CN113614941A - 电化学装置及包含其的电子装置 - Google Patents
电化学装置及包含其的电子装置 Download PDFInfo
- Publication number
- CN113614941A CN113614941A CN202080018610.8A CN202080018610A CN113614941A CN 113614941 A CN113614941 A CN 113614941A CN 202080018610 A CN202080018610 A CN 202080018610A CN 113614941 A CN113614941 A CN 113614941A
- Authority
- CN
- China
- Prior art keywords
- active material
- positive electrode
- less
- electrochemical device
- equal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本申请涉及电化学装置及包含其的电子装置。本申请的电化学装置包括负极、隔离膜、电解液和正极,所述正极包括正极集流体和正极活性材料层,所述正极活性材料层包含正极活性材料,所述正极经过碳酸二甲酯溶剂洗涤后,在85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在25℃‑170℃范围内失重量小于0.3%。本申请提供的正极具有提高的疏水面积,从而提高了正极的疏水性能。在湿度较高的环境下转运和操作时,该正极的吸水性显著降低,从而显著降低了电极转运和储存的成本。
Description
技术领域
本申请涉及储能领域,具体涉及一种电化学装置及包含其的电子装置,特别是锂离子电池。
背景技术
随着消费电子类的产品如笔记本电脑、手机、平板电脑、移动电源和无人机等的普及,对其中的电化学装置的要求越来越严格。例如,不仅要求电池轻便,而且还要求电池拥有高容量和较长的工作寿命。锂离子电池凭借其具有能量密度高、安全性高、无记忆效应和工作寿命长等突出的优点已经在市场上占据主流地位。
锂离子电池高镍三元正极材料的理论比容量高,安全性能高,相对于锂电极的电势约为4.3V,有希望成为新一代的锂离子电池正极材料。然而,锂离子电池高镍三元正极材料表面结构不稳定。一方面在浆料配制过程中,高镍三元正极材料易吸收水分和二氧化碳,浆料粘度反弹剧烈,造成无法正常涂布。另一方面,电极中的高镍材料容易在吸收水分的同时也会吸收空气中的二氧化碳,导致表面附着一层非电化学活性的碳酸氢盐、碳酸盐和碱式碳酸盐。在形成碳酸盐的同时,体相活性锂也会损失,导致电池性能急剧下降,造成电池质量异常波动。由此可见,提高高镍三元正极材料和正极的空气稳定性变得至关重要。
发明内容
本申请提供了一种电化学装置,以试图在至少某种程度上解决至少一种存在于相关领域中的问题。本申请还提供了使用包含该电化学装置的电子装置。
在一个实施例中,本申请提供了一种电化学装置,所述电化学装置包括负极、隔离膜、电解液和正极,所述正极包括正极集流体和正极活性材料层,所述正极活性材料层包含正极活性材料,所述正极经过碳酸二甲酯溶剂洗涤后,在85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在25℃至170℃范围内失重量小于0.3%。
在一些实施例中,所述正极经过碳酸二甲酯溶剂洗涤后,在85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在170℃至300℃范围内失重量小于10%。
在一些实施例中,所述正极活性材料层对水的接触角为100°至160°。
在一些实施例中,所述正极活性材料层对所述电解液的接触角为10°至60°。
在一些实施例中,根据傅里叶转换红外线光谱测试,所述正极活性材料层在900cm-1至1100cm-1范围内具有至少一个吸收峰。
在一些实施例中,所述正极活性材料层包含有机含硅添加剂,所述有机含硅添加剂包括至少一种具有式(R1)m-Si-(R2)n的化合物,其中
R1、R2各自独立地选自取代或未取代的C1-20烷基、取代或未取代的C1-20烯基、取代或未取代的C1-20烷氧基、取代或未取代的Ra-O-Rb-基团、胺基、-OH或其任意组合,
Ra选自取代或未取代的C1-20烷基、取代或未取代的C1-20烯基或其任意组合,
Rb选自取代或未取代的C1-20亚烷基、亚胺基、取代或未取代的C1-20亚烯基或其任意组合,
m=1至3,以及
n=1至3;并且
其中,R1和R2中的至少一个的碳原子数≥5;
取代时,取代基为卤素、含杂原子基团中的至少一种;所述杂原子包括B、N、O、Si、P、S中的至少一种。
在一些实施例中,所述有机含硅添加剂包含CH3(CH2)15Si(OCH3)3、CH3(CH2)10Si(OCH3)3、CH3(CH2)7Si(OCH3)3、CH3(CH2)11Si(OCH3)3、NH2(CH2)2NH(CH2)3Si(OCH3)3、NH2(CH2)2NH(CH2)3Si(OC2H5)3、CH3OCH2CH2O(CH2)3Si(OCH3)3、CH3OCH2CH2O(CH2)3Si(OC2H5)3中的至少一种。
在一些实施例中,基于所述正极活性材料层的总重量,所述有机含硅添加剂的含量为0.08wt%至5wt%。
在一些实施例中,基于所述有机含硅添加剂的总重量,邻近所述正极活性材料表面的有机含硅添加剂的重量百分比为5wt%至50wt%。
在一些实施例中,所述正极活性材料包括至少一种具有式LixNiyCozMnkMqOb-aTa的化合物,其中,M选自由以下组成的群组中的至少一种:B、Mg、Al、Si、P、S、Ti、Cr、Fe、Co、Ni、Cu、Zn、Ga、Y、Zr、Mo、Ag、W、In、Sn、Pb、Sb和Ce,T为卤素,并且x、y、z、k、q、a和b分别满足:0.2<x≤1.2、0<y≤1、0≤z≤1、0≤k≤1、0≤q≤1、1≤b≤2以及0≤a≤1。
在一些实施例中,0.9<x≤1.2、0.6<y≤1、0≤z≤0.3。
在另一个实施例中,本申请提供一种电子装置,其包括根据本申请的实施例所述的电化学装置。
在锂离子电池的制备过程中,锂离子正极材料由于其较强的敏感性容易与空气中的水分和二氧化碳发生副反应。导致性能恶化。本发明的目的在于提供一种正极及其制备方法,旨在解决现有技术中锂离子电池的正极浆料和正极的空气敏感性问题。本申请提供的正极具有提高的疏水面积,从而提高了正极的疏水性能。在湿度较高的环境下转运和操作时,该正极的吸水性显著降低,从而显著降低了电极转运和储存的成本。
本申请实施例的额外层面及优点将部分地在后续说明中描述和显示,或是经由本申请实施例的实施而阐释。
附图说明
在下文中将简要地说明为了描述本申请实施例或现有技术所必要的附图以便于描述本申请的实施例。显而易见地,下文描述中的附图仅只是本申请中的部分实施例。对本领域技术人员而言,依然可以根据这些附图中所例示的结构来获得其他实施例的附图。
图1中的上图示出了对比例1中锂离子电池化成后,正极的傅里叶转换红外线光谱(FTIR)测试的谱图;且图1中的下图示出了实施例1中锂离子电池化成后,正极的傅里叶转换红外线光谱(FTIR)测试的谱图;。
图2中的左图示出了实施例1中的正极在45%恒温恒湿静态空气环境存储20天后TG-MS结果;且图2中的右图示出了对比例1中的正极在45%恒温恒湿静态空气环境存储20天后TG-MS结果。
图3中的左图示出了实施例6中的正极与电解液的接触角测试结果;且图3中的右图示出了实施例6中的正极与水的接触角测试结果。
图4示出了对比例6和实施例15中的正极在45%恒温恒湿静态空气环境中存储时碳酸根含量的变化。
图5示出了实施例1及对比例1中的正极在45%湿度下存储时含水量的变化以及存储20天后,烘烤后的失水率。
图6示出了实施例2中正极中邻近正极活性材料表面的有机含硅添加剂含量的能量弥散X射线探测器(EDX)测试图片。
具体实施方式
本申请的实施例将会被详细的描示在下文中。本申请的实施例不应该被解释为对本申请的限制。
有时在本文中以范围格式呈现量、比率和其它数值。应理解,此类范围格式是用于便利及简洁起见,且应灵活地理解,不仅包含明确地指定为范围限制的数值,而且包含涵盖于所述范围内的所有个别数值或子范围,如同明确地指定每一数值及子范围一般。
在具体实施方式及权利要求书中,由术语“中的一者”、“中的一个”、“中的一种”或其他相似术语所连接的项目的列表可意味着所列项目中的任一者。例如,如果列出项目A及B,那么短语“A及B中的一者”意味着仅A或仅B。在另一实例中,如果列出项目A、B及C,那么短语“A、B及C中的一者”意味着仅A;仅B;或仅C。项目A可包含单个元件或多个元件。项目B可包含单个元件或多个元件。项目C可包含单个元件或多个元件。
在具体实施方式及权利要求书中,由术语“中的至少一者”、“中的至少一个”、“中的至少一种”或其他相似术语所连接的项目的列表可意味着所列项目的任何组合。例如,如果列出项目A及B,那么短语“A及B中的至少一者”意味着仅A;仅B;或A及B。在另一实例中,如果列出项目A、B及C,那么短语“A、B及C中的至少一者”意味着仅A;或仅B;仅C;A及B(排除C);A及C(排除B);B及C(排除A);或A、B及C的全部。项目A可包含单个元件或多个元件。项目B可包含单个元件或多个元件。项目C可包含单个元件或多个元件。
一、电化学装置
在一些实施例中,本申请提供了一种电化学装置,所述电化学装置包括负极、隔离膜、电解液和正极。
所述电化学装置包括发生电化学反应的任何装置。
在一些实施例中,本申请的电化学装置包括,但不限于:所有种类的一次电池、二次电池、燃料电池、太阳能电池或电容。
在一些实施例中,所述电化学装置是锂二次电池。
在一些实施例中,锂二次电池包括,但不限于:锂金属二次电池、锂离子二次电池、锂聚合物二次电池或锂离子聚合物二次电池。
正极
在一些实施例中,所述正极包括正极集流体和正极活性材料层,所述正极活性材料层包含正极活性材料,所述正极经过碳酸二甲酯溶剂洗涤后,85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在约25℃至约170℃范围内失重量小于0.3%。
在一些实施例中,所述正极经过碳酸二甲酯溶剂洗涤后,85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在约170℃至约300℃范围内失重量小于10%。在一些实施例中,所述正极经过碳酸二甲酯溶剂洗涤后,85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在约170℃至约300℃范围内失重量小于9%、小于8%、小于7%、小于6%、小于5%、小于4%、小于3%、小于2%或小于1%。
在一些实施例中,所述正极活性材料层对水的接触角为约100°至约160°。在一些实施例中,所述正极活性材料层对水的接触角为100°、110°、120°、130°、140°、150°、160°或这些数值中任意两者组成的范围。
在一些实施例中,所述正极活性材料层对所述电解液的接触角为约10°至约60°。在一些实施例中,所述正极活性材料层对所述电解液的接触角为10°、20°、30°、40°、50°、60°或这些数值中任意两者组成的范围。
在一些实施例中,根据傅里叶转换红外线光谱测试,所述正极活性材料层在约900cm-1至约1100cm-1范围内具有至少一个吸收峰。
在一些实施例中,所述正极活性材料层包含有机含硅添加剂,所述有机含硅添加剂包括至少一种具有式(R1)m-Si-(R2)n的化合物,其中
R1、R2各自独立地选自取代或未取代的C1-20烷基、取代或未取代的C1-20烯基、取代或未取代的C1-20烷氧基、取代或未取代的Ra-O-Rb-基团、-OH或其任意组合,
Ra选自取代或未取代的C1-20烷基、取代或未取代的C1-20烯基或其组合,
Rb选自取代或未取代的C1-20亚烷基、亚胺基、取代或未取代的C1-20亚烯基或其组合,m=1至3,以及
n=1至3;并且
其中,R1和R2中的至少一个的碳原子数≥5;
取代时,取代基为卤素、含杂原子基团中的至少一种;所述杂原子包括B、N、O、Si、P、S中的至少一种。
在一些实施例中,R1、R2各自独立地选自取代或未取代的C1-15烷基、取代或未取代的C1-15烯基、取代或未取代的C1-15烷氧基、取代或未取代的Ra-O-Rb-基团、胺基、-OH或其任意组合,
Ra选自取代或未取代的C1-15烷基、取代或未取代的C1-15烯基或其任意组合,
Rb选自取代或未取代的C1-15亚烷基、亚胺基、取代或未取代的C1-15亚烯基或其任意组合,
m=1至3,以及
n=1至3;并且
其中,R1和R2中的至少一个的碳原子数≥5;
取代时,取代基为卤素、含杂原子基团中的至少一种;所述杂原子包括B、N、O、Si、P、S中的至少一种。
在一些实施例中,含杂原子基团包括胺基、硝基、氰基、烷氧基或其任意组合。
在一些实施例中,所述有机含硅添加剂包含CH3(CH2)15Si(OCH3)3、CH3(CH2)10Si(OCH3)3、CH3(CH2)7Si(OCH3)3、CH3(CH2)11Si(OCH3)3、NH2(CH2)2NH(CH2)3Si(OCH3)3、NH2(CH2)2NH(CH2)3Si(OC2H5)3、CH3OCH2CH2O(CH2)3Si(OCH3)3、CH3OCH2CH2O(CH2)3Si(OC2H5)3中的至少一种。
在一些实施例中,所述有机含硅添加剂包含CH3(CH2)15Si(OCH3)3、CH3(CH2)10Si(OCH3)3、CH3(CH2)7Si(OCH3)3、CH3(CH2)11Si(OCH3)3中的至少一种。
在一些实施例中,基于所述正极活性材料层的总重量,所述有机含硅添加剂的含量为约0.08wt%至约5wt%。在一些实施例中,基于所述正极活性材料层的总重量,所述有机含硅添加剂的含量为0.08wt%、0.1wt%、0.2wt%、0.5wt%、0.7wt%、1wt%、1.5wt%、2wt%、2.5wt%、3wt%、3.5wt%、4wt%、4.5wt%、5wt%或这些数值中任意两者组成的范围。
在一些实施例中,基于所述有机含硅添加剂的总重量,邻近所述正极活性材料表面的有机含硅添加剂的重量百分比为约5wt%至约50wt%。在一些实施例中,基于所述有机含硅添加剂的总重量,邻近所述正极活性材料表面的有机含硅添加剂的重量百分比为5wt%、10wt%、15wt%、20wt%、25wt%、30wt%、35wt%、40wt%、45wt%、50wt%或这些数值中任意两者组成的范围。
在一些实施例中,所述正极活性材料包括至少一种具有式LixNiyCozMnkMqOb-aTa的化合物,其中,M选自由以下组成的群组中的至少一种:B、Mg、Al、Si、P、S、Ti、Cr、Fe、Co、Ni、Cu、Zn、Ga、Y、Zr、Mo、Ag、W、In、Sn、Pb、Sb和Ce,T为卤素,并且x、y、z、k、q、a和b分别满足:0.2<x≤1.2、0<y≤1、0≤z≤1、0≤k≤1、0≤q≤1、1≤b≤2以及0≤a≤1。
在一些实施例中,0.9<x≤1.2、0.6<y≤1、0≤z≤0.3。
在一些实施例中,所述正极活性材料包括LiNi0.83Co0.12Mn0.05O2、LiNi0.96Co0.02Mn0.02O2、LiNiO2、LiCoO2、磷酸亚铁锂(LiFePO4)、锰酸锂(LiMn2O4)中的至少一种。
在一些实施例中,所述正极活性材料层进一步包括导电剂。在一些实施例中,所述导电剂包括碳纳米管、碳纤维、乙炔黑、石墨烯、科琴黑或碳黑中的至少一种。
在一些实施例中,所述正极活性材料层进一步包括粘结剂。在一些实施例中,所述粘结剂包括聚偏氟乙烯、羧甲基纤维素、丁苯橡胶、聚乙烯醇、羟丙基纤维素、二乙酰基纤维素、聚氯乙烯、羧化的聚氯乙烯、聚氟乙烯、含亚乙基氧的聚合物、聚乙烯吡咯烷酮、聚氨酯、聚四氟乙烯、聚偏1,1-二氟乙烯、聚乙烯、聚丙烯、丙烯酸(酯)化的丁苯橡胶、环氧树脂或尼龙中至少一种。
在一些实施例中,所述集流体包括铜箔或铝箔中的至少一种。
在一些实施例中,本申请提供了一种制备正极的方法,所述方法包括:
(1)将粘结剂、导电剂、正极活性材料和有机含硅添加剂加入溶剂中,混合均匀,获得正极浆料;和
(2)将正极浆料涂覆在铝箔上,干燥、滚压即获得正极。
在一些实施例中,步骤(1)包括如下步骤:将粘结剂加入到溶剂中,搅拌均匀;加入导电剂,搅拌均匀;加入正极活性材料,搅拌均匀;加入有机含硅添加剂,搅拌均匀。
在一些实施例中,步骤(1)包括如下步骤:将粘结剂加入到溶剂中,搅拌均匀;加入有机含硅添加剂,搅拌均匀;加入导电剂,搅拌均匀;加入正极活性材料,搅拌均匀。
锂离子电极材料的空气稳定性较差,在制备锂离子电池过程中,电极材料容易与空气中的水和二氧化碳发生副反应,从而导致性能恶化。因此,为了降低锂电池电极的空气敏感程度,对空气中的湿度要求较高,一般要求湿度小于2%,而且对电极的转运时间有严格要求。只有在严格的环境控制和工艺控制下才能保证电池的电极发挥正常的性能。
然而,严格控制环境空气湿度和转运时间存在如下几点问题:1)维持较低空气湿度一般需要配备大功率的除湿机或干燥风循环系统,设备的运营维护成本和折旧费用非常高;和2)除湿系统对于电力系统要求较高,电池厂每年花费在除湿系统的电费运行成本巨大,这增加了电池的制造成本。
本发明提供了一种正极,在其制备过程中通过在浆料中添加有机含硅添加剂作为疏水剂,使活性材料层中的活性材料、导电剂和粘结剂的表面均结合有疏水剂,即该疏水剂结合在正极表面上各种材料的表面。将该浆料均匀涂覆在集流体上后,使整个正极都具有疏水性,相对于现有技术可以大大提高正极的疏水表面积,使整个正极的吸湿性显著降低。在湿度较高的环境条件下,可以防止正极在转运和操作过程中吸水过多导致后续加工性能变差,从而确保了正极的固有性能,降低了储存转运成本,同时避免了对锂离子电池性能的影响。
负极
本申请实施例提供了一种负极。所述负极包括集流体和位于该集流体上的负极活性材料层。所述负极活性材料层包括根据本申请的负极材料。
在一些实施例中,负极活性材料层包括粘合剂。在一些实施例中,粘合剂包括,但不限于:聚乙烯醇、羧甲基纤维素、羟丙基纤维素、二乙酰基纤维素、聚氯乙烯、羧化的聚氯乙烯、聚氟乙烯、含亚乙基氧的聚合物、聚乙烯吡咯烷酮、聚氨酯、聚四氟乙烯、聚偏1,1-二氟乙烯、聚乙烯、聚丙烯、丁苯橡胶、丙烯酸(酯)化的丁苯橡胶、环氧树脂或尼龙。
在一些实施例中,负极活性材料层包括导电材料。在一些实施例中,导电材料包括,但不限于:天然石墨、人造石墨、碳黑、乙炔黑、科琴黑、碳纤维、金属粉、金属纤维、铜、镍、铝、银或聚亚苯基衍生物。
在一些实施例中,集流体包括,但不限于:铜箔、镍箔、不锈钢箔、钛箔、泡沫镍、泡沫铜或覆有导电金属的聚合物基底。
在一些实施例中,负极可以通过如下方法获得:在溶剂中将活性材料、导电材料和粘合剂混合,以制备活性材料组合物,并将该活性材料组合物涂覆在集流体上。
在一些实施例中,溶剂可以包括,但不限于:去离子水、N-甲基吡咯烷酮。
电解液
在一些实施例中,所述电解液包括有机溶剂、锂盐和添加剂。根据本申请的电解液的有机溶剂可为任何可作为电解液的溶剂的有机溶剂。根据本申请的电解液中使用的电解质可为任何可用于电解液的电解质。根据本申请的电解液的添加剂可为任何可作为电解液添加剂的添加剂。
在一些实施例中,所述有机溶剂包括,但不限于:碳酸乙烯酯(EC)、碳酸丙烯酯(PC)、碳酸二乙酯(DEC)、碳酸甲乙酯(EMC)、碳酸二甲酯(DMC)、碳酸亚丙酯或丙酸乙酯。
在一些实施例中,所述锂盐包括有机锂盐或无机锂盐中的至少一种。
在一些实施例中,所述锂盐包括,但不限于:六氟磷酸锂(LiPF6)、四氟硼酸锂(LiBF4)、二氟磷酸锂(LiPO2F2)、双三氟甲烷磺酰亚胺锂LiN(CF3SO2)2(LiTFSI)、双(氟磺酰)亚胺锂Li(N(SO2F)2)(LiFSI)、双草酸硼酸锂LiB(C2O4)2(LiBOB)或二氟草酸硼酸锂LiBF2(C2O4)(LiDFOB)。
在一些实施例中,所述电解液中锂盐的浓度为:约0.5mol/L至约3mol/L、约0.5mol/L至约2mol/L或约0.8mol/L至约1.5mol/L。
隔离膜
在一些实施例中,正极与负极之间设有隔离膜以防止短路。可用于本申请的隔离膜的材料和形状没有特别限制。在一些实施例中,隔离膜包括由对本申请的电解液稳定的材料形成的聚合物或无机物等。
例如,隔离膜可包括基材层和表面处理层。基材层为具有多孔结构的无纺布、膜或复合膜,基材层的材料选自聚乙烯、聚丙烯、聚对苯二甲酸乙二醇酯和聚酰亚胺中的至少一种。具体的,可选用聚丙烯多孔膜、聚乙烯多孔膜、聚丙烯无纺布、聚乙烯无纺布或聚丙烯-聚乙烯-聚丙烯多孔复合膜。
基材层的至少一个表面上设置有表面处理层,表面处理层可以是聚合物层或无机物层,也可以是混合聚合物与无机物所形成的层。
无机物层包括无机颗粒和粘结剂,无机颗粒选自氧化铝、氧化硅、氧化镁、氧化钛、二氧化铪、氧化锡、二氧化铈、氧化镍、氧化锌、氧化钙、氧化锆、氧化钇、碳化硅、勃姆石、氢氧化铝、氢氧化镁、氢氧化钙和硫酸钡中的一种或几种的组合。粘结剂选自聚偏氟乙烯、偏氟乙烯-六氟丙烯的共聚物、聚酰胺、聚丙烯腈、聚丙烯酸酯、聚丙烯酸、聚丙烯酸盐、聚乙烯呲咯烷酮、聚乙烯醚、聚甲基丙烯酸甲酯、聚四氟乙烯和聚六氟丙烯中的一种或几种的组合。
聚合物层中包含聚合物,聚合物的材料选自聚酰胺、聚丙烯腈、丙烯酸酯聚合物、聚丙烯酸、聚丙烯酸盐、聚乙烯呲咯烷酮、聚乙烯醚、聚偏氟乙烯或聚(偏氟乙烯-六氟丙烯)中的至少一种。
电子装置
本申请的电子装置可为任何使用根据本申请的电化学装置的装置。
在一些实施例中,所述电子装置包括,但不限于:笔记本电脑、笔输入型计算机、移动电脑、电子书播放器、便携式电话、便携式传真机、便携式复印机、便携式打印机、头戴式立体声耳机、录像机、液晶电视、手提式清洁器、便携CD机、迷你光盘、收发机、电子记事本、计算器、存储卡、便携式录音机、收音机、备用电源、电机、汽车、摩托车、助力自行车、自行车、照明器具、玩具、游戏机、钟表、电动工具、闪光灯、照相机、家庭用大型蓄电池或锂离子电容器等。
下面以锂离子电池为例并且结合具体的实施例说明锂离子电池的制备,本领域的技术人员将理解,本申请中描述的制备方法仅是实例,其他任何合适的制备方法均在本申请的范围内。
实施例
以下说明根据本申请的锂离子电池的实施例和对比例进行性能评估。
一、锂离子电池的制备
正极的制备
(1)将一定重量比的粘结剂聚偏氟乙烯(PVDF)、有机含硅添加剂、导电剂导电炭黑(Super P)和正极活性材料制备成正极浆料;
(2)调节正极浆料的粘度至约3000mPas至约6000mPas,将混合好的浆料均匀涂覆在铝箔上,涂覆单层厚度为40μm,双层涂覆;干燥后进行辊压制成所需电极,电极加工和转运环境湿度45%。其中,涂布电极面密度为14mg/cm2;正极放置恒温恒湿度环境吸湿性对比效果检测,放置后的正极与石墨负极组装成3.5Ah软包电池进行电池性能测试。
其中正极浆料的制备方法如下所述:
对比例1至3和5-8
将粘结剂聚偏氟乙烯、导电剂和正极活性材料按照一定重量比加入溶剂N-甲基吡咯烷酮(NMP)中,搅拌均匀,即得正极浆料。
对比例4
向正极活性材料中加入有机含硅添加剂,用高速分散机分散,得到表面包覆有有机含硅添加剂的正极活性材料;向表面包覆有有机含硅添加剂的正极活性材料中加入导电剂、粘结剂和溶剂,搅拌均匀,即得正极浆料。
实施例1
将粘结剂加入到溶剂中,搅拌均匀;加入有机含硅添加剂,搅拌均匀;加入导电剂,搅拌均匀;再向获得的混合物中加入正极活性材料,搅拌均匀,即得正极浆料。
实施例2至18
将粘结剂加入到溶剂中,搅拌均匀;加入导电剂,搅拌均匀;加入正极活性材料,搅拌均匀;再向获得的混合物中加入有机含硅添加剂,搅拌均匀,即得正极浆料。
对比例9
步骤同实施例2,区别仅在于加入的有机含硅添加剂种类不同。
负极的制备
将人造石墨、丁苯橡胶和粘结剂(羧甲基纤维素钠,CMC)按照96%:2%:2%的质量比与去离子水混合,搅拌均匀,得到负极浆料。将该负极浆料涂布在12μm厚的铜箔上。干燥,冷压,再经过裁片、焊接极耳,得到负极。
电解液的制备
在干燥氩气环境下,在碳酸丙烯酯(PC),碳酸乙烯酯(EC),碳酸二乙酯(DEC)(重量比1:1:1)混合而成的溶剂中,加入LiPF6混合均匀得到电解液,其中LiPF6的浓度为1.15mol/L。
隔离膜的制备
以聚乙烯(PE)多孔聚合薄膜作为隔离膜。
锂离子电池的制备
将正极、隔离膜、负极按顺序叠好,使隔离膜处于正极和负极中间以起到隔离的作用。卷绕得到裸电芯。将裸电芯置于外包装中,注入电解液,封装。经过化成、脱气、切边等工艺流程得到锂离子电池。
表1示出了各对比例和实施例中正极浆料制备过程中各物质种类和重量份数。
表1
“—”代表未添加该物质
二、测试方法
1、有机含硅添加剂分布测试:
采用SEM-EDX测试正极中有机含硅添加剂分布情况。首先在SEM-EDX图片中选取200μm×200μm大小的面积,测试整个面积内Si原子的数目N1;然后在该面积内测试距离活性正极材料表面1μm范围内的Si原子的个数N2。该面积内有机含硅添加剂邻近正极活性材料表面的重量百分比W1=N2/N1。
测试正极的100个不同位置处的W1值,计算其平均值W2。将W2定义为整个正极中有机含硅添加剂邻近正极活性材料表面的重量百分比。
2、接触角测试:
正极与水的接触角测试
首先将正极烘干,然后在25℃下将去离子水滴加在正极上,用接触角测量仪器测试正极与水的接触角。
正极与电解液的接触角测试
将EC、PC和DEC(重量比1:1:1)混合,加入LiPF6,混合均匀后获得电解液,其中LiPF6浓度为1.5mol/L;将该电解液滴加在正极,用接触角测量仪器测试正极与电解液的接触角。
图3中的左图示出了实施例6中的正极与电解液的接触角测试结果;且图3中的右图示出了实施例6中的正极与水的接触角测试结果。
3、热重质谱联用(TG-MS)测试:
将正极经过碳酸二甲酯溶剂洗涤后,在85℃烘干12h。然后将烘干后的正极在25℃和45%恒湿度静态空气中存储20天。将从正极表面刮下的粉体材料放置于热重坩埚中,通入20ml/min的N2。升温速度为10℃/分钟,升温到170℃,保温60分钟,然后继续升温至300℃,保温60分钟。升温过程中记录失重并且通过质谱检测气体成分,含水量是基于正极的总重量计算得到。
图2中的左图示出了实施例1中的正极在45%恒温恒湿静态空气环境存储20天后TG-MS测试结果;且图2中的右图示出了对比例1中的正极在45%恒温恒湿静态空气环境存储20天后TG-MS结果。
4、扣式电池测试:
将烘干后的双面正极的一面用N-甲基吡咯烷酮(NMP)清洗干净,85℃真空烘烤2h,取出正极冲好2025扣式电池所需的小圆片,按照泡沫镍,锂片,隔离膜,正极圆片,组装成扣式电池,注入50微升的电解液,电解液的组成EC:PC:DEC=1:1:1,且LiPF6的浓度为1.15mol/L。组装好的扣式电池在约2.7至约4.3V截至电压下,在25℃条件下,0.1C电流充放电,测试其克容量。
5、碳酸根(CO3 2-)含量测试:
将正极用0.1mol/L的稀盐酸浸泡,并且加热至120℃,同时通入N2做为载气将产生的气体通入气相色谱(GC),通过GC测试出生成的二氧化碳的含量,通过生成的二氧化碳的量计算出正极中碳酸根的含量,碳酸根含量是基于正极的总重量计算得到。
图4示出了对比例6和实施例15中的正极在45%恒温恒湿静态空气环境中存储时碳酸根含量的变化。
6、电阻测试:
将正极放置在电极电阻仪器上测试。测试条件为:25℃,压力:0.3t,测试面积:3cm2,测试等待10s,记录下正极的电阻。
7、傅里叶转换红外线光谱测试:
将约1mg至约2mg从正极表面刮下的粉体材料与200mg纯KBr混合均匀,研细,置于模具中,用5×107Pa压力在油压机上压成透明薄片,即可用于FTIR测试。
图1中的上图示出了对比例1中锂离子电池化成后,正极的傅里叶转换红外线光谱(FTIR)谱图;且图1中的下图示出了实施例1中锂离子电池化成后,正极的傅里叶转换红外线光谱(FTIR)测试的谱图;。
8、正极烘烤后失水率测试:
将在45%湿度存储20天后的正极放置于真空烘箱中,设置真空度为-90KPa,烘烤温度为85℃,烘烤时间为12h,烘烤后将正极活性材料层刮下,取1g刮下的粉体,放置于卡尔费休水分仪器中测试水含量,失水率为烘烤前后水分差值/初始水分含量。
表2示出了各对比例和实施例的相关性能测试结果。
表2
由以上测试结果可以看出,本申请通过在正极浆料中加入有机硅添加剂,使正极的吸水性以及与空气中二氧化碳的副反应明显降低,并且电阻增长率和容量衰减率均明显降低。
从实施例1和2的测试结果还可以看出,相比于有机含硅添加剂邻近正极活性材料表面的重量百分比为10wt%的正极相比,当有机含硅添加剂邻近正极活性材料表面的重量百分比为30wt%时,正极的吸水性、与空气中二氧化碳的副反应明显降低、电阻增长率和容量衰减率均进一步降低。
三、将正极在25℃和45%湿度的空气下暴露3天后制备成锂离子电池,并对其进行厚度膨胀率和容量保持率测试,其中测试方法如下所示:
A、厚度膨胀率测试方法:
将电池用两个硬质金属片夹紧,用千分尺测试金属板两侧厚度变化。
B、25℃循环容量保持率测试方法:
采用1.5C充电电流,4C放电电流进行测量。
C、45℃循环容量保持率测试方法:采用1.5C充电电流,4C放电电流进行测量。
表3示出了各对比例和实施例中锂离子电池的厚度膨胀率和容量保持率的测试结果。
表3
由以上测试结果可以看出,本申请通过在正极浆料中加入有机硅添加剂,使正极的吸水性以及与空气中二氧化碳的副反应明显降低,从而使由本申请正极制备的锂离子电池的厚度膨胀率明显降低,且容量保持率增加。
从实施例1和2的测试结果还可以看出,相比于有机含硅添加剂邻近正极活性材料表面的重量百分比为10wt%的正极相比,当有机含硅添加剂邻近正极活性材料表面的重量百分比为30wt%时,锂离子电池的厚度膨胀率进一步降低,且容量保持率进一步增加。
整个说明书中对“一些实施例”、“部分实施例”、“一个实施例”、“另一举例”、“举例”、“具体举例”或“部分举例”的引用,其所代表的意思是在本申请中的至少一个实施例或举例包含了该实施例或举例中所描述的特定特征、结构、材料或特性。因此,在整个说明书中的各处所出现的描述,例如:“在一些实施例中”、“在实施例中”、“在一个实施例中”、“在另一个举例中”,“在一个举例中”、“在特定举例中”或“举例“,其不必然是引用本申请中的相同的实施例或示例。此外,本文中的特定特征、结构、材料或特性可以以任何合适的方式在一个或多个实施例或举例中结合。
尽管已经演示和描述了说明性实施例,本领域技术人员应该理解上述实施例不能被解释为对本申请的限制,并且可以在不脱离本申请的精神、原理及范围的情况下对实施例进行改变,替代和修改。
Claims (12)
1.一种电化学装置,其包括正极,所述正极包括正极集流体和正极活性材料层,所述正极活性材料层包含正极活性材料,所述正极经过碳酸二甲酯溶剂洗涤后,在85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在25℃至170℃范围内失重量小于0.3%。
2.根据权利要求1所述的电化学装置,其中所述正极经过碳酸二甲酯溶剂洗涤后,在85℃烘干12h,在25℃和45%恒湿度静态空气中存储20天后,根据热重质谱联用测试,在170℃至300℃范围内失重量小于10%。
3.根据权利要求1所述的电化学装置,其中所述正极活性材料层对水的接触角为100°至160°。
4.根据权利要求1所述的电化学装置,其中所述正极活性材料层对所述电解液的接触角为10°至60°。
5.根据权利要求1所述的电化学装置,其中根据傅里叶转换红外线光谱测试,所述正极活性材料层在900cm-1至1100cm-1范围内具有至少一个吸收峰。
6.根据权利要求1所述的电化学装置,其中所述正极活性材料层包含有机含硅添加剂,所述有机含硅添加剂包括至少一种具有式(R1)m-Si-(R2)n的化合物,其中
R1、R2各自独立地选自取代或未取代的C1-20烷基、取代或未取代的C1-20烯基、取代或未取代的C1-20烷氧基、取代或未取代的Ra-O-Rb-基团、胺基、-OH或其任意组合,
Ra选自取代或未取代的C1-20烷基、取代或未取代的C1-20烯基或其任意组合,
Rb选自取代或未取代的C1-20亚烷基、亚胺基、取代或未取代的C1-20亚烯基或其任意组合,
m=1至3,以及
n=1至3;并且
其中,R1和R2中的至少一个的碳原子数≥5;
取代时,取代基为卤素、含杂原子基团中的至少一种;所述杂原子包括B、N、O、Si、P、S中的至少一种。
7.根据权利要求6所述的电化学装置,其中所述有机含硅添加剂包含CH3(CH2)15Si(OCH3)3、CH3(CH2)10Si(OCH3)3、CH3(CH2)7Si(OCH3)3、CH3(CH2)11Si(OCH3)3、NH2(CH2)2NH(CH2)3Si(OCH3)3、NH2(CH2)2NH(CH2)3Si(OC2H5)3、CH3OCH2CH2O(CH2)3Si(OCH3)3、CH3OCH2CH2O(CH2)3Si(OC2H5)3中的至少一种。
8.根据权利要求6所述的电化学装置,其中基于所述正极活性材料层的总重量,所述有机含硅添加剂的含量为0.08wt%至5wt%。
9.根据权利要求6所述的电化学装置,其中基于所述有机含硅添加剂的总重量,邻近所述正极活性材料表面的有机含硅添加剂的重量百分比为5wt%至50wt%。
10.根据权利要求1所述的电化学装置,其中所述正极活性材料包括至少一种具有式LixNiyCozMnkMqOb-aTa的化合物,其中,M选自由以下组成的群组中的至少一种:B、Mg、Al、Si、P、S、Ti、Cr、Fe、Co、Ni、Cu、Zn、Ga、Y、Zr、Mo、Ag、W、In、Sn、Pb、Sb和Ce,T为卤素,并且x、y、z、k、q、a和b分别满足:0.2<x≤1.2、0<y≤1、0≤z≤1、0≤k≤1、0≤q≤1、1≤b≤2以及0≤a≤1。
11.根据权利要求10所述的电化学装置,其中0.9<x≤1.2、0.6<y≤1、0≤z≤0.3。
12.一种电子装置,其包含根据权利要求1-11中任一项所述的电化学装置。