和浓度为3％改性蛭石悬浊液；
S2、将植物鞘氨醇与步骤S1中得到的浓度为0.5％蛭石悬浊液在微波辐射下反应10min，然后滴加浓度为3％蛭石悬浊液，在微波辐射下反应70min，微波辐射的条件为微波功率800w，温度30℃，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-蛭石；
S3、将白藜芦醇溶于乙醇溶液中，白藜芦醇与乙醇溶液的质量比为1：40，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-蛭石，即得白藜芦醇植物鞘氨醇-蛭石。
一种抗衰老精华液及其制备方法，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，混合温度25℃，混合时间为15min，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-蛭石混合均匀，混合温度35℃，混合时间为25min，制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应，水浴加热的温度为45℃，水浴加热的时间为35min；
(4)反应结束后，冷却至室温，即得成品。
对比例4
本对比例中，白藜芦醇植物鞘氨醇-改性蛭石是通过白藜芦醇、植物鞘氨醇和改性蛭石三者直接混合制得，其他步骤与实施例6相同。
现对实施例1-6和对比例1-4制备的抗衰老精华液进行效果测试，测试过程具体为：选取180名女性志愿者，随机分成9组，每组20名志愿者，志愿者出门前脸部清洗过后，涂抹抗衰老精华液，连续进行两周，测试结束后，请受试者做出抗衰老精华液对皮肤效果的评价，结果如表1所示。
评价标准：A、精华液显著改善皮肤弹性效果；B、精华液有改善皮肤弹性效果，但效果有限；C、精华液基本不改善皮肤弹性效果。
表1
| A/人 | B/人 | C/人 | |
| 实施例1 | 16 | 3 | 1 |
| 实施例2 | 16 | 4 | 0 |
| 实施例3 | 17 | 3 | 0 |
| 实施例4 | 17 | 2 | 1 |
| 实施例5 | 18 | 1 | 1 |
| 实施例6 | 19 | 1 | 0 |
| 对比例1 | 8 | 10 | 2 |
| 对比例2 | 6 | 6 | 8 |
| 对比例3 | 14 | 5 | 1 |
| 对比例4 | 15 | 4 | 1 |
由上表1可知，通过本发明技术方案制备的抗衰老精华液具有修复和改善皮肤弹性效果的作用，由实施例1-6制备的抗衰老精华液具有更好的修复和改善皮肤弹性效果。
最后应说明的是：以上实施例仅用以说明本发明而并非限制本发明所描述的技术方案；本领域的普通技术人员应当理解，仍然可以对本发明进行修改或等同替换；而一切不脱离本发明的精神和范围的技术方案及其改进，其均应涵盖在本发明的权利要求范围中。
Claims (10)
1.一种抗衰老精华液，其特征在于，包括以下质量百分数原料：10-15％硬脂酸、3-5.5％十六醇、0.5-3％胶原蛋白、0.6-3.1％九肽-1、0.4-2.9％生育酚乙酸酯、0.5-3％聚山梨醇酯-80、0.5-3％乙基己基甘油、0.8-1.4％聚乙二醇、0.6-1.2％葡聚糖、0.13-0.63％丁二醇、0.4-1％氢氧化钾、0.08-0.14％乙酰壳糖胺、0.5-0.8％白藜芦醇植物鞘氨醇-改性蛭石；
所述白藜芦醇植物鞘氨醇-改性蛭石是通过将植物鞘氨醇与改性蛭石进行反应，得到植物鞘氨醇-改性蛭石，再通过植物鞘氨醇-改性蛭石进行负载白藜芦醇制得，所述改性蛭石是由月桂醇油醇和环己醇对蛭石进行联合表面改性制得。
2.根据权利要求1所述的一种抗衰老精华液，其特征在于，所述白藜芦醇植物鞘氨醇-改性蛭石的制备过程包括以下步骤：
S1、将蛭石加入至月桂醇油醇和环己醇内，在微波辐射下反应0.5-2h，反应结束后用异丙醇漂洗，再经冻干粉碎后得到改性蛭石；
S2、将得到的改性蛭石加超纯水分别配置成浓度为0.3-0.8％改性蛭石悬浊液和浓度为2-4％改性蛭石悬浊液；
S3、将植物鞘氨醇与步骤S2中得到的浓度为0.3-0.8％改性蛭石悬浊液在微波辐射下反应5-15min，然后滴加浓度为2-4％改性蛭石悬浊液，在微波辐射下反应60-80min，反应结束后，通过透析纯化，最终在-50℃冻干，得到植物鞘氨醇-改性蛭石；
S4、将白藜芦醇溶于乙醇溶液中，得到白藜芦醇乙醇溶液，再向白藜芦醇乙醇溶液中加入植物鞘氨醇-改性蛭石，即得白藜芦醇植物鞘氨醇-改性蛭石。
3.根据权利要求2所述的一种抗衰老精华液，其特征在于，步骤S1中，所述白藜芦醇与乙醇溶液的质量比为1：20-30。
4.根据权利要求2所述的一种抗衰老精华液，其特征在于，步骤S1中，所述蛭石、月桂醇油醇和环己醇的质量比为1：0.5-1.5：0.5-1.5，微波辐射的条件为微波功率800w，温度30℃。
5.根据权利要求2所述的一种抗衰老精华液，其特征在于，步骤S3中，所述微波辐射的条件为微波功率800w，温度30℃。
6.一种如权利要求1-5任一项所述的抗衰老精华液的制备方法，其特征在于，包括以下步骤：
(1)按组分称取物料，将氢氧化钾、聚乙二醇和丁二醇混合均匀，制得混合物A；
(2)将硬脂酸、胶原蛋白、九肽-1、生育酚乙酸酯、聚山梨醇酯-80、乙基己基甘油、乙酰壳糖胺和白藜芦醇植物鞘氨醇-改性蛭石混合均匀制备混合物B；
(3)将步骤(1)中得到的混合物A与步骤(2)中得到的混合物B进行混合，水浴加热并剧烈搅拌反应；
(4)反应结束后，冷却至室温，即得成品。
7.根据权利要求6所述的抗衰老精华液的制备方法，其特征在于，步骤(1)中，混合温度20-35℃，混合时间为10-20min。
8.根据权利要求6所述的抗衰老精华液的制备方法，其特征在于，步骤(2)中，混合温度30-40℃，混合时间为20-30min。
9.根据权利要求6所述的抗衰老精华液的制备方法，其特征在于，步骤(3)中，水浴加热的温度为40-50℃，水浴加热的时间为30-40min。
10.根据权利要求6所述的抗衰老精华液的制备方法，其特征在于，步骤(3)中，搅拌的速率为600r/min。