CN113527917A - 一种电解铝阳极钢爪用防腐防氧化涂层材料及其制备方法 - Google Patents
一种电解铝阳极钢爪用防腐防氧化涂层材料及其制备方法 Download PDFInfo
- Publication number
- CN113527917A CN113527917A CN202110684030.9A CN202110684030A CN113527917A CN 113527917 A CN113527917 A CN 113527917A CN 202110684030 A CN202110684030 A CN 202110684030A CN 113527917 A CN113527917 A CN 113527917A
- Authority
- CN
- China
- Prior art keywords
- coating material
- coating
- aluminum
- electrolytic
- water glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种电解铝阳极钢爪用防腐防氧化涂层材料及其制备方法，其原料按质量百分含量，包括40‑70％α‑Al2O3、0‑30％γ‑Al2O3(优选5‑30％)、2‑7％硅酸铝纤维和20‑30％水玻璃。本发明提供的电解铝阳极钢爪用防腐防氧化涂层材料的原料中最大限度地使用各种氧化铝，只少量含有其它元素，可防止其它元素进入电解液，从而避免对铝制品质量的影响。本发明涂层材料结构致密，可减少腐蚀性气体的渗透量，能明显降低电极的腐蚀速率，抗腐蚀能力强，耐磨性能好。本发明涂层材料的延展性增强，适合高温环境，且在高温环境中使用时不易开裂脱落。
Description
技术领域
本发明涉及电解铝技术领域，特别是涉及一种电解铝阳极钢爪用防腐防氧化涂层材料及其制备方法。
背景技术
现代工业中的电解铝生产主要采用冰晶石-氧化铝融盐电解法，即：以碳素体作为阳极(由于碳素体连接在钢质爪一端,钢质爪的另一端与直流电源连接，因此俗称“阳极钢爪”)，以熔融状态的冰晶石作为电解液，以电解液中溶解的金属铝液作为阴极，向两极通直流电，在950℃-970℃下，在电解槽内两极上进行电化学反应得到金属铝产品。
阳极钢爪中仅有碳素体部分是与电解液接触的，碳素体以上的钢质爪部分直接暴露在电解液液面上方的空气中。由于冰晶石含氟，在电解槽内高达900℃的温度下，会产生以HF、CO2、CO气体为主的高温气体。该高温气体有腐蚀性，与空气中的氧气一起，可导致阳极钢爪严重腐蚀，阳极钢爪的腐蚀产物(主要是铁的氧化物)会进入电解液中，在生产中被引入电解铝产品从而严重影响铝产品的质量。同时，阳极钢爪外表面的碳素体会发生布多尔反应，使得碳素体消耗严重，从而增加了电解铝的生产成本。
目前，电解铝行业以在阳极钢爪上涂饰防护性涂层的方法来减轻以上高温气体的不利影响。例如，现有技术1：公开号为CN106634231A的中国专利申请中公开了一种电解铝预焙阳极防氧化涂料及其制备方法，其中的防氧化涂料由陶瓷基连续相、陶瓷基连续催化相、碱及碱土金属辅助催化相、陶瓷基补强相、稳定相、成膜相、水相在500℃下烧结得到，该防氧化涂料可在阳极钢爪碳素体表面形成一层致密的陶瓷基密封层，可以隔绝二氧化碳、氧气、空气等与碳素体的接触，从而防止碳素体的氧化剥落。然而，该防氧化涂料除了陶瓷基，还需要催化相、补强相、稳定相和成膜相，组分复杂且生产成本较高。
现有技术2：公开号为CN106189600A的中国专利申请中公开了电解铝碳阳极表面抗高温抗氧化涂料及其制备方法，该抗高温抗氧化涂料的原料包括铝溶胶、丙烯酸乳液、硼酸、甘油、氧化铝和水，能够使碳阳极抗高温抗氧化，防止碳阳极的氧化剥落，从而减少碳渣。
现有技术3：公开号为CN102424730A的中国专利申请中公开了电解铝阳极炭块抗氧化涂料及其制备方法，该涂料以硼砂或硼酸，高岭土，工业磷酸，工业硫酸铝和水为原料。
现有技术4：公开号为CN104005056A的中国专利申请中公开了一种电解铝炭阳极保护涂层的制备方法，以CA(铝酸钙)水泥为粘结剂，以电解铝生产中产生的废电解质为耐火骨料，加入外加剂制备得到。
现有技术5：公开号为CN107057412A的中国专利申请公开了一种自固化电解铝用炭阳极高温抗氧化涂料，含羟基磷腈树脂、氧化铝、氢氧化铝、铝粉、硼砂、碳化硼、氧化钙和有机助粘剂。
以上公开的电解铝阳极用防护性涂层的配方都比较复杂，且原料中除含铝元素外，还含有大量其它元素，虽然可保护电极免受腐蚀，但会向电解液中(熔融的冰晶石溶液)引入其它元素，可能会对铝产品的质量产生不利影响(例如引入其它杂质、杂质量增加导致铝产品纯度降低)。
此外，现有技术2-5公开的阳极用防护性涂层配方中均含有有机物(如现有技术2中的丙烯酸乳液、甘油；现有技术5中的羟基磷腈树脂、有机助粘剂)和/或水泥成分(如现有技术3中的高岭土；现有技术4中的粘结剂CA(铝酸钙)水泥)，有机物耐热一般不超过450℃，受热易分解挥发，使涂层中形成孔道而丧失对阳极钢爪的防护功能；水泥是水硬性胶粘剂，高温下会失水而失去强度，即使耐火水泥也不能经受900℃以上的高温，这些胶粘剂和粘结剂高温下会失去强度，使涂层粉化，既不能起到有效保护电极的作用，又进一步劣化铝产品质量。
发明内容
本发明的目的是针对现有技术中存在的技术缺陷，第一方面，提供一种尽可能少地引入其它元素的电解铝阳极钢爪用防腐防氧化涂层材料，其原料按质量百分含量，包括40-70％α-Al2O3、0-30％γ-Al2O3(优选5-30％)、2-7％硅酸铝纤维和20-30％水玻璃。
其原料优选按质量百分含量，包括45-55％α-Al2O3、15-25％γ-Al2O3、3-6％硅酸铝纤维和22-27％水玻璃。
其原料更优选按质量百分含量，包括48-52％α-Al2O3、18-22％γ-Al2O3、4-6％硅酸铝纤维和24-26％水玻璃。
α-Al2O3呈粉末状，粒度150目-325目，优选200目。
γ-Al2O3呈粉末状，粒度≤0.043mm。
硅酸铝纤维的纤维长度≤2mm，纤维横截面直径≤0.03mm，纤维中Al2O3含量＞50％。
水玻璃呈粉末状，粒度≤0.1mm，选自钠水玻璃和/或钾水玻璃，钠水玻璃中Na2O·nSiO2＞95％。选用两种时，钠水玻璃与钾水玻璃的质量比为(3-5)：1。
原料α-Al2O3、γ-Al2O3、硅酸铝纤维和水玻璃的含水量均小于0.3wt％。
第二方面，本发明提供了一种上述防腐防氧化涂层材料的制备方法，按照质量百分含量，对α-Al2O3、γ-Al2O3、硅酸铝纤维和水玻璃称重，然后混合均匀，即得到所述涂层材料。
所述混合均匀具体为：混合后在同一批涂层材料的不同位置取三个样品，分析样品中Al2O3的含量，任意两个样品中的Al2O3含量差值小于0.5％，即为混合均匀。
本发明提供的电解铝阳极钢爪用防腐防氧化涂层材料的原料最大限度地使用各种晶型的氧化铝，将其它元素含量降至最低，以避免其它元素进入电解液(熔融的冰晶石溶液)，从而对铝制品质量产生不利影响。本发明涂层材料在阳极钢爪表面可形成防护性涂层，涂层结构致密，可减少腐蚀性气体的渗透量，能明显降低电极的腐蚀速率，抗腐蚀能力强，耐磨性能好。本发明涂层材料的延展性增强，适合高温环境，在高温下不发生反应和相变，理化性质稳定，使得形成的涂层在高温环境中使用时不易开裂脱落，可使用至少三个周期(25℃常温—900℃高温—25℃常温循环一次为一个周期)。本发明的涂层材料原料均是固体粉末，便于混合均匀，使得制备出的涂层材料成品率高，质量稳定；且原料方便包装和运输。
具体实施方式
由于电解铝阳极钢爪用防腐抗氧化涂层材料用于高温(900℃左右)、含腐蚀性气体(HF、CO、CO2等)的环境中，既需要具有普通涂料的性能(如合适的粘度、附着力和施工性能)，又要具有耐高温抗腐蚀的能力。涂层材料的作用是保护阳极不受腐蚀，以避免阳极受腐蚀产物(氧化铁)进入电解槽的铝液中，影响电解铝产品的纯度和性能。电解液中混入铁元素会使最终得到的铝产品中含有Fe，Fe对铝产品的性能影响很大，例如对其延展性、脆性、化学稳定性、金属本身的色泽等都会产生较大影响，因此在工业铝产品的生产过程中尤其要避免Fe的混入。同时还要避免涂层材料中的元素进入电解槽的铝液中。
本申请从这些要求出发，以尽可能保持Al2O3最高、必要的其它成分不易还原电解为原则，独创设计一个基础配方后，再通过电解槽内环境参数对涂料可能影响的分析判断，对基本配方进行调整，然后在实验室模拟的电解槽环境中，对调整后配方的效果进行反复试验和调整。最终，确定了一种电解铝阳极钢爪用防腐防氧化涂层材料。
考虑到电解铝阳极钢爪用防腐抗氧化涂层材料的另一个重要技术难题是无机涂层材料与金属之间的较大热膨胀系数差，常规的无机非金属材料制成的涂料热膨胀系数约为(5-7)×10-6/℃，远低于金属材料的热膨胀系数(10-20)×10-6/℃。该热膨胀系数差使得涂层材料在高低温区间内会开裂和剥离。因此本发明在确定的涂层材料中还加入了合适的纤维材料，以加大涂层材料的拉伸伸长率；同时，选择塑性较大的粘结剂，使涂层材料具有高温柔软度，以适应金属的热胀冷缩。
本发明提供的电解铝阳极钢爪用防腐防氧化涂层材料，该组配设计中最大限度地以各种晶型的氧化铝产品为原料，并使得涂层材料中的Al2O3含量最大化，避免引入其它元素进入电解液，从而避免其它元素对铝产品质量的影响；同时还确保使用该涂层材料能在阳极钢爪表面形成防护性涂层，涂层能有效保护电极免受腐蚀，避免了阳极钢爪中的铁元素进入电解液，从而提高了铝产品的纯度。
该涂层材料的原料按质量百分含量，包括40-70％α-Al2O3、0-30％γ-Al2O3(优选5-30％)、2-7％硅酸铝纤维、20-30％水玻璃；优选的，包括55-70％α-Al2O3、5-15％γ-Al2O3、3-6％硅酸铝纤维、22-27％水玻璃；更优选的，包括60-65％α-Al2O3、5-10％γ-Al2O3、4-6％硅酸铝纤维、24-26％水玻璃。其中，
用于本发明中的α-Al2O3为粉末状，粒度为150目-325目(优选200目)，粉末中α-Al2O3含量＞95％。α-Al2O3(氧化铝的一种晶型)俗称刚玉，是一种高温煅烧材料，吸水率低且具有较粗的颗粒度，由于α-Al2O3达到一定流动性所需要的水量低(用水少，即吸水率低)，在干燥(如高温烧结)时其收缩量就低，可形成支撑骨架，在形成的涂层中起到支撑作用。同时，α-Al2O3的理化性质十分稳定，且具有较大的硬度(莫氏硬度9)，可提高涂层的抗腐蚀能力和耐磨性。本发明涂层材料配方中最大量地组配氧化铝中的α-Al2O3晶型，至少40wt％，最高可达70wt％。
用于本发明中的γ-Al2O3为粉末状，粒度≤0.043mm，γ-Al2O3含量＞98％，与电解液中的溶质氧化铝是同一物质，是氧化铝的另一种晶型；γ-Al2O3颗粒比较细，宏观表现比较柔软。由于α-Al2O3的粒度较大，直接用来制备涂层，涂层不够致密，使得涂层对阳极钢爪的防护效果不好；因此，本发明涂层材料将γ-Al2O3与α-Al2O3搭配使用，用α-Al2O3来形成涂层的骨架，用粒度更小的γ-Al2O3去填充α-Al2O3形成的骨架，以在阳极钢爪表面形成致密的涂层，减少腐蚀性气体的渗透量，能明显降低电极的腐蚀速率，从而较好地发挥涂层对阳极钢爪的防护作用。本发明涂层材料的原料也可以不含有γ-Al2O3，此种情形需保证α-Al2O3粉末的粒度更小，当然由此会导致α-Al2O3的成本提高。本发明经过试验探索，得到涂层材料原料中γ-Al2O3的质量百分含量在5-30％可同时兼顾涂层的性能和涂层材料的成本。
用于本发明中的硅酸铝纤维作为增强材料，目的是提高涂层抵抗金属热胀冷缩的能力，为纤维状，其纤维长度≤2mm，纤维横截面直径≤0.03mm，纤维中Al2O3含量＞50wt％。涂层材料的应用场合是900℃的高温环境，要保护的对象是内部为金属铁的阳极钢爪，由于金属铁的热膨胀系数高达(10-20)×10-6/℃，而常规无机材料的热膨胀系数不会这么高，因此，在高温环境中使用时，阳极钢爪内的金属铁会膨胀，导致含有无机材料的涂层开裂脱落；本发明在涂层材料的原料中加入的硅酸铝纤维，优选Al2O3含量高，耐高温性能好，纤维粗细长短适合的硅酸铝纤维(如玻璃纤维或陶瓷纤维，优选陶瓷纤维，因为陶瓷纤维在涂层材料中相对容易分散，经过高温后的性能保持率最高)，其能够在本发明的涂层材料中有效分散，将各原料连接成为一体，从而增强涂层材料的延展性，使得形成的涂层不易开裂脱落。
用于本发明中的水玻璃作为无机粘结剂，为粉末状，又称水玻璃粉，粒度≤0.1mm，选自钠水玻璃(硅酸钠)和/或钾水玻璃(硅酸钾)，钠水玻璃为硅酸钠水溶液，分子式为Na2O·nSiO2，硅酸钠中Na2O·nSiO2＞95％，耐高温性能好，涂层材料使用时其作为粘结剂，适合高温环境。钾水玻璃为硅酸钾水溶液，分子式为K2O·nSiO2，硅酸钾中K2O·nSiO2＞95％。当水玻璃选自钠水玻璃和钾水玻璃时，钠水玻璃与钾水玻璃的质量比为(3-5)：1(优选4:1)。由于水玻璃中的硅酸钠遇到电解质时，非常容易产生破胶，造成涂料分层沉淀，甚至失去固结能力，因此用增稠剂调节水玻璃黏度时，会因存在高价离子而导致水玻璃破胶的情况(如：膨润土作为增稠剂和γ-Al2O3等容易电离出高价离子，凹凸棒土作为增稠剂含有钙离子，导致水玻璃破胶)，适量硅酸钾与硅酸钠复配使用会使涂层材料高温下粘度增大。水玻璃在高温下可形成玻璃软化层，使得涂层具有可塑性和变形能力，与增强材料硅酸铝纤维配合使用，可使涂层具有适应金属大膨胀系数的能力，升温时不胀裂；降温时玻璃软化层紧跟钢材收缩，并逐步硬化，使涂层不剥落。
在此基础上，本发明还提供了制备上述电解铝阳极钢爪用防腐防氧化涂层材料的方法，将上述涂层材料中的各原料按照质量百分含量称重，混合均匀，即得到本发明的涂层材料，防潮密封包装备用。为保证混合的均匀性，混合后在同一批生产的涂层材料的不同位置(如不同深度，不同点)取3个样品，化验样品中Al2O3的含量，任意两个样品中的Al2O3含量差值小于0.5％，即为混合均匀。由于本发明的涂层材料中含有硅酸钠或硅酸钾成分，因此，所有原料的含水量要小于0.3wt％。
使用时，将本发明的涂层材料加水搅拌混合，水的质量为涂层材料质量的30％-50％(优选30％-40％)，刮涂或喷涂在电极(钢爪和碳块)上即形成电解铝阳极钢爪用防腐防氧化涂层。
以下结合具体实施例，更具体地说明本发明的内容，并对本发明作进一步阐述，但这些实施例绝非对本发明进行限制。
本发明涂层材料中使用的原料均为市售商品。
实施例1
本实施例涂层材料的原料按质量百分含量，包括50％α-Al2O3、20％γ-Al2O3、5％硅酸铝纤维、25％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样1，加涂层材料试样1质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝。
对比样为没有任何涂层的阳极钢爪，安装到电解槽中进行电解铝。
在涂饰涂层材料试样1的电解槽中取电解铝样，作为试验样品Ⅰ，在安装对比样的电解槽中取电解铝样，作为对比样品。
分析试验样品Ⅰ和对比样品两个电解铝产品中的Fe2O3含量和杂质总量，结果表明：试验样品Ⅰ中Fe2O3比对比样品中降低55％，试验样品Ⅰ中杂质总量比对比样品中降低25％。由于Fe2O3含量和杂质总量会受涂层外的其他因素影响(如原料本身就含有Fe2O3，且不同批次原料中Fe2O3的含量不同)，因此以相对降低量作为评价参数，实验过程请参考实施例4的描述，检测数据已换算为前述相对降低量。
实施例2
本实施例涂层材料的原料按质量百分含量，包括65％α-Al2O3、5％γ-Al2O3、7％硅酸铝纤维、23％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样2，加涂层材料试样2质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝。
对比样同实施例1。
在涂饰涂层材料试样2的电解槽中取电解铝样，作为试验样品Ⅱ，在安装对比样的电解槽中取电解铝样，作为对比样品。
分析试验样品Ⅱ和对比样品两个电解铝产品中的Fe2O3含量和杂质总量，结果表明：试验样品Ⅱ中Fe2O3比对比样品中降低45％，试验样品Ⅱ中杂质总量比对比样品中降低25％(实验过程请参考实施例4的描述，检测数据已换算为相对降低量)。
实施例3
本实施例涂层材料的原料按质量百分含量，包括40％α-Al2O3、30％γ-Al2O3、7％硅酸铝纤维、23％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样3，加涂层材料试样3质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝。
对比样同实施例1。
在涂饰涂层材料试样3的电解槽中取电解铝样，作为试验样品Ⅲ，在安装对比样的电解槽中取电解铝样，作为对比样品。
分析试验样品Ⅲ和对比样品两个电解铝产品中的Fe2O3含量和杂质总量，结果表明：试验样品Ⅲ中Fe2O3比对比样品中降低43％，试验样品Ⅲ中杂质总量比对比样品中降低20％(实验过程请参考实施例4的描述，检测数据已换算为相对降低量)。
实施例4
本实施例涂层材料的原料按质量百分含量，包括63％α-Al2O3、7％γ-Al2O3、5％硅酸铝纤维、20％硅酸钠、5％硅酸钾。
按以上含量称取原料，混合均匀后，生产出涂层材料试样4，加涂层材料试样4质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝。
对比样同实施例1。
在涂饰涂层材料试样4的电解槽中取电解铝样，作为试验样品Ⅳ，在安装对比样的电解槽中取电解铝样，作为对比样品。
分析试验样品Ⅳ和对比样品两个电解铝产品中的Fe2O3含量和杂质总量，结果试验样品Ⅳ中Fe2O3比对比样品中平均降低42％，杂质总量比对比样品中平均降低30％。实验过程如下：
实验方法：检测涂层材料中的各元素含量；然后将涂层材料涂饰于阳极钢爪上形成涂层，钢爪安装到电解槽中进行电解铝生产；最后取电解铝样分析电解铝产品中的各元素含量。
实验结果：对实施例4的涂层材料进行了6个平行样本(见表1中的样本4-1至样本4-6)的元素含量检测，涂层材料中的各元素含量见表1。
表1实施例4涂层材料的各元素含量(％)
| 样本 | Al<sub>2</sub>O<sub>3</sub> | Fe<sub>2</sub>O<sub>3</sub> | SiO<sub>2</sub> | K<sub>2</sub>O | Na<sub>2</sub>O |
| 样本4-1 | 72.50 | 0.066 | 20.46 | 1.51 | 4.89 |
| 样本4-2 | 73.12 | 0.057 | 19.89 | 1.49 | 4.91 |
| 样本4-3 | 72.48 | 0.070 | 20.25 | 3.01 | 3.74 |
| 样本4-4 | 72.45 | 0.056 | 20.33 | 2.69 | 3.81 |
| 样本4-5 | 72.49 | 0.064 | 20.29 | 1.48 | 4.99 |
| 样本4-6 | 72.43 | 0.061 | 20.73 | 1.49 | 3.92 |
表1可以看出实施例4的涂层材料中氧化铝含量较高且其它元素种类尽可能少、含量尽可能低，以保证钢爪氧化铁不进入电解铝液的同时，涂层材料中的元素也尽可能少的进入电解铝液中，即便有少量涂层材料的成分进入电解铝液中，也不会严重污染电解铝产品。
选取若干电解铝生产企业的若干电解槽，每个电解槽中选取两个规格参数均相同的阳极钢爪，将样本4-1的涂层材料分别涂饰于每个电解槽中的其中一个阳极钢爪上(编号分别“后-01”至“后-10”)，每个电解槽中另一个未涂饰的阳极钢爪编号分别“前-01”至“前-10”；用以上阳极钢爪生产电解铝，得到的电解铝产品中各元素含量见表2。
表2电解铝产品中各元素含量(％)
| 钢爪编号 | Fe | Si | K | Na | Al | 杂质总量 |
| 前-01 | 0.21 | 0.09 | 0.0021 | 0.0015 | 99.67 | 0.33 |
| 后-01 | 0.095 | 0.12 | 0.0020 | 0.0017 | 99.76 | 0.24 |
| 前-02 | 0.20 | 0.08 | 0.0012 | 0.0015 | 99.68 | 0.32 |
| 后-02 | 0.11 | 0.09 | 0.0013 | 0.0014 | 99.77 | 0.23 |
| 前-03 | 0.11 | 0.08 | 0.0011 | 0.0010 | 99.77 | 0.23 |
| 后-03 | 0.063 | 0.08 | 0.0010 | 0.0011 | 99.85 | 0.15 |
| 前-04 | 0.10 | 0.08 | 0.0012 | 0.0011 | 99.76 | 0.24 |
| 后-04 | 0.060 | 0.09 | 0.0013 | 0.0012 | 99.83 | 0.17 |
| 前-05 | 0.23 | 0.08 | 0.0011 | 0.0010 | 99.64 | 0.36 |
| 后-05 | 0.13 | 0.09 | 0.0013 | 0.0011 | 99.74 | 0.26 |
| 前-06 | 0.20 | 0.09 | 0.0012 | 0.0013 | 99.69 | 0.31 |
| 后-06 | 0.13 | 0.10 | 0.0015 | 0.0016 | 99.77 | 0.23 |
| 前-07 | 0.22 | 0.07 | 0.0011 | 0.0015 | 99.62 | 0.38 |
| 后-07 | 0.13 | 0.09 | 0.0012 | 0.0015 | 99.74 | 0.26 |
| 前-08 | 0.19 | 0.08 | 0.0012 | 0.0011 | 99.68 | 0.32 |
| 后-08 | 0.10 | 0.07 | 0.0011 | 0.0014 | 99.78 | 0.22 |
| 前-09 | 0.10 | 0.06 | 0.0013 | 0.0016 | 99.77 | 0.23 |
| 后-09 | 0.071 | 0.06 | 0.0011 | 0.0016 | 99.85 | 0.15 |
| 前-10 | 0.11 | 0.06 | 0.0010 | 0.0014 | 99.76 | 0.24 |
| 后-10 | 0.066 | 0.06 | 0.0011 | 0.0012 | 99.83 | 0.17 |
表2可以看出：电解铝产品中铝的含量，使用实施例4涂层材料(标示“后”)的实验样品均高于没有涂层(标示“前”)的对比样品，Al的含量在99.74％以上；实验样品中Fe的含量较对比样品有大幅下降，最高下降了55％(如01号钢爪)，绝对含量不超过0.13％；总杂质含量(按100％-Al％计算)实验样品不高于0.26％，较对比样品也有大幅下降，最高下降了35％(如03号和09号钢爪)。
涂料性能检测：
用已有建筑涂料的检测方法对实施例1-4的涂层材料进行参数的检测，用于评价其作为涂料性能是否合格。其中，耐洗刷性能按GB/T 9266中3.1和5.2规定的洗刷试验机和试验操作程序进行；表干时间性能按GB/T 1728中乙法的规定进行；初期干燥抗裂性按GB/T9779中5.6规定的方法进行；粘结强度性能按GB/T 9779-2005中5.7规定的方法进行；水蒸气透过率按JG/T 309中7.2规定的方法进行。以上这些检测结果表明，实施例1-4的涂层材料作为涂料，耐洗刷、表干时间、初期干燥抗裂性、粘结强度、水蒸气透过率这些性能均符合对应标准中的规定。
比较例1
涂层材料的原料按质量百分含量，包括75％α-Al2O3、5％γ-Al2O3、7％硅酸铝纤维、13％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样4，加涂层材料试样4质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，其他物体触碰涂层就会有粉末掉落，即粉化现象严重，无法进行电解铝。
比较例2
涂层材料的原料按质量百分含量，包括30％α-Al2O3、40％γ-Al2O3、5％硅酸铝纤维、25％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样5，加涂层材料试样5质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，得到的涂层出现收缩开裂现象，无法进行电解铝。
比较例3
涂层材料的原料按质量百分含量，包括40％α-Al2O3、35％γ-Al2O3、5％硅酸铝纤维、20％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样6，加涂层材料试样6质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，得到的涂层出现开裂现象，无法进行电解铝。
比较例4
涂层材料的原料按质量百分含量，包括42％α-Al2O3、30％γ-Al2O3、1％硅酸铝纤维、27％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样7，加涂层材料试样7质量45wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝，电解过程中涂层在高温下开裂脱落。
比较例5
涂层材料的原料按质量百分含量，包括40％α-Al2O3、30％γ-Al2O3、10％硅酸铝纤维、20％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样8，加涂层材料试样8质量45wt％的室温自来水，机械搅拌5分钟，各原料不能均匀分散，无法进行后续的刮涂或喷涂。
比较例6
涂层材料的原料按质量百分含量，包括48％α-Al2O3、30％γ-Al2O3、7％硅酸铝纤维、15％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样9，加涂层材料试样9质量45wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，其他物体触碰涂层就会有粉末掉落，即粉化现象严重。
比较例7
涂层材料的原料按质量百分含量，包括35％α-Al2O3、25％γ-Al2O3、7％硅酸铝纤维、35％硅酸钠。
按以上含量称取原料，混合均匀后，生产出涂层材料试样10，加涂层材料试样10质量45wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝。
按照实施例3中的试验，涂层材料试样10得到的电解铝样中杂质总量比实施例3得到的试验样品Ⅲ中的增加2.5％。
比较例8
涂层材料的原料按质量百分含量，包括50％α-Al2O3、20％γ-Al2O3、5％硅酸铝纤维、25％耐火水泥。
按以上含量称取原料，混合均匀后，生产出涂层材料试样11，加涂层材料试样11质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝。
耐火水泥为常用的无机粘结剂，主要用于无定形耐火材料，常在窑炉修复中(如配制耐火砂浆喷涂于窑炉)使用。本比较例用耐火水泥替换水玻璃作为涂层材料中的粘结剂，在阳极钢爪上形成涂层后用于电解铝时，涂层会粉化，主要原因是耐火水泥300℃左右脱水，在电解铝生产的温度(900℃)环境中脱水粉化。
比较例9
涂层材料的原料按质量百分含量，包括50％α-Al2O3、15％γ-Al2O3、5％硅酸铝纤维、30％磷酸二氢铝。
按以上含量称取原料，混合均匀后，生产出涂层材料试样12，加涂层材料试样12质量33wt％的室温自来水，机械搅拌5分钟，采用刮涂方式(也可以采用喷涂)在电解铝阳极上均匀涂饰1mm以上，自然干燥12h后，在阳极钢爪上形成涂层，安装到电解槽中进行电解铝。
磷酸二氢铝是常用的高温粘结剂，广泛用于耐火材料的修补。本比较例用磷酸二氢铝替换水玻璃作为涂层材料中的粘结剂。磷酸二氢铝作为粘结剂，高温性能非常突出，耐温高于水玻璃，但与水玻璃不同的是，磷酸二氢铝在失水后是结晶体，涂层刚性强，难以适应钢质材料在高温时较大的热膨胀率，从而制得的涂层在电解过程的高温下易开裂脱落，不可能反复使用。
实施例与比较例8-9相比可知，水玻璃是相对理想的粘结剂。水玻璃是非结晶体，没有固定的熔点，在电解过程的高温下是一个高温软化的过程，该软化过程有利于匹配钢的大膨胀系数，从而保持涂层的完整。
本发明涂层材料的各原料含量并不是相互独立的，而是相辅相成的；如α-Al2O3的含量过低，就意味着其他原料的含量要增加，比如，提高γ-Al2O3的含量以弥补α-Al2O3的含量降低，由于γ-Al2O3的粒度较细，含量过高会导致形成的涂层容易开裂；或是提高硅酸铝纤维的含量以弥补α-Al2O3的含量降低，硅酸铝纤维含量过高，纤维会导致其它原料无法均匀分散，而无法形成均匀的涂层材料；又或是提高硅酸钠的含量以弥补α-Al2O3的含量降低，由于硅酸钠是一种可溶于水的硅酸盐，涂层材料中硅酸钠含量过高，加水制备涂层时，得到的涂层流动性增大，在阳极钢爪上流淌，无法粘附在阳极钢爪上，从而无法在阳极钢爪上形成均匀的涂层。如果α-Al2O3的含量过高，其他原料的含量就要减少，比如，减少γ-Al2O3的含量，就需要α-Al2O3的粒度减小，而α-Al2O3硬度较高，研磨难度和成本非常高，无法适应工业化生产；或是减少硅酸铝纤维的含量，制备得到的涂层延展性较差，在高温下使用时无法适应阳极钢爪内部金属铁的遇热膨胀而开裂脱落；又或是减少硅酸钠的含量，硅酸钠作为粘结剂，含量过少制备得到的涂层掉粉现象严重，无法发挥其对阳极钢爪的防护作用。同样的，其它原料含量增加或减少，导致α-Al2O3的含量过低或过高，会使得制备得到的涂层容易开裂或者出现掉粉现象。
综上可见，本发明的涂层材料使用过程中有良好的施工性能、优良的粘附能力、突出的高温性能；该涂层材料应用于电解铝生产中，相比不使用该涂层材料，电解铝产品中Fe含量下降了40％以上，总杂质含量降低了20％以上，使铝产品品质提高了一个牌号，售价可以提高30-50元/吨。以企业年产50万吨铝计算，铝产品售价提高30-50元/吨，增收可达1500-2500万元/年；使用本发明涂层材料后还可节省阳极维护费386万元/年，带来显著的经济效益。
以上所述仅是本发明的优选实施方式，应当指出的是，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的内容。
Claims (10)
1.一种电解铝阳极钢爪用防腐防氧化涂层材料，其原料按质量百分含量，包括40-70％α-Al2O3、0-30％γ-Al2O3(优选5-30％)、2-7％硅酸铝纤维和20-30％水玻璃。
2.根据权利要求1所述涂层材料，其特征在于，其原料优选按质量百分含量，包括45-55％α-Al2O3、15-25％γ-Al2O3、3-6％硅酸铝纤维和22-27％水玻璃。
3.根据权利要求1所述涂层材料，其特征在于，其原料更优选按质量百分含量，包括48-52％α-Al2O3、18-22％γ-Al2O3、4-6％硅酸铝纤维和24-26％水玻璃。
4.根据权利要求1-3任一所述涂层材料，其特征在于，α-Al2O3呈粉末状，粒度150目-325目，优选200目。
5.根据权利要求1-4任一所述涂层材料，其特征在于，γ-Al2O3呈粉末状，粒度≤0.043mm。
6.根据权利要求1-5任一所述涂层材料，其特征在于，硅酸铝纤维的纤维长度≤2mm，纤维横截面直径≤0.03mm，纤维中Al2O3含量＞50％。
7.根据权利要求1-6任一所述涂层材料，其特征在于，水玻璃呈粉末状，粒度≤0.1mm，选自钠水玻璃和/或钾水玻璃，钠水玻璃中Na2O·nSiO2＞95％。
8.根据权利要求7所述涂层材料，其特征在于，钠水玻璃与钾水玻璃的质量比为(3-5)：1。
9.根据权利要求1-8任一所述涂层材料，其特征在于，α-Al2O3、γ-Al2O3、硅酸铝纤维和水玻璃的含水量均小于0.3wt％。
10.一种制备权利要求1-9任一所述涂层材料的方法，其特征在于，按照质量百分含量，对α-Al2O3、γ-Al2O3、硅酸铝纤维和水玻璃称重，然后混合均匀，即得到所述涂层材料。